CN102977834A - 一种水性聚氨酯皮革黏合剂 - Google Patents

一种水性聚氨酯皮革黏合剂 Download PDF

Info

Publication number
CN102977834A
CN102977834A CN2012104531405A CN201210453140A CN102977834A CN 102977834 A CN102977834 A CN 102977834A CN 2012104531405 A CN2012104531405 A CN 2012104531405A CN 201210453140 A CN201210453140 A CN 201210453140A CN 102977834 A CN102977834 A CN 102977834A
Authority
CN
China
Prior art keywords
performed polymer
polyurethane leather
leather adhesive
aqueous polyurethane
dmba
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012104531405A
Other languages
English (en)
Inventor
苏建丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Wenchuang Technology Co Ltd
Original Assignee
Qingdao Wenchuang Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Wenchuang Technology Co Ltd filed Critical Qingdao Wenchuang Technology Co Ltd
Priority to CN2012104531405A priority Critical patent/CN102977834A/zh
Publication of CN102977834A publication Critical patent/CN102977834A/zh
Pending legal-status Critical Current

Abstract

一种水性聚氨酯皮革黏合剂，是以IPDI、PCL1000、PG、DMBA为原料制备预聚体，加入三乙胺进行中和反应生成盐，加入羧基丁苯胶水乳液，混合均匀，得到水性聚氨酯皮革黏合剂。本发明得到的水水性聚氨酯皮革黏合剂具有固含量高、初黏力大、固化时间短、成本低等优点。

Description

一种水性聚氨酯皮革黏合剂
技术领域
本发明涉及一种水性聚氨酯皮革黏合剂，属化工领域。
背景技术        
水性聚氨酯材料存在固含量低、粘结强度和力学性能不够理想等缺点，在实际应用过程中，热存在少量有机溶剂，环保性差。按照绿色化学和保护环境要求，环保型聚氨酯应该从原材料选用到整个生产应用过程，都应具有环境友好、无毒害的特性。
本专利采用价格低廉、产量丰富，具有天然生物降解特性的葡萄糖作为交联剂对水性聚氨酯进行改性。为了提高固含量，采用羧基丁苯胶与水混合后再对聚氨酯预聚体进行分散，制得水性聚氨酯皮革胶黏剂，该胶黏剂具有固含量高、初黏力大、固化时间短、成本低等优点。
发明内容
本发明的目的是提供一种水性聚氨酯皮革黏合剂，得到的黏合剂具有固含量高、初黏力大、固化时间短、成本低等优点。
为实现以上目的，本发明的一种水性聚氨酯皮革黏合剂，其步骤具体为：
(1) 以异佛尔酮二异氰酸酯(IPDI)、聚己内酯二醇(PCL1000)、葡萄糖(PG)、二羟甲基丁酸(DMBA)为原料制备预聚体，反应2h。
(2) 降温至40℃，加入三乙胺进行中和反应生成盐，反应3-5min。
(3) 加入羧基丁苯胶(CSBL)和水的混合乳液乳化1h，得到水性聚氨酯皮革黏合剂。
步骤(1)中预聚体原料的配比为：IPDI与PCL1000、PG、DMBA的摩尔比为1.3:1-1.4:1，PG占预聚体质量的2%-3%，DMBA占预聚体质量的5%-6%。
步骤(2)中三乙胺的物质的量与DMBA的物质的量相同。
步骤(3)中羧基丁苯胶(CSBL)的用量为预聚体总质量的50%，水的用量为预聚体总质量的2倍。
本发明产生的有益效果为，本专利采用价格低廉、产量丰富，具有天然生物降解特性的葡萄糖作为交联剂对水性聚氨酯进行改性。此外，在聚氨酯预聚体乳化时，采用羧基丁苯胶与水均匀混合后，再对聚氨酯预聚体进行分散，能够制得固含量高的水性聚氨酯皮革黏合剂，降低生产成本，并且增加了产品的初黏力和缩短了产品的固化时间。
实施例
实施例1：
以异佛尔酮二异氰酸酯(IPDI)、聚己内酯二醇(PCL1000)、葡萄糖(PG)、二羟甲基丁酸(DMBA)为原料制备预聚体，反应2h，聚体原料的配比为：IPDI与PCL1000、PG、DMBA的摩尔比为1.3:1，PG占预聚体质量的2%，DMBA占预聚体质量的5%。降温至40℃，加入三乙胺进行中和反应生成盐，反应3min，三乙胺的物质的量与DMBA的物质的量相同。加入羧基丁苯胶(CSBL)和水的混合乳液乳化1h，羧基丁苯胶(CSBL)的用量为预聚体总质量的50%，水的用量为预聚体总质量的2倍，最终得到水性聚氨酯皮革黏合剂。
实施例2：
以异佛尔酮二异氰酸酯(IPDI)、聚己内酯二醇(PCL1000)、葡萄糖(PG)、二羟甲基丁酸(DMBA)为原料制备预聚体，反应2h，聚体原料的配比为：IPDI与PCL1000、PG、DMBA的摩尔比为1.35:1，PG占预聚体质量的2%，DMBA占预聚体质量的5%。降温至40℃，加入三乙胺进行中和反应生成盐，反应3min，三乙胺的物质的量与DMBA的物质的量相同。加入羧基丁苯胶(CSBL)和水的混合乳液乳化1h，羧基丁苯胶(CSBL)的用量为预聚体总质量的70%，水的用量为预聚体总质量的2倍，最终得到水性聚氨酯皮革黏合剂。

Claims (5)

1.一种水性聚氨酯皮革黏合剂，其特征在于：步骤如下：
(1) 以异佛尔酮二异氰酸酯(IPDI)、聚己内酯二醇(PCL1000)、葡萄糖(PG)、二羟甲基丁酸(DMBA)为原料制备预聚体，反应2h；
(2) 降温至40℃，加入三乙胺进行中和反应生成盐，反应3-5min；
(3) 加入羧基丁苯胶(CSBL)和水的混合乳液乳化1h，得到水性聚氨酯皮革黏合剂。
2.如权利要求1所述的一种水性聚氨酯皮革黏合剂，其特征在于：所述的步骤(1)中预聚体原料的配比为：IPDI与PCL1000、PG、DMBA的摩尔比为1.3:1-1.4:1，PG占预聚体质量的2%-3%，DMBA占预聚体质量的5%-6%。
3.如权利要求1所述的一种水性聚氨酯皮革黏合剂，其特征在于：所述的步骤(2)中三乙胺的物质的量与DMBA的物质的量相同。
4.如权利要求1所述的一种水性聚氨酯皮革黏合剂，其特征在于：所述的步骤(3)中羧基丁苯胶(CSBL)的用量为预聚体总质量的50%。
5.如权利要求1所述的一种水性聚氨酯皮革黏合剂，其特征在于：所述的步骤(3)中水的用量为预聚体总质量的2倍。
CN2012104531405A 2012-11-13 2012-11-13 一种水性聚氨酯皮革黏合剂 Pending CN102977834A (zh)