CN102863168A - 一种岗石填料 - Google Patents
一种岗石填料 Download PDFInfo
- Publication number
- CN102863168A CN102863168A CN2012103388255A CN201210338825A CN102863168A CN 102863168 A CN102863168 A CN 102863168A CN 2012103388255 A CN2012103388255 A CN 2012103388255A CN 201210338825 A CN201210338825 A CN 201210338825A CN 102863168 A CN102863168 A CN 102863168A
- Authority
- CN
- China
- Prior art keywords
- agglomerated stone
- agent
- powder modifier
- parts
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种岗石填料；本发明涉及一种岗石填料；本发明提供了一种人造岗石填料，其技术方案是：由碳酸钙和特殊酯类表面活性剂(即PD-4型粉体改性剂A剂、B剂)制成，包括下述重量份的组分：碳酸钙10000份，PD-4型粉体改性剂A剂10-12份，PD-4型粉体改性剂B剂10-14份；所述PD-4型粉体改性剂A剂为醇醚羧酸盐，PD-4型粉体改性剂B剂为聚丙烯酸钠与水制成，聚丙烯酸钠与水的比例为1∶1000。本发明在岗石加工过程中抑制大量搅拌热，在不饱和树脂液中有持久的分散防沉性，解决了岗石制品会出现气孔、起皮、龟裂等质量问题，适用于岗石加工企业。
Description
技术领域
本发明涉及一种岗石填料，尤其是一种用碳酸钙和特殊酯类表面活性剂制成的人造岗石填料。
背景技术
人造岗石一般以天然大理石碎料、碳酸钙石粉为主要原材料，以有机树脂为胶结剂，经真空搅拌、高压震荡制成方料，再经过室温固化(固化时间在7天以上)、锯切、打磨、抛光等工序制成板材。碳酸钙作为岗石的填料，可以提高制品的耐热性、耐磨性、消光性、尺寸稳定性、抗冲击性、硬度、刚度及可加工性，但是碳酸钙石粉与大理石碎料搅拌固化过程中，会产生大量搅拌热，影响树脂混合液的流动性，导致岗石的后固化过程不够充分，制品出现气孔、起皮、龟裂等质量问题；其次，现有的岗石加工企业用普通的碳酸钙原材料做一块九吨重的人造岗石，需要消耗630千克的大量不饱和树脂，生产成本较高。
发明内容
本发明的目的是要提供一种新型岗石填料及其制造方法，以解决普通碳酸钙石粉在人造岗石加工过程中产生大量搅拌热、影响岗石后固化过程不充分出现质量问题的缺陷。
其技术方案是：
一种岗石填料，由碳酸钙和特殊酯类表面活性剂(即PD-4型粉体改性剂A剂、B剂)制成，包括下述重量份的组分：碳酸钙10000份，PD-4型粉体改性剂A剂10-12份，PD-4型粉体改性剂B剂10-14份；所述PD-4型粉体改性剂A剂为醇醚羧酸盐，PD-4型粉体改性剂B剂为聚丙烯酸钠与水制成，聚丙烯酸钠与水的比例为1∶1000。
制造方法是：1、原矿处理。天然碳酸钙矿石经粗碎成粒径为30mm，在进入主机的第一螺旋输送槽和第二螺旋输送槽处；2、稀释助剂。用两台计量泵分别把特殊酯类表面活性剂PD-4的A剂、B剂分开使用，即分别用水1∶1稀释，再用两台计量泵前后计量加入到碳酸钙矿石中。如A、B组份互溶，会造成混合溶液分层不稳定，影响计量加入的效果；3、喷洒加工。使用计量泵，将稀释好的助剂计量喷雾在二次破碎的原矿表面，矿石通过螺旋进料或皮带输送进研磨主机，进行干法研磨加工即成。
醇醚羧酸盐是一类新型的多功能阴离子表面活性剂，主要表现为：1、卓越的增溶能力，适于配制功能性透明产品；2、良好的去污性、润湿性、乳化性、分散性和钙皂分散力；3、良好的发泡性和泡沫稳定性，发泡力不受水的硬度和介质pH的影响；4、耐硬水、耐酸碱、耐电解质、耐高温、对次氯酸盐和过氧化物稳定；6、具有良好的配伍性能，能与任何离子型或表面活性剂配伍，尤其对阳离子的调理性能没有干扰。
聚丙烯酸钠溶解于冷水、温水、甘油、丙二醇等介质中，对温度变化稳定，有固定金属离子的作用，能阻止金属离子对产品的消极作用，是一种具有多种特殊性能的表面活性剂。
与现有普通碳酸钙填料相比，本发明具有以下优点：
1、在岗石加工过程中抑制产生大量搅拌热，从而使树脂混合液流动性好，后固化过程充分；使岗石填料在不饱和树脂液中有持久的分散防沉性，岗石制品不会出现气孔、起皮、龟裂等质量问题；
2、用本岗石填料做一块九吨重的人造岗石，仅需要消耗540-570千克的不饱和树脂，降低生产成本9.5-14％以上。
具体实施方式
一种岗石填料，由碳酸钙和特殊酯类表面活性剂(即PD-4型粉体改性剂A剂、B剂)制成，包括下述重量份的组分，天然碳酸钙矿石10000份，PD-4型粉体改性剂A剂10份，PD-4型粉体改性剂B剂12份；所述PD-4型粉体改性剂A剂为醇醚羧酸盐，PD-4型粉体改性剂B剂为聚丙烯酸钠与水制成，聚丙烯酸钠与水的比例为1∶1000。
制造方法是：
1、原矿处理。10000份天然碳酸钙矿石经粗碎成粒径为30mm，在进入主机的第一螺旋输送槽和第二螺旋输送槽处；2、稀释助剂。用两台计量泵分别把特殊酯类表面活性剂PD-4的A剂、B剂分开使用，即分别用水1∶1稀释，再用两台计量泵前后计量加入到碳酸钙矿石中；3、喷洒加工。使用计量泵，将稀释好的助剂计量喷雾在二次破碎的原矿表面，矿石通过螺旋进料或皮带输送进研磨主机，进行干法研磨加工即成。
Claims (1)
1.一种岗石填料，由碳酸钙和特殊酯类表面活性剂(即PD-4型粉体改性剂A剂、B剂)制成，其特征是：包括下述重量份的组分：碳酸钙10000份，PD-4型粉体改性剂A剂10-12份，PD-4型粉体改性剂B剂10-14份；所述PD-4型粉体改性剂A剂为醇醚羧酸盐，PD-4型粉体改性剂B剂为聚丙烯酸钠与水制成，聚丙烯酸钠与水的比例为1∶1000。