CN102816388A - 一种空调机用阻燃聚丙烯及其制备方法 - Google Patents
一种空调机用阻燃聚丙烯及其制备方法 Download PDFInfo
- Publication number
- CN102816388A CN102816388A CN2012103394627A CN201210339462A CN102816388A CN 102816388 A CN102816388 A CN 102816388A CN 2012103394627 A CN2012103394627 A CN 2012103394627A CN 201210339462 A CN201210339462 A CN 201210339462A CN 102816388 A CN102816388 A CN 102816388A
- Authority
- CN
- China
- Prior art keywords
- preparation
- refrigeration system
- mixtures
- flame redardant
- polypropylene flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供一种空调机用阻燃聚丙烯,由下列原料组成,以重量份数表示法为:共聚聚丙烯40-55%、均聚聚丙烯5-15%、阻燃剂2-8%、聚烯烃弹性体10-15%、润滑剂15-20%、无机填料1-2%、紫外线吸收剂0.1-0.5%、光稳定剂0.1-0.5%和金属离子钝化剂0.1-0.5%;使用该配方制作出来的聚丙烯组合物紫外线吸收效果好、能抑制光氧化还原或光老化、不易脆化、光泽度高和耐候效果明显,生产过程中无毒,无刺激性气味,低碳环保,价格低廉,阻燃性能优异,热稳定性高,光泽度高、磨损率低适用于空调等家电领域。
Description
技术领域
本发明涉及高分子材料领域,尤其涉及一种空调机用阻燃聚丙烯及其制备方法。
背景技术
随着社会的发展,人们生活水平的提高,空调已经走进了千家万户,空调能对房间内空气的温度、湿度、洁净度和空气流速等参数进行调节,满足使用者的需求,而随着人性化理念的普及,及新型和谐社会的构成,制作空调外壳用的聚丙烯材料要求也随之提高了,不断改进聚丙烯的各种特性,以达到使用者对安全舒适的需要是非常必要的。
现有的空调机用聚丙烯材料,主要采用在聚丙烯树脂中增加热塑性弹性体和阻燃剂,中国专利CN 101805480 A公开了阻燃聚丙烯材料及其制备方法,但是考虑到以上专利配方对吸收紫外线效果不好,不能抑制光氧化还原或光老化等方面,现有技术就显得略有不足。
发明内容
本发明提供一种空调机用阻燃聚丙烯,解决现有阻燃聚丙烯材料中的紫外线效果不好、不能抑制光氧化还原或光老化、易脆化、光泽度低和耐候效果不明显等技术问题。
本发明采用以下技术方案:
一种空调机用阻燃聚丙烯,由下列原料组成,以重量份数表示法为:
共聚聚丙烯 40-55%;
均聚聚丙烯 5-15%;
阻燃剂 2-8%;
聚烯烃弹性体 10-15%;
润滑剂 15-20%;
无机填料 1-2%;
紫外线吸收剂 0.1-0.5%;
光稳定剂 0.1-0.5%;
金属离子钝化剂 0.1-0.5%。
作为本发明的一种优选技术方案:其中,所述共聚聚丙烯为BT310SE0-100或K7926中的一种或多种混合物,熔融指数为6-30g/10min。
作为本发明的一种优选技术方案:所述均聚聚丙烯为C30G、T50G或T30G中的一种或多种混合物,熔融指数为10-15g/10min。
作为本发明的一种优选技术方案:根据权利要求1所述的一种空调机用阻燃聚丙烯及其制备方法,其特征在于:所述阻燃剂采用FR100-A、氢氧化镁或氢氧化铝中的一种或多种混合物。
作为本发明的一种优选技术方案:所述聚烯烃弹性体采用POE8401或POE8411中的一种或多种混合物, 熔融指数30.0g/10 min,密度0.885g/cm。
作为本发明的一种优选技术方案:所述润滑剂采用滑石粉或碳酸钙中的一种或多种混合物。
作为本发明的一种优选技术方案:所述紫外线吸收剂选用UV-327或UV531中的一种或多种混合物。
作为本发明的一种优选技术方案:所述光稳定剂采用受阻胺光稳定剂HS-944或HALS中的一种或多种混合物。
作为本发明的一种优选技术方案:所述无机填料选用TiO2或云母粉中的一种或多种混合物。
作为本发明的一种优选技术方案:空调机用阻燃聚丙烯的制备方法为:
第一步:按照上文所述重量分数比称取各种原料:共聚聚丙烯、均聚聚丙烯阻燃剂、聚烯烃弹性体、润滑剂、无机填料、紫外线吸收剂、光稳定剂和金属离子钝化剂。
第二步:将上述原料放入转速为200-500转/分钟的高混机中混合均匀。
第三步:将第二步混合后的物料投放到长径比为28:1的双螺杆挤出机中,挤出机温度设置:一区:160-200℃,二区170-200℃,三区170-210℃,四区180-210℃,五区180-220℃,六区180-230℃,七区180-230℃,停留2分钟。
