CN103013054A - 一种阻燃型环氧乙烯基酯树脂及制作方法 - Google Patents

一种阻燃型环氧乙烯基酯树脂及制作方法 Download PDF

Info

Publication number
CN103013054A
CN103013054A CN2011102898400A CN201110289840A CN103013054A CN 103013054 A CN103013054 A CN 103013054A CN 2011102898400 A CN2011102898400 A CN 2011102898400A CN 201110289840 A CN201110289840 A CN 201110289840A CN 103013054 A CN103013054 A CN 103013054A
Authority
CN
China
Prior art keywords
vinyl ester
ester resin
epoxy vinyl
type epoxy
burning type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102898400A
Other languages
English (en)
Inventor
安庆升
肖海刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Institute of Electromechanical Engineering
Original Assignee
Shanghai Institute of Electromechanical Engineering
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Institute of Electromechanical Engineering filed Critical Shanghai Institute of Electromechanical Engineering
Priority to CN2011102898400A priority Critical patent/CN103013054A/zh
Publication of CN103013054A publication Critical patent/CN103013054A/zh
Pending legal-status Critical Current

Abstract

本发明涉及不饱和聚酯树脂技术领域，尤其涉及一种阻燃型环氧乙烯基酯树脂。为提高环氧乙烯基酯树脂阻燃性能，本发明提供一种阻燃型环氧乙烯基酯树脂及其制作方法，其组成成份及重量配比：反应型阻燃环氧乙烯基酯树脂、Al2O3·3H2O(ATH)氢氧化铝、十溴联苯醚；反应型阻燃环氧乙烯基酯树脂∶Al2O3·3H2O(ATH)氢氧化铝∶十溴联苯醚＝100∶60∶10。本发明阻燃型环氧乙烯基酯树脂，与现有技术相比，其优点和有益效果是：阻燃效率高，能使复合材料有良好自熄性或难燃性；力学性能、电性能、耐候性及热变性温度良好。

