CN102795834A

CN102795834A - Pug for manufacturing Nixing pottery square pottery

Info

Publication number: CN102795834A
Application number: CN2012102945069A
Authority: CN
Inventors: 杨建军
Original assignee: Individual
Current assignee: Individual
Priority date: 2012-08-17
Filing date: 2012-08-17
Publication date: 2012-11-28

Abstract

The invention discloses pug for manufacturing Nixing pottery square pottery, which comprises the following components by weight: 9-11 parts of Nixing pottery materials, and 0.5-2.5 parts of Yixing purple clay, wherein the Nixing pottery material is 80-120 meshes, and the Yixing purple clay is 50-80 meshes. According to the invention, on the basis of the Nixing pottery material, Yixing purple clay is added into the pug, and thus the obtained pug has a large particle size, a small mesh number, a small shrinking percentage; the sintering yield of the square Nixing pottery is greatly increased; because of the arrangement characteristic of particles inside the Yixing purple clay, the air permeability, and the air permeability of the prepared pottery is improved; the pug of the invention can also be used for manufacturing pottery with other shapes.

Description

A kind of pug of making the square pottery of the emerging pottery of mud

Technical field

The present invention relates to the making field of the emerging pottery of square mud, be specifically related to a kind of pug of making the square pottery of the emerging pottery of mud.

Background technology

The emerging pottery of Qiezhou mud, (the purple mud of formal name used at school is made pottery) is with Jiangsu boccaro pottery, Yunnan Jian Shui pottery, Rongchang County, Chongqing makes pottery and claim China's " four your name pottery ".Qiezhou potting history can be traceed back to Neolithic period, and to Tang of Sui period, technology is quite ripe through 3,000 years development.Through Song, unit, bright, clear development, the emerging pottery of mud is the late Qing Dynasty Emperor XianFeng, prosperous gradually during the time ruled by Emperor Guang Xu, and the emerging pottery of mud workshop reaches family more than 40, and to the Republic of China first years of a historical period, the emerging pottery of mud has been that reputation widely spreads, and it is overseas to enjoy great prestige.After the founding of New, set up in 1956 mud start construction skill factory, set up the state-run county pottery art factory of admiring in 1958, the emerging pottery of mud gets into fast-developing period.To the end of the year 2008, the emerging pottery of mud has developed into 20 enterprises nearly, and the practitioner is the people more than 1000, more than 4,500 ten thousand yuan of annual value of production.

Though the developing history of the emerging pottery of mud is long, its shape of product limits to very much.Kind surplus the emerging pottery assortment of mud have 600, product mainly are divided into daily pottery and industrial art is made pottery two big types.Daily pottery mainly contains the electric cooker courage, stewes handleless cup, the jar of salted vegetables, water tumbler, tea set, lubricant plug, salt handleless cup, caddy and electric-heating cooking utensil etc.; Industrial art is made pottery and is mainly contained decoration vase miscellaneous, flowerpot, wall hanging, extension dish, tripodia tripod, smoked ancient cooking vessel and antique replica etc., in these kinds, square pottery is arranged seldom; Major cause is that distinct, the protrusion of square pottery corner angle is the curve rounding off unlike circular pottery; And the shrinking percentage of the emerging pottery pug of mud is big, the order number of the thin refining of particle is high; Base substrate is in sintering procedure, and edges and corners are easy to cracking, and it is low that it burns till rate; Cause production cost high, thereby the development of the emerging pottery of square mud is restricted.

Summary of the invention

Technical problem to be solved by this invention provides the pug that a kind of shrinking percentage is little, particle is big, square pottery that make burns till the high square pottery of the emerging pottery of making mud of rate.

For solving the problems of the technologies described above, the present invention adopts following technical scheme:

In weight part, its component is: 9～11 parts in the emerging pottery material of mud, 0.5～2.5 part in the purple mud in Yixing; Wherein the emerging pottery material of mud is 80～120 orders, and the purple mud in Yixing is 50～80 orders.

In the such scheme, its preferred version is that in weight part, its component is: 9.4～10 parts in the emerging pottery material of mud, 1～2 part in the purple mud in Yixing; Wherein the emerging pottery material of mud is 90～100 orders, and the purple mud in Yixing is 60～70 orders.

In the such scheme, its more preferably scheme be that in weight part, its component is: 1.5 parts in the purple mud of 9.8 parts in the emerging pottery material of mud, Yixing; Wherein the emerging pottery material of mud is 95 orders, and the purple mud in Yixing is 65 orders.

In the such scheme, the emerging pottery material of said mud can for get 5～6 parts in eastern mud with 4～5 parts of pulverize separately of western mud, mix and obtain.

Pug of the present invention has added the purple mud in Yixing on the basis of the emerging pottery material of mud, the pug particle that obtains is bigger, and the order number of pug reduces; Its shrinking percentage is less; Improved the rate of burning till of the emerging pottery of square mud greatly, and since the inner particle alignment characteristic of the purple mud in Yixing, its good permeability; The pottery ventilation property of processing also is improved, and pug of the present invention can be used to make the pottery of other shapes equally.

