CN102925104A - Leaking stoppage material for plastic pipelines and equipment and production method for leaking stoppage material - Google Patents
Leaking stoppage material for plastic pipelines and equipment and production method for leaking stoppage material Download PDFInfo
- Publication number
- CN102925104A CN102925104A CN201210427235XA CN201210427235A CN102925104A CN 102925104 A CN102925104 A CN 102925104A CN 201210427235X A CN201210427235X A CN 201210427235XA CN 201210427235 A CN201210427235 A CN 201210427235A CN 102925104 A CN102925104 A CN 102925104A
- Authority
- CN
- China
- Prior art keywords
- patching materials
- potter
- clay
- asbestos
- equipment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a leaking stoppage material for plastic pipelines and equipment. The leaking stoppage material comprises the following raw materials in parts by weight: 0.8 to 1.2 parts of asbestos material, 1.6 to 1.8 parts of argil, 1.25 to 1.5 parts of engine oil and 0.5 to 0.7 part of tung oil. The leaking stoppage material is solid at normal temperature and normal pressure, and can be deformed by slight extrusion. A method for preparing the leaking stoppage material comprises the following steps of: mixing the argil and the engine oil uniformly; gradually adding the mixture into the asbestos material while stirring; and slowly adding the tung oil, mixing uniformly, so as to obtain the leaking stoppage material. The leaking stoppage material is easy to prepare, remarkable in leaking stoppage effect on the plastic pipelines, the equipment and the like, low in cost and easy to popularize.
Description
Technical field
The present invention relates to the pipe plugging field, be specifically related to a kind of patching materials for plastic conduit, equipment and production method thereof.
Background technology
In chemical plant actual production Working environment, engineering plastics pipe and equipment easily wear out in use for some time, are out of shape until leak, when repairing pipe leakage by traditional method, generally all need in short-term arrestment running, impact is normal produces, existing material for quickly stopping leakage contains Resins, epoxy more, and cost is higher, and certain toxicity is arranged.
Summary of the invention
Provide a kind of patching materials for plastic conduit, equipment and production method thereof in technical problem to be solved by this invention, at pipeline, when leaking appears in equipment, can use the timely mending-leakage of this material, guarantee the production order.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is: a kind of patching materials for plastic conduit, equipment is characterized in that comprising following raw material by weight: asbestos material, 0.8-1.2 part; Potter's clay 1.6-1.8 part, machine oil 1.25-1.5 part.
The preferred patching materials that is used for plastic conduit, equipment comprises following raw material by weight: asbestos material, 0.8-1.2 part; Potter's clay 1.6-1.8 part, machine oil 1.25-1.5 part.
The raw material of described patching materials also comprises tung oil 0.5-0.7 part.
Described asbestos material is asbestos wool or asbestos twine, and asbestos twine is the section shape of 5-10cm.
The granularity of described potter's clay is 325 orders, its silica weight content 〉=53%.
Described patching materials is solid-state under normal temperature, normal pressure, pushes a little deformable.
The method for preparing described patching materials is pressed mixing with 50% potter's clay and all machine oil first, then it is added in the asbestos wool gradually, and the limit edged stirs, and progressively adds residue potter's clay again, gets patching materials behind the mixing.
Prepare the described method that contains the patching materials of tung oil, with 50% potter's clay and all machine oil mixings, then it is added in the asbestos material gradually first, the limit edged stirs, and progressively adds residue potter's clay again, and the last tung oil mixing that slowly adds gets patching materials.
In the selected starting material of the present invention:
Asbestos material has flexibility, resists a property, splits a minute property, and good insulating is acidproof, alkaline-resisting more satisfactory.
Potter's clay has good plasticity-, and tool is in the freeze-thaw-characteristic of excellence, good sound absorption, good ventilation property, water-permeable, good weather resistance, erosion resistance.
Machine oil has sealing and anti-leakage, antirust corrosion protection, lubricated anti-attrition, cools, cleans the characteristic such as cleaning.
Tung oil is, has that fast drying, light specific gravity, glossiness are good, a strong adhesion, the characteristic such as heat-resisting, acidproof, alkaline-resisting, anticorrosion, antirust, non-conductive.
The characteristics of this prescription are the solids that makes mixture formation definite shape, and are softer, slightly can be out of shape under the extruding.When pipeline and equipment have leakage, patching materials of the present invention is squeezed in leak, patching materials can be out of shape and enters leak when extruding, can block fast and effectively leakage point.
A kind of patching materials and production method thereof for plastic conduit, equipment provided by the invention have following beneficial effect:
1, on the production line that does not allow to stop production, by using this material, can realize Rapid leakage repairing, guarantee to produce and carry out smoothly.
2, this patching materials starting material of using are simple and easy to, and compound method is simple, and cost is lower, is fit to promote.
Embodiment
Further specify the present invention below in conjunction with embodiment, but the scope of protection of present invention is not limited to the scope of embodiment statement.
