CN103013154A - Resin glass fiber formulation and flowerpot made thereby - Google Patents
Resin glass fiber formulation and flowerpot made thereby Download PDFInfo
- Publication number
- CN103013154A CN103013154A CN2012105540026A CN201210554002A CN103013154A CN 103013154 A CN103013154 A CN 103013154A CN 2012105540026 A CN2012105540026 A CN 2012105540026A CN 201210554002 A CN201210554002 A CN 201210554002A CN 103013154 A CN103013154 A CN 103013154A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- resin glass
- fiber powder
- parts
- flowerpot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a resin glass fiber formulation and a flowerpot made thereby. The resin glass fiber formulation comprises the following components in part by weight: 80-95 parts of resin glass fiber powder and 5-20 parts of epoxide resin, wherein the resin glass fiber powder has the copper content of smaller than 5%. The resin glass fiber flowerpot is made from the following components in part by weight: 80-95 parts of resin glass fiber powder and 5-20 parts of epoxide resin, wherein the resin glass fiber powder has the copper content of smaller than 5%. Due to characteristics of the resin glass fiber powder, the flowerpot made from the resin glass fiber powder as a raw material has the characteristics of water resistance, corrosion resistance, moth resistance, acid and alkali resistance, aging resistance, light weight (compared with a clay flowerpot), low probability of breakage and the like; and a small amount of heavy metal exists in the resin glass fiber powder, so that during slow release of the heavy metal, the color and luster of a flower can be more bright and beautiful and the flowering phase can be prolonged.
Description
Technical field
The present invention relates to the recycling of industrial waste, specifically, relate to a kind of resin glass fiber prescription of industrial waste and flowerpot of being made by this prescription of deriving from.
Background technology
Flourish along with electronic industry, the processing of waste electron wiring board, useless copper-clad plate scrap stock and defect ware grows with each passing day.Correspondingly waste printed circuit board, the processing of copper-clad plate sorting process residual these industrial solid wastes of resin glass fiber powder after extracting metal, disposal also become a large thorny difficult problem.Arbitrarily topple over and can cause secondary pollution, burning, landfill can produce high expense and consume land resources.How properly to dispose and effectively fully utilize the resin glass fiber powder and become the important topic that the solution environmental issue faces.
Summary of the invention
The object of the invention is to propose a kind ofly can recycle the resin glass fiber powder approach that extracts in the industrial waste, and then drawn a kind of prescription, and have this prescription to make a kind of flowerpot.
Prescription provided by the invention comprises the component of following parts by weight:
Resin glass fiber powder: 80～95 parts
Resins, epoxy: 5～20 parts
Described resin glass fiber powder copper factor is less than 5%.
The recovery approach of the resin glass fiber powder in the prescription be with the scrap stock of useless electronic circuit board, copper-clad plate or one or more the mixture in the defect ware pulverize, heating, screening, extract and obtain copper factor behind the metal powder less than 5% resin glass fiber powder; Reclaiming the most preferred result of leaching process is that described resin glass fiber powder copper factor is 1.5～2.0%, and leaded rate is 0.1～0.2%, and containing the zinc rate is 0.1～0.2%.On the basis of above-mentioned prescription, preferred version is that the shared parts by weight of Resins, epoxy are 12～15 parts, and the shared parts by weight of resin glass fiber powder are 85～88 parts.Described Resins, epoxy also is from various Resins, epoxy such as the discarded and expired of factory and the amine through reclaiming, ester class, alcohols, alkene class, benzene classes.
In the prescription of the present invention, because the resin glass fiber powder possesses waterproof, anticorrosion, anti-soda acid and heat insulation, flame-retardant and many other characteristic, it is cooperated with Resins, epoxy, can be directly used in the stopping composition of rubber, plastic industry and the stopping composition of antiseepage mending-leakage etc., and can cooperate other raw materials to make various products, thereby have recovery value to a certain degree.Simultaneously, this prescription can be realized and performance like the ceramic phase after processing, can also be used to make and use pottery as the product of main raw in the traditional technologys such as flowerpot, tile, and this prescription proportion pottery is less, products obtained therefrom is lightweight more, this prescription has satisfied simultaneously the recycling industrial waste and has made two functions of daily living article, has realized the comprehensive utilization of resin glass fiber powder.