Description

一种阻燃型环氧乙烯基酯树脂及制作方法
技术领域
本发明涉及不饱和聚酯树脂技术，尤其是一种阻燃型环氧乙烯基酯树脂。
背景技术
树脂基复合材料具有优异的物理力学、电气绝缘、耐高低温等性能，在国民经济各领域得到越来越广泛应用。树脂基复合材料由基体材料和增强材料组成。增强材料多为无机不燃材料，而基体材料为有机化合物，成型后的复合材料具有可燃性，树脂基复合材料的氧指数为18左右，大气环境下易燃烧，对于阻燃要求较高的制品，必须进行基体树脂的阻燃改型，才能满足使用要求。通常阻燃改型办法是在基体材料中添加阻燃剂，阻燃剂有添加型和反应型两类。其一是在树脂基体中直接掺入阻燃剂；另一种是阻燃剂作为一种单体原料通过化学反应复合到聚合物份子链上，达到阻燃自熄目的。
发明内容
本发明要解决的技术问题是提供一种阻燃型环氧乙烯基酯树脂及其制作方法，以增强材料阻燃性能。
为解决上述技术问题，本发明是通过以下的技术方案实现的，一种阻燃型环氧乙烯基酯树脂，其组成成份及重量配比：
反应型阻燃环氧乙烯基酯树脂、Al2O3·3H2O(ATH)氢氧化铝、十溴联苯醚；
反应型阻燃环氧乙烯基酯树脂∶Al2O3·3H2O(ATH)氢氧化铝∶十溴联苯醚＝100∶60∶10。
所述的阻燃型环氧乙烯基酯树脂制作方法，其包括如下步骤：
步骤一：阻燃型环氧乙烯基酯树脂的组成成份重量配比：反应型阻燃环氧乙烯基酯树脂、Al2O3·3H2O(ATH)氢氧化铝、十溴联苯醚；
反应型阻燃环氧乙烯基酯树脂∶Al2O3·3H2O(ATH)氢氧化铝∶十溴联苯醚＝100∶60∶10
步骤二：在塑料或金属容器中，按配比将反应型阻燃环氧乙烯基酯树脂里首先与800目的Al2O3·3H2O(ATH)氢氧化铝混合，搅匀后静止10份钟，再次添加十溴联苯醚，充分搅拌后待用。
本发明阻燃型环氧乙烯基酯树脂，与现有技术相比，其优点和有益效果是：阻燃效率高，能使复合材料有良好自熄性或难燃性；力学性能、电性能、耐候性及热变性温度等较好。
具体实施方式
以导弹发射箱试验样品材料为本发明实施例：
选择阻燃型环氧乙烯基酯树脂，其组成成份重量配比为：
反应型阻燃环氧乙烯基酯树脂、Al2O3·3H2O(ATH)氢氧化铝、十溴联苯醚；
反应型阻燃环氧乙烯基酯树脂∶Al2O3·3H2O(ATH)氢氧化铝∶十溴联苯醚＝100∶60∶10。
阻燃型环氧乙烯基酯树脂制作方法
在塑料或金属容器中，按配比将反应型阻燃环氧乙烯基酯树脂里与800目的Al2O3·3H2O(ATH)氢氧化铝混合，搅匀后静止10份钟，再添加十溴联苯醚，充分搅拌后待用。
试验样品制作及取样
根据环境温度，在阻燃型环氧乙烯基酯树脂中，按配比加入2～4％过氧化甲乙酮和1～2％环烷酸钴固化剂，采用复合材料手糊工艺，将无碱玻璃纤维织物浸渍上述阻燃树脂成型制作复合材料板材试样，并常温固化24小时。
取样方法是根据玻璃纤维增强塑料拉伸、弯曲试验方法(GB/T1447-83、GB/T1449-83)和民用飞机舱内非金属材料燃烧性能要求(HB5470-91)，分别取样。
试样试验检测
依据玻璃纤维增强塑料拉伸、弯曲试验方法(GB/T1447-83、GB/T1449-83)、民用飞机舱内非金属材料燃烧性能要求(HB5470-91)以及不饱和聚酯树脂粘度测定方法(GB/T7193.1-87)分别对试样进行检测(见表1)。
表1试样性能指标
上述试样结果表明其阻燃性能优越，力学性能和工艺性能良好。
按上述阻燃树脂配方比例配制一定重量的树脂，采用复合材料缠绕工艺应用发射箱加强筋制作。过程表明，阻燃树脂体系配制过程简单、方便，成型工艺性能良好，常温固化易于控制，质量稳定。

Claims (2)

1.一种阻燃型环氧乙烯基酯树脂，其特征在于组成成份及重量配比：
反应型阻燃环氧乙烯基酯树脂、Al2O3·3H2O(ATH)氢氧化铝、十溴联苯醚；
反应型阻燃环氧乙烯基酯树脂∶Al2O3·3H2O(ATH)氢氧化铝∶十溴联苯醚＝100∶60∶10。
2.根据权利要求书1所述的阻燃型环氧乙烯基酯树脂制作方法，其特征在于包括如下步骤：
步骤一：阻燃型环氧乙烯基酯树脂的组成成份及重量配比：反应型阻燃环氧乙烯基酯树脂、Al2O3·3H2O(ATH)氢氧化铝、十溴联苯醚；
反应型阻燃环氧乙烯基酯树脂∶Al2O3·3H2O(ATH)氢氧化铝∶十溴联苯醚＝100∶60∶10
步骤二：在塑料或金属容器中，按配比将反应型阻燃环氧乙烯基酯树脂里与800目的Al2O3·3H2O(ATH)氢氧化铝混合，搅匀后静止10份钟，再添加十溴联苯醚，充分搅拌后待用。
CN2011102898400A 2011-09-27 2011-09-27 一种阻燃型环氧乙烯基酯树脂及制作方法 Pending CN103013054A (zh)