CN103066188A - 一种蓝光激发碳点发光的白光led及其制备方法 - Google Patents
一种蓝光激发碳点发光的白光led及其制备方法 Download PDFInfo
- Publication number
- CN103066188A CN103066188A CN2013100304873A CN201310030487A CN103066188A CN 103066188 A CN103066188 A CN 103066188A CN 2013100304873 A CN2013100304873 A CN 2013100304873A CN 201310030487 A CN201310030487 A CN 201310030487A CN 103066188 A CN103066188 A CN 103066188A
- Authority
- CN
- China
- Prior art keywords
- silane
- blue
- carbon point
- bowl
- functionalized carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种蓝光激发碳点发光的白光LED及其制备方法,该白光LED包括绝缘底座、碗形反射镜、蓝光LED芯片和透镜,碗形反射镜设置在绝缘底座上,碗形反射镜与绝缘底座之间设有导热片,蓝光LED芯片固定在碗形反射镜中,蓝光LED芯片上覆盖有硅烷功能化碳点,碗形反射镜的外部设置有透镜,透镜内填充透明封装材料;将有机多元酸加入在氮气保护下沸腾回流的硅烷液体中,使有机多元酸热解合成硅烷功能化碳点,将蓝光LED芯片固定在碗形反射镜中,将硅烷功能化碳点涂覆在蓝光LED芯片上并固化,在碗形反射镜的外部放置透镜并填充满透明封装材料。本发明有利于提高LED的发光效率、使用稳定性和寿命。
Description
技术领域
本发明涉及一种白光LED及其制备方法,具体的说是通过蓝光LED激发硅烷功能化碳点发光制造的一种白光LED,属于半导体照明技术领域。
背景技术
LED是一种新型固态光源,具有节能、牢固、环保、寿命长和体积小等优点,己成为光电子、照明等领域的研究热点。其中,白光LED已经成为新一代的照明光源,广泛应用于大型显示屏、景观照明、汽车用灯、液晶显示器背光源和装饰等领域。
目前,白光LED主要有三基色LED芯片组合和荧光粉转换波长得到,而后者是目前获得白光LED的主流技术。如利用InGaN蓝光LED芯片激发稀土荧光粉,或者用紫外LED芯片激发外层三基色荧光粉,产生的多色光混合形成白光。但是当前稀土荧光粉的光谱中缺少红色成分,导致其显色指数和发光效率都不高,且荧光粉的制备通常采用传统的高温固相法,合成温度高,导致成本高,不利于LED的商业化发展。同时,三基色不同荧光粉的吸收/激发/发射光谱、寿命、耐热、化学稳定性不一致,色坐标和色域不易调制,且发光材料之间因光线的交互相吸而降低了LED荧光产率,对白光LED的应用造成了巨大的阻碍。荧光粉材料是微米或几十微米量级的固体不透明颗粒,存在较严重的挡光问题,导致发光不均匀。而且在白光LED装配时荧光粉以悬浊液形式分散于封装胶中,存在沉降问题,导致荧光粉涂覆不均匀,造成发光不均。
因此,需要研发一类新型的成本低、色域宽、显色指数高、稳定性好、透明、均匀分散的荧光转换材料来制备白光LED以解决现有技术存在的问题和不足。
发明内容
针对现有白光LED技术存在的问题,本发明提供一种蓝光激发碳点发光的白光LED,以解决目前白光LED显色性偏低、色域偏窄和稳定性差等问题。本发明还提供一种该白光LED的制备方法。
本发明的蓝光激发碳点发光的白光LED,采用以下技术方案:
该白光LED,包括绝缘底座、碗形反射镜、蓝光LED芯片和透镜,碗形反射镜设置在绝缘底座上,碗形反射镜与绝缘底座之间设有导热片,蓝光LED芯片固定在碗形反射镜中,蓝光LED芯片上覆盖有硅烷功能化碳点,绝缘底座上设置有两个与蓝光LED芯片连接的电极,碗形反射镜的外部设置有透镜,透镜内填充透明封装材料,将电极焊线、碗形反射镜、硅烷功能化碳点和蓝光LED芯片包裹在绝缘底座上。
所述蓝光LED芯片的发射波长为420nm-480nm。