The present invention also provides a kind of resin glass fiber type flowerpot of being made by above-mentioned prescription, is made by the component of following parts by weight:
Resin glass fiber powder: 80～95 parts
Resins, epoxy: 5～20 parts
Described resin glass fiber powder copper factor is less than 5%.
Preferably, described resin glass fiber powder copper factor is 1.5～2.0%, and leaded rate is 0.1～0.2%, and containing the zinc rate is 0.1～0.2%.The shared parts by weight of Resins, epoxy are 12～15 parts, and the shared parts by weight of resin glass fiber powder are 85～88 parts.
Flowerpot provided by the invention only need pour into deployed raw material special mould, then suppresses getting final product with 500 tonnes oil press.
Gained flowerpot of the present invention can be made by mix mineral dye in making processes the flowerpot of different colours.Because the characteristic of resin glass fiber powder, have waterproof, anticorrosion, Anti-moth-eating, anti-soda acid, anti-aging with its flowerpot that makes as raw material, lightweight (relatively potter's clay flowerpot), the characteristics such as be difficult for breaking.In addition, because a small amount of heavy metal content is arranged in the resin glass fiber powder, in the slow dispose procedure of heavy metal, can make the color and luster of flowers more gorgeous, the characteristics such as longer blooming period.
Embodiment
Embodiment 1
Prescription provided by the invention comprises the component of following parts by weight:
Resin glass fiber powder: 90kg
Resins, epoxy: 20kg
Described resin glass fiber powder copper factor is for being 3%.
The recovery approach of the resin glass fiber powder in the prescription be with the scrap stock of useless electronic circuit board, copper-clad plate or one or more the mixture in the defect ware pulverize, heating, screening, extract and obtain copper factor behind the metal powder less than 5% resin glass fiber powder.
Embodiment 2
Resin glass fiber powder: 90kg
Resins, epoxy: 20kg
Described resin glass fiber powder copper factor is 1.8%, and leaded rate is 0.15%, and containing the zinc rate is 0.2%.
Embodiment 3
Resin glass fiber powder: 86kg
Resins, epoxy: 14kg
Described resin glass fiber powder copper factor is 1.8%, and leaded rate is 0.15%, and containing the zinc rate is 0.2%.
Embodiment 4
The making resin glass fiber type of selecting materials by filling a prescription among the embodiment 1 flowerpot pours into special mould with deployed raw material during making, then suppresses getting final product with 500 tonnes oil press.
Embodiment 5
The making resin glass fiber type of selecting materials by filling a prescription among the embodiment 2 flowerpot pours into special mould with deployed raw material during making, then suppresses getting final product with 500 tonnes oil press.
Embodiment 6
The making resin glass fiber type of selecting materials by filling a prescription among the embodiment 3 flowerpot pours into special mould with deployed raw material during making, then suppresses getting final product with 500 tonnes oil press.
According to the elaboration in the above specification sheets, those skilled in the art in the invention can also carry out suitable change and modification to above-mentioned embodiment.Therefore, the content of mentioning in above-described embodiment is not to be limitation of the invention, and under the prerequisite that does not break away from inventive concept of the present invention, any apparent replacement is all within protection scope of the present invention.
Claims (6)
1. resin glass fiber prescription comprises the component of following parts by weight:
Resin glass fiber powder: 80～95 parts
Resins, epoxy: 5～20 parts
Described resin glass fiber powder copper factor is less than 5%.
2. prescription according to claim 1, it is characterized in that: described resin glass fiber powder copper factor is 1.5～2.0%, and leaded rate is 0.1～0.2%, containing the zinc rate is 0.1～0.2%.
3. prescription according to claim 1 and 2, it is characterized in that: the shared parts by weight of Resins, epoxy are 12～15 parts, the shared parts by weight of resin glass fiber powder are 85～88 parts.
4. resin glass fiber type flowerpot, made by the component of following parts by weight:
Resin glass fiber powder: 80～95 parts
Resins, epoxy: 5～20 parts
Described resin glass fiber powder copper factor is less than 5%.
5. prescription according to claim 4, it is characterized in that: described resin glass fiber powder copper factor is 1.5～2.0%, and leaded rate is 0.1～0.2%, containing the zinc rate is 0.1～0.2%.
6. according to claim 4 or 5 described prescriptions, it is characterized in that: the shared parts by weight of Resins, epoxy are 12～15 parts, and the shared parts by weight of resin glass fiber powder are 85～88 parts.