CN102807712A - Formula of modified ethylene-propylene-diene monomer (EPDM) rubber - Google Patents
Formula of modified ethylene-propylene-diene monomer (EPDM) rubber Download PDFInfo
- Publication number
- CN102807712A CN102807712A CN2012102615533A CN201210261553A CN102807712A CN 102807712 A CN102807712 A CN 102807712A CN 2012102615533 A CN2012102615533 A CN 2012102615533A CN 201210261553 A CN201210261553 A CN 201210261553A CN 102807712 A CN102807712 A CN 102807712A
- Authority
- CN
- China
- Prior art keywords
- rubber
- accounts
- serving
- prescription
- epdm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a formula of modified ethylene-propylene-diene monomer (EPDM) rubber. The modified EPDM rubber comprises EPDM rubber and additives, wherein the additives comprise tricresyl phosphate serving as a flame retardant, 2,6-butylated hydroxytoluene serving as an antioxidant, zinc oxide serving as a light stabilizer, vinyltriethoxysilane serving as a coupling agent, sulfur serving as a cross-linking agent and zinc dimethyldithiocarbamate serving as an accelerator. A high-temperature-resistant agent and a corrosion inhibitor are added into the EPDM rubber, so that a rubber pipe made of the modified EPDM rubber has high-temperature resistance, electric corrosion is slowed down, and the service life of the rubber pipe is prolonged; and an impact modifier is added, so that the mechanical properties and elasticity of the rubber pipe can be improved, and the rubber pipe is difficult to break.
Description
Technical field
The present invention relates to a kind of plastic formula, be specifically related to a kind of prescription of modified EPT rubber.
Background technology
Along with the develop rapidly of automotive industry, the improving constantly of vehicle performance, the rubber hose that automobile is used has proposed higher technical requirements, and sebific duct must stand the high temperature test more than 150 ℃ around the mover; If sizing material contains zinc, high temperature can generate insoluble precipitate with the anti-corrosion of metal additive reaction in the quench liquid down, can block the pipeline of mover, makes the temperature of car engine cooling system increasingly high.
The automobile radiators sebific duct is the flexible conduit that connects between motor car engine and the scatterer, and major function is to carry quench liquid, guarantees that engine health turns round normally.Terpolymer EP rubber is as the main raw of radiator rubber hose, and the working temperature of present domestic radiator rubber hose reaches 125 ℃, uses the terpolymer EP rubber of sulfur cross-linking can't satisfy current request for utilization.
Galvanic corrosion is meant automobile in operational process, forms potential difference between mover and the scatterer, under secular high temperature and high pressure effect, and the phenomenon that the radiator rubber hose inwall is cracked, it has a strong impact on the work-ing life of sebific duct.
Therefore, the novel tertiary ethylene-propylene rubber(EPR) material of a kind of high temperature resistant, anti-electrocorrosion, good toughness, long service life is the problem of current research.
Summary of the invention
The object of the present invention is to provide the prescription of the modified EPT rubber of a kind of high temperature resistant, anti-electrocorrosion, good toughness, long service life.
Technical scheme of the present invention is that a kind of prescription of modified EPT rubber comprises terpolymer EP rubber and additive; Described additive is high temperature resistant dose, inhibiter, static inhibitor, anti-impact modifier and coupling agent; Described high temperature resistant dose is organo-silicone rubber, and inhibiter is a coloured glaze base benzothiazole, and static inhibitor is a polyoxyethylene stearic acid ester; Anti-impact modifier is a Yodo Sol GH 28, and coupling agent is an aminopropyl triethoxysilane.
In preferred embodiment of the present invention; The weight proportion scope of each composition is that terpolymer EP rubber accounts for 81%-89% in the prescription of said modified EPT rubber; Organo-silicone rubber accounts for 3.5%-5.3%, and coloured glaze base benzothiazole accounts for 1.7%-2.9%, and polyoxyethylene stearic acid ester accounts for 1.3%-2.4%; Yodo Sol GH 28 accounts for 3.4%-5.6%, and aminopropyl triethoxysilane accounts for 1.1%-2.8%.
In preferred embodiment of the present invention; The weight proportion of each composition is that terpolymer EP rubber accounts for 85% in the prescription of said modified EPT rubber; Organo-silicone rubber accounts for 4.3%, and coloured glaze base benzothiazole accounts for 2.5%, and polyoxyethylene stearic acid ester accounts for 1.7%; Yodo Sol GH 28 accounts for 4.4%, and aminopropyl triethoxysilane accounts for 2.1%.
