CN102936644A - 一种提高双辊薄带连铸无取向电工钢磁性能的方法 - Google Patents
一种提高双辊薄带连铸无取向电工钢磁性能的方法 Download PDFInfo
- Publication number
- CN102936644A CN102936644A CN2012104916272A CN201210491627A CN102936644A CN 102936644 A CN102936644 A CN 102936644A CN 2012104916272 A CN2012104916272 A CN 2012104916272A CN 201210491627 A CN201210491627 A CN 201210491627A CN 102936644 A CN102936644 A CN 102936644A
- Authority
- CN
- China
- Prior art keywords
- oriented electrical
- electrical steel
- roll
- twin
- continuous casting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (2)