CN103102764A - 一种高耐磨水性玻璃漆及其制备方法 - Google Patents

一种高耐磨水性玻璃漆及其制备方法 Download PDF

Info

Publication number
CN103102764A
CN103102764A CN2012104526977A CN201210452697A CN103102764A CN 103102764 A CN103102764 A CN 103102764A CN 2012104526977 A CN2012104526977 A CN 2012104526977A CN 201210452697 A CN201210452697 A CN 201210452697A CN 103102764 A CN103102764 A CN 103102764A
Authority
CN
China
Prior art keywords
water
paint
weight part
mentioned weight
rev
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104526977A
Other languages
English (en)
Other versions
CN103102764B (zh
Inventor
吴协静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI KEMUBAI WATER-BASED MATERIAL Co Ltd
Original Assignee
HEFEI KEMUBAI WATER-BASED MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI KEMUBAI WATER-BASED MATERIAL Co Ltd filed Critical HEFEI KEMUBAI WATER-BASED MATERIAL Co Ltd
Priority to CN201210452697.7A priority Critical patent/CN103102764B/zh
Publication of CN103102764A publication Critical patent/CN103102764A/zh
Application granted granted Critical
Publication of CN103102764B publication Critical patent/CN103102764B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高耐磨水性玻璃漆及其制备方法，它是由下述重量份的原料组成：水性氨基树脂889055-65、水性氨基树脂88908-10、二丙二醇丁醚1-3、纯水10-15、古尔胶0.4-0.6、二甲基硅油0.2-0.4、琥珀酸二异辛酯磺酸钠0.2-0.6、氧化铝0.3-0.5、N-叔丁基-2-苯骈噻唑次磺酰胺0.2-0.4、流平剂0.3-0.5、改性硅藻土0.3-0.6、环氧硬脂酸辛酯0.8-1.2；本发明生产的水性玻璃漆无气泡、不结块、无异物、无沉淀分层现象、可以用水无限稀释、能减低成本、环保、漆膜有很强的内聚力和粘附力，在常温下耐磨性强，加入的改性硅藻土作为增稠剂，增强了漆膜的附着力，加入的环氧硬脂酸辛酯进一步增强了漆膜的粘附力。

Description

一种高耐磨水性玻璃漆及其制备方法
技术领域
本发明主要涉及一种漆及其制备方法，尤其涉及一种高耐磨水性玻璃漆及其制备方法。
背景技术
作为一种功能性、环保型水性涂料，水性玻璃漆具有装饰效果明显漆膜色彩绚丽、易于清洗等优点，广泛应用于灯具、酒杯、花瓶、酒瓶、风灯、烛台、玻璃装饰用品等，然而水性玻璃漆因其溶剂的渗透性弱，水性漆对玻璃的润湿性差，基材表面的光洁度高等缘故，导致水性漆难以在玻璃器材上产生良好的附着，严重妨碍了玻璃漆的发展，目前水性玻璃漆的种类主要有聚氨酯水分散体系、水溶性聚丙烯酸树脂型、丙烯酸酯改性聚氨酯型、存在的主要问题是附着力差、耐化学品性差、耐溶剂性不良、耐水煮性差。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种高耐磨水性玻璃漆及其制备方法。
本发明是通过以下技术方案实现的：
一种高耐磨水性玻璃漆，它是由下述重量份的原料组成：
水性氨基树脂8890 55-65、聚氨酯树脂8-10、二丙二醇丁醚1-3、纯水10-15、古尔胶0.4-0.6、二甲基硅油 0.2-0.4、琥珀酸二异辛酯磺酸钠 0.2-0.6、氧化铝0.3-0.5、N-叔丁基-2-苯骈噻唑次磺酰胺0.1-0.2、流平剂0.3-0.5、改性硅藻土0.3-0.6、环氧硬脂酸辛酯 0.8-1.2、硬酯酸锌0.08-0.1；
所述的改性硅藻土的制备方法为：
硅藻土用10-15%盐酸浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干；
将部分物料溶于水中，再加入硅藻土重量2-3%的环氧四氢邻苯二甲酸二辛酯、1-2%的抗氧剂DSTP、2-3%的柠檬酸三丁酯、3-5%氧化铝，高速1200-1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即为所述改性硅藻土。
一种高耐磨水性玻璃漆的制备方法，包括以下步骤：
（1）将上述重量份的聚氨酯树脂与硬脂酸锌在55-60℃下加热搅拌5-8分钟，充分混合后，常温冷却；
（2）将上述重量份的水性氨基树脂8890与步骤（1）的混合物加入反应缸内，在500-600转/分的条件下，均匀搅拌8-12分钟；
（3）加入上述重量份的二丙二醇丁醚、纯水、古尔胶、二甲基硅油，在1000-1300转/分的条件下，均匀搅拌8-12分钟；
（4）加入上述重量份的琥珀酸二异辛酯磺酸钠、氧化铝、N-叔丁基-2-苯骈噻唑次磺酰胺、流平剂、环氧硬脂酸辛酯，在500-800转/分的条件下，均匀搅拌25-35分钟；
（5）加入上述重量份的改性硅藻土，搅拌均匀，即得到所述水性玻璃漆。
本发明的优点：
本发明生产的水性玻璃漆无气泡、不结块、无异物、无沉淀分层现象、可以用水无限稀释、能减低成本、环保、漆膜有很强的内聚力和粘附力，在常温下耐磨性强，加入的改性硅藻土作为增稠剂，增强了漆膜的附着力，加入的环氧硬脂酸辛酯进一步增强了漆膜的粘附力。
具体实施方式
实施例1
一种高耐磨水性玻璃漆，它是由下述重量份的原料组成：
水性氨基树脂889065、氨基树脂10、二丙二醇丁醚3、纯水15、古尔胶0.6、二甲基硅油 0.4、琥珀酸二异辛酯磺酸钠 0.6、氧化铝0.5、N-叔丁基-2-苯骈噻唑次磺酰胺0.4、流平剂0.5、改性硅藻土0.6、环氧硬脂酸辛酯 1.2、硬酯酸锌0.08；
所述的改性硅藻土的制备方法为：
硅藻土用15%盐酸浸泡4小时，去离子水洗涤，再用12%氢氧化钠溶液浸泡4小时，再用去离子水洗涤至中性，烘干；
将部分物料溶于水中，再加入硅藻土重量3%的环氧四氢邻苯二甲酸二辛酯、2%的抗氧剂DSTP、3%的柠檬酸三丁酯、5%氧化铝，高速1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即为所述改性硅藻土。
一种高耐磨水性玻璃漆的制备方法，包括以下步骤：
（1）将上述重量份的聚氨酯树脂与硬脂酸锌在55-60℃下加热搅拌5-8分钟；
（2）将上述重量份的水性氨基树脂8890与步骤（1）的混合物加入反应缸内，在500-600转/分的条件下，均匀搅拌8-12分钟；
（3）加入上述重量份的二丙二醇丁醚、纯水、古尔胶、二甲基硅油，在1000-1300转/分的条件下，均匀搅拌12分钟；
（4）加入上述重量份的琥珀酸二异辛酯磺酸钠、氧化铝、N-叔丁基-2-苯骈噻唑次磺酰胺、流平剂、环氧硬脂酸辛酯，在800转/分的条件下，均匀搅拌35分钟；
（5）加入上述重量份的改性硅藻土，搅拌均匀，即得到所述水性玻璃漆。
性能测试：
固化后，漆膜硬度为2H、喷涂于玻璃上透光率为95%；用蘸有清水的纱布擦拭涂层2分钟，涂层完整不脱落，说明其在常温下耐磨性、附着力好；将漆喷在平板玻璃上，待漆膜固化后放入装有UV-B的紫外灯箱中，按照GB/T14522-93进行实验，选择4小时黑暗，4小时光照的条件下实验4天，漆膜的黄变?E≤6，不起泡，保持了一定附着力。

