CN102911587A - 一种高硬度耐磨防尘环氧地坪及其施工工艺 - Google Patents
一种高硬度耐磨防尘环氧地坪及其施工工艺 Download PDFInfo
- Publication number
- CN102911587A CN102911587A CN 201210411276 CN201210411276A CN102911587A CN 102911587 A CN102911587 A CN 102911587A CN 201210411276 CN201210411276 CN 201210411276 CN 201210411276 A CN201210411276 A CN 201210411276A CN 102911587 A CN102911587 A CN 102911587A
- Authority
- CN
- China
- Prior art keywords
- ground
- parts
- coated
- adopt
- resisting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高硬度耐磨防尘环氧地坪,包括:环氧树脂E51 30-50份;环氧树脂DDH331 20-45份;水40-50份;共溶剂3-8份;环氧树脂固化剂WH-1000 20-25份;消泡剂3054-8388 0.3-0.5份;润湿剂LC-100 2-3份;抗刮伤剂4026B;钛白粉R-902 5-10份;消泡剂SP-602 1.2-1.5份;增稠剂OS-6040 1-2份。本发明提供的环氧地坪具有较高的硬度及耐磨性能,能够有效防尘,提高地坪洁净度,同时本发明提供的环氧地坪的施工工艺能够有效提高地坪平整度,增加观赏性的同时能够节约材料,延长使用寿命。
Description
技术领域
本发明涉及一种高硬度耐磨防尘环氧地坪及其施工工艺。。
背景技术
随着科学技术的进步,人民生活水平的提高,人们对生活环境的要求也越来越高了,空气质量以及生活环境的清洁程度便是衡量人们生活环境是否健康的重要标准,目前我们所使用的地面多为混凝土地面,这样的地面坚固耐压具有非常好的实用性,但是由于混凝土的成分为水泥及砂,容易起灰尘,造成空气质量下降,很大程度上影响了人们的生活环境,不利于长期使用。
发明内容
发明目的:本发明的目的是为了解决现有技术的不足本发明提供了一种能够有效防尘且具有高硬度耐磨特性的环氧地坪及其施工工艺。
技术方案:本发明公开了一种高硬度耐磨防尘环氧地坪,所述的高硬度耐磨防尘环氧地坪,按重量记份,由下述组分组成:
环氧树脂 E51 30-50份;
环氧树脂 DDH331 20-45份;
水 40-50份;
共溶剂 3-8份;
环氧树脂固化剂 WH-1000 20-25份;
消泡剂3054-8388 0.3-0.5份;
润湿剂 LC-100 2-3份;
抗刮伤剂 4026B;
钛白粉 R-902 5-10份;
消泡剂 SP-602 1.2-1.5份;
增稠剂 OS-6040 1-2份。
所述的共溶剂为丙二醇甲醚。
所述的高硬度耐磨防尘环氧地坪,其施工工艺为:
(a)素地处理:清扫地面,除去地面油污,将地面打磨,修补,除尘;
(b)底涂;
(c)研磨修饰:采用打磨机W300将地面局部研磨修饰、整平;
(d)中涂:采用所述的环氧树脂涂料与石英粉、石英粉混合成水性环氧砂浆,用镘刀将所述的水性环氧砂浆均匀涂布地面,施工温度为0-30℃,涂布完成后;
(e)批涂:采用砂纸打磨中涂后的地坪,采用所述的水性环氧树脂涂料与石英粉混合,涂布于地面;
(f)面涂:采用辊筒将水性环氧树脂涂料采用辊涂的方式涂布于地面,辊涂后地面养护6-8h;
(g)养护:地面在封闭条件下,养护25-40h。
有益效果:本发明提供的环氧地坪具有较高的硬度及耐磨性能,能够有效防尘,提高地坪洁净度,同时本发明提供的环氧地坪的施工工艺能够有效提高地坪平整度,增加观赏性的同时能够节约材料,延长使用寿命。
具体实施方式
下面结合具体实施例,进一步阐明本发明。
实施例1:
一种高硬度耐磨防尘环氧地坪,所述的高硬度耐磨防尘环氧地坪,按重量记份,由下述组分组成:
环氧树脂 E51 32份;
环氧树脂 DDH331 28份;
水 50份;
丙二醇甲醚 7份;
环氧树脂固化剂 WH-1000 22份;
消泡剂3054-8388 0.3份;
润湿剂 LC-100 2.3份;
抗刮伤剂 4026B 0.2份;
钛白粉 R-902 5份;
消泡剂 SP-602 1.2份;
增稠剂 OS-6040 1份。