Compared with prior art, the present invention has the following advantages:

1, the order number of pug reduces, particle increases, and makes base substrate in sintering procedure, and shrinking percentage reduces, and the harvest rate is high;

2, owing to the adding of the purple mud in Yixing, firing temperature improves, and the color after the base substrate burning is ripe is more rich and varied, and quality is changeable more naturally;

3, be convenient to adopt the slice method of forming to make square pottery, expanded the forming method of the emerging pottery base substrate of mud, make the shape of the emerging pottery of mud present variation, satisfy various demands;

4, because the adding of the purple mud in Yixing, the emerging pottery tea set of the mud of producing, more ventilative, suitablely make tea, support kettle and play.

Embodiment

With embodiment the present invention is described further below, but the present invention is not limited to these embodiment.

Following embodiment is all in weight part.

Embodiment 1:

Get 5 parts in eastern mud, 4 parts of pulverize separately to 80 orders of western mud, mix and obtain the emerging pottery material of mud.Take by weighing 2.5 parts in the purple mud in Yixing, be crushed to 50 orders, the purple mud of the emerging pottery material of mud and Yixing is mixed promptly obtain a kind of pug of making the square pottery of the emerging pottery of mud.

Use 100 of the square teapot base substrates of the emerging pottery of mud that the pug of present embodiment makes, put into kiln and fire, wait to burn ripe, cooling back and take out, wherein 90 intact, the rate of burning till is 90%.

Embodiment 2:

Get 6 parts in eastern mud, 4 parts of pulverize separately to 90 orders of western mud, mix and obtain the emerging pottery material of mud.Take by weighing 2 parts in the purple mud in Yixing, be crushed to 60 orders, the purple mud of the emerging pottery material of mud and Yixing is mixed promptly obtain a kind of pug of making the square pottery of the emerging pottery of mud.

Use 100 of the square vase base substrates of the emerging pottery of mud that the pug of present embodiment makes, put into kiln and fire, wait to burn ripe, cooling back and take out, wherein 92 intact, the rate of burning till is 92%.

Embodiment 3:

Get 6 parts in eastern mud, 5 parts of pulverize separately to 100 orders of western mud, mix and obtain the emerging pottery material of mud.Take by weighing 0.5 part in the purple mud in Yixing, be crushed to 70 orders, the purple mud of the emerging pottery material of mud and Yixing is mixed promptly obtain a kind of pug of making the square pottery of the emerging pottery of mud.

Use 100 of the square teacup base substrates of the emerging pottery of mud that the pug of present embodiment makes, put into kiln and fire, wait to burn ripe, cooling back and take out, wherein 95 intact, the rate of burning till is 95%.

Embodiment 4:

Get 5 parts in eastern mud, 4.8 parts of pulverize separately to 95 orders of western mud, mix and obtain the emerging pottery material of mud.Take by weighing 1.5 parts in the purple mud in Yixing, be crushed to 65 orders, the purple mud of the emerging pottery material of mud and Yixing is mixed promptly obtain a kind of pug of making the square pottery of the emerging pottery of mud.

Use 100 of the square tripod base substrates of the emerging pottery of mud that the pug of present embodiment makes, put into kiln and fire, wait to burn ripe, cooling back and take out, wherein 89 intact, the rate of burning till is 89%.

Embodiment 5:

Get 5 parts in eastern mud, 4.4 parts of pulverize separately to 120 orders of western mud, mix and obtain the emerging pottery material of mud.Take by weighing 1 part in the purple mud in Yixing, be crushed to 80 orders, the purple mud of the emerging pottery material of mud and Yixing is mixed promptly obtain a kind of pug of making the square pottery of the emerging pottery of mud.

Use 100 of the square flowerpot base substrates of the emerging pottery of mud that the pug of present embodiment makes, put into kiln and fire, wait to burn ripe, cooling back and take out, wherein 90 intact, the rate of burning till is 90%.

Claims

1. pug of making the square pottery of the emerging pottery of mud, it is characterized in that: in weight part, its component is: 9～11 parts in the emerging pottery material of mud, 0.5～2.5 part in the purple mud in Yixing; Wherein the emerging pottery material of mud is 80～120 orders, and the purple mud in Yixing is 50～80 orders.

2. a kind of pug of making the square pottery of the emerging pottery of mud according to claim 1, it is characterized in that: in weight part, its component is: 9.4～10 parts in the emerging pottery material of mud, 1～2 part in the purple mud in Yixing; Wherein the emerging pottery material of mud is 90～100 orders, and the purple mud in Yixing is 60～70 orders.

3. a kind of pug of making the square pottery of the emerging pottery of mud according to claim 2, it is characterized in that: in weight part, its component is: 9.8 parts in the emerging pottery material of mud, 1.5 parts in the purple mud in Yixing; Wherein the emerging pottery material of mud is 95 orders, and the purple mud in Yixing is 65 orders.

4. according to any described a kind of pug of making the square pottery of the emerging pottery of mud of claim 1～3, it is characterized in that: the emerging pottery material of said mud for get 5～6 parts in eastern mud with 4～5 parts of pulverize separately of western mud, mix and obtain.