CN103085421A - 硅胶布的加工工艺 - Google Patents

硅胶布的加工工艺 Download PDF

Info

Publication number
CN103085421A
CN103085421A CN2012105084911A CN201210508491A CN103085421A CN 103085421 A CN103085421 A CN 103085421A CN 2012105084911 A CN2012105084911 A CN 2012105084911A CN 201210508491 A CN201210508491 A CN 201210508491A CN 103085421 A CN103085421 A CN 103085421A
Authority
CN
China
Prior art keywords
silica gel
glue
coating
cloth
processing technology
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012105084911A
Other languages
English (en)
Other versions
CN103085421B (zh
Inventor
陈乔霖
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JINGJIANG XINGJIE POWER EQUIPMENT MANUFACTURING Co Ltd
Original Assignee
JINGJIANG XINGJIE POWER EQUIPMENT MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JINGJIANG XINGJIE POWER EQUIPMENT MANUFACTURING Co Ltd filed Critical JINGJIANG XINGJIE POWER EQUIPMENT MANUFACTURING Co Ltd
Priority to CN201210508491.1A priority Critical patent/CN103085421B/zh
Publication of CN103085421A publication Critical patent/CN103085421A/zh
Application granted granted Critical
Publication of CN103085421B publication Critical patent/CN103085421B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种硅胶布的加工工艺，包括以下工艺流程：织布→配胶→涂覆烘干→复卷→检验→入库。本发明操作简单方便，降低了使用成本，减少了环境污染。

Description

硅胶布的加工工艺
技术领域
 本发明涉及硅胶布的加工工艺。
背景技术
   硅胶布是硅橡胶涂覆玻璃纤维布，是一种具有耐酸碱、耐磨、耐高低温性能、高绝缘性能，多用途的复活材料新产品。在国外近几年发展很快，基本上以每年递增15%的速度增长，以被广泛地应用于建筑、电气绝缘、管道柔性连接、化工防腐、密封等领域。进口的压延的硅胶布，压延的硅胶布的厚度正常的都在1毫末，而且没有柔韧性，胶不能渗透到玻纤布里面去，就像一块板一样的，使用效果不是太好。以前化工厂管道里面都是用四氟内衬，用防腐油漆来防腐，使用成本高，环境也易受到污染。
发明内容
 本发明的目的是提供一种操作简单方便，能降低使用成本，减少环境污染的硅胶布的加工工艺。
    本发明是这样实现的：一种硅胶布的加工工艺，其特征在于：包括以下工艺流程：织布→配胶→涂覆烘干→复卷→检验→入库。
    本发明所述的织布是指用多尼尔织布机织布，在织布的过程中选用0.65微米的纱来进行并捻，经纬密度按200*190来进行织造，确保基布表面没有毛羽和跳纱。
    本发明所述的配胶是指配硅橡胶，硅橡胶有液体和固体的，液体胶很昂贵，但操作起来很方便直接将胶倒到容器里面，加上双二四、耐高温色浆、硫化剂，按100:0.5~2:2~~5:0.5~2的比例进行配置，固体胶的价格每吨是液体胶的一半，但需要先分切、甲苯溶解、研磨后加双二四、耐高温色浆、硫化剂，按100:0.5~2:2~5:0.5~2的比例配置。
   本发明所述的涂覆烘干是指在玻璃纤维布上涂覆硅橡胶后烘干，根据需要通过调节涂布机上厚度控制器，当涂覆厚度为0.15~0.35毫米时，涂布机有5节烘箱设定每一节烘箱的温度分别为70~100℃、110~150℃、160~200℃、200~240℃、240~260℃，每节烘箱烘干时间为1分钟左右。
   本发明操作简单方便，降低了使用成本，减少了环境污染。
具体实施方式~
    一种硅胶布的加工工艺，其特征在于：包括以下工艺流程：织布→配胶→涂覆烘干→复卷→检验→入库。所述的织布是指用多尼尔织布机织布，在织布的过程中选用0.65微米的纱来进行并捻，经纬密度按200*190来进行织造，确保基布表面没有毛羽和跳纱。所述的配胶是指配硅橡胶，硅橡胶有液体和固体的，液体胶很昂贵，但操作起来很方便直接将胶倒到容器里面，加上双二四、耐高温色浆、硫化剂，按100:0.5~2:2~5:0.5~2的比例进行配置，固体胶的价格每吨是液体胶的一半，但需要先分切、甲苯溶解、研磨后加双二四、耐高温色浆、硫化剂，按100:0.5~2:2~5:0.5~2的比例配置。所述的涂覆烘干是指在玻璃纤维布上涂覆硅橡胶后烘干，根据需要通过调节涂布机上厚度控制器，当涂覆厚度为0.15~0.35毫米时，涂布机有5节烘箱设定每一节烘箱的温度分别为70~100℃、110~150℃、160~200℃、200~240℃、240~260℃，每节烘箱烘干时间为1分钟左右。具体实施时，改进了以前用0.9微米的纱来并捻，经纬密度用130*140来织造的工艺，这样有效的增强了基布的强度，以前的拉力强度0.4毫米的是1900N/50MM，改进后的是2400N/50MM。在生产过程中，液体胶容易吸附在过辊上，为了克服这一难题，经过反复的试验，我们把镀铬的过辊改成了喷涂特氟龙的过辊，这样过辊上就没有任何胶液附属在上面，操作起来也很方便，大大的节约了成本和人工工时，没有改进前每做30米就需暂停下清理过辊，改进以后全天候的生产都能确保过辊干净，涂覆平整均匀。没有改进前每小时只能做60米，改进以后每小时可以做到90米，按门幅1.8米计算，每小时就多生产了54平方米，按30元每平方计算，一天就提高了产值38880元，成本也降低了一半。发明生产的硅胶布替代了靠进口的压延的硅胶布，压延的硅胶布的厚度正常的都在1毫末，而且没有柔韧性，胶不能渗透到玻纤布里面去，就像一块板一样的，以前化工厂管道里面都是用四氟内衬，用防腐油漆来防腐，现都改用了硅胶布，用硅胶布内衬在化工管道里面，起到了脱硫、脱脂、防腐的作用，极大的降低了用户的成本，环境也受不到污染。

