CN102877377A - 一种含有玻璃纤维的滤纸的制备工艺 - Google Patents

一种含有玻璃纤维的滤纸的制备工艺 Download PDF

Info

Publication number
CN102877377A
CN102877377A CN2012103604451A CN201210360445A CN102877377A CN 102877377 A CN102877377 A CN 102877377A CN 2012103604451 A CN2012103604451 A CN 2012103604451A CN 201210360445 A CN201210360445 A CN 201210360445A CN 102877377 A CN102877377 A CN 102877377A
Authority
CN
China
Prior art keywords
filter paper
powder
modified nano
parts
weight portion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103604451A
Other languages
English (en)
Other versions
CN102877377B (zh
Inventor
陈登宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI PHOENIX FILTER CO., LTD.
Original Assignee
Bengbu Phoenix International Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bengbu Phoenix International Co Ltd filed Critical Bengbu Phoenix International Co Ltd
Priority to CN201210360445.1A priority Critical patent/CN102877377B/zh
Publication of CN102877377A publication Critical patent/CN102877377A/zh
Application granted granted Critical
Publication of CN102877377B publication Critical patent/CN102877377B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有玻璃纤维的滤纸的制备工艺，其滤纸是由下述重量份的原料制得：木浆纤维40-45，稻草纤维40-45，玻璃纤维30-35，改性纳米高岭石粉1-2，改性纳米矿物粉2-4，醋丙乳液2-3，钠基膨润土0.6-0.8，氢氧化镁0.5-0.1，壳聚糖0.4-0.8,滑石粉0.5-1，十二烷基硫酸钠1-2，PAE湿强剂0.3-0.5。本发明所得滤纸具有强度高过滤精度高、耐水性好等优点，在常温及高温工况下有稳定的性能指标，具有较好的耐温和过滤效果。

Description

一种含有玻璃纤维的滤纸的制备工艺
技术领域
本发明涉及滤纸领域，确切地说是一种含有玻璃纤维的滤纸的制备工艺。
背景技术                            
作为一种有效的过滤介质，过滤纸已被广泛地用于各个领域。根据组成滤纸的纤维种类不同，过滤纸的性能、用途也不一样，有用于一般场合的普通滤纸，用于高温下的的玻璃纤维滤纸，也有超净用聚丙烯滤纸等。根据滤纸是否浸胶，可以分为两大类，即浸胶滤纸和非浸胶滤纸。浸胶滤纸又分为固化滤纸和非固化滤纸。
随着过滤要求的不断提高，任何由单种纤维组成的滤纸都越来越难以满足使用上的要求，所以由多种纤维组合而成的滤纸应运而生。滤纸生产中常用的纤维有木质纤维、化学纤维、玻璃纤维等。
发明内容
本发明的目的在于提供一种强度高、过滤精度高的含有玻璃纤维的滤纸的制备工艺。
上述目的通过以下方案实现：
一种含有玻璃纤维的滤纸的制备工艺，其特征在于：包括以下步骤：
（1）将高岭石放入碳酸钠与高锰酸钾混合溶液中浸泡3-5小时后，取出干燥，而后研磨成纳米粉末后即得改性纳米高岭石粉，备用；
（2）将5-7重量份伊利石、4-6重量份碳酸钙、12-14重量份页岩混匀后，放入浓度为10-20%的乙酸溶液中浸泡6-8小时后，取出水洗，再于600-700℃煅烧2-4小时，而后研磨成纳米粉末，即得改性纳米矿物粉，备用；
（3）将40-45重量份木浆纤维、40-45重量份稻草纤维、30-35重量份玻璃纤维按重量份混匀后放入碎浆机碎解，得到固含量5-6%的浆料，再加入0.3-0.5重量份PAE湿强剂继续碎解，得混合浆料；
（4）将改性纳米高岭石粉、改性纳米矿物粉、以及其余原料按重量份加入步骤（3）所得混合浆料中，加热到70-80℃；
所述的含有玻璃纤维的滤纸是由下述重量份的原料制得：木浆纤维40-45，稻草纤维40-45，玻璃纤维30-35，改性纳米高岭石粉1-2，改性纳米矿物粉2-4，醋丙乳液2-3，钠基膨润土0.6-0.8，氢氧化镁0.5-0.1，壳聚糖0.4-0.8,滑石粉0.5-1，十二烷基硫酸钠1-2，PAE湿强剂0.3-0.5；
（5）经疏解机疏解后，再磨浆，磨浆后所得浆料经过加水调浆，至固含量2-3%后，按照常规造纸工艺抄纸，成型压榨、干燥即得。
所述的一种含有玻璃纤维的滤纸的制备工艺，其特征在于：所述的醋丙乳液的固含量为35-40%。
所述的一种含有玻璃纤维的滤纸的制备工艺，其特征在于：所述的碳酸钠与高锰酸钾混合溶液由9-10g/L的碳酸钠溶液与0.8-1g/L的高锰酸钾溶液等体积混合而得。 
本发明的有益效果为：本发明原料采用的改性高岭石粉以及改性纳米矿物粉增加了滤纸的吸附性能。本发明所得滤纸具有透水性好、过滤面积大、最大孔径小、过滤精度高、耐水性好等优点，在常温及高温工况下有稳定的性能指标，具有较好的耐温和过滤效果，湿伸长率≤ 1%，湿耐破度≥ 350KPa，抗张强度/kN·m-1 2.26，过滤精度＜ 10μm，杂质去除率＞ 99%。
具体实施方式
一种含有玻璃纤维的滤纸的制备工艺，包括以下步骤：
（1）将高岭石放入碳酸钠与高锰酸钾混合溶液中浸泡5小时后，取出干燥，而后研磨成纳米粉末后即得改性纳米高岭石粉，备用；
（2）将5重量份（kg）伊利石、6重量份碳酸钙、14重量份页岩混匀后，放入浓度为20%的乙酸溶液中浸泡8小时后，取出水洗，再于700℃煅烧4小时，而后研磨成纳米粉末，即得改性纳米矿物粉，备用；
（3）将45重量份木浆纤维、40重量份稻草纤维、30重量份玻璃纤维按重量份混匀后放入碎浆机碎解，得到固含量6%的浆料，再加入0.5重量份PAE湿强剂继续碎解，得混合浆料；
（4）将改性纳米高岭石粉、改性纳米矿物粉、以及其余原料按重量份加入步骤（3）所得混合浆料中，加热到80℃；
所述的含有玻璃纤维的滤纸是由下述重量份（kg）的原料制得：木浆纤维45，稻草纤维40，玻璃纤维30，改性纳米高岭石粉2，改性纳米矿物粉4，醋丙乳液3，钠基膨润土0.6，氢氧化镁0.5，壳聚糖0.4,滑石粉0.5，十二烷基硫酸钠2，PAE湿强剂0.5；
（5）经疏解机疏解后，再磨浆，磨浆后所得浆料经过加水调浆，至固含量2-3%后，按照常规造纸工艺抄纸，成型压榨、干燥即得。
所述的醋丙乳液的固含量为40%。
所述的碳酸钠与高锰酸钾混合溶液由10g/L的碳酸钠溶液与1g/L的高锰酸钾溶液等体积混合而得。

