CN102850957B - 一种以淀粉为原料的木材胶粘剂的制备方法 - Google Patents

一种以淀粉为原料的木材胶粘剂的制备方法 Download PDF

Info

Publication number
CN102850957B
CN102850957B CN201210317005.8A CN201210317005A CN102850957B CN 102850957 B CN102850957 B CN 102850957B CN 201210317005 A CN201210317005 A CN 201210317005A CN 102850957 B CN102850957 B CN 102850957B
Authority
CN
China
Prior art keywords
parts
starch
raw material
wood adhesive
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210317005.8A
Other languages
English (en)
Other versions
CN102850957A (zh
Inventor
计慷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU DELAIER BUILDING MATERIALS SCIENCE AND TECHNOLOGY CO LTD
Original Assignee
SUZHOU DELAIER BUILDING MATERIALS SCIENCE AND TECHNOLOGY CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU DELAIER BUILDING MATERIALS SCIENCE AND TECHNOLOGY CO LTD filed Critical SUZHOU DELAIER BUILDING MATERIALS SCIENCE AND TECHNOLOGY CO LTD
Priority to CN201210317005.8A priority Critical patent/CN102850957B/zh
Publication of CN102850957A publication Critical patent/CN102850957A/zh
Application granted granted Critical
Publication of CN102850957B publication Critical patent/CN102850957B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种以淀粉为原料的木材胶粘剂的制备方法，属于粘结剂技术领域。采用如下重量份的原料制成：植物淀粉20～30份、明矾5～10份、氧化镁4～7份、聚乙烯醇2～8份、苯酚2～3份、氢氧化钠2～3份、羟甲基丙烯酰胺1份、高岭土2～4份、膨润土2～4份、壳聚糖4～8份、甘油2～4份、乙二胺四乙酸二钠1份、琼脂2份、纤维素3～6份、水30～50份。本发明提供的木材胶粘剂的技术效果是：采用的原料无素无害，无有机溶剂添加，符合大众对家具质量的要求。以淀粉为主要原料，可以制得强度较高的木材，粘接力强，为转基因的作物提供了新的用途。

