CN103059803A - 一种涂布用的转移胶水的制法及其涂布方法 - Google Patents

一种涂布用的转移胶水的制法及其涂布方法 Download PDF

Info

Publication number
CN103059803A
CN103059803A CN2012105632009A CN201210563200A CN103059803A CN 103059803 A CN103059803 A CN 103059803A CN 2012105632009 A CN2012105632009 A CN 2012105632009A CN 201210563200 A CN201210563200 A CN 201210563200A CN 103059803 A CN103059803 A CN 103059803A
Authority
CN
China
Prior art keywords
coating
transfer glue
transfer
glue
coated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012105632009A
Other languages
English (en)
Other versions
CN103059803B (zh
Inventor
胥国芳
孙晓
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG TAIBAO PACKAGING PRODUCT CO Ltd
Original Assignee
SHANDONG TAIBAO PACKAGING PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANDONG TAIBAO PACKAGING PRODUCT CO Ltd filed Critical SHANDONG TAIBAO PACKAGING PRODUCT CO Ltd
Priority to CN201210563200.9A priority Critical patent/CN103059803B/zh
Publication of CN103059803A publication Critical patent/CN103059803A/zh
Application granted granted Critical
Publication of CN103059803B publication Critical patent/CN103059803B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明具体涉及一种涂布用的转移胶水的制法及其涂布方法。制法的特征在于步骤如下：1)将酒精、水按1∶1的比例混合，并搅拌均匀，作为稀释剂；2)将树脂乳液和有机热固化聚甲基脲树脂按照1∶0.005的比例混合，并搅拌均匀，作为转移胶粘剂；3)将稀释剂与转移胶水按照1∶20比例混合，搅拌均匀，制得转移胶水。涂布方法的特征在于涂布时采用网纹辊上胶的方式，涂布压力0.2MPa，冷缸压力0.3MPa，烘道张力0.2MPa。本发明具有如下优点：1)转移胶水的粘合力低，增强了转移产品的铝层剥离效果并保护了图案的完整，杜绝了在涂布过程中出现的拉丝现象。2)采用网纹辊上胶的方式，涂布均匀易控制。