所述硅烷功能化碳点是将有机多元酸加入氮气保护下沸腾回流硅烷液体中使有机多元酸热解合成得到的硅烷共价键修饰的功能化碳点,是一种透明、均匀、稳定的胶体发光材料,避免了传统荧光粉在封装胶中的沉降、分散性差、颗粒不均匀、吸收和透过不均匀等问题。碳点的制备均温度较低,与传统荧光粉的高温生产工艺相比,具有操作温度低,制作时间短等优势。
所述硅烷功能化碳点的激发波长从绿光520nm到红光650nm,通过蓝光LED激发发红绿黄光碳点按不同比例混合后的硅烷功能化碳点,可以得到不同颜色、色度值、色温、显色指数的白光LED。
透明封装材料为环氧树脂、硅胶或硅树脂等。
上述白光LED的制备方法,包括以下步骤:
(1)制备硅烷功能化碳点,使硅烷在氮气保护下沸腾回流,将有机多元酸以0.002g/mL-5g/mL的比例加入回流的硅烷液体中,使有机多元酸热解合成硅烷共价键结合的功能化碳点,冷却后纯化即得到透明、均匀、稳定的胶体发光材料硅烷功能化碳点;通过控制柠檬酸的加入量和反应时间可以得到发黄光、绿光和红光的硅烷功能化碳点;
(2)在绝缘底座上固定导热片,再将碗形反射镜固定在导热片上,
(3)将发射波长为420nm-480nm的蓝光LED芯片固定在碗形反射镜中,将两个电极分别置于绝缘底座的两侧,并分别通过金线与蓝光LED芯片P电极和N电极焊接在一起;
(4)将0.2μL-8μL步骤(1)制备的硅烷功能化碳点涂敷在己固定且已连接好电极的蓝光LED芯片上,在60-120℃下加热1-4小时使其固化;
(5)硅烷功能化碳点固化后,在碗形反射镜的外部放置透镜,将两个电极与金线的连接点、金线、碗形反射镜、硅烷功能化碳点和蓝光LED芯片包裹在绝缘底座上,在透镜内填充满透明封装材料,然后置于烘箱中90-150°C下加热1-4小时,透明封装材料固化后即得到白光LED。
步骤(4)中的硅烷功能化碳点的可以是发黄光的硅烷功能化碳点,可以是发红光、绿光和黄光的三种硅烷功能化碳点中任意两种任意比例的混合体,也可以是发红光、绿光和黄光的三种硅烷功能化碳点任意比例的混合体。
本发明利用蓝光LED芯片激发碳点发光制备白光LED,解决了目前LED照明技术中显色性偏低、色域较窄和稳定性差等问题,避免了传统荧光粉在分散剂中的沉降、分散性差、颗粒不均匀、吸收和透过不均匀等问题,有利于提高LED的发光效率、使用稳定性和寿命。
附图说明
图1是本发明蓝光LED激发碳点发光的白光LED的结构示意图。
图2是本发明制备的白光LED的发光光谱图。
图3是本发明制备的白光LED的色度坐标图。
其中:1、有绝缘底座,2、导热片,3、碗形反射镜,4、金线,5、蓝光LED芯片,6、硅烷功能化碳点,7、电极,8、透镜,9、透明封装材料。
具体实施方式
如图1所示,本发明的蓝光激发碳点发光的白光LED,包括绝缘底座1、碗形反射镜3、蓝光LED芯片5和透镜8,碗形反射镜3设置在绝缘底座1上,碗形反射镜3与绝缘底座1之间设有导热片2,蓝光LED芯片固定在碗形反射镜3中,蓝光LED芯片上覆盖有硅烷功能化碳点6,绝缘底座1的两侧各设置一个电极7,两个电极7分别通过一根金线4与蓝光LED芯片5连接,碗形反射镜3的外部设置有透镜8,透镜8内填充透明封装材料9,将两个电极7与金线4的连接点、金线4、碗形反射镜3、硅烷功能化碳点6和蓝光LED芯片5包裹在绝缘底座1上。其中蓝光LED芯片5的发射波长为420nm-480nm。
上述白光LED的制备方法,包括以下步骤:
(1)制备硅烷功能化碳点,使硅烷(如:γ-(β-氨乙基)氨丙基三乙氧基硅烷、γ-(β-氨乙基)氨丙基三甲氧基硅烷、γ-巯丙基三乙氧基硅烷、γ-巯丙基三甲氧基硅烷、苯胺甲基三乙氧基硅烷、苯胺甲基三甲氧基硅烷、γ-(2,3-环氧丙氧)丙基三乙氧基硅烷等)在氮气保护下沸腾回流,将有机多元酸(如:酒石酸、柠檬酸、琥珀酸、均苯四甲酸、苹果酸等)以0.002g/mL-5g/mL的比例加入回流的硅烷液体中,使多元酸热解合成硅烷共价键结合的功能化碳点,冷却纯化后即得到透明、均匀、稳定的胶体发光材料硅烷功能化碳点;
有机多元酸以0.002g/mL-0.05g/mL的比例加入回流的硅烷液体,反应1min-60min得到发绿光碳点;有机多元酸以0.05g/mL-0.4g/mL的比例加入回流的硅烷液体,反应1min-90min得到发黄光碳点;有机多元酸以0.4g/mL-5g/mL的比例加入回流的硅烷液体,反应1min-100min得到发红光碳点。
