CN103112112A - 一种轻质防火复合保温板的制备工艺 - Google Patents
一种轻质防火复合保温板的制备工艺 Download PDFInfo
- Publication number
- CN103112112A CN103112112A CN2013100306775A CN201310030677A CN103112112A CN 103112112 A CN103112112 A CN 103112112A CN 2013100306775 A CN2013100306775 A CN 2013100306775A CN 201310030677 A CN201310030677 A CN 201310030677A CN 103112112 A CN103112112 A CN 103112112A
- Authority
- CN
- China
- Prior art keywords
- composite insulation
- preparation process
- minutes
- parts
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种轻质防火复合保温板的制备工艺,其包括如下步骤:将改性酚醛树脂23-25份、乳化剂0.7-0.9份、固化剂2-3份乳化3-4分钟;加入发泡粉1-1.5份、发泡剂5-6份,高速搅拌1-2分钟;加入聚苯颗粒10-12份搅拌1-2分钟;将上述物料加入模具中,压好上盖,烘干10-15分钟,拆模即成轻质防火复合保温板。本制备工艺简单,设备投入少,容易操作,省工、省时,降低了生产成本,节省能源消耗。
Description
技术领域
本发明涉及保温材料领域,尤其涉及一种轻质防火复合保温板的制备工艺。背景技术
根据社会发展需要,建筑节能逐渐得到重视,国家对建筑物节能指标有强制性要求。在建筑物的地面、内墙、外墙加设保温材料是建筑节能的主要手段,目前常用的建筑保温材料具有多种类型,如聚氨脂发泡板、聚苯板、聚苯颗粒保温板、酚醛树脂板、发泡水泥保温板等,这些保温材料在保温性能、防火性、防水性、强度、重量、成本、寿命、工艺及施工难度等方面各具优缺点,适用范围狭隘,难以兼顾新型建筑对保温、阻燃、防水及寿命等各方面的要求。
发明内容
本发明的目的在于提供一种轻质防火复合保温板的制备方法,通过该方法制备的轻质防火复合保温板,具有强度高,保温性好,阻燃性、防水性等各项指标理想等特点。
为实现上述技术目的,本发明采用以下技术方案:一种轻质防火复合保温板的制备工艺,包括如下步骤:将改性酚醛树脂23-25份、乳化剂0.7-0.9份、固化剂2-3份,用混料机乳化3-4分钟;将乳化的浆体投入高速搅拌机内,加入发泡粉1-1.5份、发泡剂5-6份,高速搅拌1-2分钟至均匀;加入聚苯颗粒10-12份,在容器中搅拌1-2分钟;将上述物料加入模具中,压好上盖,烘干10-15分钟,待模具温度达到50℃-60℃,拆模即成轻质防火复合保温板。
本发明具有以下有益效果:本制备工艺简单,设备投入少,容易操作,省工、省时,降低了生产成本,节省能源消耗。采用该工艺制备的保温板,因为聚苯颗粒周围包覆有改性酚醛树脂发泡浆体,对聚苯颗粒起到隔离作用,提高了保温板的阻燃性;另外,其具有密度小,强度高,保温性佳,易于施工等优点,可广泛应用于建筑、装饰、地暖等领域。
具体实施方式
实施例一
将改性酚醛树脂23kg、乳化剂0.7kg、固化剂2kg,用混料机乳化3.5分钟;将乳化的浆体投入高速搅拌机内,加入发泡粉1kg、发泡剂5kg,高速搅拌2分钟至均匀;加入聚苯颗粒10kg,在容器中搅拌1分钟;将上述物料加入1000mm×2000mm×50mm模具中,压好上盖,烘干10分钟,待模具温度达到55℃,拆模即成轻质防火复合保温板。
实施例二
将改性酚醛树脂25kg、乳化剂0.9kg、固化剂3kg,用混料机乳化4分钟;将乳化的浆体投入高速搅拌机内,加入发泡粉1.5kg、发泡剂6kg,高速搅拌1分钟至均匀;加入聚苯颗粒12kg,在容器中搅拌2分钟;将上述物料加入1000mm×2000mm×50mm模具中,压好上盖,烘干15分钟,待模具温度达到60℃,拆模即成轻质防火复合保温板。
实施例3
将改性酚醛树脂24kg、乳化剂0.8kg、固化剂2.5kg,用混料机乳化3分钟;将乳化的浆体投入高速搅拌机内,加入发泡粉1.5kg、发泡剂6kg,高速搅拌1.5分钟至均匀;加入聚苯颗粒12kg,在容器中搅拌1.5分钟;将上述物料加入1000mm×2000mm×50mm模具中,压好上盖,烘干13分钟,待模具温度达到50℃,拆模即成轻质防火复合保温板。
Claims (1)
1.一种轻质防火复合保温板的制备工艺,其特征在于,其包括如下步骤:将改性酚醛树脂23-25份、乳化剂0.7-0.9份、固化剂2-3份,用混料机乳化3-4分钟;将乳化的浆体投入高速搅拌机内,加入发泡粉1-1.5份、发泡剂5-6份,高速搅拌1-2分钟至均匀;加入聚苯颗粒10-12份,在容器中搅拌1-2分钟;将上述物料加入模具中,压好上盖,烘干10-15分钟,待模具温度达到50℃-60℃,拆模即成轻质防火复合保温板。