CN103015170A - Method for producing antibacterial and deodorizing viscose fiber fabric - Google Patents
Method for producing antibacterial and deodorizing viscose fiber fabric Download PDFInfo
- Publication number
- CN103015170A CN103015170A CN2012104990707A CN201210499070A CN103015170A CN 103015170 A CN103015170 A CN 103015170A CN 2012104990707 A CN2012104990707 A CN 2012104990707A CN 201210499070 A CN201210499070 A CN 201210499070A CN 103015170 A CN103015170 A CN 103015170A
- Authority
- CN
- China
- Prior art keywords
- fiber fabric
- viscose fiber
- deodorizing
- antibacterial
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for producing an antibacterial and deodorizing viscose fiber fabric. The method comprises the steps of heating a viscose fiber fabric in a citric acid solution, taking the viscose fiber fabric out of the citric acid solution, and soaking the viscose fiber fabric in a sodium phosphate solution; taking the viscose fiber fabric out of the sodium phosphate solution, extruding the viscose fiber fabric by pressing hardly, putting the viscose fiber fabric into water, adding a penetrating agent and a softening agent into the water, and soaking the viscose fiber fabric; and taking the viscose fiber fabric out of the water, extruding the viscose fiber fabric by pressing hardly, drying the viscose fiber fabric in a heating box, soaking the viscose fiber fabric in a cuprammonium solution, taking the viscose fiber fabric out of the cuprammonium solution, and drying to obtain the antibacterial and deodorizing viscose fiber fabric. Therefore, according to the method for producing the antibacterial and deodorizing viscose fiber fabric, viscose fibers are subjected to chemical modification, the produced copper chelate viscose fiber fabric has deodorizing and antibacterial functions, added functional groups can react with sulfide in the air, and the growth of bacteria is inhibited and the bacteria are killed, so that the odor caused by the growth of the bacteria is prevented, and the antibacterial and deodorizing viscose fiber fabric can be widely used in the fields of clothes and the like.
Description
Technical field
The present invention relates to the weaving face fabric field, particularly relate to a kind of manufacture method of antibacterial and deodorizing viscose face fabric.
Background technology
Viscose refers to a kind of cellulose of extracting from the cellulosic materials such as timber and plant bar, viscose is processed, and obtains spinning solution, makes artificial fibre through wet spinning again, obtains at last viscose face fabric.Viscose is divided into common viscose fiber, koplon and high tenacity staple fibre, common viscose fiber has general Physical Mechanical and chemical property, koplon has the higher degree of polymerization, brute force and wet modulus, and high tenacity staple fibre has higher brute force and fatigue performance.
The increase of bacterium all can cause foul smell in the situations such as the oral cavity of human body, breathing, hair, pin and human secretion, stench generally can affect people's autonomic nerve, thereby produce nose heave, headache, irritated, taediumvitae, strong stench will stimulate people's sympathetic nerve, impel sympathetic nerve to go short of, cause human blood-pressure to raise, Pulse Rate increases, and human internal organ is worked the mischief.Especially weaving face fabric directly contacts with human body, can directly cause damage to human body.The antibacterial and deodorizing effect of viscose face fabric is not remarkable in the tradition, and this causes the oozy peculiar smell of human body itself to remove, thereby affects people in the bearing of social life, can cause harmful effect to interpersonal relationships.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of manufacture method of antibacterial and deodorizing viscose face fabric.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of manufacture method of antibacterial and deodorizing viscose face fabric is provided, comprises that step is:
(1) viscose face fabric is put in the citric acid solution, citric acid solution was heated 2-5 hour, put in the sodium radio-phosphate,P-32 solution behind the taking-up viscose face fabric and flooded 1-2 hour;
(2) take out viscose face fabric firmly be squeezed to ooze out without solution after, put into water, adding bleeding agent and softener in the water flooded 1-2 hour;
(3) take out viscose face fabric, firmly be squeezed to without solution and ooze out, put into heating cabinet and dry, put into the copper ammon solution dipping 30 minutes again, drying obtains the antibacterial and deodorizing viscose face fabric after taking out.
In a preferred embodiment of the present invention, the concentration of citric acid solution is 3-9mol/L described in the step (1), and the concentration of described sodium radio-phosphate,P-32 solution is 8-11 mol/L.
In a preferred embodiment of the present invention, described in the step (3) heating-up temperature 140-160 ℃ of heating cabinet.
In a preferred embodiment of the present invention, the concentration of copper ammon solution is 0.03-0.05mol/L described in the step (3).
