CN103073957B - 一种彩色铅笔芯及其制备方法 - Google Patents

一种彩色铅笔芯及其制备方法 Download PDF

Info

Publication number
CN103073957B
CN103073957B CN201310013224.1A CN201310013224A CN103073957B CN 103073957 B CN103073957 B CN 103073957B CN 201310013224 A CN201310013224 A CN 201310013224A CN 103073957 B CN103073957 B CN 103073957B
Authority
CN
China
Prior art keywords
sodium carbonate
lead
colored pencil
pencil lead
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310013224.1A
Other languages
English (en)
Other versions
CN103073957A (zh
Inventor
董川
游志校
翟晓倩
苏丽霞
于洋
张建刚
王晓丽
李丽霞
周叶红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Aoyue Austrian Mstar Technology Ltd
Original Assignee
Shanxi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi University filed Critical Shanxi University
Priority to CN201310013224.1A priority Critical patent/CN103073957B/zh
Publication of CN103073957A publication Critical patent/CN103073957A/zh
Application granted granted Critical
Publication of CN103073957B publication Critical patent/CN103073957B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种彩色铅笔芯及其制备方法，彩色铅笔芯的原料组分及其含量按质量份数计：硫代硫酸钠62-73，显色剂13-20，羧甲基纤维素钠7-15，高岭土0-8；所述的显色剂由碳酸钠和酸碱指示剂组成。彩色铅笔芯的制备方法：按比例称量好原料，将碳酸钠和酸碱指示剂混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀，然后加入羧甲基纤维素钠和高岭土，搅拌均匀，倒入模具中，晾干，取出即可。本发明提供的彩色铅笔芯，遇水和久置于空气中皆可褪色，粘到手上和衣物上易清洗，无残留，无毒无害，适合于临时标记、字画练习等不需要长期保存的场合使用。