(2)在绝缘底座1上固定导热片2,再将碗形反射镜3固定在导热片2上,
(3)将发射波长为420nm-480nm的蓝光LED芯片固定在碗形反射镜3中,将两个电极7分别置于绝缘底座1的两侧,并分别通过金线与蓝光LED芯片P电极和N电极焊接在一起。
(4)将0.2μL-8μL步骤(1)制备的硅烷功能化碳点涂敷在己固定且已连接好电极的蓝光LED芯片上,在60-120℃下加热1-4小时使其固化;
(5)硅烷功能化碳点固化后,在碗形反射镜3的外部放置透镜8,将两个电极7与金线4的连接点、金线4、碗形反射镜3、硅烷功能化碳点6和蓝光LED芯片5包裹在绝缘底座1上,在透镜8内填充满高折射率透明封装材料9(环氧树脂、硅胶或硅树脂等),然后置于烘箱中90-150°C下加热1-4小时,透明封装材料固化后即得到白光LED。
步骤(4)中的硅烷功能化碳点的可以是发黄光的硅烷功能化碳点,可以是发红光、绿光和黄光的三种硅烷功能化碳点中任意两种任意比例的混合体,也可以是发红光、绿光和黄光的三种硅烷功能化碳点任意比例的混合体。
按上述方法采用发射波长为460nm的蓝光LED芯片及可发出黄光的硅烷功能化碳点得到的白光LED的发光光谱图和色度坐标图如图2和图3所示。
Claims (8)
1.一种蓝光激发碳点发光的白光LED,包括绝缘底座、碗形反射镜、蓝光LED芯片和透镜,碗形反射镜设置在绝缘底座上,其特征是:碗形反射镜设置在绝缘底座上,碗形反射镜与绝缘底座之间设有导热片,蓝光LED芯片固定在碗形反射镜中,蓝光LED芯片上覆盖有硅烷功能化碳点,绝缘底座上设置有两个与蓝光LED芯片连接的电极,碗形反射镜的外部设置有透镜,透镜内填充透明封装材料,将电极焊线、碗形反射镜、硅烷功能化碳点和蓝光LED芯片包裹在绝缘底座上。
2.根据权利要求1所述的蓝光激发碳点发光的白光LED,其特征是:所述蓝光LED芯片的发射波长为420nm-480nm。
3.根据权利要求1所述的蓝光激发碳点发光的白光LED,其特征是:所述硅烷功能化碳点是将有机多元酸加入氮气保护下沸腾回流硅烷液体中使有机多元酸热解合成得到的硅烷共价键修饰的功能化碳点。
4.一种权利要求1所述蓝光激发碳点发光的白光LED的制备方法,其特征是:包括以下步骤:
(1)将有机多元酸以0.002g/mL-5g/mL的比例加入回流的硅烷液体中,使有机多元酸热解合成硅烷共价键修饰的功能化碳点,冷却纯化后即得到硅烷功能化碳点;
(2)在绝缘底座上固定导热片,再将碗形反射镜固定在导热片上,
(3)将发射波长为420nm-480nm的蓝光LED芯片固定在碗形反射镜中,将两个电极分别置于绝缘底座的两侧,并分别通过金线与蓝光LED芯片P电极和N电极焊接在一起;
(4)将0.2μL-8μL步骤(1)制备的硅烷功能化碳点涂敷在己固定且已连接好电极的蓝光LED芯片上,在60-120℃下加热1-4小时固化;
(5)硅烷功能化碳点固化后,在碗形反射镜的外部放置透镜,将两个电极与金线的连接点、金线、碗形反射镜、硅烷功能化碳点和蓝光LED芯片包裹在绝缘底座上,在透镜内填充满透明封装材料,然后置于烘箱中90-150°C下加热1-4小时,透明封装材料固化后即得到白光LED。
5.根据权利要求4所述的蓝光激发碳点发光的白光LED的制备方法,其特征是:所述步骤(1)中有机多元酸以0.002g/mL-0.05g/mL的比例加入回流的硅烷液体,反应1分钟-60分钟得到发绿光硅烷功能化碳点。
6.根据权利要求4所述的蓝光激发碳点发光的白光LED的制备方法,其特征是:所述步骤(1)中有机多元酸以0.05g/mL-0.4g/mL的比例加入回流的硅烷液体,反应1分钟-90分钟得到发黄光硅烷功能化碳点。
7.根据权利要求4所述的蓝光激发碳点发光的白光LED的制备方法,其特征是:所述步骤(1)中有机多元酸以0.4g/mL-5g/mL的比例加入回流的硅烷液体,反应1分钟-100分钟得到发红光硅烷功能化碳点。
8.根据权利要求4所述的蓝光激发碳点发光的白光LED的制备方法,其特征是:所述步骤(4)中的硅烷功能化碳点是发黄光的硅烷功能化碳点,或者是发红光、绿光和黄光的三种硅烷功能化碳点中任意两种任意比例的混合体,或者是发红光、绿光和黄光的三种硅烷功能化碳点任意比例的混合体。