CN103450803A - Crystal varnish - Google Patents
Crystal varnish Download PDFInfo
- Publication number
- CN103450803A CN103450803A CN 201210176724 CN201210176724A CN103450803A CN 103450803 A CN103450803 A CN 103450803A CN 201210176724 CN201210176724 CN 201210176724 CN 201210176724 A CN201210176724 A CN 201210176724A CN 103450803 A CN103450803 A CN 103450803A
- Authority
- CN
- China
- Prior art keywords
- pigment
- natural
- varnish
- crystal varnish
- turps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses crystal varnish. The crystal varnish is prepared from water-proof finish, phosphatization paint, a pigment, a diluent and a filling material, wherein the diluent is a natural plant solvent extracted from a plant juice. The pigment is a natural pigment or a pigment prepared from natural materials. The crystal varnish comprises the natural ingredients, does not contain toxic chemical solvents such as benzene and toluene, contains an appropriate amount of heavy metal ions such as mercury, aluminum, cadmium and lead, has no excitant smell, does not volatilize fluoric acid ester poison gas, is health and environmentally friendly, has excellent performances, is convenient for construction and has a wide application range.
Description
Technical field
The invention belongs to the wood lacquer field, be specifically related to a kind of crystal varnish.
Background technology
The chemosynthesis paint is mostly containing benzene, formaldehyde, heavy metal etc., and a large amount of uses can cause atmosphere, Land pollution and Air quality to descend, and gives people's living environment and healthyly brings serious impact.Along with the reinforcement of society to Environmental awareness, people more and more focus on this environment of existence, in order to limit the pollution of objectionable impurities to human ecological environment, the Chinese government has issued the national standards such as GB18581-2001 " limits of harmful substances in coating ", GB18582-2001 " limits of harmful substances in coating ".The formulation of standard limits and has reduced the pollution of objectionable impurities to a certain extent, but is still to contain the objectionable impuritiess such as a certain amount of heavy metal, formaldehyde, alkane alkene organism, isocyanic ester in product that can be up to standard.Tradition colour polyurethane furniture lacquer can distribute poisonous irritant gas, is detrimental to health, and complex process, must the professional construct, the construction inconvenience of doing it yourself.And much environment-friendly type coatings are in order to reach environmental protection, some performances after the paint film forming can not be guaranteed.
Summary of the invention
What the present invention will solve is exactly that existing chemosynthesis paint is because mostly easily causing environmental pollution containing benzene, formaldehyde, heavy metal etc., affect the problem of HUMAN HEALTH, a kind of heavy metal ion such as chemical classes solvent and mercury, aluminium, chromium that do not contain are provided, nontoxic having no irritating odor, and easy construction, widely applicable MED high-performance electrophoresis paint.
The present invention is prepared and is obtained by natural resin, thinner, pigment, filler, the weight proportion of each component is: natural resin 58-62%, pigment 8-12%, filler 10-15%, thinner 15-20%, wherein natural resin is obtained by vegetables oil and vegetable solid resin, the natural phant solvent of thinner for refining from water, and pigment is natural pigment or natural goods processed pigment.
The natural resin that the present invention adopts is obtained at 280 ℃ of-290 ℃ of lower heat refinings by weight by following ingredients: oleum lini 60-63%, tung oil 14-16%, rosin 11-13%, turps 9-11%, wherein oleum lini is that essence is floated type, and tung oil, rosin, turps are state's one-level.
The thinner that the present invention adopts is turps or spearmint oil; Pigment is selected natural pigment or natural goods processed pigment, as titanium dioxide, and organic middle Huang; Filler is available calcium carbonate, talcum powder, coarse whiting etc., for reaching good extinction effect, and preferred calcium carbonate, for convenience of the preparation of paint, preferred calcium carbonate superfine powder.
The present invention has following advantage:
1, each moiety is natural product,, containing heavy metal ion such as the poisonous chemical classes solvent such as benzene, toluene and mercury, aluminium, cadmium, lead, does not contain any toxic and harmful substance.
2, can distribute natural plant fragrance.
3, poisonous harmless, have no irritating odor, floride-free acid esters poison gas volatilization, health environment-friendly.
4, excellent performance, fast drying, color various, bright-colored, ornamental strong, sticking power is good, hardness is high, opacifying power is high, snappiness is good, paint film is plentiful, hard, the moisture-proof scrubbing resistance.