Claims (2)

1.一种高耐磨水性玻璃漆，其特征在于它是由下述重量份的原料组成：
水性氨基树脂8890 55-65、聚氨酯树脂8-10、二丙二醇丁醚1-3、纯水10-15、古尔胶0.4-0.6、二甲基硅油 0.2-0.4、琥珀酸二异辛酯磺酸钠 0.2-0.6、氧化铝0.3-0.5、N-叔丁基-2-苯骈噻唑次磺酰胺0.1-0.2、流平剂0.3-0.5、改性硅藻土0.3-0.6、环氧硬脂酸辛酯 0.8-1.2、硬酯酸锌0.08-0.1；
所述的改性硅藻土的制备方法为：
硅藻土用10-15%盐酸浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干；
将部分物料溶于水中，再加入硅藻土重量2-3%的环氧四氢邻苯二甲酸二辛酯、1-2%的抗氧剂DSTP、2-3%的柠檬酸三丁酯、3-5%氧化铝，高速1200-1500转/分搅拌，得到分散液，分散液烘干粉碎成超细粉末，即为所述改性硅藻土。
2.一种如权利要求1所述的高耐磨水性玻璃漆的制备方法，其特征在于包括以下步骤：
（1）将上述重量份的聚氨酯树脂与硬脂酸锌在55-60℃下加热搅拌5-8分钟，充分混合后，常温冷却；
（2）将上述重量份的水性氨基树脂8890与步骤（1）的混合物加入反应缸内，在500-600转/分的条件下，均匀搅拌8-12分钟；
（3）加入上述重量份的二丙二醇丁醚、纯水、古尔胶、二甲基硅油，在1000-1300转/分的条件下，均匀搅拌8-12分钟；
（4）加入上述重量份的琥珀酸二异辛酯磺酸钠、氧化铝、N-叔丁基-2-苯骈噻唑次磺酰胺、流平剂、环氧硬脂酸辛酯，在500-800转/分的条件下，均匀搅拌25-35分钟；
（5）加入上述重量份的改性硅藻土，搅拌均匀，即得到所述水性玻璃漆。
CN201210452697.7A 2012-11-13 2012-11-13 一种高耐磨水性玻璃漆及其制备方法 Expired - Fee Related CN103102764B (zh)