CN102837532A - 表面改性涂料涂覆的书写板及其配套书写液 - Google Patents

表面改性涂料涂覆的书写板及其配套书写液 Download PDF

Info

Publication number
CN102837532A
CN102837532A CN2012103449723A CN201210344972A CN102837532A CN 102837532 A CN102837532 A CN 102837532A CN 2012103449723 A CN2012103449723 A CN 2012103449723A CN 201210344972 A CN201210344972 A CN 201210344972A CN 102837532 A CN102837532 A CN 102837532A
Authority
CN
China
Prior art keywords
writing
coating
ethanol
liquid
writing board
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103449723A
Other languages
English (en)
Other versions
CN102837532B (zh
Inventor
董川
杨振华
张月霞
弓晓娟
游建梅
双少敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi color Environmental Protection Technology Co., Ltd.
Original Assignee
Shanxi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi University filed Critical Shanxi University
Priority to CN201210344972.3A priority Critical patent/CN102837532B/zh
Publication of CN102837532A publication Critical patent/CN102837532A/zh
Application granted granted Critical
Publication of CN102837532B publication Critical patent/CN102837532B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种表面改性涂料涂覆的书写板及其配套书写液，书写板是在浅色亚光底板上涂一层显色涂料制成。显色涂料是将百里酚酞溶于乙醇中，加入戊二醛40-60℃反应0.5-1.5小时、再加入二甲苯、丙酮、聚氨基甲酸酯，搅拌均匀，最后加入粘结剂，充分搅拌制得。配套使用的书写液，是将NaOH或KOH溶解于水中，加入乙醇，最后加入香味剂，搅拌均匀制得。书写液可在本发明的书写板上书写出蓝色字迹，字迹可用湿布擦除。本发明书写板制作工艺简单，涂料一次涂覆可重复使用6个月以上；所用书写液配方简单、实用、经济。本产品适合在学校、家庭、办公及各种需要书写的场合使用。