According to the invention is a kind of prescription of modified EPT rubber; Through in terpolymer EP rubber, adding high temperature resistant dose, inhibiter; That the sebific duct that modified EPT rubber is processed has is high temperature resistant, slow down electrocorrosion; Increase the work-ing life of sebific duct, the anti-impact modifier of interpolation can improve the mechanical property and the elasticity of sebific duct, makes not easy fracture of sebific duct.
Embodiment
Set forth in detail in the face of preferred embodiment of the present invention down, thereby protection scope of the present invention is made more explicit defining so that advantage of the present invention and characteristic can be easier to it will be appreciated by those skilled in the art that.
According to the invention is a kind of prescription of modified EPT rubber; Comprise terpolymer EP rubber and additive, described additive is high temperature resistant dose, inhibiter, static inhibitor, anti-impact modifier and coupling agent, and described high temperature resistant dose is organo-silicone rubber; Inhibiter is a coloured glaze base benzothiazole; Static inhibitor is a polyoxyethylene stearic acid ester, and anti-impact modifier is a Yodo Sol GH 28, and coupling agent is an aminopropyl triethoxysilane.
Further; The weight proportion scope of each composition is that terpolymer EP rubber accounts for 81%-89% in the prescription of said modified EPT rubber; Organo-silicone rubber accounts for 3.5%-5.3%, and coloured glaze base benzothiazole accounts for 1.7%-2.9%, and polyoxyethylene stearic acid ester accounts for 1.3%-2.4%; Yodo Sol GH 28 accounts for 3.4%-5.6%, and aminopropyl triethoxysilane accounts for 1.1%-2.8%.
Further, the weight proportion of each composition is that terpolymer EP rubber accounts for 85% in the prescription of said modified EPT rubber, and organo-silicone rubber accounts for 4.3%; Coloured glaze base benzothiazole accounts for 2.5%; Polyoxyethylene stearic acid ester accounts for 1.7%, and Yodo Sol GH 28 accounts for 4.4%, and aminopropyl triethoxysilane accounts for 2.1%.
High temperature resistant dose can make terpolymer EP rubber after processing sebific duct, have the melt temperature above 180 ℃, prevents that sebific duct is softening.
Inhibiter can effectively reduce sebific duct that terpolymer EP rubber processes by galvanic etching, increases the work-ing life of sebific duct.
Static inhibitor increases the electroconductibility of product surface, prevents that electrostatic from gathering, and is used to increase the safety performance of terpolymer EP rubber equally.
Coupling agent can improve its dispersiveness and tackiness, adds the carrying out of fast response, is used to reduce the terpolymer EP rubber synthetic reaction times, saves production cost.
According to the invention is a kind of prescription of modified EPT rubber; Through in terpolymer EP rubber, adding high temperature resistant dose, inhibiter; That the sebific duct that modified EPT rubber is processed has is high temperature resistant, slow down electrocorrosion; Increase the work-ing life of sebific duct, the anti-impact modifier of interpolation can improve the mechanical property and the elasticity of sebific duct, makes not easy fracture of sebific duct.
The above is merely embodiment of the present invention; But protection scope of the present invention is not limited thereto; Any those of ordinary skill in the art are in the technical scope that the present invention disclosed; Variation or the replacement that can expect without creative work all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (3)
1. the prescription of a modified EPT rubber; It is characterized in that: comprise terpolymer EP rubber and additive, described additive is high temperature resistant dose, inhibiter, static inhibitor, anti-impact modifier and coupling agent, and described high temperature resistant dose is organo-silicone rubber; Inhibiter is a coloured glaze base benzothiazole; Static inhibitor is a polyoxyethylene stearic acid ester, and anti-impact modifier is a Yodo Sol GH 28, and coupling agent is an aminopropyl triethoxysilane.
2. the prescription of modified EPT rubber according to claim 1; It is characterized in that: the weight proportion scope of each composition is that terpolymer EP rubber accounts for 81%-89% in the prescription of said modified EPT rubber; Organo-silicone rubber accounts for 3.5%-5.3%, and coloured glaze base benzothiazole accounts for 1.7%-2.9%, and polyoxyethylene stearic acid ester accounts for 1.3%-2.4%; Yodo Sol GH 28 accounts for 3.4%-5.6%, and aminopropyl triethoxysilane accounts for 1.1%-2.8%.
3. the prescription of modified EPT rubber according to claim 2; It is characterized in that: the weight proportion of each composition is that terpolymer EP rubber accounts for 85% in the prescription of said modified EPT rubber; Organo-silicone rubber accounts for 4.3%, and coloured glaze base benzothiazole accounts for 2.5%, and polyoxyethylene stearic acid ester accounts for 1.7%; Yodo Sol GH 28 accounts for 4.4%, and aminopropyl triethoxysilane accounts for 2.1%.