5, the present invention constructs simply, uses widely, can brush on iron and steel, woodenware, cement wall surface, paint film is plentiful,
| Test item | Technical indicator | Assay |
| Benzene % | ≤0.5 | Do not detect |
| Toluene and dimethylbenzene summation % | 10 | Do not detect |
Hard, the moisture-proof scrubbing resistance, levelling property is splendid, and the feel exquisiteness is inhibited from yellowing, especially to wood furniture, can play a very good protection.
Table 1 is the detected result of the thinner of the present invention's use, and wherein benzene, toluene and detecting of dimethylbenzene summation are limited to 0.001%:
Table 1
Table 2 is crystal varnish feature of environmental protection detected result of the present invention, wherein benzene, toluene and detecting of dimethylbenzene summation are limited to 0.001%, detecting of dissoluble lead is limited to 0.5mg/kg, and detecting of soluble cadmium and soluble chromium is limited to 0.3mg/kg, and detecting of soluble mercury is limited to 0.01mg/kg:
Table 2
Table 3 is performance test results of the present invention:
Table 3
Embodiment
Embodiment 1
Oleum lini 600kg, tung oil 140kg are dropped in reactor, stir and be warming up to 280 ℃-290 ℃, then be incubated to viscosity and reach-4 glasss of 150-160s/ (25 ± 2) ℃.Cool to 260 ℃-270 ℃, add rosin 110kg, reheat, continue to be incubated to viscosity painting-4 glasss of 300-320s/ (25 ± 2) ℃ in the time of 280 ℃.Then be cooled to 260 ℃, go out turps 90kg latting drown for still, reach the viscosity needed: be coated with-4 glasss of 180-200s/ (25 ± 2) ℃. after reaching fineness≤30um after filtration, check into tank standby.
Get natural resin 580kg, titanium dioxide 80kg, fineness is 325 purpose calcium carbonate superfine powder 100kg, turps 150kg.The 300kg natural resin is dropped in the material pot, add titanium dioxide 80kg, calcium carbonate superfine powder 100kg, then add 100kg turps to grind, grind 40-60 minute, it is fixed that milling time is come by required paint fineness.Remaining 280kg natural resin and 50kg turps are after the paint detection reaches fineness≤35um, add by amount according to required viscosity index, continue to grind maintenance fineness≤35um, fineness, viscosity touch the mark rear canned, obtain white paint, outward appearance is even white fluid.
Embodiment 2
Raw material oleum lini 624kg, tung oil 156kg are dropped in reactor, stir and be warming up to 280 ℃-290 ℃, then be incubated to viscosity and reach painting-4 glass 150-160s/ (25 ± 2) ℃.Add rosin 120kg after being cooled to 260 ℃-270 ℃, reheat, in the time of 280 ℃, continue to be incubated to viscosity painting-4 glasss of 300-320s/ (25 ± 2) ℃. then be cooled to 260 ℃, go out turps 100kg latting drown for still, reach the viscosity needed and be coated with-4 glasss of 180-200/ (25 ± 2) ℃.After reaching fineness≤35um after filtration, check into tank standby.
Get the 600kg natural resin, organic middle yellow 100kg, fineness is 325 purpose calcium carbonate superfine powder 125kg, turps 175kg.The 400kg natural resin is dropped in the material pot, add organic middle yellow 100kg, calcium carbonate superfine powder 125kg, then add 100kg turps to grind 40-60 minute, it is fixed that milling time is come by required paint fineness.Remaining 200kg natural resin and 75kg turps, after paint detects and to reach fineness≤35um, then add by amount according to required viscosity index, continue to grind to keep fineness≤35um, and fineness, viscosity touch the mark rear canned, obtain crystal varnish.
Claims (5)
1. crystal varnish, the weight proportion that it is characterized in that each component is: water-resistant paint 58-62%, pigment 8-12%, filler 10-15%, thinner 15-20%, wherein natural resin is obtained by vegetables oil and vegetable solid resin, the natural phant solvent of thinner for refining from water, and pigment is natural pigment or natural goods processed pigment.
2. crystal varnish according to claim 1 is characterized in that the weight proportion of natural resin composition is: oleum lini 60-63%, and tung oil 14-16%, rosin 11-13%, turps 9-11%, obtain through the high temperature heat refining.
3. crystal varnish according to claim 2, is characterized in that natural resin obtains at 280 ℃ of-290 ℃ of lower heat refinings, and wherein oleum lini is that essence is floated type, and tung oil, rosin, turps are state's one-level.
4. according to claim 1 or 2 or 3 described crystal varnish, it is characterized in that thinner is turps or spearmint oil.
5. according to claim 1 or 2 or 3 described crystal varnish, it is characterized in that filler is calcium carbonate.