Description

表面改性涂料涂覆的书写板及其配套书写液
技术领域
本发明涉及教学用具，具体属于一种表面改性涂料涂覆的书写板及其配套书写液。
背景技术
为了克服黑板粉笔粉尘污染的问题，市场上出现了很多无尘书写板及其书写液。如专利CN100355843C和CN100432165C分别公开了一种蓝色书写液和一种红色书写液。这些书写液所用书写板面板可以是表面光滑的玻璃、米黄色或乳白色的亚光彩钢板、塑料板等。从根本上解决了粉尘污染，大大改善了教学环境。然而，这些产品也存在着不足，无尘板写字后擦除需要专用的擦洗液，而且擦除效果不太理想。专利CN1186410C公开了一种白板书写液。书写液由酸碱指示剂和碱液组成，可用于教学板书，办公记事等。虽然该书写液不再需要专用的擦洗液，然而书写液成本较高，由于我国广大农村地区经济不是很发达，因此高成本的书写液不利于无尘板在我国的大面积推广。
发明内容
本发明的目的在于提供一种成本较低、无毒、无刺激性气味、对人体和环境无害的表面改性涂料涂覆的书写板及其配套书写液。其书写字迹很容易被水擦除，且书写板上不会形成书写液阴影。
本发明提供的一种表面改性涂料涂覆的书写板，包括浅色亚光底板，在底板上涂有一层显色涂料，所述显色涂料由如下方法制得：
涂料组分按重量百分比计：乙醇82-90%，百里酚酞3%-6%，丙酮1-5%，聚氨基甲酸酯0.1-0.2%，二甲苯0.1-0.3%，戊二醛0.1-3%，粘结剂2.0-5.2%；
涂料制备：按上述比例，将百里酚酞溶于乙醇中，加入戊二醛40-60℃反应0.5-1.5小时、再加入二甲苯、丙酮、聚氨基甲酸酯，搅拌均匀，最后加入粘结剂，充分搅拌。
所述的粘结剂选用聚苯乙烯或聚乙烯醇。
当将涂料涂于浅色亚光底板过夜后，乙醇挥发，剩余百里酚酞均匀渗透于底板中，由于戊二醛的存在可以使百里酚酞发生交联，更好的结合在一起。加入聚氨基甲酸酯可以使百里酚酞呈粘性，使得涂料呈胶粘状态，便于百里酚酞更好的粘附于白板表面。粘结剂可以使百里酚酞在底板表面形成多层薄膜，利于多次重复使用。
本发明提供的一种与上述表面改性涂料涂覆的书写板配套使用的书写液，其组分按重量百分比计：
NaOH 2.5-9.0%
水 82-90%
乙醇 2.1-8.0%
香味剂 0-1%
书写液的制备方法：按上述配比，将NaOH溶解于水中，加入乙醇，最后加入香味剂，搅拌均匀即可。
所述的NaOH可以用KOH代替。
书写液可在本发明的书写板上书写，由于书写液中的氢氧化钠与底板中的百里酚酞接触而产生蓝色，这样在书写板上就书写出蓝色字迹。另外，书写字迹使用湿布擦除即可。由于百里酚酞不溶于水，因此湿布可以擦除书写字迹，但是百里酚酞仍然牢固附着于底板表面，仅有极少量损失。实验证明，一次涂布好的书写板可以连续使用6个月以上（每天10小时）。
与现有技术相比，本发明所使用原料价廉易得，涂料一次涂覆可重复使用6月以上（每天使用10小时）；制作工艺简单，只需将配好的涂料涂于底板上过夜后即可使用，所使用书写液配方简单、实用、经济。本产品适合在学校、家庭、办公及各种需要书写的场合使用。本书写液不需专用擦除液，水擦即可，使用本产品可以大大降低书写成本。而且使用本产品安全、环保。
具体实施方式
实施例1
书写板涂料的组分和含量为：乙醇89.7g，百里酚酞6g，丙酮1g，聚氨基甲酸酯0.1g，二甲苯0.2g，戊二醛1g，聚苯乙烯2g。
涂料的制备方法：将6g百里酚酞溶于89.7g乙醇中，加入1g戊二醛，50℃反应1小时后，加入0.2g二甲苯、1g丙酮、0.1g聚氨基甲酸酯，搅拌均匀，最后加入2g聚苯乙烯。将此涂料涂到浅色亚光塑料板上，放置过夜，使涂料充分渗透到微孔中。
书写液配方：NaOH 9g，水85.8mL，乙醇5g，香味剂0.2g。
书写液制备方法：将9gNaOH溶解于85.8ml水中，加入5g乙醇，再加入0.2g香味剂，搅拌均匀即可。
书写后蓝色字迹清晰，笔迹干后，用湿布擦除无笔迹残留和污染，可重复使用8个月（每天10小时）。
实施例2
书写板涂料的组分和含量为：乙醇88g，百里酚酞5.4g，丙酮3.4g，聚氨基甲酸酯0.2g，二甲苯0.3g，戊二醛0.5g，聚苯乙烯2.1g
涂料的制备方法：将5.4g百里酚酞溶于88g乙醇中，加入0.5g戊二醛，40℃反应1.5小时后，加入0.3g二甲苯、3.4g丙酮、0.2g聚氨基甲酸酯，搅拌均匀，最后加入2.1g聚苯乙烯。将此涂料涂到浅色亚光塑料板上，放置过夜，使涂料充分渗透到微孔中。
书写液配方：NaOH 7g，水86mL，乙醇7g。
书写液制备方法：将7gNaOH溶解于86ml水中，加入7g乙醇，搅拌均匀即可。
书写后蓝色字迹清晰，笔迹干后，用湿布擦除无笔迹残留和污染，可重复使用7.5个月（每天10小时）。
实施例3
书写板涂料的组分和含量为：乙醇85g，百里酚酞4.3g，丙酮3.6g，聚氨基甲酸酯0.15g，二甲苯0.25g，戊二醛2.7g，聚乙烯醇4g
涂料的制备方法：将4.3g百里酚酞溶于85g乙醇中，加入2.7g戊二醛，50℃反应1小时后，加入0.25g二甲苯、3.6g丙酮，加入0.15g聚氨基甲酸酯，搅拌均匀，最后加入4g聚乙烯醇。将此涂料涂到浅色亚光板上，放置过夜，使涂料充分渗透到微孔中。
书写液配方：KOH 5.5g，水87mL，乙醇7g，香味剂0.5g。
书写液制备方法：将5.5gKOH溶解于87ml水中，加入7g乙醇，再加入0.5g香味剂，搅拌均匀即可。
书写后蓝色字迹清晰，笔迹干后，用湿布擦除无笔迹残留和污染，可重复使用6.8个月（每天10小时）。
实施例4
书写板覆盖膜涂料的组分和含量为：乙醇84.5g，百里酚酞4g，丙酮4.7g，聚氨基甲酸酯0.18g，二甲苯0.12g，戊二醛1.5g，聚乙烯醇5g
涂料的制备方法：将4g百里酚酞溶于84.5g乙醇中，加入1.5g戊二醛，60℃反应0.5小时后，加入0.12g二甲苯、4.7g丙酮、0.18g聚氨基甲酸酯，搅拌均匀，最后加入5g聚乙烯醇。将此涂料涂到微孔塑料底板上，放置过夜，使涂料充分渗透到微孔中。
书写液配方：KOH 5g，水89mL，乙醇5.6g，香味剂0.4g。
书写液制备方法：将5gKOH溶解于89ml水中，加入5.6g乙醇，再加入0.4g香味剂，搅拌均匀即可。
书写后蓝色字迹清晰，笔迹干后，用湿布擦除无笔迹残留和污染，可重复使用6.5个月（每天10小时）。
实施例5
书写板覆盖膜涂料的组分和含量为：乙醇83.7g，百里酚酞3.8g，丙酮4.8g，聚氨基甲酸酯0.2g，二甲苯0.15g，戊二醛2.85g，聚苯乙烯4.5g
涂液的制备方法：将3.8g百里酚酞溶于83.7g乙醇中，加入2.85g戊二醛，60℃搅拌反应0.5小时后，加入0.15g二甲苯、4.8g丙酮、4.5g聚苯乙烯，搅拌均匀，最后加入0.2g聚氨基甲酸酯。将此涂料涂到多空塑料板上，放置过夜，使涂料充分渗透到微孔中。
书写液配方：NaOH 4g，水88mL，乙醇8g。
书写液制备方法：将4gNaOH溶解于88ml水中，加入8g乙醇，搅拌均匀即可。
书写后蓝色字迹清晰，笔迹干后，用湿布擦除无笔迹残留和污染，可重复使用6个月（每天10小时）。
实施例6
书写板覆盖膜涂料的组分和含量为：乙醇86g，百里酚酞5g，丙酮2.75g，聚氨基甲酸酯0.12g，二甲苯0.28g，戊二醛2.75g，聚乙烯醇3.1g
涂液的制备方法：将5g百里酚酞溶于86g乙醇中，加入2.75g戊二醛，50℃搅拌反应1小时后，加入2.75g丙酮、3.1g聚乙烯醇溶解，搅拌均匀，最后加入0.12g聚氨基甲酸酯。将此涂料涂到亚光板上，放置过夜，使涂料充分渗透到微孔中。
书写液配方：KOH 6g，水88.3mL，乙醇5.4g，香味剂0.3g。
书写液制备方法：将6gKOH溶解于88.3ml水中，加入5.4g乙醇，0.3g香味剂，搅拌均匀即可。
书写后蓝色字迹清晰，笔迹干后，用湿布擦除无笔迹残留和污染，可重复使用7个月（每天10小时）。