Description

一种涂布用的转移胶水的制法及其涂布方法
技术领域
本发明具体涉及一种涂布用的转移胶水的制法及其涂布方法。
背景技术
镭射膜的加工步骤为涂布、转移和分切，技术人员发现在涂布过程中容易发生拉丝的现象，造成涂布后出现毛点，在后续的转移工序中，铝层很难剥离，在剥离时也不能保证图案的完整，废品率高。技术人员经过研究发现，是涂布工序中所用的转移胶水粘结力太强所致。
发明内容
本发明的目的在于解决现有技术镭射膜涂布工艺中所使用的转移胶水粘结力太强，造成涂布后易出现粘合和毛点现象的缺陷，提供一种制作方便、涂布时不会发生拉丝，涂布后不易粘合的涂布用的转移胶水的制法及其涂布方法。
本发明是通过如下技术方案来实现的：
即一种涂布用的转移胶水的制法，其特征在于步骤如下：
1)将酒精、水按1∶1的比例混合，并搅拌均匀，作为稀释剂；
2)将树脂乳液和有机热固化聚甲基脲树脂按照1∶0.005的比例混合，并搅拌均匀，作为转移胶粘剂；
3)将稀释剂与转移胶水按照1∶20比例混合，搅拌均匀，制得转移胶水。
一种涂布用的转移胶水的涂布方法，其特征在于涂布时采用网纹辊上胶的方式，涂布压力0.2mpa，冷缸压力0.3mpa，烘道张力0.2mpa。
作为本发明的一个优选方案：涂布时涂布机的车速90--120米/分钟。
作为本发明的一个优选方案：涂布时烘箱温度为80-120℃。
本发明采用的各种原材料在市场上都很容易获得。其中酒精，树脂乳液，有机热固化聚甲基脲树脂都是通用的商品名称。例如：树脂乳液采用的生产厂家是广东汕头龙湖昌丰化工有限公司，型号为TB-01，有机热固化聚甲基脲树脂采用生产厂家是上海维凯化学品有限公司，型号为FW1017。
本发明具有如下优点：
1)树脂乳液和有机热固化聚甲基脲树脂的配合使用，并添加稀释剂，降低了转移胶水的粘合力，增强了转移产品的铝层剥离效果并保护了图案的完整，杜绝了在涂布过程中出现的拉丝现象。
2)采用网纹辊上胶的方式，涂布均匀易控制。
具体实施方式
实施例1
制作转移胶水的步骤如下：
1)将酒精、水按1∶1的比例混合，并搅拌均匀，作为稀释剂；
2)将树脂乳液和有机热固化聚甲基脲树脂按照1∶0.005的比例混合，并搅拌均匀，作为转移胶粘剂；
3)将稀释剂与转移胶水按照1∶20比例混合，搅拌均匀，制得转移胶水。
涂布时采用网纹辊上胶的方式，涂布压力0.2mpa，冷缸压力0.3mpa，烘道张力0.2mpa。
涂布机的车速90米/分钟。
涂布时烘箱温度为80℃。
本实施例将树脂乳液和有机热固化聚甲基脲树脂的配合使用，并添加稀释剂，降低了转移胶水的粘合力，增强了转移产品的铝层剥离效果并保护了图案的完整，杜绝了在涂布过程中出现的拉丝现象。
本实施例采用网纹辊上胶的方式，涂布均匀易控制。
实施例2
制作转移胶水的步骤同实施例1。
涂布时采用网纹辊上胶的方式，涂布压力0.2mpa，冷缸压力0.3mpa，烘道张力0.2mpa。
涂布机的车速100米/分钟。
涂布时烘箱温度为90℃。
本实施例将树脂乳液和有机热固化聚甲基脲树脂的配合使用，并添加稀释剂，降低了转移胶水的粘合力，增强了转移产品的铝层剥离效果并保护了图案的完整，杜绝了在涂布过程中出现的拉丝现象。
本实施例采用网纹辊上胶的方式，涂布均匀易控制。
实施例3
制作转移胶水的步骤同实施例1。
涂布时采用网纹辊上胶的方式，涂布压力0.2mpa，冷缸压力0.3mpa，烘道张力0.2mpa。
涂布机的车速110米/分钟。
涂布时烘箱温度为100℃。
本实施例将树脂乳液和有机热固化聚甲基脲树脂的配合使用，并添加稀释剂，降低了转移胶水的粘合力，增强了转移产品的铝层剥离效果并保护了图案的完整，杜绝了在涂布过程中出现的拉丝现象。
本实施例采用网纹辊上胶的方式，涂布均匀易控制。

Claims (4)

1.一种涂布用的转移胶水的制法，其特征在于步骤如下：
1)将酒精、水按1∶1的比例混合，并搅拌均匀，作为稀释剂；
2)将树脂乳液和有机热固化聚甲基脲树脂按照1∶0.005的比例混合，并搅拌均匀，作为转移胶粘剂；
3)将稀释剂与转移胶水按照1∶20比例混合，搅拌均匀，制得转移胶水。
2.一种涂布用的转移胶水的涂布方法，其特征在于涂布时采用网纹辊上胶的方式，涂布压力0.2mpa，冷缸压力0.3mpa，烘道张力0.2mpa。
3.根据权利要求2所述的涂布用的转移胶水的涂布方法，其特征在于涂布时涂布机的车速90～120米/分钟。
4.根据权利要求2所述的涂布用的转移胶水的涂布方法，其特征在于涂布时烘箱温度为80～120℃。
CN201210563200.9A 2012-12-24 2012-12-24 一种涂布用的转移胶水的制法及其涂布方法 Active CN103059803B (zh)