CN103102766B - 一种高附着力水性玻璃漆及其制备方法 - Google Patents

一种高附着力水性玻璃漆及其制备方法 Download PDF

Info

Publication number
CN103102766B
CN103102766B CN201210452271.1A CN201210452271A CN103102766B CN 103102766 B CN103102766 B CN 103102766B CN 201210452271 A CN201210452271 A CN 201210452271A CN 103102766 B CN103102766 B CN 103102766B
Authority
CN
China
Prior art keywords
aqueous
water
infusorial earth
paint
modification infusorial
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210452271.1A
Other languages
English (en)
Other versions
CN103102766A (zh
Inventor
吴协静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI KEMUBAI WATER-BASED MATERIAL Co Ltd
Original Assignee
HEFEI KEMUBAI WATER-BASED MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI KEMUBAI WATER-BASED MATERIAL Co Ltd filed Critical HEFEI KEMUBAI WATER-BASED MATERIAL Co Ltd
Priority to CN201210452271.1A priority Critical patent/CN103102766B/zh
Publication of CN103102766A publication Critical patent/CN103102766A/zh
Application granted granted Critical
Publication of CN103102766B publication Critical patent/CN103102766B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高附着力水性玻璃漆及其制备方法，它是由下述重量份的原料组成：水性环氧树脂乳液55-65、水性氨基树脂8-10、二丙二醇丁醚1-3、纯水10-15、分散剂F-501？0.4-0.6、消泡剂X-401？0.2-0.4、润湿剂gsk-588？0.2-0.6、纳米碳粉0.3-0.5、附着力促进剂BOK-M-210？0.2-0.4、流平剂0.3-0.5、改性硅藻土0.3-0.6、柠檬酸三丁酯？0.8-1.2、硬酯酸单甘油酯0.08-1；本发明生产的水性玻璃漆无气泡、不结块、无异物、无沉淀分层现象、可以用水无限稀释、能减低成本、环保、漆膜有很强的内聚力和粘附力，在常温下耐磨性强，加入的改性硅藻土作为增稠剂，增强了漆膜的附着力，加入的水性硅烷偶联剂和附着力促进剂进一步增强了漆膜的粘附力。

