CN103087595A - Nonhazardous aqueous environment-friendly synthetic resin paint - Google Patents
Nonhazardous aqueous environment-friendly synthetic resin paint Download PDFInfo
- Publication number
- CN103087595A CN103087595A CN2012104345581A CN201210434558A CN103087595A CN 103087595 A CN103087595 A CN 103087595A CN 2012104345581 A CN2012104345581 A CN 2012104345581A CN 201210434558 A CN201210434558 A CN 201210434558A CN 103087595 A CN103087595 A CN 103087595A
- Authority
- CN
- China
- Prior art keywords
- parts
- synthetic resin
- resin emulsion
- coating
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to nonhazardous aqueous environment-friendly synthetic resin paint. The paint mainly consists of the following components in parts by weight: 40-70 parts of synthetic resin emulsion, 0.1-2 parts of carboxymethylcellulose, 40-55 parts of purified water, 40-60 parts of calcium carbonate, 3-12 parts of titanium dioxide, 1-6 parts of kaolin, 8-28 parts of talcum powder, 8-18 parts of wollastonite in powder, 10-30 parts of lithopone, 2-22 parts of renal mica, 1-10 parts of bentonite thickener, 1-10 parts of lauryl alcohol ester, 3-10 parts of propylene glycol and 2-10 parts of additive and assistant. The preparation method comprises the following steps of: mixing water, powder and the assistant and agitating; then, heating to about 60-110 DEG C; adding the synthetic resin emulsion and a film forming agent to stir uniformly; maintaining the temperature at 60-100 DEG C; and then adding the thickener to filter. The nonhazardous aqueous environment-friendly synthetic resin paint which uses the synthetic resin as a main base material does not contain harmful substances such as free formaldehyde, benzene, toluene, ethylbenzene and dimethylbenzene through result analysis of selective examination of Shenzhen Inspection Department. Meanwhile, the contents of soluble heavy metals and volatile organic compounds (VOC) are nearly zero which is far lower than the test reference standard. The test shows that the product meets the national standard in washability, alkali resistance, contrast ratio and the like, and is non-toxic and healthy and environment-friendly, and damage of formaldehyde in the paint to human body is removed.
Description
Technical field the present invention relates to a kind of synthetic resins toxicological harmless Environmental Protective Water-paint and preparation method thereof
The background technology resin latex dope is present main interior wall coating, is take synthetic resin emulsion as binding material, adds pigment, filler and various auxiliary agent, the slim interior wall coating that forms through grinding.Because synthetic resin emulsion used is different, performance, the class of the coating of concrete kind are also just variant.Synthetic resin emulsion commonly used has: acrylic ester emulsion, vinylbenzene one acrylate copolymer emulsion, vinyl acetate between to for plastic one third ethene acid esters emulsion ", vinylchlorid one vinylidene chloride emulsion etc.The kind of resin latex dope commonly used and applicable building class: interim or common building: ethene-vinyl acetate emulsion copolymer paint.Middle-grade building: vinyl acetate between to for plastic-acrylic latex coating, styrene-acrylic latex paint, vinyl acetate between to for plastic-tertiary ethylene carbonate emulsion copolymer paint.Top-grade building: pure acrylic acid emulsion paint, silicon the third emulsion paint, aqueous polyurethane coating, aqueous fluorocarbon coating.Can be divided into inferior light, half inferior light, high light and mercerising etc. by the coating film gloss degree.Can be divided into elasticity and non-resilient by being coated with film type.Compare with the emulsion paint of general significance, elastic coating can cover the fine cracks of metope.
Summary of the invention the present invention can prepare the environmental protection coating material of objectionable impuritiess such as not containing free formaldehyde, benzene, toluene, ethylbenzene, dimethylbenzene by mixing a certain proportion of synthetic resin emulsion, has flexible coating, smooth exquisiteness, seepage force, strong adhesion, and inexpensive, be convenient to the advantage for preparing and construct.This synthetic resin emulsion consists of: multiple vinylbenzene, acrylate monomer be through emulsion, vinylformic acid, methacrylic acid, methyl methacrylate, and the multiple units such as methyl esters, esters of acrylic acid and functional aid are poly-, the emulsion that forms by the Optimization Technology copolymerization.
Technical scheme provided by the invention is: a kind of synthetic resins toxicological harmless Environmental Protective Water-paint, it consists of: 40-70 part synthetic resin emulsion, 0.1-2 part carboxymethyl cellulose, 40-55 part pure water, 40-60 part calcium carbonate, 3-12 part titanium dioxide, 1-6 part kaolin, 8-28 part talcum powder, 8-18 part wollastonite powder, 10-30 part zinc sulfide white, 2-22 part kidney mica, 1-10 part bentonite thickener, 1-10 part lauryl alcohol ester, 3-10 part propylene glycol, 2-10 part additive and auxiliary agent etc.(by weight)
The technological specification of the specific embodiment of the invention and each flow process is as follows: water and raw material prepare and stir with auxiliary agent in proportion, again temperature is raised to about 60-110 degree, add synthetic resin emulsion and film forming to stir, temperature keeps the 60-100 degree, then adds thickening material to filter to form.
The outstanding feature of the coating of the present invention's preparation is:
1, the major part of the main raw material of this coating source is abundant, and cheap
2, this coating preparation technique is simpler, and processing parameter is more easy to control
3, this coating environmental protection, toxicological harmless, do not produce or the harmful free formaldehyde that volatilizees, stupid be the toxic substances such as thing
4, this coating can be in indoor curing, easy construction, be convenient to the construction of the methods such as indoor brushing, roller coating, spray.
Claims (6)
1. synthetic resins toxicological harmless Environmental Protective Water-paint, it consists of: 40-70 part synthetic resin emulsion, 0.1-2 part carboxymethyl cellulose, 40-55 part pure water, 40-60 part calcium carbonate, 3-12 part titanium dioxide, 1-6 part kaolin, 8-28 part talcum powder, 8-18 part wollastonite powder, 10-30 part zinc sulfide white, 2-22 part kidney mica, 1-10 part bentonite thickener, 1-10 part lauryl alcohol ester, 3-10 part propylene glycol, 2-10 part additive and auxiliary agent etc.(by weight).
2. coating according to claim 1, its technical characterictic is: this synthetic resin emulsion is through emulsion, vinylformic acid, methacrylic acid, methyl methacrylate through multiple vinylbenzene, acrylate monomer, the multiple units such as methyl esters, esters of acrylic acid and functional aid are poly-, the emulsion that forms by the Optimization Technology copolymerization.
3. coating according to claim 2 and synthetic resins composition, its scope of asking for protection is: the starting material of the preparation flow of this synthetic resin emulsion, preparation method and selected synthetic resin emulsion, and the blending ratio of material.
4. coating according to claim 1 and 2, its functional character is: this exclusive synthetic resin emulsion is through certain procedures and the prepared coating of raw material does not produce or the objectionable impurities such as the free formaldehyde that volatilizees, benzene, toluene, ethylbenzene, dimethylbenzene.
5. according to claim 1,2 or 4 described coating, its technical characterictic is: water and powder prepare and stir with auxiliary agent in proportion, again temperature is raised to about 60-110 degree, add synthetic resin emulsion and film forming to stir, temperature keeps the 60-100 degree, then adds thickening material to filter to form.
6. according to claim 1,2,4 or 5 described coating and production processes thereof, its scope of asking for protection is: the preparation flow of this coating, preparation method and the starting material of choosing, and raw-material blending ratio.