The granularity of described potter's clay is 325 orders, its silica weight content 〉=53%.
Embodiment 1:
A kind of patching materials for plastic conduit, equipment comprises following raw material: asbestos wool, 5kg; 325 order potter's clay 9kg, machine oil 6.25kg; Described patching materials is solid-state under normal temperature, normal pressure, pushes a little deformable.
When preparing described patching materials, first 50% potter's clay and all machine oil are pressed mixing, then it is added in the asbestos wool gradually, the limit edged stirs, and progressively adds residue potter's clay again, gets patching materials behind the mixing.
Embodiment 2:
A kind of patching materials for plastic conduit, equipment comprises following raw material: asbestos wool, 4kg, 325 order potter's clay 9kg, machine oil 6.25kg, tung oil 3.5 kg; Described patching materials is solid-state under normal temperature, normal pressure, pushes a little deformable.
When preparing described patching materials, first 50% potter's clay and all machine oil are pressed mixing, then it is added in the asbestos wool gradually, the limit edged stirs, and progressively adds residue potter's clay again, gets patching materials behind the mixing.
The gained patching materials is softer among above-mentioned two embodiment, quality guaranteed period is 30 days, can be used for the leak stopping of pipeline and equipment pressure≤49KPa, during leak stopping, repeatedly this envelope material is pressed into leakage position step by step, compacting is when system pressure is larger, can wrap up better effects if with the glass-fiber-fabric winding or with sheet iron at pipeline outer-layer.
Embodiment 3:
A kind of patching materials for plastic conduit, equipment comprises following raw material: asbestos twine, 5kg; 325 order potter's clay 9kg, machine oil 6.25kg; Tung oil 3 kg, described patching materials are solid-state under normal temperature, normal pressure, push a little deformable.
When preparing described patching materials, asbestos twine is cut into the segment of 5-10cm, then with 50% potter's clay and all machine oil mixings, then add gradually it in asbestos twine, the limit edged stirs, and progressively adds residue potter's clay again, and the last tung oil mixing that slowly adds gets patching materials.
Embodiment 4:
A kind of patching materials for plastic conduit, equipment comprises following raw material: asbestos wool, 6kg; 325 order potter's clay 8.5kg, machine oil 7.5kg; Described patching materials is solid-state under normal temperature, normal pressure, pushes a little deformable.
When preparing described patching materials, asbestos twine is cut into the segment of 5-10cm, with 50% potter's clay and all machine oil mixings, then add gradually it in asbestos twine, the limit edged stirs, progressively add residue potter's clay, the last tung oil mixing that slowly adds gets patching materials, is applicable to the leaked substance water content slightly large again.
With respect to the patching materials in embodiment 1 and 2, patching materials among the embodiment 3 and 4 is harder, quality guaranteed period is 15 days, can be used for the leak stopping of pipeline and equipment pressure≤49KPa, during leak stopping, repeatedly this envelope material is pressed into leakage position step by step, compacting when system pressure is larger, can be twined with glass-fiber-fabric or wrap up with sheet iron at pipeline outer-layer, better effects if, to be applicable to leaked substance be gaseous state or contain a small amount of moisture content.
Claims (8)
1. a patching materials that is used for plastic conduit, equipment is characterized in that comprising following raw material by weight: asbestos material, 0.8-1.2 part; Potter's clay 1.6-1.8 part, machine oil 1.25-1.5 part.
2. the patching materials for plastic conduit, equipment according to claim 1 is characterized in that comprising following raw material by weight: asbestos material, 1 part; 1.8 parts in potter's clay, 1.25 parts in machine oil.
3. the patching materials for plastic conduit, equipment according to claim 1, it is characterized in that: the raw material of described patching materials also comprises tung oil 0.5-0.7 part.
4. described patching materials for plastic conduit, equipment one of according to claim 1-3, it is characterized in that: described asbestos material is asbestos wool or asbestos twine, asbestos twine is the section shape of 5-10cm.
5. described patching materials for plastic conduit, equipment one of according to claim 1-3, it is characterized in that: the granularity of described potter's clay is 325 orders, its silica weight content 〉=53%.
6. described patching materials for plastic conduit, equipment one of according to claim 1-3, it is characterized in that: described patching materials for solid-state, pushes deformable a little under normal temperature, normal pressure.
7. prepare the method for patching materials described in the claim 1, it is characterized in that: first 50% potter's clay and all machine oil are pressed mixing, then it is added in the asbestos wool gradually, the limit edged stirs, and progressively adds residue potter's clay again, gets patching materials behind the mixing.
8. the method for preparing patching materials described in the claim 3, it is characterized in that: with 50% potter's clay and all machine oil mixings, then it is added in the asbestos material gradually first, the limit edged stirs, progressively add residue potter's clay, the last tung oil mixing that slowly adds gets patching materials again.