所述的高硬度耐磨防尘环氧地坪,其施工工艺为:
(a)素地处理:清扫地面,除去地面油污,将地面打磨,修补,除尘;
(b)底涂;
(c)研磨修饰:采用打磨机W300将地面局部研磨修饰、整平;
(d)中涂:采用所述的环氧树脂涂料与石英粉、石英粉混合成水性环氧砂浆,用镘刀将所述的水性环氧砂浆均匀涂布地面,施工温度为15℃,涂布完成后;
(e)批涂:采用砂纸打磨中涂后的地坪,采用所述的水性环氧树脂涂料与石英粉混合,涂布于地面;
(f)面涂:采用辊筒将水性环氧树脂涂料采用辊涂的方式涂布于地面;
(g)养护:地面封闭26h。
实施例2:
一种高硬度耐磨防尘环氧地坪,所述的高硬度耐磨防尘环氧地坪,按重量记份,由下述组分组成:
环氧树脂 E51 41份;
环氧树脂 DDH331 32份;
水 45份;
丙二醇甲醚 6份;
环氧树脂固化剂 WH-1000 21份;
消泡剂3054-8388 0.5份;
润湿剂 LC-100 2.8份;
抗刮伤剂 4026B 0.2份;
钛白粉 R-902 9份份;
消泡剂 SP-602 1.4份份;
增稠剂 OS-6040 1.8份。
所述的高硬度耐磨防尘环氧地坪,其施工工艺为:
(a)素地处理:清扫地面,除去地面油污,将地面打磨,修补,除尘;
(b)底涂;
(c)研磨修饰:采用打磨机W300将地面局部研磨修饰、整平;
(d)中涂:采用所述的环氧树脂涂料与石英粉、石英粉混合成水性环氧砂浆,用镘刀将所述的水性环氧砂浆均匀涂布地面,施工温度为28℃,涂布完成后;
(e)批涂:采用砂纸打磨中涂后的地坪,采用所述的水性环氧树脂涂料与石英粉混合,涂布于地面;
(f)面涂:采用辊筒将水性环氧树脂涂料采用辊涂的方式涂布于地面;
(g)养护:地面封闭40h。
实施例3:
一种高硬度耐磨防尘环氧地坪,所述的高硬度耐磨防尘环氧地坪,按重量记份,由下述组分组成:
环氧树脂 E51 50份;
环氧树脂 DDH331 45份;
水 50份;
丙二醇甲醚 8份;
环氧树脂固化剂 WH-1000 25份;
消泡剂3054-8388 0.5份;
润湿剂 LC-100 3份;
抗刮伤剂 4026B 0.45份;
钛白粉 R-902 8份;
消泡剂 SP-602 1.3份;
增稠剂 OS-6040 1.8份。
所述的高硬度耐磨防尘环氧地坪,其施工工艺为:
(a)素地处理:清扫地面,除去地面油污,将地面打磨,修补,除尘;
(b)底涂;
(c)研磨修饰:采用打磨机W300将地面局部研磨修饰、整平;
(d)中涂:采用所述的环氧树脂涂料与石英粉、石英粉混合成水性环氧砂浆,用镘刀将所述的水性环氧砂浆均匀涂布地面,施工温度为28℃,涂布完成后;
(e)批涂:采用砂纸打磨中涂后的地坪,采用所述的水性环氧树脂涂料与石英粉混合,涂布于地面;
(f)面涂:采用辊筒将水性环氧树脂涂料采用辊涂的方式涂布于地面;
(g)养护:地面封闭40h。
上述实施例只为说明本发明的技术构思及特点,其目的是让熟悉该技术领域的技术人员能够了解本发明的内容并据以实施,并不能以此来限制本发明的保护范围。凡根据本发明精神实质所作出的等同变换或修饰,都应涵盖在本发明的保护范围之内。
Claims (3)
1.本发明公开了一种高硬度耐磨防尘环氧地坪,其特征在于:所述的高硬度耐磨防尘环氧地坪,按重量记份,由下述组分组成:
环氧树脂 E51 30-50份;
环氧树脂 DDH331 20-45份;
水 40-50份;
共溶剂 3-8份;
环氧树脂固化剂 WH-1000 20-25份;
消泡剂3054-8388 0.3-0.5份;
润湿剂 LC-100 2-3份;
抗刮伤剂 4026B;
钛白粉 R-902 5-10份;
消泡剂 SP-602 1.2-1.5份;
增稠剂 OS-6040 1-2份。
2.根据权利要求1所述的一种高硬度耐磨防尘环氧地坪,其特征在于:所述的共溶剂为丙二醇甲醚。
3.根据权利要求1所述的一种高硬度耐磨防尘环氧地坪,其特征在于:所述的高硬度耐磨防尘环氧地坪,其施工工艺为:
(a)素地处理:清扫地面,除去地面油污,将地面打磨,修补,除尘;
(b)底涂;
(c)研磨修饰:采用打磨机W300将地面局部研磨修饰、整平;
(d)中涂:采用所述的环氧树脂涂料与石英粉、石英粉混合成水性环氧砂浆,用镘刀将所述的水性环氧砂浆均匀涂布地面,施工温度为0-30℃,涂布完成后;
(e)批涂:采用砂纸打磨中涂后的地坪,采用所述的水性环氧树脂涂料与石英粉混合,涂布于地面,地面涂布完成后养护6-8h;
(f)面涂:采用辊筒将水性环氧树脂涂料采用辊涂的方式涂布于地面,辊涂后地面养护6-8h;
(g)养护:地面在封闭条件下,养护25-40h。