CN103059571A - 一种耐寒橡胶 - Google Patents
一种耐寒橡胶 Download PDFInfo
- Publication number
- CN103059571A CN103059571A CN2012105958037A CN201210595803A CN103059571A CN 103059571 A CN103059571 A CN 103059571A CN 2012105958037 A CN2012105958037 A CN 2012105958037A CN 201210595803 A CN201210595803 A CN 201210595803A CN 103059571 A CN103059571 A CN 103059571A
- Authority
- CN
- China
- Prior art keywords
- rubber
- parts
- present
- white carbon
- dicumyl peroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提出了一种耐寒橡胶，所述组合物组分包括以下重量组分：硅橡胶100份，白炭黑50份，二苯基硅二醇4份，三氧化二铁2份，过氧化二异丙苯0.5-2份；还提供了所述组合物制得的胶、制备方法及耐低温评价方法。当过氧化二异丙苯用量为1份时，该橡胶的耐低温性能最佳，做成的密封制品在-80℃环境下正常使用，无裂痕。
Description
技术领域
本发明涉及汽车工业领域，特别涉及一种耐寒橡胶。
背景技术
低温对橡胶制品的物理机械性能影响很大，主要表现在橡胶制品变硬(硬度、拉伸强度升高)、变脆、弹性消失及其他一些老化现象，使其原有质量降低。
目前，汽车里含有大量的橡胶密封件，当汽车在气温很低的环境行驶时，特别像在东北等非常寒冷的地域，橡胶密封件在低温环境下弹性下降，发生脆性损坏，导致漏油漏气等，直接影响汽车的安全行驶。因此，加快新材料的开发速度，提高橡胶制品在寒冷环境中的质量，具有重要的意义。
发明内容
本发明提出一种耐寒橡胶，解决了现有技术中低温对橡胶密封材料的脆性损坏问题。
本发明的技术方案是这样实现的：耐寒橡胶，含有以下物质及重量份：硅橡胶100份，白炭黑50份，二苯基硅二醇4份，三氧化二铁2份，过氧化二异丙苯0.5-2份。
本发明的制备方法与现有的橡胶制备方法相同。
本发明通过加入不同量的过氧化二异丙苯，研究硅橡胶的耐低温性能。
本发明的有益效果是：
(1)本发明获得了一种耐寒橡胶，能够在汽车制造过程中，起到一定的密封作用，降低低温环境对橡胶脆性破坏造成的损失；
(2)本发明获得了一种耐寒的橡胶制品，能够用在汽车零件的各种密封位置，使汽车能够安全行驶。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动性的前提下，还可以根据这些附图获得其他的附图。
图1为本发明实验装置的示意图。
具体实施方式
本发明经过广泛而深入的研究，通过加入不同含量的过氧化二异丙苯，获得一种耐寒橡胶，然后进行耐低温实验，从而完成本发明。本发明的实验装置如图1所示，包括：橡胶开炼机10，平板硫化机20，橡胶裁片机30，耐低温实验40。
硅橡胶生胶
硅橡胶具有优异的耐热性、耐寒性、介电性、耐臭氧和耐大气老化等性能，硅橡胶突出的性能是使用温度宽广，能在-60℃(或更低的温度)至+250℃(或更高的温度)下长期使用。硅橡胶按其硫化特性可分为热硫化型硅橡胶和室温硫化型硅橡胶两类。按性能和用途的不同可分为通用型、超耐低温型、超耐高温型、高强力型、耐油型、医用型等等。按所用单体的不同，可分为甲基乙烯基硅橡胶，甲基苯基乙烯基硅橡胶、氟硅，腈硅橡胶等。
为了达到本发明的耐寒性能，本发明采用了苯基硅橡胶生胶。
白炭黑
白炭黑是白色粉末状X-射线无定形硅酸和硅酸盐产品的总称，主要是指沉淀二氧化硅、气相二氧化硅、超细二氧化硅凝胶和气凝胶，也包括粉末状合成硅酸铝和硅酸钙等。白炭黑是多孔性物质，其组成可用SiO2·nH2O表示，其中nH2O是以表面羟基的形式存在。能溶于苛性碱和氢氟酸，不溶于水、溶剂和酸(氢氟酸除外)。耐高温、不燃、无味、无嗅、具有很好的电绝缘性。
优选地，所述的白炭黑属于沉淀法白炭黑，合成过程如下：
采用水玻璃溶液与酸反应，经沉淀、过滤、洗涤、干燥和煅烧而得到白炭黑。反应式为：Na2SiO3+2H+-＞白炭黑+2Na++H2O
耐寒组分
本发明的耐寒组分包括：
二苯基硅二醇 4
三氧化二铁 2
下面结合具体实施例，进一步阐述本发明。下列实施例中未注明具体条件的实验方法，通常按照国家标准测定。若没有相应的国家标准，则按照通用的国际标准、常规条件、或按照制造厂商所建议的条件进行。除非另外说明，否则所有的份数为重量份，所有的百分比为重量百分比，所述的聚合物分子量为数均分子量。
除非另有定义或说明，本文中所使用的所有专业与科学用语与本领域技术熟练人员所熟悉的意义相同。此外任何与所记载内容相似或均等的方法及材料皆可应用于本发明方法中。
对比例：
选用0.5、1、1.5、2份的过氧化二异丙苯。
硅橡胶100份；白炭黑50份；二苯基硅二醇4份；三氧化二铁2份；过氧化二异丙苯0.5、1、1.5、2份，起耐寒作用的主要是硅橡胶和过氧化二异丙苯。
工艺条件如下：
硅橡胶生胶在双辊开炼机上进行塑炼，辊温在50℃以下，包辊后，依次加入白炭黑、三氧化二铁、二苯基硅二醇、过氧化二异丙苯，打三角包薄通六次后下片。在混炼之前一定要保持辊筒干净，没有被污染。使用平板硫化机进行一段硫化，加压硫化：一段硫化180℃×正硫化时间；热烘箱硫化：二段硫化200℃×6h。将硅橡胶硫化胶在冲片机上压成哑铃型试片进行耐低温实验。
耐低温实验过程：将哑铃型试样放置在高低温试验箱中，温度以10℃为间隔，从0℃降至-100℃，试样在每个温度下停放10分钟后，取出试样测试其硬度、进行拉伸强度和断裂伸长率实验并用小锤直接敲打试样观察其脆断性能，然后计算性能保持率。
C＝b/a×100％
C-性能保持率；a-浸泡前的硬度、拉伸强度和断裂伸长率；
b-浸泡后的硬度、拉伸强度和断裂伸长率
该胶的性能及耐低温性能如下表所示：
从上表可以看出，当过氧化二异丙苯用量为1份时，制得的橡胶耐低温性能最优。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (3)
1.一种耐寒橡胶，包含主体橡胶，其特征在于，包括：含有以下组分及重量份：硅橡胶100份，白炭黑50份，二苯基硅二醇4份，三氧化二铁2份，过氧化二异丙苯0.5-2份。
2.根据权利要求1所述的耐寒橡胶，其特征在于，所述的硅橡胶为苯基硅橡胶。
3.根据权利要求1所述的耐寒橡胶，其特征在于，所述的白炭黑为沉淀法白炭黑。