CN103060636B - 一种耐腐蚀导电铝合金及其制备方法 - Google Patents

一种耐腐蚀导电铝合金及其制备方法 Download PDF

Info

Publication number
CN103060636B
CN103060636B CN201310016924.6A CN201310016924A CN103060636B CN 103060636 B CN103060636 B CN 103060636B CN 201310016924 A CN201310016924 A CN 201310016924A CN 103060636 B CN103060636 B CN 103060636B
Authority
CN
China
Prior art keywords
melting
alloy
aluminum alloy
aluminium
silicon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310016924.6A
Other languages
English (en)
Other versions
CN103060636A (zh
Inventor
耿振铎
王玉平
常晓晓
杨新伟
徐国亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGZHOU SHAORUI INTELLECTUAL PROPERTY SERVICE CO.,LTD.
QINGYUAN HONGYUE ALUMINUM CO.,LTD.
Original Assignee
Henan Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henan Normal University filed Critical Henan Normal University
Priority to CN201310016924.6A priority Critical patent/CN103060636B/zh
Publication of CN103060636A publication Critical patent/CN103060636A/zh
Application granted granted Critical
Publication of CN103060636B publication Critical patent/CN103060636B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种耐腐蚀导电铝合金及其制备方法，本发明的目的是设计一种耐腐蚀性性能好且具备优良的导电性能的耐腐蚀导电铝合金及其制备方法。本发明的技术方案是，一种耐腐蚀导电铝合金，它的组份为：镁、铁、硅、锰、铈或同等量的镧，铝。其制备方法为：先将铝锭熔融，然后加入镧或铈或以上两种稀土的等量混合稀土，升温直至熔融，过程中保持真空，搅拌均匀，除气除杂，然后浇铸备用；铁、硅、锰中间合金：采用真空熔炼，将铝锭熔融，然后按照合金所需比例添加铁、硅、锰，升温直至完全熔融，然后浇铸备用。本发明具有良好的耐腐蚀性，可以在不增加输电线损的基础上，大大降低铝合金线缆在沿海地区的腐蚀性损耗，提高铝合金线缆在上述环境中的使用寿命。

Description

一种耐腐蚀导电铝合金及其制备方法
技术领域：
    本发明涉及合金材料，特别是一种耐腐蚀导电铝合金及其制备方法。
背景技术：
    目前，我国沿海地区使用的输电线缆大多为传统的导电铝合金，这种线缆虽然满足输电需求，但沿海的自然环境却使传统铝合金导线的使用寿命较短，需要经常更换输电线缆，导致使用成本较高。而传统的5XXX铝镁合金金是最耐海洋性腐蚀的铝合金，常常用于舰船建造等方面，但导电率却无法达到日常输电要求。因此，现在急需一种铝镁合金，在具有较高耐腐蚀性的基础上兼备优良的导电性能。
发明内容：
本发明的目的是设计一种耐腐蚀性性能好且具备优良的导电性能的耐腐蚀导电铝合金及其制备方法。
本发明的技术方案是，一种耐腐蚀导电铝合金，其特征在于：它的重量组份为：2.3-3.6%镁、0.1-0.2%铁、0.05-0.1%硅、0.06-0.1%锰、0.05-0.5%铈或同等量的镧，余量为铝。
一种耐腐蚀导电铝合金的制备方法，其特征在于：Al-RE中间合金：采用真空熔炼，先在750℃下将铝锭熔融，然后加入高纯稀土镧或铈或以上两种稀土的等量混合稀土，升温直至完全熔融，过程中保持真空，搅拌均匀，除气除杂，然后浇铸备用; 铁、硅、锰中间合金: 采用真空熔炼，先在750℃下将铝锭熔融，然后按照合金所需比例添加铁、硅、锰，升温直至完全熔融，过程中保持真空，搅拌均匀，除气除杂，然后浇铸备用。在上述加工工艺中，除镁外其他的合金元素均以中间合金形式加入。
本发明具有良好的耐腐蚀性，可以在不增加输电线损的基础上，大大降低铝合金线缆在沿海地区的腐蚀性损耗，提高铝合金线缆在上述环境中的使用寿命。
附图说明：
   图1是本发明制备的合金表面用扫描隧道电子显微镜扫描显示的图片，
图2是合金微观组织的扫描隧道电子显微镜扫描显示的图片。
具体实施方式：
详细描述实施例，
本发明所述导电铝合金成分按照重量计算，其构成为：2.3-3.6镁（Mg）、0.1-0.2铁（Fe）、0.05-0.1硅（Si）、0.06-0.1锰（Mn）、0.05-0.5铈（Ce）或同等量的镧（La）, 余量为铝（Al）。在具有较高耐腐蚀性的基础上兼备优良的导电性能。其中稀土元素先事先制备成铝-稀土中间合金备用。铝为普通工业纯铝，镁为工业镁锭，铁、硅、锰分别制备成中间合金备用。熔炼时先在750℃下将铝锭熔融，然后依次加入铝锰、铝铁、铝硅中间合金，最后加入铝稀土中间合金，完全熔融后除气除杂，最后在700℃左右水平连铸成为细圆杆材，（具体组分参照表1）。然后经过多道次拉拔及退火，制备成为导线线缆。
各种中间合金制备流程如下。Al-RE中间合金：采用真空熔炼，先在750℃下将铝锭熔融，然后加入高纯稀土镧（La）或（Ce）或以上两种稀土的等量混合稀土，升温直至完全熔融，过程中保持真空，搅拌均匀，除气除杂，然后浇铸备用; 铁、硅、锰中间合金: 采用真空熔炼，先在750℃下将铝锭熔融，然后按照合金所需比例添加铁、硅、锰，升温直至完全熔融，过程中保持真空，搅拌均匀，除气除杂，然后浇铸备用。
上述耐腐蚀导电铝合金，所述铝合金成分按照重量计算，其构成为：2.3-3.6镁（Mg）、0.1-0.2铁（Fe）、0.05-0.1硅（Si）、0.06-0.1锰（Mn）、0.05-0.5铈（Ce）或同等量的镧（La）, 余量为铝（Al）。
【表1】
 将上述合金按照之前所述工艺拉至成线材，退火后测量其工艺性能，结果见表2
【表2】

Claims (2)

1.一种耐腐蚀导电铝合金的制备方法，其特征在于：熔炼时先在750℃下将铝锭熔融，然后依次加入铝锰、铝铁、铝硅中间合金，再加入铝稀土中间合金，完全熔融后除气除杂，最后在700℃左右水平连铸成为细圆杆材，该杆材铝合金重量组份为：2.3-3.6% 镁、0.1-0.2% 铁、0.05-0.1% 硅、0.06-0.1% 锰、0.05-0.5% 铈或同等量的镧，余量为铝；Al-RE 中间合金：采用真空熔炼，先在750℃下将铝锭熔融，然后加入高纯稀土镧或铈升温直至完全熔融，过程中保持真空，搅拌均匀，除气除杂，然后浇铸备用; 铁、硅、锰中间合金: 采用真空熔炼，先在750℃下将铝锭熔融，然后按照合金所需比例添加铁、硅、锰，升温直至完全熔融，过程中保持真空，搅拌均匀，除气除杂，然后浇铸备用。
2.如权利要求1 所述的一种耐腐蚀导电铝合金的制备方法，其特征在于：在上述加工工艺中，除镁外其他的合金元素均以中间合金形式加入。
CN201310016924.6A 2013-01-17 2013-01-17 一种耐腐蚀导电铝合金及其制备方法 Expired - Fee Related CN103060636B (zh)