Claims (4)

1.一种硅胶布的加工工艺，其特征在于：包括以下工艺流程：织布→配胶→涂覆烘干→复卷→检验→入库。
2.根据权利要求1所述的硅胶布的加工工艺，其特征在于：所述的织布是指用多尼尔织布机织布，在织布的过程中选用0.65微米的纱来进行并捻，经纬密度按200*190来进行织造，确保基布表面没有毛羽和跳纱。
3.根据权利要求1所述的硅胶布的加工工艺，其特征在于：所述的配胶是指配硅橡胶，硅橡胶有液体和固体的，液体胶很昂贵，但操作起来很方便直接将胶倒到容器里面，加上双二四、耐高温色浆、硫化剂，按100:0.5~2:2~5:0.5~2的比例进行配置，固体胶的价格每吨是液体胶的一半，但需要先分切、甲苯溶解、研磨后加双二四、耐高温色浆、硫化剂，按100:0.5~2:2~5:0.5~2的比例配置。
4.根据权利要求1所述的硅胶布的加工工艺，其特征在于：所述的涂覆烘干是指在玻璃纤维布上涂覆硅橡胶后烘干，根据需要通过调节涂布机上厚度控制器，当涂覆厚度为0.15~0.35毫米时，涂布机有5节烘箱设定每一节烘箱的温度分别为70~100℃、110~150℃、160~200℃、200~240℃、240~260℃，每节烘箱烘干时间为1分钟左右。
CN201210508491.1A 2012-12-04 2012-12-04 硅胶布的加工工艺 Expired - Fee Related CN103085421B (zh)