Claims (5)

1.一种表面改性涂料涂覆的书写板，包括浅色亚光底板，其特征在于：所述的亚光底板上涂有一层显色涂料，所述显色涂料由如下方法制得：
涂料组分按重量百分比计：乙醇82-90%，百里酚酞3%-6%，丙酮1-5%，聚氨基甲酸酯0.1%，二甲苯0.1-0.3%，戊二醛0.1-3%，粘结剂2.0-5.2%；
涂料制备：按上述比例，将百里酚酞溶于乙醇中，加入戊二醛40-60℃反应0.5-1.5小时、再加入二甲苯、丙酮、聚氨基甲酸酯，搅拌均匀，最后加入粘结剂，充分搅拌。
2.按权利要求1所述的一种表面改性涂料涂覆的书写板，其特征在于：所述的粘结剂是聚苯乙烯或聚乙烯醇。
3.一种与权利要求1所述的表面改性涂料涂覆的书写板配套使用的书写液，其特征在于：其组分按重量百分比计：
NaOH 2.5-8%
水 82-90%
乙醇 2.1-8%
香味剂 0-1%。
4.按权利要求3所述的表面改性涂料涂覆的书写板配套使用的书写液，其特征在于：所述的NaOH用KOH代替。
5.按权利要求3所述的表面改性涂料涂覆的书写板配套使用的书写液的制备方法，其特征在于：按配比，将NaOH溶解于水中，加入乙醇，最后加入香味剂，搅拌均匀即可。
CN201210344972.3A 2012-09-17 2012-09-17 表面改性涂料涂覆的书写板及其配套书写液 Active CN102837532B (zh)