CN103045030B - A kind of waterproof paint - Google Patents
A kind of waterproof paint Download PDFInfo
- Publication number
- CN103045030B CN103045030B CN201210543079.3A CN201210543079A CN103045030B CN 103045030 B CN103045030 B CN 103045030B CN 201210543079 A CN201210543079 A CN 201210543079A CN 103045030 B CN103045030 B CN 103045030B
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- waterproof paint
- waterproof
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of waterproof paint, component and the proportioning of this coating are as follows, with parts by weight, polyvinyl alcohol 20-30 part, hydroxyl Synolac 15-20 part, aminoresin 20-25 part, red iron oxide 10-15 part, water glass 5-10 part, pitch 10-15 part, Sodium hexametaphosphate 99 3-5 part, tributyl phosphate 1-5 part, phenylformic acid 10-15 part, zinc oxide 2-5 part, glycerine 1-3 part.This water-borne coatings environmentally safe, harmless, safety and environmental protection.
Description
Technical field
The present invention relates to waterproof paint, especially a kind of high molecular water-proof paint and preparation method thereof being suitable for building trade application.
Background technology
The waterproof paint of building trade application is generally at normal temperatures in the viscous liquid high molecular synthetic material without solid shape, forms waterproof membrane after coating after the volatilization of solvent or the evaporation of moisture or reaction solidification in substrate surface.Current building trade water-proof material used be generally divided into the flexible waterproof material that comprises waterproof roll, waterproof paint, sealing cement etc. and based on cement matrix, add the rigidity water-proofing material of water-resisting agent and other auxiliary agents.Although kind is enriched, generally have physical and mechanical property difference, work-ing life is short, excessive with the gap in work-ing life of buildings, the shortcomings such as range of application is narrow and small, dangerous environmental protection.
CN102108234A discloses a kind of colorful environment-friendly synthetic macromolecular waterproof coating, it is grouped into by the one-tenth of following weight part: petroleum resin 3-7 part, SEBS5-15 part, SBS5-15 part, thermoplastic polyurethane elastomer 510 parts, terpine resin 4-8 part, poly alpha methylstyrene 4-8 part, tung oil 2-5 part, mica powder 10-15 part, antioxidant D 0.2-0.5 part, antioxidant 264 0.2-0.5 part, defoamer 0.2-0.5 part, UV light absorber 0.3-0.5 part, 120# solvent 35-45 part, ethyl acetate 5-15 part, mill base 1-3 part.The colorful environment-friendly synthetic macromolecular waterproof coating of this invention has certain acid and alkali-resistance and uviolizing, heat insulation, anti-aging, waterproof, anti-leakage performance, and shortcoming is that the embrittlement phenomenon under cold condition is obvious, tensile strength and elongation at break lower.
CN102079918A discloses a kind of building water-proof paint, its composition weight percent is as follows: Vinyl Acetate Copolymer 30-50, ethene-vinyl acetate polymkeric substance 20-30, kaolin 6-10, film coalescence aid 0.5-2.5, coarse whiting 6-10, dispersion agent 0.1-3, defoamer 0.3-0.8, silicon sol 3-8, the deionized water of surplus.The building water-proof paint easy construction that this invention provides, with low cost, good leak-proof effect, shortcoming is high-low temperature resistant and chemical corrosion resistance inequality, and mechanical property is also poor.
Summary of the invention
The object of the invention is, overcomes the deficiencies in the prior art, provides a kind of and has excellent high molecular water-proof paint, be suitable for being coated in multiple substrate surface.
For achieving the above object, the present invention adopts following technical scheme:
A kind of waterproof paint, component and the proportioning of this coating are as follows, with parts by weight, polyvinyl alcohol 20-30 part, hydroxyl Synolac 15-20 part, aminoresin 20-25 part, red iron oxide 10-15 part, water glass 5-10 part, pitch 10-15 part, Sodium hexametaphosphate 99 3-5 part, tributyl phosphate 1-5 part, phenylformic acid 10-15 part, zinc oxide 2-5 part, glycerine 1-3 part.
The preparation method of high molecular water-proof paint of the present invention, comprises the following steps:
(1) hydroxyl Synolac and aminoresin emulsification are heated to 60-170 DEG C;
(2) add red iron oxide, water glass, pitch, Sodium hexametaphosphate 99, tributyl phosphate, phenylformic acid, zinc oxide, glycerine also stirs 1-5 hour;
(3) add polyvinyl alcohol, high-speed stirring 30-60min, be cooled to room temperature.
Compared with prior art, the present invention has following beneficial effect:
1, anticorrosive, anti-aging, bonding force is strong, high temperature resistant, low temperature resistant, ductility is good, elongation at break is high, and multiple excellent properties rolls into one.
2, water-borne coatings environmentally safe, harmless, safety and environmental protection.
Embodiment
For better the present invention being described, be convenient to understand technical scheme of the present invention, typical but non-limiting embodiment of the present invention is as follows:
Embodiment 1:
A kind of waterproof paint, component and the proportioning of this coating are as follows, with parts by weight, polyvinyl alcohol 20 parts, hydroxyl Synolac 15 parts, 20 parts, aminoresin, red iron oxide 10 parts, water glass 5 parts, pitch 10 parts, Sodium hexametaphosphate 99 3 parts, tributyl phosphate 1 part, 10 parts, phenylformic acid, 2 parts, zinc oxide, glycerine 1 part.
Embodiment 2:
A kind of waterproof paint, component and the proportioning of this coating are as follows, with parts by weight, polyvinyl alcohol 30 parts, hydroxyl Synolac 20 parts, 25 parts, aminoresin, red iron oxide 15 parts, water glass 10 parts, pitch 15 parts, Sodium hexametaphosphate 99 5 parts, tributyl phosphate 5 parts, 15 parts, phenylformic acid, 5 parts, zinc oxide, glycerine 3 parts.
Claims (1)
1. a waterproof paint, is characterized in that: component and the proportioning of this coating are as follows, with parts by weight, polyvinyl alcohol 20-30 part, hydroxyl Synolac 15-20 part, aminoresin 20-25 part, red iron oxide 10-15 part, water glass 5-10 part, pitch 10-15 part, Sodium hexametaphosphate 99 3-5 part, tributyl phosphate 1-5 part, phenylformic acid 10-15 part, zinc oxide 2-5 part, glycerine 1-3 part.