CN103045094A - Special micaceous iron epoxy intermediate paint - Google Patents
Special micaceous iron epoxy intermediate paint Download PDFInfo
- Publication number
- CN103045094A CN103045094A CN 201110313036 CN201110313036A CN103045094A CN 103045094 A CN103045094 A CN 103045094A CN 201110313036 CN201110313036 CN 201110313036 CN 201110313036 A CN201110313036 A CN 201110313036A CN 103045094 A CN103045094 A CN 103045094A
- Authority
- CN
- China
- Prior art keywords
- pigment
- natural
- special
- thinner
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to special micaceous iron epoxy intermediate paint. The special micaceous iron epoxy intermediate paint is prepared from pure water, electrophoretic paint, phosphide paint, a pigment, a thinner and a filler, wherein the thinner is a natural plant solvent refined from plant juice, and the pigment is a natural pigment or a pigment processed from natural matters. All components of the special micaceous iron epoxy intermediate paint disclosed by the invention have no toxic chemical solvents, such as benzene, methylbenzene and the like, and the special micaceous iron epoxy intermediate paint further has the advantages of appropriate amount of mercury, aluminum, cadmium, lead and other heavy metal ions, no irritant odor, no volatilization of fluoric acid ester toxic gas, healthy and environment-friendly properties, excellent performance, simple construction and good stability.
Description
Technical field
The invention belongs to the metallic paint field, be specifically related to a kind of special cloud iron hoop oxygen intermediate coat.
。
Background technology
The chemosynthesis lacquer contains benzene, formaldehyde, heavy metal etc. mostly, and a large amount of uses can cause atmosphere, Land pollution and Air quality to descend, and seriously influences for people's living environment and healthy bringing.Along with the reinforcement of society to Environmental awareness, this environment that people more and more pay attention to surviving, in order to limit objectionable impurities to the pollution of human ecological environment, the Chinese government has issued the national standards such as GB18581-2001 " limits of harmful substances in the coating ", GB18582-2001 " limits of harmful substances in the coating ".The formulation of standard limits and has reduced the pollution of objectionable impurities to a certain extent, but is still to contain the objectionable impuritiess such as a certain amount of heavy metal, formaldehyde, alkane alkene organism, isocyanic ester in the product that can be up to standard.Tradition colour polyurethane furniture lacquer can distribute poisonous irritant gas, is detrimental to health, and complex process, must the professional construct the construction inconvenience of doing it yourself.And much environment-friendly type coatings are in order to reach environmental protection, and some performances after the paint film forming can not be guaranteed.
Summary of the invention
What the present invention will solve is exactly that existing chemosynthesis lacquer easily causes environmental pollution because mostly containing benzene, formaldehyde, heavy metal etc., affect the problem of HUMAN HEALTH, a kind of heavy metal ion such as chemical classes solvent and mercury, aluminium, chromium that do not contain are provided, nontoxic having no irritating odor, and easy construction, widely applicable MED high-performance electrophoresis lacquer.
The present invention is prepared and is got by natural resin, thinner, pigment, filler, the weight proportion of each component is: natural resin 58-62%, pigment 8-12%, filler 10-15%, thinner 15-20%, wherein natural resin is got by vegetables oil and vegetable solid resin, the natural phant solvent of thinner for from water, refining, and pigment is natural pigment or natural goods processed pigment.
The natural resin that the present invention adopts is got at 280 ℃ of-290 ℃ of lower heat refinings by weight by following ingredients: oleum lini 60-63%, tung oil 14-16%, rosin 11-13%, turps 9-11%, wherein oleum lini is that essence is floated type, and tung oil, rosin, turps are state's one-level.
The thinner that the present invention adopts is turps or spearmint oil; Pigment is selected natural pigment or natural goods processed pigment, such as titanium dioxide, and organic middle Huang; Filler is available calcium carbonate, talcum powder, coarse whiting etc., and for reaching good extinction effect, preferred calcium carbonate is the preparation of convenient lacquer, preferred calcium carbonate superfine powder.
