CN103074127A - 省油锭配方 - Google Patents
省油锭配方 Download PDFInfo
- Publication number
- CN103074127A CN103074127A CN2013100348674A CN201310034867A CN103074127A CN 103074127 A CN103074127 A CN 103074127A CN 2013100348674 A CN2013100348674 A CN 2013100348674A CN 201310034867 A CN201310034867 A CN 201310034867A CN 103074127 A CN103074127 A CN 103074127A
- Authority
- CN
- China
- Prior art keywords
- prescription
- content
- camphor
- acid
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种省油锭配方，由樟脑、棕榈酸、硬脂酸、鲸蜡醇、薄荷醇、龙脑、硬脂酸苯酯、棕榈酸鲸蜡酯以及二茂铁组成，其中樟脑的重量百分比含量为30-90％，棕榈酸的重量百分比含量为4-10％，硬脂酸的重量百分比含量为4-10％。本发明的组成物质稳定、安全而且毒性小，不产生二次污染，成本低；节油15%以上且可以提高辛烷值。
Description
技术领域
本发明涉及一种省油锭配方，用于改善汽、柴油燃烧的性质，满足更好的经济性和更清洁的环保性能。
背景技术
随着机动车的不断普及，汽、柴油的消费规模也在不断增加。然而，汽、柴油作为一种不可再生资源，大家也越来越关注如何节能以及如何注重环保。例如，中国专利ZL200820120000.5就公开了一种省油锭，用于提高车辆节能和降低排放污染物，该省油锭包括一内层体和一表层体，其中，所述表层体包覆于所述内层体外部周围。
然而，现有技术中的省油锭配方安全性和稳定性不足，毒性和成本都有待进一步降低。此外，节油效率的不断提高也是永恒的课题。
因此，有必要研究一种节油效率更高、成本更低的省油锭，以解决现有技术中存在的问题。
发明内容
考虑到至少一个上述问题而完成了本发明，并且本发明的一个目的在于提供一种省油锭配方，其特征在于该配方由樟脑、棕榈酸、硬脂酸、鲸蜡醇（又名十六烷醇）、薄荷醇、龙脑、硬脂酸苯酯、棕榈酸鲸蜡酯以及二茂铁组成，其中樟脑的重量百分比含量为30-90％，棕榈酸的的重量百分比含量为4-10％，硬脂酸的重量百分比含量为4-10％。
根据本发明另一方面，所述硬脂酸的含量高于棕榈酸的含量。
与现有技术相比，本发明的有益效果在于：
1、所选用的组成物质稳定、安全，而且毒性小，不产生二次污染，并且以廉价的天然有机化合物为主要成分；
2、配方既能降低汽柴油消耗（节油15%以上），又能提高辛烷值；
3、方便使用与运输，能制成锭剂，并且所制的锭剂易溶于汽柴油。
因此，本发明对汽柴油燃烧的性质有所改善，满足更好的经济性和更清洁的环保性能。
附图说明
图1是根据本发明优选实施例省油锭配方中的樟脑的结构式。
图2是根据本发明优选实施例省油锭配方中的薄荷醇的结构式。
图3是根据本发明优选实施例省油锭配方中的龙脑的结构式。
图4是根据本发明优选实施例省油锭配方中的二茂铁的结构式。
具体实施方式
下面结合附图，通过优选实施例来描述本发明的最佳实施方式，这里的具体实施方式在于详细地说明本发明，而不应理解为对本发明的限制，在不脱离本发明的精神和实质范围的情况下，可以做出各种变形和修改，这些都应包含在本发明的保护范围之内。
参见图1－4，其中示出了本发明优选实施例的省油锭配方中的几种物质。一种省油锭配方，主要由樟脑、棕榈酸、硬脂酸、鲸蜡醇（又名十六烷醇）、薄荷醇、龙脑、硬脂酸苯酯、棕榈酸鲸蜡酯以及二茂铁组成。
优选地，所述硬脂酸的含量高于棕榈酸的含量。
优选地，还可以以原有的配方为基础，调节各组分的比例。
优选地，上述配方主要以樟脑（camphor,Cm，C10H16O）（YT-091205）或以Cm与有机酸混配（YTN-091212）为主。
Cm主要存在于樟科植物樟树的挥发油中，纯的Cm为白色的结晶性固体，易升华，具有特殊香味，其熔点为170-175℃，而沸点只有204℃。由于这些特性，Cm易燃烧，易溶解于汽柴油中，而且易制成锭剂，有一定的节油效果，优选地，樟脑Cm的重量百分比含量为30-90％。