The invention has the beneficial effects as follows: the manufacture method of antibacterial and deodorizing viscose face fabric of the present invention, the method is by carrying out chemical modification to viscose, the viscose face fabric that the copper chelating is arranged that obtains has smelly eliminating, antibiotic function, the functional group that increases can react with airborne sulfide, can suppress simultaneously the growth with kill bacteria, thereby prevent the stink that bacterial growth causes, be widely used in the fields such as dress ornament, decoration, medical treatment.
The specific embodiment
The below is described in detail preferred embodiment of the present invention, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
Embodiment one:
(1) viscose face fabric is put in the citric acid solution, the 9mol/L citric acid solution was heated 2 hours, put in the 8mol/L sodium radio-phosphate,P-32 solution behind the taking-up viscose face fabric and flooded 1.5 hours;
(2) take out viscose face fabric firmly be squeezed to ooze out without solution after, put into water, adding bleeding agent and softener in the water flooded 1.5 hours;
(3) take out viscose face fabric, firmly be squeezed to without solution and ooze out, put into heating cabinet and dry, described heating cabinet Temperature Setting is 160 ℃, put into 0.03mol/L copper ammon solution dipping 30 minutes, drying obtains the antibacterial and deodorizing viscose face fabric after taking out again.
Embodiment two:
(1) viscose face fabric is put in the citric acid solution, the 3mol/L citric acid solution was heated 5 hours, put in the 10mol/L sodium radio-phosphate,P-32 solution behind the taking-up viscose face fabric and flooded 2 hours;
(2) take out viscose face fabric firmly be squeezed to ooze out without solution after, put into water, adding bleeding agent and softener in the water flooded 2 hours;
(3) take out viscose face fabric, firmly be squeezed to without solution and ooze out, put into heating cabinet and dry, described heating cabinet Temperature Setting is 160 ℃, put into 0.045mol/L copper ammon solution dipping 30 minutes, drying obtains the antibacterial and deodorizing viscose face fabric after taking out again.
Embodiment three:
(1) viscose face fabric is put in the citric acid solution, the 7mol/L citric acid solution was heated 4 hours, put in the 11mol/L sodium radio-phosphate,P-32 solution behind the taking-up viscose face fabric and flooded 1 hour;
(2) take out viscose face fabric firmly be squeezed to ooze out without solution after, put into water, adding bleeding agent and softener in the water flooded 1.5 hours;
(3) take out viscose face fabric, firmly be squeezed to without solution and ooze out, put into heating cabinet and dry, described heating cabinet Temperature Setting is 150 ℃, put into 0.05mol/L copper ammon solution dipping 30 minutes, drying obtains the antibacterial and deodorizing viscose face fabric after taking out again.
The manufacture method of the antibacterial and deodorizing viscose face fabric that the present invention discloses, the method is by carrying out chemical modification to viscose, the viscose face fabric that the copper chelating is arranged that obtains has smelly eliminating, antibiotic function, the functional group that increases can react with airborne sulfide, can suppress simultaneously the growth with kill bacteria, thereby prevent the stink that bacterial growth causes, be widely used in the fields such as dress ornament, decoration, medical treatment.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (4)
1. the manufacture method of an antibacterial and deodorizing viscose face fabric is characterized in that, comprises that step is:
(1) viscose face fabric is put in the citric acid solution, citric acid solution was heated 2-5 hour, put in the sodium radio-phosphate,P-32 solution behind the taking-up viscose face fabric and flooded 1-2 hour;
(2) take out viscose face fabric firmly be squeezed to ooze out without solution after, put into water, adding bleeding agent and softener in the water flooded 1-2 hour;
(3) take out viscose face fabric, firmly be squeezed to without solution and ooze out, put into heating cabinet and dry, put into the copper ammon solution dipping 30 minutes again, drying obtains the antibacterial and deodorizing viscose face fabric after taking out.
2. the manufacture method of antibacterial and deodorizing viscose face fabric according to claim 1 is characterized in that, the concentration of citric acid solution is 3-9mol/L described in the step (1), and the concentration of described sodium radio-phosphate,P-32 solution is 8-11 mol/L.
3. the manufacture method of antibacterial and deodorizing viscose face fabric according to claim 1 is characterized in that, described in the step (3) heating-up temperature 140-160 ℃ of heating cabinet.
4. the manufacture method of antibacterial and deodorizing viscose face fabric according to claim 1 is characterized in that, the concentration of copper ammon solution is 0.03-0.05mol/L described in the step (3).