Description

一种高附着力水性玻璃漆及其制备方法
技术领域
本发明主要涉及一种漆及其制备方法，尤其涉及一种高附着力水性玻璃漆及其制备方法。
背景技术
作为一种功能性、环保型水性涂料，水性玻璃漆具有装饰效果明显漆膜色彩绚丽、易于清洗等优点，广泛应用于灯具、酒杯、花瓶、酒瓶、风灯、烛台、玻璃装饰用品等，然而水性玻璃漆因其溶剂的渗透性弱，水性漆对玻璃的润湿性差，基材表面的光洁度高等缘故，导致水性漆难以在玻璃器材上产生良好的附着，严重妨碍了玻璃漆的发展，目前水性玻璃漆的种类主要有聚氨酯水分散体系、水溶性聚丙烯酸树脂型、丙烯酸酯改性聚氨酯型、存在的主要问题是附着力差、耐化学品性差、耐溶剂性不良、耐水煮性差。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种高附着力水性玻璃漆及其制备方法。
本发明是通过以下技术方案实现的：
一种高附着力水性玻璃漆，它是由下述重量份的原料组成：
水性环氧树脂乳液55-65、水性氨基树脂8-10、二丙二醇丁醚1-3、纯水10-15、分散剂F-501（广州市鑫瑞化工）0.4-0.6、消泡剂X-401（广州市鑫瑞化工）0.2-0.4、润湿剂gsk-588（深圳高斯印刷材料公司）0.2-0.6、纳米碳粉0.3-0.5、附着力促进剂BOK-M-210（广州市鑫瑞化工）0.2-0.4、流平剂0.3-0.5、改性硅藻土0.3-0.6、柠檬酸三丁酯0.8-1.2、硬酯酸单甘油酯0.08-0.1；
所述的改性硅藻土的制备方法为：
硅藻土用10-15%盐酸浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干；
将部分物料溶于水中，再加入硅藻土重量2-3%的马来酸二辛酯、1-2%的平平加O、2-3%的柠檬酸三丁酯、3-5%纳米碳粉，高速1200-1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即为所述改性硅藻土。
一种高附着力水性玻璃漆的制备方法，包括以下步骤：
（1）将上述重量份的水性氨基树脂与其质量0.1-0.2%的锌粉、0.3-0.5%的环氧四氢邻苯二甲酸二辛酯、0.08-0.1%的纳米陶土，混合加入反应缸中，在400-500转/分的条件下，搅拌混合3-4分钟；
（2）加入上述重量份的水性环氧树脂乳液、硬酯酸单甘油酯在500-600转/分的条件下，均匀搅拌8-12分钟；
（3）加入上述重量份的二丙二醇丁醚、纯水、分散剂F-501、消泡剂X-401，在1000-1300转/分的条件下，均匀搅拌8-12分钟；
（4）加入上述重量份的润湿剂gsk-588、纳米碳粉、附着力促进剂BOK-M-210、流平剂、柠檬酸三丁酯，在500-800转/分的条件下，均匀搅拌25-35分钟；
（5）加入上述重量份的改性硅藻土，搅拌均匀，即得到所述水性玻璃漆。
具体实施方式
实施例1
一种高附着力水性玻璃漆，它是由下述重量份的原料组成：
水性环氧树脂乳液65、水性氨基树脂10、二丙二醇丁醚3、纯水15、分散剂F-501（广州市鑫瑞化工）0.6、消泡剂X-401（广州市鑫瑞化工）0.4、润湿剂gsk-588（深圳高斯印刷材料公司）0.6、纳米碳粉0.5、附着力促进剂BOK-M-210（广州市鑫瑞化工）0.4、流平剂0.5、改性硅藻土0.6、柠檬酸三丁酯1.2、硬酯酸单甘油酯0.08；
所述的改性硅藻土的制备方法为：
硅藻土用15%盐酸浸泡4小时，去离子水洗涤，再用12%氢氧化钠溶液浸泡4小时，再用去离子水洗涤至中性，烘干；
将部分物料溶于水中，再加入硅藻土重量3%的马来酸二辛酯、2%的平平加O、3%的柠檬酸三丁酯、5%纳米碳粉，高速1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即为所述改性硅藻土。
一种高附着力水性玻璃漆的制备方法，包括以下步骤：
（1）将上述重量份的水性氨基树脂与其质量0.2%的锌粉、0.5%的环氧四氢邻苯二甲酸二辛酯、0.081%的纳米陶土，混合加入反应缸中，在500转/分的条件下，搅拌混合3-4分钟；
（2）加入上述重量份的水性环氧树脂乳液、硬酯酸单甘油酯在500-600转/分的条件下，均匀搅拌8-12分钟；
（3）加入上述重量份的二丙二醇丁醚、纯水、分散剂F-501、消泡剂X-401，在1000-1300转/分的条件下，均匀搅拌12分钟；
（4）加入上述重量份的润湿剂gsk-588、纳米碳粉、附着力促进剂BOK-M-210、流平剂、柠檬酸三丁酯，在800转/分的条件下，均匀搅拌35分钟；
（5）加入上述重量份的改性硅藻土，搅拌均匀，即得到所述水性玻璃漆。
性能测试：
固化后，漆膜硬度为2H、喷涂于玻璃上透光率为95%；用蘸有清水的纱布擦拭涂层2分钟，涂层完整不脱落，说明其在常温下耐磨性、附着力好；将漆喷在平板玻璃上，待漆膜固化后放入装有UV-B的紫外灯箱中，按照GB/T14522-93进行实验，选择4小时黑暗，4小时光照的条件下实验4天，漆膜的黄变?E≤6，不起泡，保持了一定附着力。

Claims (1)

1.一种高附着力水性玻璃漆，其特征在于它是由下述重量份的原料组成：水性环氧树脂乳液55-65、水性氨基树脂8-10、二丙二醇丁醚1-3、纯水10-15、分散剂F-5010.4-0.6、消泡剂X-4010.2-0.4、润湿剂gsk-5880.2-0.6、氧化铝0.3-0.5、附着力促进剂BOK-M-2100.2-0.4、流平剂0.3-0.5、改性硅藻土0.3-0.6、柠檬酸三丁酯0.8-1.2、硬脂酸单甘油酯0.08-0.1；
所述的改性硅藻土的制备方法为：硅藻土用10-15%盐酸浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干；将部分物料溶于水中，再加入硅藻土重量2-3%的马来酸二辛酯、1-2%的平平加O、2-3%的柠檬酸三丁酯、3-5%纳米碳粉，高速1200-1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即为所述改性硅藻土。
CN201210452271.1A 2012-11-13 2012-11-13 一种高附着力水性玻璃漆及其制备方法 Expired - Fee Related CN103102766B (zh)