CN102936345A - Sbs胶乳的制备方法 - Google Patents

Sbs胶乳的制备方法 Download PDF

Info

Publication number
CN102936345A
CN102936345A CN 201210422923 CN201210422923A CN102936345A CN 102936345 A CN102936345 A CN 102936345A CN 201210422923 CN201210422923 CN 201210422923 CN 201210422923 A CN201210422923 A CN 201210422923A CN 102936345 A CN102936345 A CN 102936345A
Authority
CN
China
Prior art keywords
sbs
latex
preparation
emulsifying agent
mass ratio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201210422923
Other languages
English (en)
Inventor
王耀斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi High Tech Energy Development Co Ltd
Original Assignee
Shaanxi High Tech Energy Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shaanxi High Tech Energy Development Co Ltd filed Critical Shaanxi High Tech Energy Development Co Ltd
Priority to CN 201210422923 priority Critical patent/CN102936345A/zh
Publication of CN102936345A publication Critical patent/CN102936345A/zh
Pending legal-status Critical Current

Abstract

本发明SBS胶乳的制备方法涉及一种胶乳的制备方法。本发明所述的SBS胶乳的制备方法，将乳化剂，溶剂与SBS混合，将水慢慢加入到混合物中，放置30min后加入稳定剂和絮凝剂，接着减压蒸馏，获得SBS胶乳。本发明制备获得的SBS胶乳中SBS颗粒分散均匀，颗粒间没有聚结现象，是一种稳定性好、性能优良的乳液。

Description

SBS胶乳的制备方法
技术领域
本发明涉及一种胶乳的制备方法。 
背景技术
改性乳化沥青是以乳状液高分子聚合物对乳化沥青进行改性或者对高分子聚合物改性沥青进行乳化所得到的产品。改性乳化沥青是一种新型沥青路面结合料，同时具备改性沥青和乳化沥青的优点，如热稳定性较高，软化点较高，成膜性、粘附性、回弹性能、低温性能较好，脆点较低。改性乳化沥青比乳化沥青有更好的抗低温开裂性能和抗疲劳耐久性能：与改性沥青相比可节约沥青用量10％～20％。且改性乳化沥青应用范围宽，性能优良，特别是结合稀浆封层技术对路面进行微表处理，可以消除路面的开裂、光滑、车辙、松散、老化等病害。因此高品质改性乳化沥青的研发，对公路事业有重大的实际意义，同时也潜藏着莫大的商机。
SBS作为一种兼顾高、低温性能的改性剂，在改性沥青领域得到广泛的应用，但SBS作为改性剂制备改性乳化沥青时，当SBS质量分数低于3％，改性沥青能够被很好地乳化，但是改性效果不佳；当SBS质量分数为3％～5％，改性沥青可以被乳化，但是乳液的稳定性差。 
发明内容
本发明旨在提供一种乳化性能优良的SBS胶乳制备方法。
本发明所述的SBS胶乳的制备方法，将乳化剂，溶剂与SBS混合，将水慢慢加入到混合物中，放置30min后加入稳定剂和絮凝剂，接着减压蒸馏，获得SBS胶乳。
优选地，乳化剂与SBS的质量比为8：100。
更优选地，乳化剂为阳离子乳化剂，非离子乳化剂和阴离子乳化剂。
进一步优选地，阳离子乳化剂，非离子乳化剂和阴离子乳化剂的质量比为3：1：1。
优选地，溶剂与SBS的质量比值为3.5。
优选地，絮凝剂与SBS的质量比为4：100。
优选地，稳定剂与SBS的质量比为0.4：100。
优选地，乳化的温度为65℃。
本发明制备获得的SBS胶乳中SBS颗粒分散均匀，颗粒间没有聚结现象，是一种稳定性好、性能优良的乳液。
具体实施方式
实施例一。
将8公斤乳化剂，3500公斤溶剂与100公斤SBS混合，其中乳化剂包括质量比为3：1：1的阳离子乳化剂，非离子乳化剂和阴离子乳化剂，将水慢慢加入到混合物中，在温度为65℃下放置30min后加入0.4公斤稳定剂和4公斤絮凝剂，接着减压蒸馏，获得SBS胶乳。 

Claims (8)

1.SBS胶乳的制备方法，其特征在于将乳化剂，溶剂与SBS混合，将水慢慢加入到混合物中，放置30min后加入稳定剂和絮凝剂，接着减压蒸馏，获得SBS胶乳。
2.如权利要求1所述的SBS胶乳的制备方法，其特征在于乳化剂与SBS的质量比为8：100。
3.如权利要求1或2所述的SBS胶乳的制备方法，其特征在于乳化剂为阳离子乳化剂，非离子乳化剂和阴离子乳化剂。
4.如权利要求3所述的SBS胶乳的制备方法，其特征在于阳离子乳化剂，非离子乳化剂和阴离子乳化剂的质量比为3：1：1。
5.如权利要求1所述的SBS胶乳的制备方法，其特征在于溶剂与SBS的质量比值为3.5。
6.如权利要求1所述的SBS胶乳的制备方法，其特征在于絮凝剂与SBS的质量比为4：100。
7.如权利要求1所述的SBS胶乳的制备方法，其特征在于稳定剂与SBS的质量比为0.4：100。
8.如权利要求1所述的SBS胶乳的制备方法，其特征在于乳化的温度为65℃。
CN 201210422923 2012-10-30 2012-10-30 Sbs胶乳的制备方法 Pending CN102936345A (zh)