CN105236927A - Resin glass fiber fireproof board and preparation method thereof - Google Patents
Resin glass fiber fireproof board and preparation method thereof Download PDFInfo
- Publication number
- CN105236927A CN105236927A CN201510550815.1A CN201510550815A CN105236927A CN 105236927 A CN105236927 A CN 105236927A CN 201510550815 A CN201510550815 A CN 201510550815A CN 105236927 A CN105236927 A CN 105236927A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- resin glass
- parts
- board
- magnesium chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A resin glass fiber fireproof board and a preparation method thereof. The resin glass fiber fireproof board includes the following components: 50-70 parts of resin glass fiber powder, 15-25 parts of volcano ash, 10-20 parts of magnesium oxide and 2-8 parts of magnesium chloride or magnesium chloride hexahydrate. The preparation method includes the steps of weighing the components according to the ratio, mixing the components in a stirring machine and stirring the components with addition of water in a proper amount, and moulding the board in a roll-pressing manner on a board making machine, maintaining the board for 8-12 h in a natural temperature maintaining manner, and cutting the board into required shape and size to obtain the fireproof board. In the invention, the resin glass fiber powder is matched with filling materials and a fireproof adhesive so that the fireproof board has excellent fireproof performance. The resin glass fiber fireproof board is small in specific gravity, is lighter in weight and satisfies recycle utilization of industrial waste materials and daily life electronic waste products, thereby achieving comprehensive utilization of the resin glass fiber powder.
Description
Technical field
The present invention relates to a kind of resin glass fiber PLASTIC LAMINATED and preparation method thereof, refer in particular to a kind of utilize the waste printed circuit board of recovery, copper-clad plate treated extraction useful metal powder after the PLASTIC LAMINATED prepared for main raw material of resin glass fiber powder and preparation method thereof.
Background technology
Flourish along with electronic industry, the process of waste electron wiring board, useless copper-clad plate scrap stock and defect ware grows with each passing day.Correspondingly waste printed circuit board, copper-clad plate sorting process extracting the process of these industrial solid wastes of resin glass fiber powder residual after metal, dispose and also become a large difficult problems.Arbitrarily topple over and can cause secondary pollution, burning, landfill can produce high expense and consume land resources.How properly to dispose and effectively fully utilize resin glass fiber powder and become the important topic solving environmental issue and face.Meanwhile, because resin glass fiber powder possesses waterproof, anticorrosion, anti-soda acid and heat insulation, flame-retardant and many other characteristic, therefore rubber, the stopping composition of plastic industry and the stopping composition etc. of antiseepage mending-leakage can be directly used in, thus there is recovery value to a certain degree.
Summary of the invention
The problem that the present invention need solve is to provide PLASTIC LAMINATED that a kind of fiberglass resin powder utilizing the waste and old circuit board of recovery to produce prepared for main raw material and preparation method thereof.
The invention provides a kind of fiberglass resin PLASTIC LAMINATED, the composition group component of this PLASTIC LAMINATED is, resin glass fiber powder, volcanic ash, magnesium oxide, magnesium chloride or magnesium chloride hexahydrate; The proportioning that described each component is counted by weight is, 50 ~ 70 parts, resin glass fiber powder, volcanic ash 15 ~ 25 parts, 10 ~ 20 parts, magnesium oxide, magnesium chloride or magnesium chloride hexahydrate 2 ~ 8 parts.
Wherein, described resin glass fiber powder is by waste and old circuit board, copper-clad plate scrap stock and the defect ware thereof reclaimed from society or industrial and mining enterprises, obtains after the physical treatment modes such as pulverizing, separation extract metal powder.
The preparation method of described PLASTIC LAMINATED is, after the composition group component of described PLASTIC LAMINATED is taken in proportion, add appropriate water after described starting material being put into stirrer mixing to stir, again through laminator roll extrusion compression moulding, natural thermal insulation maintenance 8-12 hour, cutting is tailored into specification shape and size, to obtain final product.
The recovery approach of the resin glass fiber powder in raw material is after the mixture of one or more in the useless electronic circuit board, copper-clad plate scrap stock or the defect ware that are generically and collectively referred to as useless copper-clad plate is pulverized (first coarse breaking fine crushing again), magnetic separation or washing, metal is separated with nonmetal and obtains resin glass fiber powder after extracting metal powder; Reclaiming the most preferred result of leaching process is that described resin glass fiber powder copper factor is less than 0.2%, and water content is less than 3%.Volcanic ash is commercially available eruption and natural volcanic ash, and major ingredient is active silica and activated alumina, plays the effect of high-temperature-resistant adhesive in the present invention.Magnesium oxide is commercial, in this as fire-resistant stopping composition.Magnesium chloride or magnesium chloride hexahydrate are commonly called as halogen sheet, are high-temperature-resistant adhesive.
The present invention utilizes useless electronic circuit board, the industrial residue that copperclad plate scrap stock and defect ware produce after getting copper, the resin glass fiber powder obtained after processing treatment is again as main raw material, after coordinating some other auxiliary materials, just can produce one and burn more than three hours time still intact fire-proof board through 1200 ° of C high temperature.Because resin glass fiber powder possesses waterproof, anticorrosion, anti-soda acid and heat insulation, flame-retardant and many other characteristic, so in the present invention, resin glass fiber powder through with the coordinating of stopping composition and fire resistant adhesive, after processing, gained PLASTIC LAMINATED can realize excellent fire resistance, and proportion is little, more lightweight, meets the function recycling industrial waste and daily life electronic waste, achieves the comprehensive utilization of resin glass fiber powder.
