CN102827434A - 一种新型阻燃发泡材料 - Google Patents
一种新型阻燃发泡材料 Download PDFInfo
- Publication number
- CN102827434A CN102827434A CN201210321824XA CN201210321824A CN102827434A CN 102827434 A CN102827434 A CN 102827434A CN 201210321824X A CN201210321824X A CN 201210321824XA CN 201210321824 A CN201210321824 A CN 201210321824A CN 102827434 A CN102827434 A CN 102827434A
- Authority
- CN
- China
- Prior art keywords
- flame retardant
- novel flame
- foam material
- foaming material
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种新型阻燃发泡材料,其主要由聚氯乙烯、氯醋共聚树脂、阻燃剂、硅油、稳定剂、发泡剂、交联剂及发泡助剂按照常规方法制备而成:其中,所述的阻燃剂由三氧化锑、LHX-999无机阻燃剂、氢氧化镁、氢氧化铝和硼酸锌组成。采用上述方案后,本发明的新型阻燃发泡材料,其阻燃剂采用三氧化锑、LHX-999无机阻燃剂、氢氧化镁、氢氧化铝和硼酸锌的搭配组合,从而具有优良的阻燃性能,达到GB50222-1995标准B1级要求。
Description
技术领域
本发明涉及建材领域,具体涉及阻燃发泡材料。
背景技术
阻燃发泡材料因其具有质轻、阻燃等性能,被广泛用于各种需要防火的场合。但现有阻燃发泡材料,其阻燃性能仍不是太理想,无法满足某些防火要求较高的场合,在使用上还是受到一些局限。
发明内容
本发明的目的是提供一种阻燃性能较好的新型阻燃发泡材料。
为了实现上述目的,本发明采用如下技术方案:
一种新型阻燃发泡材料,主要由如下重量份组份按照常规方法制备而成:
其中,所述的阻燃剂由如下重量比例的组份组成:
上述稳定剂采用钙锌复合稳定剂。
上述交联剂采用DCP交联剂。
上述发泡剂采用AC发泡剂。
采用上述方案后,本发明的新型阻燃发泡材料,其阻燃剂采用三氧化锑、LHX-999无机阻燃剂、氢氧化镁、氢氧化铝和硼酸锌的搭配组合,从而具有优良的阻燃性能,达到GB50222-1995标准B1级要求。
具体实施方式
实施例1:
本发明的一种新型阻燃发泡材料,主要由如下重量份组份按照常规方法制备而成:
其中,所述的阻燃剂由如下重量比例的组份组成:
实施例2:
本发明的一种新型阻燃发泡材料,主要由如下重量份组份按照常规方法制备而成:
其中,所述的阻燃剂由如下重量比例的组份组成:
实施例3:
本发明的一种新型阻燃发泡材料,主要由如下重量份组份按照常规方法制备而成:
其中,所述的阻燃剂由如下重量比例的组份组成:
上述各实施例中,稳定剂采用钙锌复合稳定剂;交联剂采用DCP交联剂;发泡剂采用AC发泡剂;发泡助剂采用常规发泡助剂;LHX-999无机阻燃剂的销售商为深圳市联合鑫科技有限公司。采用上述方案后,本发明的新型阻燃发泡材料,本发明的新型阻燃发泡材料,其阻燃剂采用三氧化锑、LHX-999无机阻燃剂、氢氧化镁、氢氧化铝和硼酸锌的搭配组合,从而具有优良的阻燃性能,达到GB50222-1995标准B1级要求。且其保温隔热性能达到GB/T10294-2008标准的要求。
表1为本发明的新型阻燃发泡材料的阻燃性能检验数据,表2为本发明的新型阻燃发泡材料的隔热性能检验数据。
表1
表2
Claims (4)
1.一种新型阻燃发泡材料,其特征在于:主要由如下重量份组份按照常规方法制备而成:
其中,所述的阻燃剂由如下重量比例的组份组成:
2.根据权利要求1所述的一种新型阻燃发泡材料,其特征在于:上述稳定剂采用钙锌复合稳定剂。
3.根据权利要求1所述的一种新型阻燃发泡材料,其特征在于:上述交联剂采用DCP交联剂。
4.根据权利要求1所述的一种新型阻燃发泡材料,其特征在于:上述发泡剂采用AC发泡剂。