Description

一种彩色铅笔芯及其制备方法
技术领域
本发明涉及一种书写材料，具体是一种适合于临时标记、字画练习等不需要长期保存的场合使用的彩色铅笔芯及其制备方法。
背景技术
现有技术中，用于书写、制图和绘画的普通铅笔芯基本上由黏土和石墨粉组成，在使用过程中存在擦除不彻底，不卫生，沾到手上难清洗等缺点，对使用者健康不利；现有的彩色铅笔芯的制作原料和工艺复杂如专利CN1302316A，原料对环境有污染，书写的字迹不能自动褪色，不适合于临时标记、字画练习等不需要长期保存的场合使用。
发明内容
本发明目的在于提供一种彩色铅笔芯及其制备方法，本发明提供的彩色铅笔芯，遇水和久置于空气中皆可褪色，粘到手上和衣物上易清洗，无残留，各组分均无毒无害，适合于临时标记、字画练习等不需要长期保存的场合使用。
本发明提供的一种彩色铅笔芯，它的组分及其含量按质量份数计：硫代硫酸钠62-73，显色剂：13-20，羧甲基纤维素钠7-15，高岭土0-8。
所述的显色剂由碳酸钠和酸碱指示剂组成，所述的酸碱指示剂为酚酞、间硝基苯酚、百里香酚酞或邻甲酚酞，碳酸钠和酸碱指示剂摩尔比为1︰0.4-2，优选摩尔比为1︰0.5-1.2。
本发明提供的一种彩色铅笔芯的制备方法：按上述比例，称量好原料，将碳酸钠和酸碱指示剂混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀，然后加入羧甲基纤维素钠和高岭土（可不加高岭土），搅拌均匀，倒入模具中，晾干，取出即可。
与现有技术相比本发明具有如下优点和效果：本发明采用硫代硫酸钠作为主体，硫代硫酸钠为无色透明单斜晶体，无毒、无臭且硬度高；羧甲基纤维素钠作为粘合剂，使粉粒之间结合力提高，保障铅笔芯不易折断；高岭土可进一步提高铅笔芯的硬度及覆盖率；碳酸钠和酸碱指示剂作为显色剂具有非常好的显色效果，而且所使用酸碱指示剂不同，铅笔芯的颜色也不相同。在纸上书写后，用水擦拭即可褪色，且不留痕迹，该铅笔颜色鲜艳，书写流畅、清晰，无掉渣情况，硬度与光滑度也符合要求。在45°C温度条件下，稳定性好，不变形。本发明不需要特殊的生产设备，生产工艺简单，易于批量生产。
具体实施方式
实施例1：制备红色铅笔芯
组分：硫代硫酸钠7g，碳酸钠0.565g，酚酞1.186g，羧甲基纤维素钠1g。
制备方法：将酚酞和碳酸钠混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀，然后加入羧甲基纤维素钠并搅拌均匀，倒入模具中，晾干，取出，即可。
效果：采用Wolff-wilborn铅笔硬度测试方法，测得该铅笔芯的硬度为5H，色度高，覆盖率好。耐受温度45℃。
实施例2：制备红色铅笔芯
组分：硫代硫酸钠7g，碳酸钠0.421g，酚酞0.883g，羧甲基纤维素钠0.9g，高岭土0.8g。
制备方法：将酚酞和碳酸钠混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀，然后加入羧甲基纤维素钠和高岭土并搅拌均匀，倒入模具中，晾干，取出，即可。
效果：采用Wolff-wilborn铅笔硬度测试方法，测得该铅笔芯的硬度为4H，色度很高，覆盖率很好。耐受温度45℃。
实施例3：制备黄色铅笔芯
组分：硫代硫酸钠7g，碳酸钠0.812g，间硝基苯酚1.077g，羧甲基纤维素钠1.5g。
制备方法：将间硝基苯酚和碳酸钠混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀，然后加入羧甲基纤维素钠并搅拌均匀，倒入模具中，晾干，取出，即可。
效果：采用Wolff-wilborn铅笔硬度测试方法，测得该铅笔芯的硬度为3H，色度高，覆盖率好。耐受温度45℃。
实施例4：制备蓝色铅笔芯
组分：硫代硫酸钠7g，碳酸钠0.348g，百里香酚酞1.401g，羧甲基纤维素钠1.4g，高岭土0.1g。
制备方法：将百里香酚酞和碳酸钠混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀，然后加入羧甲基纤维素钠和高岭土并搅拌均匀，倒入模具中，晾干，取出，即可。
效果：采用Wolff-wilborn铅笔硬度测试方法，测得该铅笔芯的硬度为4H，色度高，覆盖率好。耐受温度45℃。
实施例5：制备紫色铅笔芯
组分：硫代硫酸钠7g，碳酸钠0.533g，邻甲酚酞1.217g，羧甲基纤维素钠0.8g，高岭土0.8g。
制备方法：将邻甲酚酞和碳酸钠混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀，然后加入羧甲基纤维素钠和高岭土并搅拌均匀，倒入模具中，晾干，取出，即可。
效果：采用Wolff-wilborn铅笔硬度测试方法，测得该铅笔芯的硬度为2H，色度高，覆盖率好。耐受温度45℃。
实施例6：制备红色铅笔芯
组分：硫代硫酸钠5g，碳酸钠0.21g，酚酞0.74g，羧甲基纤维素钠1g。
制备方法：将酚酞和碳酸钠混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀，然后加入羧甲基纤维素钠并搅拌均匀，倒入模具中，晾干，取出，即可。
效果：采用Wolff-wilborn铅笔硬度测试方法，测得该铅笔芯的硬度为5H，色度较高，覆盖率较好。耐受温度45℃。
实施例7：制备橙色铅笔芯
组分：硫代硫酸钠7g，碳酸钠0.358g，酚酞0.7g、间硝基苯酚0.66g，羧甲基纤维素钠1.4g。
制备方法：将酚酞及间硝基苯酚和碳酸钠混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀，然后加入羧甲基纤维素钠并搅拌均匀，倒入模具中，晾干，取出，即可。
效果：采用Wolff-wilborn铅笔硬度测试方法，测得该铅笔芯的硬度为3H，色度高，覆盖率好。耐受温度45℃。
实施例8：制备紫色铅笔芯
组分：硫代硫酸钠7g，碳酸钠0.149g，邻甲酚酞1.291g，羧甲基纤维素钠1.4g。
制备方法：将邻甲酚酞和碳酸钠混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀，然后加入羧甲基纤维素钠并搅拌均匀，倒入模具中，晾干，取出，即可。
效果：采用Wolff-wilborn铅笔硬度测试方法，测得该铅笔芯的硬度为3H，色度较高，覆盖率较好。耐受温度45℃。
实施例9：制备紫色铅笔芯
组分：硫代硫酸钠7g，碳酸钠0.447g，邻甲酚酞1.291g，羧甲基纤维素钠1.5g。
制备方法：将邻甲酚酞和碳酸钠混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀，然后加入羧甲基纤维素钠并搅拌均匀，倒入模具中，晾干，取出，即可。
效果：采用Wolff-wilborn铅笔硬度测试方法，测得该铅笔芯的硬度为3H，色度较高，覆盖率较好。耐受温度45℃。
上述实施例制得的铅笔芯，在纸上书写流畅，字迹清晰，颜色鲜艳；用水擦拭即可褪色，且不留痕迹；如不擦拭，3-4天自动褪为无色。
本发明不受上述实施例的限制，本文中所描述的具体实施例仅是对本发明精神作举例说明，凡由本发明制作的各种铅笔都在本发明的要求保护范围内。

Claims (2)

1.一种彩色铅笔芯，特征在于，它的组分及其含量按质量份数计：硫代硫酸钠62-73，显色剂13-20，羧甲基纤维素钠7-15，高岭土0-8；所述的显色剂由碳酸钠和酸碱指示剂组成，碳酸钠和酸碱指示剂摩尔比为1︰0.4-2，所述的酸碱指示剂为酚酞、间硝基苯酚、百里香酚酞或邻甲酚酞；
彩色铅笔芯的制备方法：按比例称量好原料，将碳酸钠和酸碱指示剂混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀,然后加入羧甲基纤维素钠，搅拌均匀，倒入模具中，晾干，取出即可；或者，
按比例称量好原料，将碳酸钠和酸碱指示剂混合，滴加无水乙醇调至稠糊状，再将熔融的硫代硫酸钠倒入其中搅拌均匀,然后加入羧甲基纤维素钠和高岭土，搅拌均匀，倒入模具中，晾干，取出即可。
2.如权利要求1所述的一种彩色铅笔芯，其特征在于，所述碳酸钠和酸碱指示剂的摩尔比为1︰0.5-1.2。
CN201310013224.1A 2013-01-14 2013-01-14 一种彩色铅笔芯及其制备方法 Expired - Fee Related CN103073957B (zh)