Embodiment
The invention discloses a kind of fiberglass resin PLASTIC LAMINATED, the raw material composition group component of this PLASTIC LAMINATED is, resin glass fiber powder, volcanic ash, magnesium oxide, magnesium chloride or magnesium chloride hexahydrate; The proportioning that described each component is counted by weight is, 50 ~ 70 parts, resin glass fiber powder, volcanic ash 15 ~ 25 parts, 10 ~ 20 parts, magnesium oxide, magnesium chloride or magnesium chloride hexahydrate 2 ~ 8 parts.Wherein, described resin glass fiber powder is pulverized through routine by the mixture of one or more in the waste and old circuit board, the scrap stock of copper-clad plate or the defect ware that reclaim from society or industrial and mining enterprises, heating, screen and obtain after extracting metal powder process.
The invention also discloses the preparation method of this PLASTIC LAMINATED, after taking in proportion by the raw material composition group component of described PLASTIC LAMINATED, add appropriate water after described starting material being put into stirrer mixing to stir, again through laminator roll extrusion compression moulding, natural thermal insulation maintenance 8-12 hour, cutting is tailored into specification shape and size, to obtain final product.
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
After getting resin glass fiber 60 parts, volcanic ash 20 parts, 15 parts, magnesium oxide, halogen sheet 5 parts, all put into stirrer mix and blend, then through laminator roll extrusion compression moulding, natural thermal insulation maintenance 8-12 hour, can cut and be tailored into specification shape and size, obtain finished product.
Embodiment 2
After getting resin glass fiber 50 parts, volcanic ash 10 parts, 10 parts, magnesium oxide, halogen sheet 2 parts, all put into stirrer mix and blend, then through laminator roll extrusion compression moulding, natural thermal insulation maintenance 8-12 hour, can cut and be tailored into specification shape and size, obtain finished product.
Embodiment 3
After getting resin glass fiber 70 parts, volcanic ash 25 parts, 20 parts, magnesium oxide, halogen sheet 8 parts, all put into stirrer mix and blend, then through laminator roll extrusion compression moulding, natural thermal insulation maintenance 8-12 hour, can cut and be tailored into specification shape and size, obtain finished product.
50 ~ 70 parts, resin glass fiber powder, volcanic ash 15 ~ 25 parts, 10 ~ 20 parts, magnesium oxide, magnesium chloride or magnesium chloride hexahydrate 2 ~ 8 parts
Embodiment 4
After getting resin glass fiber 55 parts, volcanic ash 17.5 parts, 12.5 parts, magnesium oxide, halogen sheet 3.5 parts, all put into stirrer mix and blend, then through laminator roll extrusion compression moulding, natural thermal insulation maintenance 8-12 hour, can cut and be tailored into specification shape and size, obtain finished product.
Embodiment 5
After getting resin glass fiber 65 parts, volcanic ash 22.5 parts, 17.5 parts, magnesium oxide, halogen sheet 6.5 parts, all put into stirrer mix and blend, then through laminator roll extrusion compression moulding, natural thermal insulation maintenance 8-12 hour, can cut and be tailored into specification shape and size, obtain finished product.
In production practice, utilize fire-proof board prepared by technical scheme disclosed by the invention, major dimension size: 2440 × 1220 × 1.0 and 2440 × 1220 × 1.5mm, main property is tensile strength >=50MPa, bending strength >=90MPa, high temperature resistant >=1200 DEG C after tested.
PLASTIC LAMINATED (and combination) there is no country or industry standard, but should meet the related request of CECS200:2006 " construction steel structure fireproofing technique code ", GB/T8624-1997 " Classification on burning behaviour for building materials " middle A level non-fire material, GB6566 " radioactive material radionuclides limitation " category-A and GB50325 " code for indoor environmental pollution control of civil building engineering ".Engineering specification is then GB50016-2006 " Code for fire protection design of buildings " and GB50045-2005 " Code for fire protection design of high rise buildings ".After testing according to the PLASTIC LAMINATED that technical solution of the present invention is produced, reaching and exceeded the set quota of aforementioned GB, real oldly must to give up for repairing, turning waste into wealth, protection of the environment, interests offspring product.
Claims (3)
1. a resin glass fiber PLASTIC LAMINATED, the composition group component of this PLASTIC LAMINATED is,
Resin glass fiber powder, volcanic ash, magnesium oxide, magnesium chloride or magnesium chloride hexahydrate;
The proportioning that described each component is counted by weight is, 50 ~ 70 parts, resin glass fiber powder, volcanic ash 15 ~ 25 parts, 10 ~ 20 parts, magnesium oxide, magnesium chloride or magnesium chloride hexahydrate 2 ~ 8 parts.
2. resin glass fiber PLASTIC LAMINATED according to claim 1, is characterized in that: described resin glass fiber powder extracts the non-metal powder after metal powder by the waste printed circuit board reclaimed, copper-clad plate through process such as pulverizing, separation.
3. the preparation method of resin glass fiber PLASTIC LAMINATED according to claim 1 and 2, it is characterized in that: after the composition group component of described PLASTIC LAMINATED is taken in proportion, add suitable quantity of water after described starting material being put into stirrer mixing to stir, again through laminator roll extrusion compression moulding, natural thermal insulation maintenance 8-12 hour, cutting is tailored into specification shape and size, to obtain final product.