CN102990241A - 高频焊机专用金属粉末焊材 - Google Patents

高频焊机专用金属粉末焊材 Download PDF

Info

Publication number
CN102990241A
CN102990241A CN2012103045058A CN201210304505A CN102990241A CN 102990241 A CN102990241 A CN 102990241A CN 2012103045058 A CN2012103045058 A CN 2012103045058A CN 201210304505 A CN201210304505 A CN 201210304505A CN 102990241 A CN102990241 A CN 102990241A
Authority
CN
China
Prior art keywords
metal powder
welding
wlding
percent
component
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103045058A
Other languages
English (en)
Other versions
CN102990241B (zh
Inventor
张�林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201210304505.8A priority Critical patent/CN102990241B/zh
Publication of CN102990241A publication Critical patent/CN102990241A/zh
Application granted granted Critical
Publication of CN102990241B publication Critical patent/CN102990241B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种高频焊机专用金属粉末焊材,它包括以下重量百分比的组分:Cu:40-65、Zn:25-50、KBF4:4-6、H3BO3:2-3、Sn:2-3。本发明所提供的高频焊机专用金属粉末焊材可适用于金刚石工具的焊接、合金焊接或其它异形件的焊接等,适用面广,其熔点低,焊接强度高,可有效保证焊接件的产品质量;同时避免使用银等贵重金属,使得焊接成本较低。

