CN102816267B - 工程塑料用光亮润滑助剂 - Google Patents
工程塑料用光亮润滑助剂 Download PDFInfo
- Publication number
- CN102816267B CN102816267B CN201110151666.3A CN201110151666A CN102816267B CN 102816267 B CN102816267 B CN 102816267B CN 201110151666 A CN201110151666 A CN 201110151666A CN 102816267 B CN102816267 B CN 102816267B
- Authority
- CN
- China
- Prior art keywords
- auxiliary agent
- engineering plastics
- stearic acid
- brightening
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种工程塑料用光亮润滑助剂,特点是:包含的各组分及各组分的重量百分比为,硬脂酸:75%~80%;多乙烯多胺:15%~20%;抗氧剂:1%;接枝物:2%~3%;引发剂:0.1%。由此,将其用于PA6、PA66、PBT、PET玻纤增强改性工程塑料中,可以降低造料时的电流、扭距,提高材料熔融指数。对于造粒后注塑的制品,可以有效防止制品表面玻纤外露现象,提高制品表面的光泽度,对制品的机械性能影响不大,尤其对材料的韧性有一定提高。
Description
技术领域
本发明涉及一种助剂,尤其涉及一种工程塑料用光亮润滑助剂。
背景技术
在改性工程塑料中,用途最广,用量最大的是玻纤增强,阻燃增强和填充改性复合材料,如玻纤增强PA6和PA66,阻燃增强PBT,填充PP等等。这些改性工程塑料由于具有优异的力学性能、电绝缘性、耐化学腐蚀性、耐候性、易加工等诸多优点,而广泛用于汽车零部件,家电,电子,通讯,电脑等设备部件。
随着国民经济的快速发展,我国对化工新材料的需求进入高速成长期,同时对产品的质量要求也达到一个新的高度。对工程塑料的要求不仅仅是力学性能,用户更注意材料的表观性能,加工流动性,产品性能的均一性。这也正是改性工程塑料界的一大深题,如玻纤增强尼龙表面粗糙,高填充PP的光洁度差等。如何提高产品内在及外观质量,节能降耗是摆在行业面前的一个技术问题。因此,在加工过程中助剂的选择至关重要,而加快助剂产业的发展更是迫在眉睫。
发明内容
本发明的目的就是为了解决现有技术中存在的上述问题,提供一种工程塑料用光亮润滑助剂。
本发明的目的通过以下技术方案来实现:
工程塑料用光亮润滑助剂,其中:包含的各组分及各组分的重量百分比为,硬脂酸:75%~80%;多乙烯多胺:15%~20%;抗氧剂:1%;接枝物:2%~3%;引发剂:0.1%。
上述的工程塑料用光亮润滑助剂,其中:所述硬脂酸类型为C16含量大于97%的硬脂酸;或是C18含量大于97%的硬脂酸。
进一步地,上述的工程塑料用光亮润滑助剂,其中:所述的抗氧剂为四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯和三(2.4-二叔丁基苯基)亚磷酸酯的混合物。
更进一步地,上述的工程塑料用光亮润滑助剂,其中:所述的接枝物为试剂型甲基丙烯酸缩水甘油酯。
再进一步地,上述的工程塑料用光亮润滑助剂,其中:所述的引发剂为试剂型过氧化二异丙苯。
本发明技术方案的优点主要体现在:将其用于PA6、PA66、PBT、PET玻纤增强改性工程塑料中,可以降低造料时的电流、扭距,提高材料熔融指数。对于造粒后注塑的制品,可以有效防止制品表面玻纤外露现象,提高制品表面的光泽度,对制品的机械性能影响不大,尤其对材料的韧性(缺口冲击强度、断裂伸长率)有一定提高。
本发明的目的、优点和特点,将通过下面优选实施例的非限制性说明进行解释。这些实施例仅是应用本发明技术方案的典型范例,凡采取等同替换或者等效变换而形成的技术方案,均落在本发明要求保护的范围之内。
具体实施方式
〖实施例一〗
工程塑料用光亮润滑助剂,其特别之处在于:包含的各组分及各组分的重量百分比为,75%的硬脂酸,15%的多乙烯多胺,1%的抗氧剂,2%的接枝物,0.1%的引发剂。
