CN102814018A - Abc干粉灭火剂生产工艺 - Google Patents

Abc干粉灭火剂生产工艺 Download PDF

Info

Publication number
CN102814018A
CN102814018A CN201110154985XA CN201110154985A CN102814018A CN 102814018 A CN102814018 A CN 102814018A CN 201110154985X A CN201110154985X A CN 201110154985XA CN 201110154985 A CN201110154985 A CN 201110154985A CN 102814018 A CN102814018 A CN 102814018A
Authority
CN
China
Prior art keywords
ammonium phosphate
silication
extinguishing agent
production technology
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201110154985XA
Other languages
English (en)
Inventor
张永安
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU WUYUE SYNTHETIC FIRE SCI-TECH Co Ltd
Original Assignee
SUZHOU WUYUE SYNTHETIC FIRE SCI-TECH Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU WUYUE SYNTHETIC FIRE SCI-TECH Co Ltd filed Critical SUZHOU WUYUE SYNTHETIC FIRE SCI-TECH Co Ltd
Priority to CN201110154985XA priority Critical patent/CN102814018A/zh
Publication of CN102814018A publication Critical patent/CN102814018A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种ABC干粉灭火剂生产工艺,通过在传统的ABC干粉灭火剂生产工艺的基础上,对加入的辅料云母粉、白炭黑和滑石粉进行个别硅化处理,待辅料单独硅化处理后,再投入混合硅化装置与原料磷酸铵一齐进行硅化,通过这一步操作,使得硅油尽可能的与原料磷酸铵接触,尽可能多的包裹在磷酸铵的外表面,以达到充分硅化的目的,硅化效果较好,同时保质期较长、粒度与灭火器能够很好匹配。