作为本发明的一种优选技术方案:选择无规共聚聚丙烯BT310,熔点超过280℃,热变形温度超过260℃,拉伸强度>170MPa,弯曲强度>220MPa,缺口冲击强度〉16MPa,熔体粘度低,流动性好。
作为本发明的一种优选技术方案:选择的阻燃剂FR100-A热稳定性高,环保,无毒低烟,对环境不造成影响,耐寒耐侯,不易析出,可提高制品成型流动性且成本低廉。
作为本发明的一种优选技术方案:选择的聚烯烃弹性体采用POE8401,耐热性、耐寒性、耐候性、耐老化优异且价格低廉。
作为本发明的一种优选技术方案:选择的紫外线吸收剂采用UV327,能强烈吸收波长为270-380纳米的紫外线,化学性质稳定,挥发性极小,与聚烯烃相容性好。
本发明使用的所有原料均为共知的已有,使用方法和功能均为已有技术。
本发明所述一种空调机用阻燃聚丙烯采用以上技术方案与现有技术相比,具有以下技术效果:1、紫外线吸收效果好、能抑制光氧化还原或光老化、不易脆化、光泽度高和耐候效果明显;2、生产过程中无毒,无刺激性气味,低碳环保,价格低廉;3、阻燃性能优异,热稳定性高,光泽度高、磨损率低。
具体实施方式
以下通过实施例更加详细地阐述本发明的内容。
实施例1:
第一步:按照下文所述重量分数比称取各种原料
共聚聚丙烯 BT310,东莞市樟木头塑胶原料市场 52.8%;
均聚聚丙烯 T30G,辽宁华锦原料有限公司 10%;
阻燃剂 FR100-A,昆山市陆家镇仕泰隆塑料城 4%;
聚烯烃弹性体 POE(8401),东莞市塑伯橡塑胶有限公司 13%;
润滑剂 CaCO3/滑石粉,誉普化工有限公司 18%;
无机填料 TiO2(Re60),上海颜钛实业 1.5%;
紫外线吸收剂 UV-327,南京惊天为化工 0.3%;
光稳定剂 HALS,南京米兰化工 0.2%;
金属离子钝化剂 深圳正宏昌商贸有限公司 0.2%。
第二步:将上述原料放入转速为200-500转/分钟的高混机中混合均匀。
第三步:将第二步混合后的物料投放到长径比为28:1的双螺杆挤出机中,挤出机温度设置:一区:160-200℃,二区170-200℃,三区170-210℃,四区180-210℃,五区180-220℃,六区180-230℃,七区180-230℃,停留2分钟。
测试性能:
对实施例1进行韧性测试与热变形温度测试,韧性测试根据ISO180:结果见表一:
拉伸强度MPa | 弯曲强度MPa | Izod冲击强度23℃ | Izod冲击强度-20℃ | 硬度 | 热变形温度 | 500h光老化冲击强度保持率 | |
实施例1 | 34.3 | 43 | 37J/m | 27J/m | 98 | 140℃ | 100% |
表一
上述实施例只是用于对本发明的内容进行阐述,而不是限制,因此在与本发明的权利要求书相当的含义和范围内的任何改变,都应该认为是包括在权利要求书的范围内。
Claims (10)
1.一种空调机用阻燃聚丙烯及其制备方法,其特征在于:其组成成份以重量份数表示法为:
共聚聚丙烯 40-55%;
均聚聚丙烯 5-15%;
阻燃剂 2-8%;
聚烯烃弹性体 10-15%;
润滑剂 15-20%;
无机填料 1-2%;
紫外线吸收剂 0.1-0.5%;
光稳定剂 0.1-0.5%;
金属离子钝化剂 0.1-0.5%。
2.根据权利要求1所述的一种空调机用阻燃聚丙烯及其制备方法:其组成成份以重量份数表示法为:
共聚聚丙烯 52.8%;
均聚聚丙烯 10%;
阻燃剂 4%;
聚烯烃弹性体 13%;
润滑剂 18%;
无机填料 1.5%;
紫外线吸收剂 0.3%;
光稳定剂 0.2%;
金属离子钝化剂 0.2%。
3.根据权利要求1所述的一种空调机用阻燃聚丙烯及其制备方法,其特征在于:所述共聚聚丙烯为BT310SE0-100或K7926中的一种或多种混合物,熔融指数为6-30g/10min。
4.根据权利要求1所述的一种空调机用阻燃聚丙烯及其制备方法,其特征在于:所述均聚聚丙烯为C30G、T50G或T30G中的一种或多种混合物,熔融指数为10-15g/10min。
5.根据权利要求1所述的一种空调机用阻燃聚丙烯及其制备方法,其特征在于:所述阻燃剂采用FR100-A、氢氧化镁或氢氧化铝中的一种或多种混合物。
6.根据权利要求1所述的一种空调机用阻燃聚丙烯及其制备方法,其特征在于:所述聚烯烃弹性体采用POE8401或POE8411中的一种或多种混合物, 熔融指数30.0g/10 min,密度0.885g/cm。
7.根据权利要求1所述的一种空调机用阻燃聚丙烯及其制备方法,其特征在于:所述润滑剂采用滑石粉或碳酸钙中的一种或多种混合物。
8.根据权利要求1所述的一种空调机用阻燃聚丙烯及其制备方法,其特征在于:所述紫外线吸收剂选用UV-327或UV-531中的一种或多种混合物。
9.根据权利要求1所述的一种空调机用阻燃聚丙烯及其制备方法,其特征在于:所述光稳定剂采用受阻胺光稳定剂HS-944或HALS中的一种或多种混合物。
10.根据权利要求1所述的一种空调机用阻燃聚丙烯及其制备方法,其特征在于:所述无机填料选用TiO2或云母粉中的一种或多种混合物。