Description

一种以淀粉为原料的木材胶粘剂的制备方法
技术领域
本发明提供了一种以淀粉为原料的木材胶粘剂，属于粘结剂技术领域。
背景技术
随着人们对家居环保条件的越来越重视，对于家具中释放出的VOC气体、有机溶剂等也提出了越来越苛刻的要求。传统的家具用的胶粘剂中，基本都带有有机溶剂，这些溶剂的不易在短期内释放完全，而会长期不断地缓慢向外产生，这就会对人们的身体健康产生影响。
与此同时，人们对转基因食品，例如转基因的大豆、小麦等，也持有谨慎地态度。因此，将转基因食品用于其它方面的用途有利于原料的充分利用。
发明内容
针对以上对现有技术的评述，本发明所要解决的技术问题是：家具常用的胶粘剂中有机溶剂使用量多，转基因粮食不被人们认可，资源无法得到充分利用。采用的技术方案是：
一种以淀粉为原料的木材胶粘剂的制备方法，采用如下重量份的原料制成：植物淀粉20～30份、明矾5～10份、氧化镁4～7份、聚乙烯醇2～8份、苯酚2～3份、氢氧化钠2～3份、羟甲基丙烯酰胺1份、高岭土2～4份、膨润土2～4份、壳聚糖4～8份、甘油2～4份、乙二胺四乙酸二钠1份、琼脂2份、纤维素3～6份、水30～50份。
上述的木材胶粘剂的制备方法是：
S1：在反应窗口中加入水，升温到30～50℃；
S2：在开启搅拌的条件下，加入植物淀粉、明矾、氧化镁、聚乙烯醇、苯酚、氢氧化钠，反应温度30～50℃，反应60～240分钟；
S3：加入羟甲基丙烯酰胺、壳聚糖、甘油、乙二胺四乙酸二钠、琼脂、纤维素，开启搅拌，反应温度30～40℃，反应时间60～120分钟；
S4：降温到20～30℃，保温时间60～120分钟；
S5：升温到30～40℃，加入高岭土、膨润土，搅拌均匀，即可。
所述的纤维素优选为甲基纤维素、乙基纤维素、羟乙基纤维素、羟丙基纤维素、羧甲基纤维素中的一种或几种任意比例混合物。
上述的植物淀粉优选自玉米淀粉、小麦淀粉、小麦淀粉、土豆淀粉、木薯淀粉。
本发明提供的木材胶粘剂的技术效果是：采用的原料无素无害，无有机溶剂添加，符合大众对家具质量的要求。以淀粉为主要原料，可以制得强度较高的木材，粘接力强，为转基因的作物提供了新的用途。
具体实施方式
按表1所示的重量比称取各组分
表1实施例1～实施例3的重量配比
上述的纤维素可以选自甲基纤维素、乙基纤维素、羟乙基纤维素、羟丙基纤维素、羧甲基纤维素中的一种或几种任意比例混合物，都可以实现本发明的技术方案。本实施例中采用羟丙基纤维素。
上述的植物淀粉可以选自玉米淀粉、小麦淀粉、小麦淀粉、土豆淀粉、木薯淀粉，都可以实现本发明的技术方案。本实施例中采用小麦淀粉。
制备方法是：
实施例1
S1：在反应窗口中加入水，升温到30℃；
S2：在开启搅拌的条件下，加入植物淀粉、明矾、氧化镁、聚乙烯醇、苯酚、氢氧化钠，反应温度30℃，反应60分钟；
S3：加入羟甲基丙烯酰胺、壳聚糖、甘油、乙二胺四乙酸二钠、琼脂、纤维素，开启搅拌，反应温度30℃，反应时间60分钟；
S4：降温到20℃，保温时间60分钟；
S5：升温到30℃，加入高岭土、膨润土，搅拌均匀，即可。
实施例2
与实施例1的区别在于：S1中的温度为40℃；S2中的反应温度为40℃，反应时间为120分钟；S3中反应温度35℃，反应时间100分钟；S4中25℃，保温时间100分钟；S5中的温度为35℃。
实施例3
与实施例1的区别在于：S1中的温度为50℃；S2中的反应温度为50℃，反应时间为240分钟；S3中反应温度40℃，反应时间120分钟；S4中30℃，保温时间120分钟；S5中的温度为40℃。
性能测试
采用上述实施例的木材胶粘剂，使用滚筒涂胶机对木板进行涂胶，单面涂胶量为150～170g/m3。采用常规热压制板工艺，单位压力1.0～1.2MPa，温度110～120℃，时间0.5～0.8min/mm，以专利CN 200410017054中公开的木材粘胶剂作为对照例。考察胶合板的强度干强，并在60条件下浸泡4小时，取出冷却，测定其耐水强度。试验结果如表2所示。
表2实施例1～实施例3以及对照例的试验结果
  实施例1   实施例2   实施例3   对照例
  强度干强   7.1MPa   7.2MPa   7.1MPa   5.4MPa
  耐水强度   2.4MPa   2.5MPa   2.6MPa   1.7MPa

Claims (1)

1.一种以淀粉为原料的木材胶粘剂的制备方法，采用如下重量份的原料制成：植物淀粉20份、明矾10份、氧化镁5份、聚乙烯醇6份、苯酚2份、氢氧化钠3份、羟甲基丙烯酰胺1份、高岭土2份、膨润土2份、壳聚糖4份、甘油2份、乙二胺四乙酸二钠1份、琼脂2份、纤维素4份、水50份；所述的纤维素是羟丙基纤维素，所述的植物淀粉是小麦淀粉；制备方法如下：S1：在反应窗口中加入水，升温到40℃；S2：在开启搅拌的条件下，加入植物淀粉、明矾、氧化镁、聚乙烯醇、苯酚、氢氧化钠，反应温度40℃，反应120分钟；S3：加入羟甲基丙烯酰胺、壳聚糖、甘油、乙二胺四乙酸二钠、琼脂、纤维素，开启搅拌，反应温度35℃，反应时间100分钟；S4：降温到25℃，保温时间100分钟；S5：升温到35℃，加入高岭土、膨润土，搅拌均匀，即可。
CN201210317005.8A 2012-08-30 2012-08-30 一种以淀粉为原料的木材胶粘剂的制备方法 Expired - Fee Related CN102850957B (zh)