Description

高频焊机专用金属粉末焊材
技术领域
本发明涉及高频焊机焊材制备技术领域,具体涉及一种高频焊机专用金属粉末焊材。 
背景技术
金刚石锯片已广泛应用于石材、陶瓷和玻璃加工业中,金刚石锯片是在钢铁基体上按照一定的间隔焊接多个金刚石刀头构成的。现有技术中是通过人工在金刚石锯片的锯齿上铺设铜焊片,利用铜焊片将刀头焊接在金刚石锯片上,这样做的缺陷是操作麻烦,每焊一个锯齿都需要将铜焊片放置到锯齿上并对准,而且所放置的铜焊片还易被风吹掉落,影响焊接效果和效率。另外有一些在用的银基纤焊料,其不足之处在于,银焊料的需求大,银的成本高昂,大量使用银焊料既会造成金刚石锯片的焊接成本升高,同时也造成银资源的短缺。对于其它的一些铜焊料来说,其熔点高,在焊接金刚石锯片时容易造成金刚石刀头表面碳化,且使钢基体变形严重矫正困难,焊接的产品质量极差。 
发明内容
本发明所要解决的问题便是提供一种熔点低、焊接强度高且焊接成本低的高频焊机专用金属粉末焊材。 
一种高频焊机专用金属粉末焊材,包括以下重量百分比的组分:Cu(铜):40-65、Zn(锌):25-50、KBF4(氟硼酸钾):4-6、H3BO3(硼酸):2-3、Sn(锡):2-3。 
作为优选:所述组分为以下重量百分比的组分:Cu:50、Zn:40、KBF4:5、H3BO3:3、Sn:2。 
作为优选:所述组分中还含有以下重量百分比的组分:Sb(锑):0.5。 
作为优选:所述组分中还含有以下重量百分比的组分:Cd(镉):1。 
本发明所提供的高频焊机专用金属粉末焊材可适用于金刚石工具的焊接、合金焊接或其它异形件的焊接等,适用面广,其熔点低,焊接强度高,可有效保证焊接件的产品质量;同时避免使用银等贵重金属,使得焊接成本较低。 
具体实施方式
下面将结合具体实施例对本发明作进一步详细说明。 
一种高频焊机专用金属粉末焊材,包括以下重量百分比的组分:Cu(铜):40-65、Zn(锌):25-50、KBF4(氟硼酸钾):4-6、H3BO3(硼酸):2-3、Sn(锡):2-3、其它微量元素。 
实施例一: 
一种高频焊机专用金属粉末焊材,包括以下重量百分比的组分:Cu(铜):50、Zn(锌):40、KBF4(氟硼酸钾):5、H3BO3(硼酸):3、Sn(锡):2。
实施例二: 
一种高频焊机专用金属粉末焊材,包括以下重量百分比的组分:Cu(铜):40、Zn(锌):50、KBF4(氟硼酸钾):6、H3BO3(硼酸):2、Sn(锡):2。
实施例三: 
一种高频焊机专用金属粉末焊材,包括以下重量百分比的组分:Cu(铜):65、Zn(锌):25、KBF4(氟硼酸钾):4、H3BO3(硼酸):3、Sn(锡):3。
实施例四: 
一种高频焊机专用金属粉末焊材,包括以下重量百分比的组分:Cu(铜):60、Zn(锌):30、KBF4(氟硼酸钾):5、H3BO3(硼酸):3、Sn(锡):2。
实施例五: 
一种高频焊机专用金属粉末焊材,包括以下重量百分比的组分:Cu(铜):45、Zn(锌):45、KBF4(氟硼酸钾):5、H3BO3(硼酸):3、Sn(锡):2。
实施例六: 
一种高频焊机专用金属粉末焊材,包括以下重量百分比的组分:Cu(铜):50、Zn(锌):40、KBF4(氟硼酸钾):5、H3BO3(硼酸):2.5、Sn(锡):2、Sb(锑):0.5。
实施例七: 
一种高频焊机专用金属粉末焊材,包括以下重量百分比的组分:Cu(铜):50、Zn(锌):40、KBF4(氟硼酸钾):5、H3BO3(硼酸):2、Sn(锡):2、Cd(镉):1。
实施例八: 
一种高频焊机专用金属粉末焊材,包括以下重量百分比的组分:Cu(铜):50、Zn(锌):40、KBF4(氟硼酸钾):4、H3BO3(硼酸):2.5、Sn(锡):2、Sb(锑):0.5、Cd(镉):1。
本发明所提供的高频焊机专用金属粉末焊材可适用于金刚石工具的焊接、合金焊接或其它异形件的焊接等,适用面广,其熔点低,焊接强度高,可有效保证焊接件的产品质量;同时避免使用银等贵重金属,使得焊接成本较低。 
本发明的焊材为铜基焊材,在铜基焊材内加入Zn和Sn,因它们的熔点低,通过调节Zn和Sn在组分中的比例可实现调节焊材熔点的目的,调整Zn、Sn、Cu的比例可调节熔点和强度;同时KBF4和H3BO3易溶于水,遇水后成浆糊状,具有极强的粘连性,更易涂刷,同时其还具有助溶、脱氧、浮渣的效果;在焊材中加入其它微量元素可增强焊材的性能,在焊材中加入Sb后,可有效提高焊接强度,在焊材中加入Cd后,可进一步增强强度、抗拉力,抗冲击性能更好。 
本发明可适用于铜合金之间、铜与铁之间、铜合金与铁合金之间、铜合金与铁之间以及铜与铁合金之间的焊接,使用时在本发明所述的粉末焊材中加入适量水勾兑后涂刷在焊接母体上,再利用高频焊机焊接即可。 

Claims (4)

1.一种高频焊机专用金属粉末焊材,其特征在于:包括以下重量百分比的组分:Cu:40-65、Zn:25-50、KBF4:4-6、H3BO3:2-3、Sn:2-3。
2.根据权利要求1所述的高频焊机专用金属粉末焊材,其特征在于:所述组分为以下重量百分比的组分:Cu:50、Zn:40、KBF4:5、H3BO3:3、Sn:2。
3.根据权利要求1所述的高频焊机专用金属粉末焊材,其特征在于:所述组分中还含有以下重量百分比的组分:Sb:0.5。
4.根据权利要求1或3所述的高频焊机专用金属粉末焊材,其特征在于:所述组分中还含有以下重量百分比的组分:Cd:1。
CN201210304505.8A 2012-08-24 2012-08-24 高频焊机专用金属粉末焊材 Expired - Fee Related CN102990241B (zh)