CN102925104B - Leaking stoppage material for plastic pipelines and equipment and production method for leaking stoppage material - Google Patents
Leaking stoppage material for plastic pipelines and equipment and production method for leaking stoppage material Download PDFInfo
- Publication number
- CN102925104B CN102925104B CN201210427235.XA CN201210427235A CN102925104B CN 102925104 B CN102925104 B CN 102925104B CN 201210427235 A CN201210427235 A CN 201210427235A CN 102925104 B CN102925104 B CN 102925104B
- Authority
- CN
- China
- Prior art keywords
- equipment
- clay
- potter
- asbestos
- patching materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a leaking stoppage material for plastic pipelines and equipment. The leaking stoppage material comprises the following raw materials in parts by weight: 0.8 to 1.2 parts of asbestos material, 1.6 to 1.8 parts of argil, 1.25 to 1.5 parts of engine oil and 0.5 to 0.7 part of tung oil. The leaking stoppage material is solid at normal temperature and normal pressure, and can be deformed by slight extrusion. A method for preparing the leaking stoppage material comprises the following steps of: mixing the argil and the engine oil uniformly; gradually adding the mixture into the asbestos material while stirring; and slowly adding the tung oil, mixing uniformly, so as to obtain the leaking stoppage material. The leaking stoppage material is easy to prepare, remarkable in leaking stoppage effect on the plastic pipelines, the equipment and the like, low in cost and easy to popularize.
Description
Technical field
The present invention relates to pipe plugging field, be specifically related to a kind of patching materials for plastic conduit, equipment and production method thereof.
Background technology
In chemical plant actual production Working environment, engineering plastics pipe and equipment in use for some time easily aging, distortion until leak, while repairing pipe leakage by traditional method, generally all need arrestment running in short-term, impact is normal produces, existing material for quickly stopping leakage contains epoxy resin more, and cost is higher, and has certain toxicity.
Summary of the invention
Be to provide a kind of patching materials for plastic conduit, equipment and production method thereof in technical problem to be solved by this invention, in the time that leaking appears in pipeline, equipment, can use the timely mending-leakage of this material, ensure the production order.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is: a kind of patching materials for plastic conduit, equipment, is characterized in that comprising following raw material by weight: asbestos material, 0.8-1.2 part; Potter's clay 1.6-1.8 part, machine oil 1.25-1.5 part.
Preferably, for the patching materials of plastic conduit, equipment, comprise following raw material by weight: asbestos material, 0.8-1.2 part; Potter's clay 1.6-1.8 part, machine oil 1.25-1.5 part.
The raw material of described patching materials also comprises tung oil 0.5-0.7 part.
Described asbestos material is asbestos wool or asbestos twine, the section shape that asbestos twine is 5-10cm.
The granularity of described potter's clay is 325 orders, its silica weight content >=53%.
Described patching materials is solid-state under normal temperature, normal pressure, pushes a little deformable.
Prepare the method for described patching materials, first by 50% potter's clay and all machine oil by mixing, then it is added in asbestos wool gradually, limit edged stirs, more progressively adds residue potter's clay, after mixing patching materials.
The method of the described patching materials containing tung oil of preparation, first mixes 50% potter's clay and all machine oil, then it is added in asbestos material gradually, and limit edged stirs, more progressively adds residue potter's clay, finally slowly adds tung oil to mix to obtain patching materials.
In the selected starting material of the present invention:
Asbestos material, has flexibility, anti-tensile, splits a point property, and good insulating is acidproof, alkaline-resisting more satisfactory.
Potter's clay, has good plasticity-, and tool is in excellent freeze-thaw-characteristic, good sound absorption, good ventilation property, water-permeable, good weather resistance, erosion resistance.
Machine oil, has sealed against leakage, antirust corrosion protection, lubricates anti-attrition, cools, cleans the characteristics such as clean.
Tung oil is, has that fast drying, light specific gravity, glossiness are good, a strong adhesion, the characteristic such as heat-resisting, acidproof, alkaline-resisting, anticorrosion, antirust, non-conductive.
The feature of this formula is the solids that makes mixture formation definite shape, softer, slightly under extruding, can be out of shape.In the time that pipeline and equipment have leakage, patching materials of the present invention is squeezed in to leak, in the time of extruding, patching materials can be out of shape and enters leak, can block fast and effectively leakage point.
A kind of patching materials for plastic conduit, equipment provided by the invention and production method thereof, have following beneficial effect:
1, do not allowing, on the production line stopping production, by using this material, can to realize Rapid leakage repairing, ensureing to produce and carry out smoothly.
