CN102993866A - Environmentally-friendly water-based paint for wood ware - Google Patents
Environmentally-friendly water-based paint for wood ware Download PDFInfo
- Publication number
- CN102993866A CN102993866A CN 201210458058 CN201210458058A CN102993866A CN 102993866 A CN102993866 A CN 102993866A CN 201210458058 CN201210458058 CN 201210458058 CN 201210458058 A CN201210458058 A CN 201210458058A CN 102993866 A CN102993866 A CN 102993866A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmentally
- paint
- friendly
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an environmentally-friendly water-based paint for wood ware. The paint comprises the following constituent parts: 15-22 parts of waterborne polyurethane resin, 20-32 parts of acrylic emulsion, 45-60 parts of waterborne hydroxylated acrylic resin emulsion, 0.5-2 parts of dispersing agent, 1-5 parts of flatting agent, 2-4 parts of antifoaming agent and 30-50 parts of deionized water. The paint for wood ware further comprises 1-2 parts of nanometer zirconia. The environmentally-friendly water-based paint for wood ware forms transparent and non-yellow films, is very bright, has good elastic extension rate, cold resistance and strong adhesion, is non-toxic, non-ignitable, safe and environmental-friendly and is an environmentally-friendly product for substituting for solvent paints; and the benzene content of the paint can reach national standards, is used for furniture decoration, is non-toxic and harmless and does not pollute the environment, so that the health levels of people are improved.
Description
Technical field
The present invention relates to a kind of paint, especially a kind of environment-friendly water-based wood lacquer.
Background technology
Single-component water-based woodwork coating in the market has environmental protection, simple operation and other advantages, but has the shortcomings such as high lac varnish gloss is not high, hardness is low, sticking power is bad, wear no resistance, chemical resistant properties is not good.Double-component aqueous wood paint has that film-forming temperature is low, strong adhesion, wear resistance is good, hardness is high and the high-performance such as chemicals-resistant, good weatherability, but double-component aqueous wood paint is in the market compared with the solvent-based two-component wood lacquer, still has wear resistance, resistance to marring is poor, hardness is low, levelling property is poor, defoaming is poor problem.In recent years, along with the continuous enhancing of whole world environmental consciousness, the environmental regulation of various countries is increasingly harsh, and is severeer to the restriction of organic volatile in the coating (VOC) content.The continuous developing in woodwork coating market more requires the water-borne wood coating of low VOC to adapt with it, and the novel aqueous woodwork coating of low VOC or zero VOC discharging has become the focus of research and development.At present, use more ACRYLIC EMULSION in the mono-component aqueous wood lacquer and have quick-drying, the advantage such as fast light, weathering resistance, chemical resistant properties are excellent, and the transparency is good.But the acrylic ester emulsion hardness that second-order transition temperature is low is also low, occurs easily after-tacking; The then film-forming properties that second-order transition temperature is high is relatively poor, easily produces be full of cracks, needs to add the solubility promoter of more amount, thus do not reach the purpose of the low VOC of water-borne coatings, and snappiness is also relatively poor.
Summary of the invention
The technical problem to be solved in the present invention provides a kind of environment-friendly water-based wood lacquer.
For solving the problems of the technologies described above, environment-friendly water-based wood lacquer of the present invention, it comprises following integral part, waterborne polyurethane resin 15-22 part, ACRYLIC EMULSION 20-32 part, water based acrylic resin emulsion 45-60 part, dispersion agent 0.5-2 part, flow agent 1-5 part, defoamer 2-4, deionized water 30-50 part.
Described wood lacquer also comprises nano zircite 1-2 part.
Environment-friendly water-based wood lacquer film forming of the present invention is transparent non-yellowing, very bright, and the elastic extension rate is all good, cold-resistant splits, strong adhesion, does not nontoxicly fire, and safety and environmental protection is the environmentfriendly products of replace solvents lacquer.Its benzene content can be up to state standards, and is used for the furniture finishing, and nontoxic, environmentally safe has improved people's health level.
Embodiment
Embodiment 1
Environment-friendly water-based wood lacquer of the present invention, it comprises following integral part, 17 parts of waterborne polyurethane resins, 25 parts of ACRYLIC EMULSION, 50 parts of water based acrylic resin emulsions, 0.5 part of dispersion agent, 4 parts of flow agents, defoamer 4,50 parts of deionized waters, 1 part of nano zircite.
Embodiment 2
Environment-friendly water-based wood lacquer of the present invention, it comprises following integral part, 22 parts of waterborne polyurethane resins, 20 parts of ACRYLIC EMULSION, 60 parts of water based acrylic resin emulsions, 2 parts of dispersion agents, 5 parts of flow agents, defoamer 2-4,30 parts of deionized waters, 2 parts of nano zircites.
Embodiment 3
Environment-friendly water-based wood lacquer of the present invention, it comprises following integral part, 15 parts of waterborne polyurethane resins, 20 parts of ACRYLIC EMULSION, 40 parts of water based acrylic resin emulsions, 0.5 part of dispersion agent, 1 part of flow agent, defoamer 4,50 parts of deionized waters, 2 parts of nano zircites.
The above only is to preferred embodiment of the present invention, is not that the present invention is done other forms of restriction, and any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the equivalent embodiment of equal variation.Every the present invention program's content that do not break away from, all drops in protection scope of the present invention any simple modification, equivalent variations and remodeling that above embodiment does according to technical spirit of the present invention.
Claims (2)
1. environment-friendly water-based wood lacquer, it is characterized in that: it comprises following integral part, waterborne polyurethane resin 15-22 part, ACRYLIC EMULSION 20-32 part, water based acrylic resin emulsion 45-60 part, dispersion agent 0.5-2 part, flow agent 1-5 part, defoamer 2-4, deionized water 30-50 part.
2. according to environment-friendly water-based wood lacquer claimed in claim 1, it is characterized in that: described wood lacquer also comprises nano zircite 1-2 part.