Claims (3)

1.一种含有玻璃纤维的滤纸的制备工艺，其特征在于：包括以下步骤：
（1）将高岭石放入碳酸钠与高锰酸钾混合溶液中浸泡3-5小时后，取出干燥，而后研磨成纳米粉末后即得改性纳米高岭石粉，备用；
（2）将5-7重量份伊利石、4-6重量份碳酸钙、12-14重量份页岩混匀后，放入浓度为10-20%的乙酸溶液中浸泡6-8小时后，取出水洗，再于600-700℃煅烧2-4小时，而后研磨成纳米粉末，即得改性纳米矿物粉，备用；
（3）将40-45重量份木浆纤维、40-45重量份稻草纤维、30-35重量份玻璃纤维按重量份混匀后放入碎浆机碎解，得到固含量5-6%的浆料，再加入0.3-0.5重量份PAE湿强剂继续碎解，得混合浆料；
（4）将改性纳米高岭石粉、改性纳米矿物粉、以及其余原料按重量份加入步骤（3）所得混合浆料中，加热到70-80℃；
所述的含有玻璃纤维的滤纸是由下述重量份的原料制得：木浆纤维40-45，稻草纤维40-45，玻璃纤维30-35，改性纳米高岭石粉1-2，改性纳米矿物粉2-4，醋丙乳液2-3，钠基膨润土0.6-0.8，氢氧化镁0.5-0.1，壳聚糖0.4-0.8,滑石粉0.5-1，十二烷基硫酸钠1-2，PAE湿强剂0.3-0.5；
（5）经疏解机疏解后，再磨浆，磨浆后所得浆料经过加水调浆，至固含量2-3%后，按照常规造纸工艺抄纸，成型压榨、干燥即得。
2.根据权利要求1所述的一种含有玻璃纤维的滤纸的制备工艺，其特征在于：所述的醋丙乳液的固含量为35-40%。
3.根据权利要求1所述的一种含有玻璃纤维的滤纸的制备工艺，其特征在于：所述的碳酸钠与高锰酸钾混合溶液由9-10g/L的碳酸钠溶液与0.8-1g/L的高锰酸钾溶液等体积混合而得。
CN201210360445.1A 2012-09-25 2012-09-25 一种含有玻璃纤维的滤纸的制备工艺 Active CN102877377B (zh)