进一步来看,为了符合常用PA66的制备,硬脂酸类型为C16含量大于97%的硬脂酸。多乙烯多胺为进口高纯度多乙烯多胺。同时,抗氧剂为四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯和三(2.4-二叔丁基苯基)亚磷酸酯的混合物。
同时,考虑到最终成型的效果,接枝物为试剂型甲基丙烯酸缩水甘油酯,引发剂为试剂型过氧化二异丙苯。
其制备过程大致如下:先将硬脂酸和1%抗氧剂加入反应釜中充分熔融的情况下,在反应釜中滴加多乙烯多胺,反应生成多元脂肪酸酰胺,然后加入接枝物和引发剂进行接枝反应冷却粉碎后得到相应产品。
再进一步结合塑料制备的过程来看,以一种增强PA66的制备为例,其由以下以重量百分比的原料组成:PA6670%,无碱玻纤30%,复合抗氧剂0.3%;本发明的工程塑料用光亮润滑助剂0.5%皆可。其中所述的PA66为河南平顶山神马集团产的PA66(FYR27),无碱玻纤为桐乡巨石集团产的988A,复合抗氧剂为上海西尼尔化工科技有限公司产的TA-1096。
上述增强PA66的制备方法为:先将PA66切片、复合抗氧剂、本发明的工程塑料用光亮润滑助剂加入高速搅拌机中,然后高速混合3分钟。将混合后的物料加入双螺杆挤出机的料斗,加热熔融后,从玻纤口加入无碱玻纤,经螺杆挤出后,拉带、冷却、切粒。
由此,采用了工程塑料用光亮润滑助剂,整个产品性能满足要求,其外观光亮,无玻纤外露,流动性好。
〖实施例二〗
工程塑料用光亮润滑助剂,其与众不同之处在于:包含的各组分及各组分的重量百分比为,80%的硬脂酸,20%的多乙烯多胺,1%的抗氧剂,3%的接枝物,0.1%的引发剂。
进一步来看,为了符合常用PBT的制备,硬脂酸类型为C18含量大于97%的硬脂酸。多乙烯多胺为进口高纯度多乙烯多胺。同时,抗氧剂为四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯和三(2.4-二叔丁基苯基)亚磷酸酯的混合物。
同时,考虑到最终成型的效果,接枝物为试剂型甲基丙烯酸缩水甘油酯,引发剂为试剂型过氧化二异丙苯。
其制备过程与实施例一类似,在此不在赘述。
采用本工程塑料用光亮润滑助剂来配合一种阻燃增强PBT的制备,其由以下以重量百分比的原料组成:PBT 55%;阻燃剂20%;无碱玻纤25%;复合抗氧剂0.3%;本发明的工程塑料用光亮润滑助剂0.6%。
其中所述的PBT为仪征化纤有限公司产的PBTL2100;阻燃剂为市售的溴系阻燃剂与三氧化二锑的复配物;无碱玻纤为桐乡巨石集团产的988A,复合抗氧剂为上海西尼尔化工科技有限公司产的TA-1136。
上述阻燃增强PBT的制备方法为:先将PBT切片、阻燃剂、复合抗氧剂、本发明的工程塑料用光亮润滑助剂加入高速搅拌机中,然后高速混合3分钟。将混合后的物料加入双螺杆挤出机的料斗,加热熔融后,从玻纤口加入无碱玻纤,经螺杆挤出后,拉带、冷却、切粒。
同样,值得的成品外观光亮,无玻纤外露,流动性好。
〖实施例三〗
工程塑料用光亮润滑助剂,其包含的各组分及各组分的重量百分比为,78%的硬脂酸,18%的多乙烯多胺,1%的抗氧剂,2.5%的接枝物,0.1%的引发剂。
进一步来看,为了符合常用塑料制品的制备,硬脂酸类型为C18含量大于97%的硬脂酸。多乙烯多胺为进口高纯度多乙烯多胺。同时,抗氧剂为四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯和三(2.4-二叔丁基苯基)亚磷酸酯的混合物。
同时,考虑到最终成型的效果,接枝物为试剂型甲基丙烯酸缩水甘油酯,引发剂为试剂型过氧化二异丙苯。
通过上述的文字表述可以看出,采用本发明后,将其用于PA6、PA66、PBT、PET玻纤增强改性工程塑料中,可以降低造料时的电流、扭距,提高材料熔融指数。对于造粒后注塑的制品,可以有效防止制品表面玻纤外露现象,提高制品表面的光泽度,对制品的机械性能影响不大,尤其对材料的韧性(缺口冲击强度、断裂伸长率)有一定提高。
Claims (1)
1.工程塑料用光亮润滑助剂,其特征在于:包含各组分及各组分的重量百分比为,硬脂酸:75%~80%;多乙烯多胺:15%~20%;抗氧剂:1%;接枝物:2%~3%;引发剂:0.1%;包含的组分的重量百分比之和为100%;
所述硬脂酸为C18含量大于97%的硬脂酸;
所述的抗氧剂为四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯和三(2,4-二叔丁基苯基)亚磷酸酯的混合物;
所述的接枝物为试剂型甲基丙烯酸缩水甘油酯;
所述的引发剂为试剂型过氧化二异丙苯。