Description

ABC干粉灭火剂生产工艺
技术领域
本发明涉及一种干粉灭火剂生产工艺,具体涉及一种ABC干粉灭火剂生产工艺。
背景技术
哈龙灭火剂具有低成本、高效性的特点,但是哈龙灭火剂的主要成分是卤代烷,使用后对大气臭氧层产生严重的破坏,故停止使用,此后一直没有十分理想的替代品来用于消防灭火。
目前用的较多且效果较好的产品是消防干粉,其主要原料是磷酸铵,极易吸水而结块,不利于干粉的使用和保存。为了使干粉延长保质期、易于保存,通常通过硅化工艺来实现,即在干粉表面裹上一层硅油,以隔绝水与干粉的接触。
现有含质量分数为80%-85%磷酸铵的干粉,利用传统ABC工艺,将原料与辅料混在一起硅化,制造出的干粉灭火效果并不是很理想,且保质期也不是很长,粒度较粗或者较细,不能使干粉与灭火器很好的匹配。
因此,一种能够使制造出的干粉具有较好灭火效果、较长保质期、粒度与灭火器匹配的功能的ABC干粉灭火剂生产工艺。
发明内容
为解决上述技术问题,本发明的目的在于提供一种能够使制造出的干粉具有较好灭火效果、较长保质期、粒度与灭火器匹配的功能的ABC干粉灭火剂生产工艺。
为达到上述目的,本发明的技术方案如下:一种ABC干粉灭火剂生产工艺,所述干粉灭火剂包括质量百分含量为80%-85%的磷酸铵,所述工艺包括如下步骤:
(1)称量原料磷酸铵;
(2)将上述磷酸铵加入到粉碎机中粉碎;
(3)将上述粉碎好的原料进行分离;
(4)将分离过后的磷酸铵通入硅化设备中,加入硅油质量百分比为0.1%-1%和辅料云母、白炭黑和滑石粉,所述的辅料云母的质量百分比为3%-5%、白炭黑的质量百分比为0.5%-3%和滑石粉的质量百分比为6%-12%分别进行硅化处理,进行个别硅化后再投入硅化设备中;
(5)将硅化好的半成品进行干燥处理;
(6)再通过筛网进行过筛;
(7)包装称重得成品。
优选的,所述的筛网采用243μm筛网。
优选的,分离过程后将粗颗粒的原料重新加入粉碎机。
优选的,过筛后将粗颗粒的原料重新加入粉碎机。
通过上述技术方案,本发明技术方案的有益效果是:通过在传统的ABC干粉灭火剂生产工艺的基础上,对加入的辅料云母粉、白炭黑和滑石粉进行个别硅化处理,待辅料单独硅化处理后,再投入混合硅化装置与原料磷酸铵一齐进行硅化,通过这一步操作,使得硅油尽可能的与原料磷酸铵接触,尽可能多的包裹在磷酸铵的外表面,以达到充分硅化的目的,硅化效果较好,同时保质期较长、粒度与灭火器能够很好匹配。
附图说明
为了更清楚地说明本发明实施例技术中的技术方案,下面将对实施例技术描述中所需要使用的附图作简单地介绍,显而易见地,下面描述中的附图仅仅是本发明的一些实施例,对于本领域普通技术人员来讲,在不付出创造性劳动的前提下,还可以根据这些附图获得其他的附图。
图1为本发明一种ABC干粉灭火剂生产工艺实施例1的工艺流程图;
图2为本发明一种ABC干粉灭火剂生产工艺实施例2的工艺流程图。
具体实施方式
下面将结合本发明实施例中的附图,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
本发明提供了一种能够使制造出的干粉具有较好灭火效果、较长保质期、粒度与灭火器匹配的功能的ABC干粉灭火剂生产工艺。
实施例1,
如图1所示,一种ABC干粉灭火剂生产工艺,所述干粉灭火剂包括质量百分含量为80%的磷酸铵,所述工艺包括如下步骤:
(1)称量原料磷酸铵;
(2)将上述磷酸铵加入到粉碎机中粉碎;
(3)将上述粉碎好的原料通过分离装置进行分离;
(4)将分离过后的磷酸铵通入硅化设备中,加入硅油质量百分比为1%和辅料云母、白炭黑和滑石粉,所述的辅料云母的质量百分比为5%、白炭黑的质量百分比为3%和滑石粉的质量百分比为11%分别进行硅化处理,进行个别硅化后再投入硅化设备中。
在原料磷酸铵与辅料混合硅化过程中,首先将辅料云母粉、白炭黑和滑石粉进行单独硅化,将这三种物料充分硅化后,再投入到混合硅化装置中,与磷酸铵一起进行硅化;通过这一步工艺流程,使得混合硅化时,硅油尽可能的与磷酸铵接触、包裹在磷酸铵的表面,使之达到较好的硅化效果,从而可以很好的隔绝其与水的接触,提高了灭火效果,延长了干粉的保质期。
(5)将硅化好的半成品进行通入干燥设备进行干燥处理;
(6)将上述干燥后的物料再通过筛网进行过筛,此中所选的筛网采用243μm筛网,可以筛选出与灭火器干粉规格相符合的物料,从而使得干粉与灭火器能很好匹配。
(7)包装称重得成品。
采用实施例技术方案,通过在传统的ABC干粉灭火剂生产工艺的基础上,对加入的辅料云母粉、白炭黑和滑石粉进行个别硅化处理,待辅料单独硅化处理后,再投入混合硅化装置与原料磷酸铵一齐进行硅化,通过这一步操作,使得硅油尽可能的与原料磷酸铵接触,尽可能多的包裹在磷酸铵的外表面,以达到充分硅化的目的,硅化效果较好,同时保质期较长,一般采用的灭火器需要的粒径在0.3mm左右,通过本实施例技术方案,可以使干粉粒径与灭火器能够很好匹配。
实施例2,
如图2所示,其余与实施例1相同,不同之处在于,在上述分离过程中粒径符合条件的干粉进入下一工艺流程,否则重新加入粉碎机进行粉碎。
同样,过筛后粒径符合条件的干粉进入下一工艺流程,否则重新加入粉碎机,进行粉碎。
本实施例技术方案,不仅可以使该ABC干粉灭火剂生产工艺达到具有较好灭火效果的目的,同时使得干粉的斥水性较好,无明显吸水,不易结块,使得保质期较长,粒度与灭火器匹配度较好,还可以使原料达到充分利用的目的,节省了成本。
实施例3,
其余与上述实施例相同,不同之处在于,所述干粉灭火剂包括质量百分含量为84.4%的磷酸铵、0.1%的硅油、3%的云母、0.5%的白炭黑和12%的滑石粉。
实施例4,
其余与上述实施例相同,不同之处在于,所述干粉灭火剂包括质量百分含量为85%的磷酸铵、1%的硅油、5%的云母、3%的白炭黑和6%的滑石粉。
实施例5,
其余与上述实施例相同,不同之处在于,所述干粉灭火剂包括质量百分含量为82.5%的磷酸铵、0.5%的硅油、4.5%的云母、2.5%的白炭黑和10%的滑石粉,此为最佳方案。
通过上述技术方案,经过对产品进行检测分析,均能产生相关的有益效果,落在相同的数值范围内(具体见下表1),本发明技术方案的有益效果是:通过在传统的ABC干粉灭火剂生产工艺的基础上,对加入的辅料云母粉、白炭黑和滑石粉进行个别硅化处理,待辅料单独硅化处理后,再投入混合硅化装置与原料磷酸铵一齐进行硅化,通过这一步操作,使得硅油尽可能的与原料磷酸铵接触,尽可能多的包裹在磷酸铵的外表面,以达到充分硅化的目的,硅化效果较好,同时保质期较长、粒度与灭火器能够很好匹配。
表1:
对所公开的实施例的上述说明,使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的,本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下,在其它实施例中实现。因此,本发明将不会被限制于本文所示的这些实施例,而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。

Claims (4)

1.一种ABC干粉灭火剂生产工艺,其特征在于,所述干粉灭火剂包括质量百分含量为80%-85%的磷酸铵,所述工艺包括如下步骤:
(1)称量原料磷酸铵;
(2)将上述磷酸铵加入到粉碎机中粉碎;
(3)将上述粉碎好的原料进行分离;
(4)将分离过后的磷酸铵通入硅化设备中,加入硅油质量百分比为0.1%-1%和辅料云母、白炭黑和滑石粉,所述的辅料云母的质量百分比为3%-5%、白炭黑的质量百分比为0.5%-3%和滑石粉的质量百分比为6%-12%分别进行硅化处理,进行个别硅化后再投入硅化设备中;
(5)将硅化好的半成品进行干燥处理;
(6)再通过筛网进行过筛;
(7)包装称重得成品。
2.根据权利要求1所述的ABC干粉灭火剂生产工艺,其特征在于,所述的筛网采用243μm筛网。
3.根据权利要求2所述的ABC干粉灭火剂生产工艺,其特征在于,分离过程后将粗颗粒的原料重新加入粉碎机。
4.根据权利要求2或3所述的ABC干粉灭火剂生产工艺,其特征在于,过筛后将粗颗粒的原料重新加入粉碎机。
CN201110154985XA 2011-06-10 2011-06-10 Abc干粉灭火剂生产工艺 Pending CN102814018A (zh)