棕榈酸（Palmitic acid,PA；C15H31COOH）与硬脂酸（Stearic acid,SA）广泛存在于动/植物的油脂中，属于饱和脂肪酸。它们的优点是价廉，有一定的去污性能，也有节油效果；缺点是熔点（60-70℃）较低，会给制锭带来影响；另外就是在汽柴油中的溶解度不大，相比较含十八个碳的SA溶解性要好于十六个碳的PA。优选地，棕榈酸PA的重量百分比含量为4-10％，优选地，硬脂酸SA的重量百分比含量为4-10％。
优选地，Cm与脂肪酸混配，效果要好于Cm的单一组分。其中，混配中Cm的含量高于脂肪酸，效果更好。SA的含量高于PA，将更有利。
优选地，选择在配方中加入醇（alcohol）。
许多脂肪醇是安全无毒的，醇本身易燃，加入到汽柴油中对提高辛烷值是有利的，但在汽柴油中的溶解度并不大。选择使用以下几种天然脂肪醇（这些天然脂肪醇是固体并且熔点高，有利于形成锭剂）：
a.鲸蜡醇（centanol），也叫十六烷醇，熔点是50℃左右。
b.薄荷醇（menthol），熔点40℃左右。
c.龙脑（borneol），熔点与沸点都比较高，分别为208℃与212℃，是樟脑（Cm）的还原物，易升华，易燃烧。
优选地，选择在配方中加入酯（ester）。
有机酸与脂肪酸反应很容易生成酯，此反应称为酯化反应（esterification），许多酯也是安全无毒的，易燃性与在汽柴油中的溶解性比有机酸和脂肪醇都要好，因此，省油锭改进配方中加入合适的酯是必要的。以下二种含天然产物成分的酯为固体并且熔点高，因此被加入配方中：
a.硬脂酸苯酯（phenyl stearate，PS），熔点52℃。
b.棕榈酸鲸蜡酯（cetyl palmitate,CP），也称为十六酸十六酯，熔点55-56℃。
优选地，在配方中加入二茂铁（ferrocene）。
二茂铁是人工合成的金属有机化合物，化学性质稳定，熔点174℃，沸点249℃，毒性很小。二茂铁加入很少的量于配方中可以起到两个作用，一是提高汽油的辛烷值；二是催化有机酸与脂肪醇生成酯，促进燃烧。
例如，根据以上物质特性，可实施以下省油锭配方：
| 编号 | Cm% | PA% | SA% | cetanol% | menthol% | borneol% | PS% | CP% | ferrocene% |
| YT-100205-1 | 30-90 | 2-5 | 5-10 | ||||||
| YT-100205-2 | 30-40 | 5-10 | 5-10 | 40-50 | |||||
| YT-100205-3 | 45-50 | 4-10 | 10 | 20-30 | |||||
| YT-100205-4 | 45-50 | 4-10 | 5-10 | 5-10 | 20-30 | ||||
| YT-100205-5 | 40-50 | 4-9 | 4-10 | 5-10 | 5-10 | 10-20 | 1-5 | ||
| YT-100205-6 | 40-50 | 4-10 | 5-10 | 5-10 | 20-30 | 1-5 | |||
| YT-100205-7 | 50-90 | 6-10 | 10-20 | ||||||
| YT-100205-8 | 50-60 | 5-10 | 6-10 | 5-10 | 5-10 | 4-9 | 1-5 | ||
| YT-100205-9 | 60-90 | 5-10 | 5-20 | ||||||
| YT-100205-10 | 60-70 | 5-10 | 5-10 | 4-9 | 1-5 |
本发明的有益效果在于：所选用的组成物质稳定、安全，而且毒性小，不产生二次污染，并且以廉价的天然有机化合物为主要成分；配方既能降低汽油消耗（节油15%以上），又能提高辛烷值；方便使用与运输，能制成锭剂，并且所制的锭剂易溶于汽柴油；对汽柴油燃烧的性质有所改善，满足更好的经济性和更清洁的环保性能。
相关化合物的名称、结构式和熔（沸）点数据
本发明不限于上述具体实施例。可以理解的是，在不脱离本发明的精神和实质范围的情况下，可以做出各种变形和修改，这些都应包含在本发明的保护范围之内。
Claims (2)
1.一种省油锭配方，其特征在于该配方由樟脑、棕榈酸、硬脂酸、鲸蜡醇、薄荷醇、龙脑、硬脂酸苯酯、棕榈酸鲸蜡酯以及二茂铁组成，其中樟脑的重量百分比含量为30-90％，棕榈酸的的重量百分比含量为4-10％，硬脂酸的重量百分比含量为4-10％。
2.根据权利要求1所述的省油锭配方，其特征在于所述硬脂酸的含量高于棕榈酸的含量。