CN102850756A - 鳞片硅酸盐矿物填充的聚碳酸酯合金材料 - Google Patents
鳞片硅酸盐矿物填充的聚碳酸酯合金材料 Download PDFInfo
- Publication number
- CN102850756A CN102850756A CN2012103533371A CN201210353337A CN102850756A CN 102850756 A CN102850756 A CN 102850756A CN 2012103533371 A CN2012103533371 A CN 2012103533371A CN 201210353337 A CN201210353337 A CN 201210353337A CN 102850756 A CN102850756 A CN 102850756A
- Authority
- CN
- China
- Prior art keywords
- alloy material
- parts
- filled
- silicate minerals
- scale
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种鳞片硅酸盐矿物填充的聚碳酸酯合金材料,属于高分子材料技术领域。其是由以下重量份数按的原料组成:聚碳酸酯树脂 120~150 份; ABS 树脂 36~45 份;鳞片硅酸盐矿物 12~18 份;复配阻燃剂 20~30 份;偶联剂 0.2~0.7 份;抗氧剂 0.3~0.6 份;脱模剂 1.5~2.1 份。具有力学性能好、模量高的特点。弯曲强度 80~90MPa, 弯曲模量 3500~4000MPa, 冲击强度30~36KJ/m2 断裂伸长率 34~40% ,阻燃性 V-0(1.6mm) 。
Description
技术领域
本发明属于高分子材料技术领域,具体涉及一种鳞片硅酸盐矿物填充的聚碳酸酯合金材料。
背景技术
聚碳酸酯合金材料具有较好的综合性能,但是在生产汽车制品时,由于其模量偏低,因而限制了其应用。鳞片硅酸盐是一种很好的填料,可以有效提高材料的模量,因此, 本发明尝试用鳞片硅酸盐填充聚碳酸酯材料改善其模量。
发明内容
本发明的任务在于提供一种鳞片硅酸盐矿物填充的聚碳酸酯合金材料,该材料具有成本低和模量高的长处。
本发明的任务是这样来完成的,一种鳞片硅酸盐矿物填充的聚碳酸酯合金材料,其是由以下重量份数按的原料组成:
在本发明的一个具体的实施例中,所述的聚碳酸酯树脂为双酚A型聚碳酸酯树脂。
在本发明的另一个具体的实施例中,所述的ABS树脂为马来酸酐接枝的丙烯腈-丁二烯-苯乙烯共聚物。
在本发明的又一个具体的实施例中,所述的鳞片硅酸盐矿物为平均粒径为3微米的硅酸盐粉体。
在本发明的再一个具体的实施例中,所述的复配阻燃剂由质量百分比为50%的十溴二苯乙烷和质量百分比为50%的碳酸钙组成。
在本发明的还有一个具体的实施例中,所述的偶联剂为N-β-(氨乙基)-γ-氨丙基甲基二甲氧基硅烷。
在本发明的更而一个具体的实施例中,所述的抗氧剂为四[β-(3,5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯。
在本发明的进而一个具体的实施例中,所述的脱模剂为氧化聚乙烯蜡。
由本发明提供的鳞片硅酸盐矿物填充的聚碳酸酯合金材料具有力学性能好、模量高的特点。弯曲强度 80~90MPa,弯曲模量3500~4000MPa,冲击强度30~36KJ/m2 断裂伸长率34~40%,阻燃性V-0(1.6mm)。
具体实施方式
实施例1
实施例2
实施例3
实施例4
由上述实施例1至4得到的鳞片硅酸盐矿物填充的聚碳酸酯合金材料经测试具有下表所示的技术效果:
测试项目 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
弯曲强度MPa | 80.0 | 84.5 | 87.6 | 89.3 |
弯曲模量MPa | 3530 | 3670 | 3820 | 3980 |
冲击强度MPa | 30.4 | 32.3 | 34.8 | 35.7 |
断裂伸长率% | 34.2 | 36.5 | 38.4 | 39.8 |
阻燃性V-0(1.6mm) | V-0 | V-0 | V-0 | V-0 |
Claims (8)
1.一种鳞片硅酸盐矿物填充的聚碳酸酯合金材料,其特征在于其是由以下重量份数按的原料组成:
聚碳酸酯树脂 120~150份;
ABS树脂 36~45份;
鳞片硅酸盐矿物 12~18份;
复配阻燃剂 20~30份;
偶联剂 0.2~0.7份;
抗氧剂 0.3~0.6份;
脱模剂 1.5~2.1份。
2.根据权利要求1所述的鳞片硅酸盐矿物填充的聚碳酸酯合金材料,其特征在于所述的聚碳酸酯树脂为双酚A型聚碳酸酯树脂。
3.根据权利要求1所述的鳞片硅酸盐矿物填充的聚碳酸酯合金材料,其特征在于所述的ABS树脂为马来酸酐接枝的丙烯腈-丁二烯-苯乙烯共聚物。
4.根据权利要求1所述的鳞片硅酸盐矿物填充的聚碳酸酯合金材料,其特征在于所述的鳞片硅酸盐矿物为平均粒径为3微米的硅酸盐粉体。
5.根据权利要求1所述的鳞片硅酸盐矿物填充的聚碳酸酯合金材料,其特征在于所述的复配阻燃剂由质量百分比为50%的十溴二苯乙烷和质量百分比为50%的碳酸钙组成。
6.根据权利要求1所述的鳞片硅酸盐矿物填充的聚碳酸酯合金材料,其特征在于所述的偶联剂为N-β-(氨乙基)-γ-氨丙基甲基二甲氧基硅烷。
7.根据权利要求1所述的鳞片硅酸盐矿物填充的聚碳酸酯合金材料,其特征在于所述的抗氧剂为四[β-(3,5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯。
8.根据权利要求1所述的鳞片硅酸盐矿物填充的聚碳酸酯合金材料,其特征在于所述的脱模剂为氧化聚乙烯蜡。