CN102911603A - Waterproof paint and preparation method thereof - Google Patents
Waterproof paint and preparation method thereof Download PDFInfo
- Publication number
- CN102911603A CN102911603A CN 201110227705 CN201110227705A CN102911603A CN 102911603 A CN102911603 A CN 102911603A CN 201110227705 CN201110227705 CN 201110227705 CN 201110227705 A CN201110227705 A CN 201110227705A CN 102911603 A CN102911603 A CN 102911603A
- Authority
- CN
- China
- Prior art keywords
- water
- add
- resistant paint
- agent
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an anticorrosive coating, in particular to waterproof paint and a preparation method thereof. The waterproof paint is prepared from quartz powder, talcum powder, an alcohol ester 12 film-forming auxiliary, a thickening agent, a conditioning agent, deionized water and the like. High molecular materials in emulsion of the waterproof paint can effectively form a high-elastic paint film waterproof layer in the roof construction. The waterproof paint has better permeability, a better binding performance and a stronger tensile property, and the problem of cracking damage can be effectively solved.
Description
Technical field
The present invention relates to a kind of protective system, specifically a kind of water-resistant paint and preparation method thereof.
Background technology
Traditional roof waterproof is because of concrete meeting season cracking under being exposed to the sun of the sun, and usually there is obvious oblique crack the nook of reinforced concrete plate or at central part obvious transverse crack etc. is arranged then.In case cracking, affected by temperature variation, expand with wet and contract with dry etc., the crack is enlarged gradually, add the factors such as uneven settlement of foundation or earthquake, cracking ratio is more obvious, and some engineering cracks width are also a lot of person more than 5 millimeters, therefore causes leakage of building, bring very large trouble to unit in charge of construction, to the lives of the people bring safety on hidden danger.
Summary of the invention
The objective of the invention is for overcoming above-mentioned the deficiencies in the prior art part, a kind of water-resistant paint is provided, to form a kind of coating waterproof layer of enhancing, this water-resistant paint is comprised of silica powder, talcum powder, alcohol ester 12 film coalescence aid, thickening material, conditioning agent, deionized water etc., macromolecular material in the water-resistant paint in the emulsion can effectively form snappiness paint film waterproof layer in roofing construction, have preferably perviousness, tackiness and stronger tensile property can effectively solve the impaired problem in crack.
The objective of the invention is to realize with following technical scheme: a kind of water-resistant paint, it is characterized in that: the main component weight ratio of this water-resistant paint is: raw material: emulsion 35-45, filler: silica powder 8-10, barium sulfate 4-6, talcum powder 5-6 reagent: dispersion agent 0.3-0.4, wetting agent 0.3-0.5, alcohol ester 12 film coalescence aid 2, thickening material 1, conditioning agent 0.5, deionized water 20-23;
Prepare the method for a kind of water-resistant paint as claimed in claim 1, it is characterized in that: carry out as follows:
(1) add emulsion in deionized water, silica powder, barium sulfate, talcum powder mix;
(2) in above-mentioned compound, add colorant, stir, add again dispersion agent, wetting agent, thickening material, conditioning agent stirring;
(3) the above-mentioned material that fully stirred is carried out the coarse sand mill, the fine sand mill;
(4) add alcohol ester 12 film coalescence aid and stir putting;
(5) material after above-mentioned the putting is done the viscosity adjustment, the packing warehouse-in.
Advantage of the present invention is: the macromolecular material in this water-resistant paint in the emulsion, have preferably perviousness, and tackiness and stronger tensile property can effectively solve the impaired problem in crack.Water-resistant paint is lower to the requirement of when construction weather, and the drying of water-resistant paint is comparatively quick, and is lower to the requirement of temperature, has avoided in rainy season construction environmental change to the delay of duration.
The invention will be further described below in conjunction with embodiment;
Embodiment,
The main component weight ratio of water-resistant paint is: raw material: emulsion 50, filler: silica powder 9, barium sulfate 4, talcum powder 5 reagent: dispersion agent 0.3, wetting agent 0.3, alcohol ester 12 film coalescence aid 2, thickening material 1, conditioning agent 0.5, deionized water 23;
2. prepare the method for a kind of water-resistant paint as claimed in claim 1, it is characterized in that: carry out as follows:
(1) add emulsion in deionized water, silica powder, barium sulfate, talcum powder mix;
(2) in above-mentioned compound, add colorant, stir, add again dispersion agent, wetting agent, thickening material, conditioning agent stirring;
(3) the above-mentioned material that fully stirred is carried out the coarse sand mill, the fine sand mill;
(4) add alcohol ester 12 film coalescence aid and stir putting;
(5) material after above-mentioned the putting is done the viscosity adjustment, the packing warehouse-in.
Claims (2)
1. water-resistant paint, it is characterized in that: the main component weight ratio of this water-resistant paint is: raw material: emulsion 35-45, filler: silica powder 8-10, barium sulfate 4-6, talcum powder 5-6 reagent: dispersion agent 0.3-0.4, wetting agent 0.3-0.5, alcohol ester 12 film coalescence aid 2, thickening material 1, conditioning agent 0.5, deionized water 20-23;
2. prepare the method for a kind of water-resistant paint as claimed in claim 1, it is characterized in that: carry out as follows:
(1) add emulsion in deionized water, silica powder, barium sulfate, talcum powder mix;
(2) in above-mentioned compound, add colorant, stir, add again dispersion agent, wetting agent, thickening material, conditioning agent stirring;
(3) the above-mentioned material that fully stirred is carried out the coarse sand mill, the fine sand mill;
(4) add alcohol ester 12 film coalescence aid and stir putting;
(5) material after above-mentioned the putting is done the viscosity adjustment, the packing warehouse-in.