1
The present invention has following advantage:
1, each moiety is and does not contain the heavy metal ion such as the poisonous chemical classes solvent such as benzene, toluene and mercury, aluminium, cadmium, lead, does not namely contain any toxic and harmful substance.
2, can distribute natural plant fragrance.
3, poisonous harmless, have no irritating odor floride-free acid esters poison gas volatilization, health environment-friendly.
4, excellent performance, fast drying, color various, bright-colored, ornamental strong, sticking power is good, hardness is high, opacifying power is high, snappiness is good, paint film is plentiful, hard, the moisture-proof scrubbing resistance.
5, the present invention constructs simply, uses widely, can brush on iron and steel, woodenware, cement wall surface, and paint film is plentiful, hard, the moisture-proof scrubbing resistance, and levelling property is splendid, and feel is fine and smooth, and is inhibited from yellowing, especially can play wood furniture
Test item | Technical indicator | Assay |
Benzene % | ≤0.5 | Do not detect |
Toluene and dimethylbenzene summation % | 10 | Do not detect |
Well provide protection.
Table 1 is the detected result of the thinner of the present invention's use, and wherein benzene, toluene and detecting of dimethylbenzene summation are limited to 0.001%:
Table 1
Table 2 is the special cloud iron hoop of the present invention oxygen intermediate coat feature of environmental protection detected result, wherein benzene, toluene and detecting of dimethylbenzene summation are limited to 0.001%, detecting of dissoluble lead is limited to 0.5mg/kg, and detecting of soluble cadmium and soluble chromium is limited to 0.3mg/kg, and detecting of soluble mercury is limited to 0.01mg/kg:
Table 2
Table 3 is performance test results of the present invention:
Table 3
Embodiment
Embodiment 1
Oleum lini 600kg, tung oil 140kg are dropped in the reactor, stir and be warming up to 280 ℃-290 ℃, then be incubated to viscosity and reach-4 glasss of 150-160s/ (25 ± 2) ℃.Cool to 260 ℃-270 ℃, add rosin 110kg, reheat, in the time of 280 ℃, continue to be incubated to viscosity and be coated with-4 glasss of 300-320s/ (25 ± 2) ℃.Then be cooled to 260 ℃, go out still with turps 90kg latting drown, reach the viscosity that needs: be coated with-4 glasss of 180-200s/ (25 ± 2) ℃. after reaching fineness≤30um after filtration, it is for subsequent use that check enters tank.
Get natural resin 580kg, titanium dioxide 80kg, fineness is 325 purpose calcium carbonate superfine powder 100kg, turps 150kg.The 300kg natural resin is dropped in the material pot, add titanium dioxide 80kg, calcium carbonate superfine powder 100kg, add 100kg turps again and grind, ground 40-60 minute, it is fixed that milling time is come by required paint fineness.Remaining 280kg natural resin and 50kg turps are after the paint detection reaches fineness≤35um, add by amount according to required viscosity index, continue grinding and keep fineness≤35um, fineness, viscosity touch the mark rear canned, obtain white paint, outward appearance is even white fluid.
Embodiment 2
Raw material oleum lini 624kg, tung oil 156kg are dropped in the reactor, stir and be warming up to 280 ℃-290 ℃, then be incubated to reach to viscosity and be coated with-4 glasss of 150-160s/ (25 ± 2) ℃.Add rosin 120kg after being cooled to 260 ℃-270 ℃, reheat, in the time of 280 ℃, continue to be incubated to viscosity and be coated with-4 glasss of 300-320s/ (25 ± 2) ℃. then be cooled to 260 ℃, go out still with turps 100kg latting drown, reach the viscosity that needs and be coated with-4 glasss of 180-200/ (25 ± 2) ℃.After reaching fineness≤35um after filtration, it is for subsequent use that check enters tank.
