CN102993900A - 一种用于海水中的环氧树脂涂料 - Google Patents
一种用于海水中的环氧树脂涂料 Download PDFInfo
- Publication number
- CN102993900A CN102993900A CN2012103919714A CN201210391971A CN102993900A CN 102993900 A CN102993900 A CN 102993900A CN 2012103919714 A CN2012103919714 A CN 2012103919714A CN 201210391971 A CN201210391971 A CN 201210391971A CN 102993900 A CN102993900 A CN 102993900A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- seawater
- epoxy
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种用于海水中的环氧树脂涂料，所述涂料的各组份重量比为：羧酸改性环氧树脂90-100份，钛白粉7-10份，滑石粉40-55份，玻璃粉10-30份，改性脂肪族多胺40-60份。按上述配方制得的涂料具有：该涂料在海水中涂装作业性能优异，被涂面上的润湿性好。附着力优异、漆膜的电阻3000Ωc以上，耐水性，综合性好。施工及配套要求：钢板用钢刷处理成ST—3(ISO05-5900)的标淮,然后用刮刀在海水中个进行3mm厚度涂装。应用范围：海洋结构用材、河河设备施厂等水中其他用涂料。
Description
技术领域
本发明涉及油漆技术领域，尤其是指一种用于海水中的环氧树脂涂料。
背景技术
随着海洋石油、港口码头、水力发电站及船舶工业的不断发展，许多处于海洋环境的工程结构，如钻探开采设备、钻井平台、海上油气储罐、输送管线的支撑架、栈桥、钢桩、船底及船舶内舱等，由于常年浸泡在海水中，或受潮水的涨落和浸泡，以及遭遇海上生物的冲蚀，使得结构原有的防腐层遭受破坏，此外，防止海洋附着生物的污损研究至今已有三百多年的历史，以往，海中防腐涂料组合物一般是使用焦油系环氧树脂涂料，这种涂料具有良好的防腐蚀性，耐水性和耐化学性等，但由于含有焦油，存在卫生方面的问题，而且由于涂料是黑色的，维护管理较为困难，操作时可能发生危险。
发明内容
本发明的目的在于提供一种具有较高的耐磨性、耐冲击性和强大附着力，可长期浸泡在海水中的环氧树脂涂料。
为实现上述目的，本发明所提供的技术方案为：一种用于海水中的环氧树脂涂料，按重量比取双酚A二缩水甘油醚(环氧当量190)：90-100份
苹果酸 3-5份
N，N-二甲基卞胺 0.05-0.1份
首先，在反应器中按上述加入双酚A二缩水甘油醚环氧和苹果酸进行混台后再加反应促进剂N，N-二甲基卞胺升温至130 ℃保持3h，充分反应，得羧酸改性环氧树脂；
按重量比取上述羧酸改性环氧树脂90-100份
钛白粉7-10份
滑石粉40-55份
玻璃粉10-30份
改性脂肪族多胺40-60份；
首先，在混合器中加入羧酸改性环氧树脂、钛白粉、滑石粉和玻璃粉进行充分混合，然后加入改性脂肪族多胺固化剂，搅匀，用非反应性稀释剂调整粘度，即得。
本发明的优点在于：该涂料在海水中涂装作业性能优异，被涂面上的润湿性好。附着力优异、漆膜的电阻 3000Ωc以上，耐水性，综合性好。施工及配套要求：钢板用钢刷处理成ST—3(ISO05-5900)的标淮,然后用刮刀在海水中个进行3mm厚度涂装。应用范围：海洋结构用材、河河设备施厂等水中其他用涂料。
具体实施方式
下面对本发明作进一步说明，本发明的较佳实施例为：
实施例1
本实施例所述用于海水中的环氧树脂涂料，按重量比取双酚A二缩水甘油醚(环氧当量190)： 100份
苹果酸 3.4份
N，N-二甲基卞胺 0.05份
首先，在反应器中按上述加入双酚A二缩水甘油醚环氧和苹果酸进行混台后再加反应促进剂N，N-二甲基卞胺升温至130 ℃保持3h，充分反应，得羧酸改性环氧树；
按重量比取上述羧酸改性环氧树脂 100份
钛白粉 7份
滑石粉 55份
玻璃粉 13份
改性脂肪族多胺 45份；
首先，在混合器中加入羧酸改性环氧树脂、钛白粉、滑石粉和玻璃粉进行充分混合，然后加入改性脂肪族多胺固化剂，搅匀，用非反应性稀释剂调整粘度，即得。
本涂料可以在常温下进行喷涂，操作简便，涂层具有极好的耐磨性、耐腐蚀性、较高的绝缘强度和耐冲击性，不需要底层涂料，可直接涂覆，能有效地隔绝酸、碱、盐类介质和海水的浸蚀，可广泛应用于石油化工、钻井平台、海洋运输等领域。
实施例2
本实施例与实施例1不同的是，本实施例所述的环氧树脂涂料由以下各组份按重量配比：
双酚A型环氧树胎(环氧当量190) 100份
苯基缩水甘油醚 10份
乙二胺四乙酸 2份
芳香烃改性多胺 50份
滑石粉 100份
胶体二氧化硅 2份
按上述配方将各物料依次加入到带搅拌的釜中，于30℃下充分混合，即得。
以上所述之实施例只为本发明之较佳实施例，并非以此限制本发明的实施范围，故凡依本发明之形状、原理所作的变化，均应涵盖在本发明的保护范围内。
Claims (1)
1.一种用于海水中的环氧树脂涂料，其特征在于：按重量比取双酚A二缩水甘油醚(环氧当量190)：90-100份
苹果酸 3-5份
N，N-二甲基卞胺 0.05-0.1份
首先，在反应器中按上述加入双酚A二缩水甘油醚环氧和苹果酸进行混台后再加反应促进剂N，N-二甲基卞胺升温至130 ℃保持3h，充分反应，得羧酸改性环氧树脂；
按重量比取上述羧酸改性环氧树脂 90-100份
钛白粉 7-10份
滑石粉 40-55份
玻璃粉 10-30份
改性脂肪族多胺 40-60份；
首先，在混合器中加入羧酸改性环氧树脂、钛白粉、滑石粉和玻璃粉进行充分混合，然后加入改性脂肪族多胺固化剂，搅匀，用非反应性稀释剂调整粘度，即得。