2, the starting material that this patching materials uses are simple and easy to get, and compound method is simple, and cost is lower, are applicable to promoting.
Embodiment
Further illustrate the present invention below in conjunction with embodiment, but the scope of protection of present invention is not limited to the scope of embodiment statement.
The granularity of described potter's clay is 325 orders, its silica weight content >=53%.
Embodiment 1:
For a patching materials for plastic conduit, equipment, comprise following raw material: asbestos wool, 5kg; 325 order potter's clay 9kg, machine oil 6.25kg; Described patching materials is solid-state under normal temperature, normal pressure, pushes a little deformable.
While preparing described patching materials, first by 50% potter's clay and all machine oil by mixing, then it is added in asbestos wool gradually, limit edged stirs, more progressively adds residue potter's clay, after mixing patching materials.
Embodiment 2:
For a patching materials for plastic conduit, equipment, comprise following raw material: asbestos wool, 4kg, 325 order potter's clay 9kg, machine oil 6.25kg, tung oil 3.5 kg; Described patching materials is solid-state under normal temperature, normal pressure, pushes a little deformable.
While preparing described patching materials, first by 50% potter's clay and all machine oil by mixing, then it is added in asbestos wool gradually, limit edged stirs, more progressively adds residue potter's clay, after mixing patching materials.
In above-mentioned two embodiment, gained patching materials is softer, quality guaranteed period is 30 days, can be used for the leak stopping of pipeline and equipment pressure≤49KPa, when leak stopping, repeatedly this envelope material is pressed into leakage position step by step, compacting, in the time that system pressure is larger, can be wound around with glass-fiber-fabric at pipeline outer-layer or by sheet iron wrapping, better effects if.
Embodiment 3:
For a patching materials for plastic conduit, equipment, comprise following raw material: asbestos twine, 5kg; 325 order potter's clay 9kg, machine oil 6.25kg; Tung oil 3 kg, described patching materials is solid-state under normal temperature, normal pressure, pushes a little deformable.
While preparing described patching materials, asbestos twine is cut into the segment of 5-10cm, then 50% potter's clay and all machine oil is mixed, then it is added in asbestos twine gradually, limit edged stirs, more progressively adds residue potter's clay, finally slowly adds tung oil to mix to obtain patching materials.
Embodiment 4:
For a patching materials for plastic conduit, equipment, comprise following raw material: asbestos wool, 6kg; 325 order potter's clay 8.5kg, machine oil 7.5kg; Described patching materials is solid-state under normal temperature, normal pressure, pushes a little deformable.
While preparing described patching materials, asbestos twine is cut into the segment of 5-10cm, 50% potter's clay and all machine oil are mixed, then it is added in asbestos twine gradually, limit edged stirs, progressively add again residue potter's clay, finally slowly add tung oil to mix to obtain patching materials, be applicable to leaked substance water content slightly large.
With respect to the patching materials in embodiment 1 and 2, patching materials in embodiment 3 and 4 is harder, quality guaranteed period is 15 days, can be used for the leak stopping of pipeline and equipment pressure≤49KPa, when leak stopping, repeatedly this envelope material is pressed into leakage position step by step, compacting, in the time that system pressure is larger, can be wound around with glass-fiber-fabric or wraps up with sheet iron at pipeline outer-layer, better effects if, is applicable to leaked substance and is gaseous state or containing a small amount of moisture content.
Claims (4)
1. for a patching materials for plastic conduit, equipment, it is characterized in that comprising following raw material by weight: asbestos material 0.8-1.2 part, potter's clay 1.6-1.8 part, machine oil 1.25-1.5 part, tung oil 0.5-0.7 part;
Described asbestos material is asbestos wool or asbestos twine, the section shape that asbestos twine is 5-10cm;
Its concrete preparation method is: first 50% potter's clay and all machine oil are mixed, then it is added in asbestos material gradually, limit edged stirs, more progressively adds residue potter's clay, finally slowly adds tung oil to mix to obtain patching materials.
2. the patching materials for plastic conduit, equipment according to claim 1, is characterized in that: 1 part of asbestos material; 1.8 parts, potter's clay, 1.25 parts, machine oil.
3. according to the patching materials for plastic conduit, equipment one of claim 1-2 Suo Shu, it is characterized in that: the granularity of described potter's clay is 325 orders its silica weight content >=53%.
4. according to the patching materials for plastic conduit, equipment one of claim 1-2 Suo Shu, it is characterized in that: described patching materials for solid-state, pushes a little deformable under normal temperature, normal pressure.