Get the 600kg natural resin, organic middle yellow 100kg, fineness is 325 purpose calcium carbonate superfine powder 125kg, turps 175kg.The 400kg natural resin is dropped in the material pot, add organic middle yellow 100kg, calcium carbonate superfine powder 125kg, add 100kg turps again and ground 40-60 minute, it is fixed that milling time is come by required paint fineness.Remaining 200kg natural resin and 75kg turps add by amount according to required viscosity index after the paint detection reaches fineness≤35um again, continue grinding and keep fineness≤35um, and fineness, viscosity touch the mark rear canned, obtain this lacquer.
Embodiment 3
Raw material oleum lini 630kg, tung oil 145kg are dropped in the reactor, stir and be warming up to 280 ℃-290 ℃, then be incubated to reach to viscosity and be coated with-4 glasss of 150-160s/ (25 ± 2) ℃.Add rosin 130kg after being cooled to 260 ℃-270 ℃, reheat, in the time of 280 ℃, continue to be incubated to viscosity and be coated with-4 glasss of 300-320s/ (25 ± 2) ℃. then be cooled to 260 ℃, go out still with turps 95kg latting drown, reach the viscosity that needs and be coated with-4 glasss of 180-200/ (25 ± 2) ℃.After reaching fineness≤35um after filtration, it is for subsequent use that check enters tank.
Get the 600kg natural resin, phthalocyanine blue 100kg, fineness is 325 purpose calcium carbonate superfine powder 125kg, turps 175kg.The 400kg natural resin is dropped in the material pot, add phthalocyanine blue 100kg, calcium carbonate superfine powder 125kg, add 100kg turps again and ground 40-60 minute, it is fixed that milling time is come by required paint fineness.Remaining 200kg natural resin and 75kg turps add by amount according to required viscosity index after the paint detection reaches fineness≤35um again, continue grinding and keep fineness≤35um, and fineness, viscosity touch the mark rear canned, obtain this lacquer.
The present invention is the single-component prescription, viscosity 70-90s/25 ℃, need not add other raw materials during use, and can directly brush.
Special cloud iron hoop oxygen intermediate coat is prepared and is got by natural resin, thinner, pigment, filler, and wherein natural resin is got by vegetables oil and vegetable solid resin.Each moiety of the present invention does not contain the heavy metal ion such as the poisonous chemical classes solvent such as benzene, toluene and mercury, aluminium, cadmium, lead, and is nontoxic, has no irritating odor, floride-free acid esters poison gas volatilization, and health environment-friendly, excellent performance, construction is simple, and is widely applicable.
Claims (6)
1. special cloud iron hoop oxygen intermediate coat, it is characterized in that preparing and getting by water-resistant paint, thinner, filler, the weight proportion of each component is: water-resistant paint 58-62%, pigment 8-12%, filler 10-15%, thinner 15-20%, wherein natural resin is got by vegetables oil and vegetable solid resin, the natural phant solvent of thinner for refining from water, pigment is natural pigment or natural goods processed pigment.
2. according to claim 1, special cloud iron hoop oxygen intermediate coat is characterized in that the weight proportion of natural resin composition is: oleum lini 60-63%, and tung oil 14-16%, rosin 11-13%, turps 9-11% gets through the high temperature heat refining.
3. special cloud iron hoop oxygen intermediate coat according to claim 2 is characterized in that natural resin gets at 280 ℃ of-290 ℃ of lower heat refinings, and wherein oleum lini is that essence is floated type, and tung oil, rosin, turps are state's one-level.
4. according to claim 1 and 2 or 3 described special cloud iron hoop oxygen intermediate coats, it is characterized in that thinner is turps or spearmint oil.
5. according to claim 1 and 2 or 3 described special cloud iron hoop oxygen intermediate coats, it is characterized in that filler is calcium carbonate.
6. special cloud iron hoop oxygen intermediate coat according to claim 4 is characterized in that filler is calcium carbonate.