CN103031033A - 一种粉末涂料的生产配方 - Google Patents
一种粉末涂料的生产配方 Download PDFInfo
- Publication number
- CN103031033A CN103031033A CN2012104103116A CN201210410311A CN103031033A CN 103031033 A CN103031033 A CN 103031033A CN 2012104103116 A CN2012104103116 A CN 2012104103116A CN 201210410311 A CN201210410311 A CN 201210410311A CN 103031033 A CN103031033 A CN 103031033A
- Authority
- CN
- China
- Prior art keywords
- extruder
- coating
- production formula
- formula
- powder coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种粉末涂料的生产配方,由环氧树脂、聚酯树脂、颜填料、助剂和固化促进剂配合制成,其质量百分比为:环氧树脂28%-30%,聚酯树脂28%-30%,颜填料36%-40%,助剂3%-4%,固化促进剂0.5%-1%。其制备过程是,(1)将上述各种原料按照配方比例投入混合机中的混合锅内,搅拌均匀,搅拌时间120-300秒;(2)混合后的原料倒入挤出机,挤出机温度达到生产要求时,开启主机:(3)将挤出机挤出后的片料倒入微粉机中的微粉斗内,按规定开起微粉机,制成成品。本发明粉末涂料降低了涂料的胶化时间,使涂膜在短时间内固化,从而避免涂膜表面缺陷的出现。
Description
技术领域
本发明涉及一种粉末涂料的生产配方。
背景技术
工件在固化过程中,有许多挥发物放出,这些挥发物对涂膜表面造成许多缺陷,如流平不好起皱,有划痕。
发明内容
本发明提出一种粉末涂料的生产配方,解决了现有技术中粉末涂料的缺点,使涂膜在短时间内固化,从而避免涂膜缺陷的出现。
本发明的技术方案是这样实现的:
一种粉末涂料的生产配方,由环氧树脂、聚酯树脂、颜填料、助剂和固化促进剂配合制成,其质量百分比为:环氧树脂28%-30%,聚酯树脂28%-30%,颜填料36%-40%,助剂3%-4%,固化促进剂0.5%-1%。
进一步,上述混合原料依次经过混合机、挤出机和微粉机,所述混合机中设有混合锅;所述微粉机中设有微粉斗,所述挤出机挤出后的片料是倒入所述微粉斗内。
较佳地,上述各原料混合后倒入所述混合机中搅拌均匀,搅拌时间120-300秒,使各原料达到最佳混合状态,制出的粉末涂料质量更高。
上述粉末涂料的生产工艺是:
(1)将上述各种原料按照配方比例投入混合机中的混合锅内,搅拌均匀,搅拌时间120-300秒。
(2)混合后的原料倒入挤出机,所述挤出机温度达到生产要求时,开启主 机。
(3)将上述挤出机挤出后的片料倒入微粉机中的微粉斗内,按规定开起微粉机,制成成品。
(4)质检部取样检验合格后计量包装入库。
上述混合机、挤出机、微粉机是生产粉末涂料的三台设备,中间人工接料,片料是挤出压片后的半成品。
本发明粉末涂料的优点是,在涂料中添加固化促进剂,降低涂料的固化时间,涂膜在短时间内固化,从而防止涂膜缺陷的出现。
由于降低了涂料的胶化时间,工件的挥发物放出后,没有对涂膜造成影响,从而解决了客户在使用过程中出现的涂膜缺陷问题。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案,下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍,显而易见地,下面描述中的附图仅仅是本发明的一些实施例,对于本领域普通技术人员来讲,在不付出创造性劳动的前提下,还可以根据这些附图获得其他的附图。
图1为本发明的生产工艺流程示意图。
具体实施方式
下面将结合本发明实施例中的附图,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
一种粉末涂料的生产配方,由环氧树脂、聚酯树脂、颜填料、助剂和固化促进剂配合制成,其质量百分比为:环氧树脂28%-30%,聚酯树脂28%-30%,颜填料36%-40%,助剂3%-4%,固化促进剂0.5%-1%。
通过在涂料中添加固化促进剂,降低涂料的固化时间,涂膜在短时间内固化,从而防止涂膜缺陷的出现。
上述混合原料依次经过混合机、挤出机和微粉机,所述混合机中设有混合锅;所述微粉机中设有微粉斗,所述挤出机挤出后的片料是倒入所述微粉斗内。
较佳地,上述各原料混合后倒入所述混合机中搅拌均匀,搅拌时间120-300秒,使各原料达到最佳混合状态,制出的粉末涂料质量更高。
参看图1,上述粉末涂料经过如下步骤完成制作过程:
(1)将上述各种原料按照配方比例投入混合机中的混合锅内,搅拌均匀,搅拌时间120-300秒。
(2)混合后的原料倒入挤出机,所述挤出机温度达到生产要求时,开启主机。
(3)将上述挤出机挤出后的片料倒入微粉机中的微粉斗内,按规定开起微粉机,制成成品。
(4)质检部取样检验合格后计量包装入库。
上述混合机、挤出机、微粉机是生产粉末涂料的三台设备,设备与设备之间是人工接料,片料是挤出压片后的半成品。
由于降低了涂料的胶化时间,工件的挥发物放出后,没有对涂膜造成影响,从而解决了客户在使用过程中出现的涂膜缺陷问题。固化促进剂的选择和用量。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (3)
1.一种粉末涂料的生产配方,其特征在于,由环氧树脂、聚酯树脂、颜填料、助剂和固化促进剂配合制成,其质量百分比为:环氧树脂28%-30%,聚酯树脂28%-30%,颜填料36%-40%,助剂3%-4%,固化促进剂0.5%-1%。
2.如权利要求1所述的一种粉末涂料的生产配方,其特征在于,上述混合原料依次经过混合机、挤出机和微粉机。
3.如权利要求2所述的一种粉末涂料的生产配方,其特征在于,上述各原料混合后倒入所述混合机中搅拌均匀,搅拌时间120-300秒。