CN103028818A - 一种船用双相不锈钢厚板co2气体保护焊工艺 - Google Patents

一种船用双相不锈钢厚板co2气体保护焊工艺 Download PDF

Info

Publication number
CN103028818A
CN103028818A CN2011102969139A CN201110296913A CN103028818A CN 103028818 A CN103028818 A CN 103028818A CN 2011102969139 A CN2011102969139 A CN 2011102969139A CN 201110296913 A CN201110296913 A CN 201110296913A CN 103028818 A CN103028818 A CN 103028818A
Authority
CN
China
Prior art keywords
welding
stainless steel
layer
gas shielded
thick plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102969139A
Other languages
English (en)
Inventor
王东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AVIC DINGHENG SHIPBUILDING Co Ltd
Original Assignee
AVIC DINGHENG SHIPBUILDING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by AVIC DINGHENG SHIPBUILDING Co Ltd filed Critical AVIC DINGHENG SHIPBUILDING Co Ltd
Priority to CN2011102969139A priority Critical patent/CN103028818A/zh
Publication of CN103028818A publication Critical patent/CN103028818A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种船用双相不锈钢厚板CO2气体保护焊工艺。首先采用的焊丝为药芯焊丝，然后加工待焊工件坡口和清理坡口及附近表面，并对待焊工件进行烘干，最后进行CO2气体保护焊，焊接线能量控制在1.7-2.5kJ，焊接层间温度在150oC以下。本发明的船用双相不锈钢厚板CO2气体保护焊工艺，增加了焊丝的熔敷速率，提高了不锈钢的焊接效率，焊接接头具有良好的力学性能和抗腐蚀性能。

Description

一种船用双相不锈钢厚板CO2气体保护焊工艺
技术领域
本发明涉及一种船用双相不锈钢厚板CO2气体保护焊工艺。
背景技术
双相不锈钢作为一种含有铁素体和奥氏体两相的不锈钢，其综合了铁素体不锈钢钢和奥氏体不锈钢两者的优点，具有良好的综合力学性能和耐蚀性。与奥氏体钢相比，具有优良的耐晶间腐蚀、点蚀、应力腐蚀的能力和较低的热裂倾向；与铁素体不锈钢相比，具有较低的脆化倾向，因此被广泛应用于化工、海洋工程和船舶建造等行业。利用双相不锈钢建造化学品船，可使其耐蚀性显著提高，可承载的化学品达几百种，且各舱之间不会相互渗透，船舶安全性大大提高。
对于双相不锈钢，其焊接接头力学性能和耐蚀性主要取决于组织中铁素体和奥氏体两相的适当比例。但由于焊接是一个局部加热过程，加热和冷却速度都较快，不可避免引起焊缝和热影响区相组成的改变，继而降低了焊接接头的力学性能（尤其是冲击韧性）和耐蚀性。因此，双相不锈钢的焊接要严格控制热输入。由于焊件结构、位置的复杂性，目前国内船舶建造过程中仍然以手工焊为主。其中，双相不锈钢的焊接工艺主要为手工焊条电弧焊和全氩气保护的熔化极气体保护焊，焊接效率很低。由于采用纯CO2作保护气存在使焊缝增碳和氧化焊件的危险，易引起接头性能的下降，使CO2气体保护焊应用受到限制。所以国内双相不锈钢船的焊接没有采用这一焊接效率较高的焊接方法，缺乏专门用于船用双相不锈钢的CO2气体保护焊工艺。
发明内容
本发明为了解决以上问题提供了一种焊接效率高，焊接接头力学性能和抗腐蚀性能强的船用双相不锈钢厚板CO2气体保护焊工艺。
本发明的技术方案是：首先采用的焊丝为药芯焊丝，然后加工待焊工件坡口和清理坡口及附近表面，并对待焊工件进行烘干，最后进行CO2气体保护焊，焊接线能量控制在1.7-2.5KJ，焊接层间温度在150oC以下。
所述的焊丝规格为Ф1.2mm。
所述的待焊工件坡口倾斜度为20-35o ，钝边为2mm，钝边处间隙为4-6mm。
所述的焊接层分为四层，第一层为打底焊接，第二、三层为填充焊接，第四层为盖面焊接；每层的焊接热输入分别为：第一层为第一层为1.7-1.9kJ/mm，第二层为1.8-2.2KJ/mm，第三层为1.7-1.9kJ/mm，第四层为1.7-1.9kJ/mm；各层焊接速度为70-100mm/min。
本发明增加了焊丝的熔敷速率，提高了不锈钢的焊接效率，焊接接头具有良好的力学性能和抗腐蚀性能。
具体实施方式
一种船用双相不锈钢厚板CO2气体保护焊工艺，首先采用的焊丝为药芯焊丝，然后加工待焊工件坡口和清理坡口及附近表面，并对待焊工件进行烘干，最后进行CO2气体保护焊，焊接线能量控制在1.7-2.5KJ，焊接层间温度在150oC以下，所述的焊丝规格为Ф1.2mm，所述的待焊工件坡口倾斜度为20-35o ，钝边为2mm，钝边处间隙为4-6mm，所述的焊接层分为四层，第一层为打底焊接，第二、三层为填充焊接，第四层为盖面焊接；每层的焊接热输入分别为：第一层为第一层为1.7-1.9kJ/mm，第二层为1.8-2.2KJ/mm，第三层为1.7-1.9kJ/mm，第四层为1.7-1.9kJ/mm；各层焊接速度为70-100mm/min。

Claims (4)

1.一种船用双相不锈钢厚板CO2气体保护焊工艺，其特征在于，首先采用的焊丝为药芯焊丝，然后加工待焊工件坡口和清理坡口及附近表面，并对待焊工件进行烘干，最后进行CO2气体保护焊，焊接线能量控制在1.7-2.5KJ，焊接层间温度在150oC以下。
2.根据权利要求1所述的一种船用双相不锈钢厚板CO2气体保护焊工艺，其特征在于，所述的焊丝规格为Ф1.2mm。
3.根据权利要求1所述的一种船用双相不锈钢厚板CO2气体保护焊工艺，其特征在于，所述的待焊工件坡口倾斜度为20-35o ，钝边为2mm，钝边处间隙为4-6mm。
4.根据权利要求1所述的一种船用双相不锈钢厚板CO2气体保护焊工艺，其特征在于，所述的焊接层分为四层，第一层为打底焊接，第二、三层为填充焊接，第四层为盖面焊接；每层的焊接热输入分别为：第一层为第一层为1.7-1.9kJ/mm，第二层为1.8-2.2KJ/mm，第三层为1.7-1.9kJ/mm，第四层为1.7-1.9kJ/mm；各层焊接速度为70-100mm/min。
CN2011102969139A 2011-09-29 2011-09-29 一种船用双相不锈钢厚板co2气体保护焊工艺 Pending CN103028818A (zh)