CN102977668B - 一种含有8- 羟基喹啉的金属防锈剂的制备方法 - Google Patents
一种含有8- 羟基喹啉的金属防锈剂的制备方法 Download PDFInfo
- Publication number
- CN102977668B CN102977668B CN201210433653.XA CN201210433653A CN102977668B CN 102977668 B CN102977668 B CN 102977668B CN 201210433653 A CN201210433653 A CN 201210433653A CN 102977668 B CN102977668 B CN 102977668B
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- weight part
- hydroxyquinoline
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种含有8-羟基喹啉的金属防锈剂的制备方法，将5.8-8.2重量份液化石蜡、3.5-5.7重量份乙酰柠檬酸三(2-乙基已基)酯、4-6重量份丙烯酸、3.2-5.3重量份环氧米糠油、2-3重量份二甲苯、3.2-4.7重量份聚乙烯蜡加入反应釜，升温至105-115℃，开始搅拌并加入3-6重量份尿素、0.2-0.3重量份过硫酸钾、0.3-0.5重量份硼砂、0.2-0.3重量份锌粉；升温后一段时间再停止加热按重量份将加入剩余原料加入反应釜，混匀溶解后即得。本发明防锈时间长,可达4～6个月,并对铜、铝有较好的适应性，本发明可以缓释防锈的同时在金属表面成膜，从而延长防锈时间。
Description
技术领域
本发明涉及防锈剂领域，确切地说是一种含有8- 羟基喹啉的金属防锈剂的制备方法。
背景技术
水性防锈剂是一种水基防锈溶液,可有效的保护钢、铁等材料,防止生锈。根据防锈期要求的不同,和水按一定比混合使用,防锈期限可达到几天至几月,如果有一定外包装条件,防锈时间可达一年以上。 现有防锈剂多防锈性能不佳，急需一种防锈性能好的金属防锈剂。
发明内容
本发明的目的在于提供一种防锈性能好的含有8- 羟基喹啉的金属防锈剂的制备方法。
上述目的通过以下方案实现：
一种含有8- 羟基喹啉的金属防锈剂的制备方法，其特征在于：包括以下步骤：
（1）将5.8-8.2重量份液化石蜡、3.5-5.7重量份乙酰柠檬酸三(2-乙基已基)酯、4-6重量份丙烯酸、3.2-5.3重量份环氧米糠油、2-3重量份二甲苯、3.2-4.7重量份聚乙烯蜡加入反应釜，升温至105-115℃，开始搅拌并加入3-6重量份尿素、0.2-0.3重量份过硫酸钾、0.3-0.5重量份硼砂、0.2-0.3重量份锌粉；
（2）然后以50-60℃/小时速率升温到180-195℃；
（3）反应1-2小时停止加热；
（4）按重量份将加入剩余原料加入反应釜，混匀溶解后即得；
所述的剩余原料为下述重量份的组分：苯甲酸钠0.9-1.5、癸二酸钠1.2-2.1、乙醇胺1-2、8- 羟基喹啉0.9-1.7、N-苯基-2-萘胺 1-2、甘油三醋酸酯1-2、十二烷基硫酸钠1-2、水95-105。
所述的一种含有8- 羟基喹啉的金属防锈剂的制备方法，其特征在于：所述的反应釜为不锈钢反应釜。
本发明的有益效果为：本发明与各材料的相容性好，防锈时间长,可达4-6个月,并对铜、铝材料有较好的适应性，本发明可以缓释防锈的同时在金属表面成膜，从而延长防锈时间。
具体实施方式
一种含有8- 羟基喹啉的金属防锈剂的制备方法，包括以下步骤：
（1）将5.9重量份（kg)液化石蜡、5.7重量份乙酰柠檬酸三(2-乙基已基)酯、5.1重量份丙烯酸、5.3重量份环氧米糠油、2.1重量份二甲苯、4.7重量份聚乙烯蜡加入反应釜，升温至105℃，开始搅拌并加入4重量份尿素、0.3重量份过硫酸钾、0.5重量份硼砂、0.3重量份锌粉；
（2）然后以50℃/小时速率升温到188℃；
（3）反应1.3小时停止加热；
（4）按重量份将加入剩余原料加入反应釜，混匀溶解后即得；
所述的剩余原料为下述重量份的组分：苯甲酸钠0.9、癸二酸钠1.8、乙醇胺1、8- 羟基喹啉1.1、N-苯基-2-萘胺 2、甘油三醋酸酯2、十二烷基硫酸钠2、水105。
所述的反应釜为不锈钢反应釜。
将本实施例制得的防锈剂与市售国产防锈剂进行对比实验，其中各项性能指标分别按如下方法测定：
高低温稳定性试验：根据JB/T4323.2—1999进行。
湿热防锈试验：一级灰口铸铁试片在50～70℃的防锈液中浸泡1min，取出烘干（110℃），将试片放入干燥器（底部注入500～1000ml蒸馏水）的隔板上，加盖后置于35℃±2℃条件下恒温放置，观察防锈时间。
腐蚀试验：根据JB/T4323.2—1999进行。
室内挂片试验：一级灰口铸铁试片经防锈处理后，在室内挂放，观察试片表面锈蚀状况。
封存防锈试验：一级灰口铸铁试片防锈处理后，将试片放入透明的密封塑料袋中，密封好定期观察试片的表面状况。
测定结果见表一：
表一
由表一可知，本发明防绣时间长，可达4～6个月，并对铜、铝有较好的适应性。同时经过相容性试验，本实施例与各材料的相容性佳，并不会影响部件的正常运行。
Claims (2)
1.一种含有8- 羟基喹啉的金属防锈剂的制备方法，其特征在于：包括以下步骤：
（1）将5.8-8.2重量份液化石蜡、3.5-5.7重量份乙酰柠檬酸三(2-乙基已基)酯、4-6重量份丙烯酸、3.2-5.3重量份环氧米糠油、2-3重量份二甲苯、3.2-4.7重量份聚乙烯蜡加入反应釜，升温至105-115℃，开始搅拌并加入3-6重量份尿素、0.2-0.3重量份过硫酸钾、0.3-0.5重量份硼砂、0.2-0.3重量份锌粉；
（2）然后以50-60℃/小时速率升温到180-195℃；
（3）反应1-2小时停止加热；
（4）按重量份将剩余原料加入反应釜，混匀溶解后即得；
所述的剩余原料为下述重量份的组分：苯甲酸钠0.9-1.5、癸二酸钠1.2-2.1、乙醇胺1-2、8- 羟基喹啉0.9-1.7、N-苯基-2-萘胺 1-2、甘油三醋酸酯1-2、十二烷基硫酸钠1-2、水95-105。
2.根据权利要求1所述的一种含有8- 羟基喹啉的金属防锈剂的制备方法，其特征在于：所述的反应釜为不锈钢反应釜。