CN102994869A - 一种球墨铸铁 - Google Patents
一种球墨铸铁 Download PDFInfo
- Publication number
- CN102994869A CN102994869A CN2012105074820A CN201210507482A CN102994869A CN 102994869 A CN102994869 A CN 102994869A CN 2012105074820 A CN2012105074820 A CN 2012105074820A CN 201210507482 A CN201210507482 A CN 201210507482A CN 102994869 A CN102994869 A CN 102994869A
- Authority
- CN
- China
- Prior art keywords
- cast iron
- graphite cast
- niobium
- nickel
- nodular graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种球墨铸铁，其组成近重量百分比为，2.5-4.0％的硅、2.5-3.5％的钴、0.6-0.65％的钼、0.02-0.03％的镍、2.5-4.0％的碳、0.03-0.05％的镁、0.001-0.003％的铌及余量的铁和不可避免的杂质；所述杂质的重量百分比不能超过0.5％。通过在铸铁中加入铌及镍，能够提高铸铁合金组织体的均匀和防偏析问题，并提高了铸铁的热稳定性。
Description
技术领域
本发明属于铸铁领域，特别是指一种球墨铸铁。
背景技术
铸铁合金以其生产工艺简单，对于复杂结构部件能够一次成型的优点，得到了广泛的应用。但铸铁合金在高温下，其组织结构内的马氏体结构大于其它结构，因此会发生组织结构的变化，导致铸铁的强度减小，其使用温度一般不能超过350℃。
虽然有技术提出，对铸铁合金材料进行改进并提出了一些技术方案，这些技术方案为了解决铸铁耐高温问题，加入了一些铬、锰等元素以提高强度，但在高温环境下的耐磨性能不高，而且在加入锰的量导致铸铁合金变脆，容易出现表层脱落等现象，无法满足在高温下的耐磨要求。
对于球墨铸铁的蠕变强度和蠕变断裂强度主要是靠硅和钼来提高，但是钼的偏析倾向的特性决定了随着时间的推移会导致球墨铸铁的韧性明显降低，而脆性增加。
发明内容
本发明的目的是提供一种球墨铸铁技术方案，通过本技术方案，能够克服完全依靠钼来提高球墨铸铁的组织结构的缺陷，提高热稳定性及蠕变断裂强度。
本发明是通过以下技术方案实现的：
一种球墨铸铁，其组成近重量百分比为，2.5-4.0％的硅、2.5-3.5％的钴、0.6-0.65％的钼、0.02-0.03％的镍、2.5-4.0％的碳、0.03-0.05％的镁、0.001-0.003％的铌及余量的铁和不可避免的杂质；所述杂质的重量百分比不能超过0.5％。
本发明同现有技术相比的有益效果是：
通过在铸铁中加入铌及镍，能够提高铸铁合金组织体的均匀和防偏析问题，并提高了铸铁的热稳定性。
具体实施方式
以下通过实施例来详细说明本发明的技术方案，应当理解的是，以下的实施例仅能用来解释本发明的技术方案而不能解释为是对本发明的限制。
在本发明的技术方案中，关于铸铁的冶炼工艺同现技术相同，只有配料组成有所区别。
实施例1
一种球墨铸铁，其组成近重量百分比为，2.5％的硅、2.5％的钴、0.6％的钼、0.02％的镍、2.5％的碳、0.03％的镁、0.001％的铌及余量的铁和不可避免的杂质；所述杂质的重量百分比不能超过0.5％。
实施例2
一种球墨铸铁，其组成近重量百分比为，4.0％的硅、3.5％的钴、0.65％的钼、0.03％的镍、4.0％的碳、0.05％的镁、0.003％的铌及余量的铁和不可避免的杂质；所述杂质的重量百分比不能超过0.5％。
实施例3
一种球墨铸铁，其组成近重量百分比为，3.5％的硅、3.0％的钴、0.62％的钼、0.025％的镍、3.5％的碳、0.04％的镁、0.0015％的铌及余量的铁和不可避免的杂质；所述杂质的重量百分比不能超过0.5％。
Claims (1)
1.一种球墨铸铁，其特征在于：其组成近重量百分比为，2.5-4.0％的硅、2.5-3.5％的钴、0.6-0.65％的钼、0.02-0.03％的镍、2.5-4.0％的碳、0.03-0.05％的镁、0.001-0.003％的铌及余量的铁和不可避免的杂质；所述杂质的重量百分比不能超过0.5％。