CN102787208A - 一种炼钢用纯钙包芯线 - Google Patents
一种炼钢用纯钙包芯线 Download PDFInfo
- Publication number
- CN102787208A CN102787208A CN2012103054269A CN201210305426A CN102787208A CN 102787208 A CN102787208 A CN 102787208A CN 2012103054269 A CN2012103054269 A CN 2012103054269A CN 201210305426 A CN201210305426 A CN 201210305426A CN 102787208 A CN102787208 A CN 102787208A
- Authority
- CN
- China
- Prior art keywords
- calcium
- pure calcium
- cored wire
- steel
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种炼钢用纯钙包芯线，属于包芯线，其结构包括外包覆层和包覆在外包覆层内的包覆芯体，所述的外包覆层表面设置有立棱，所述的立棱垂直于外包覆层圆截面切线，所述的外包覆层厚度为0.75～2.0mm。与现有技术相比，本发明的一种炼钢用纯钙包芯线具有穿透钢渣的穿透能力大大增加，可以减小纯钙包芯线穿渣后的变形量，使其能更好的到达钢包底部，增加了金属钙条被钢水吸收时间，减少钙气泡的形成，可明显减少钙在钢水表面的喷溅，从而提高钙的收得率等特点，因而具有很好的推广应用价值。
Description
技术领域
本发明涉及一种包芯线，尤其是一种钢铁企业炉外精炼过程中使用的高强度、高收得率炼钢用纯钙包芯线。
背景技术
包芯线技术当今已成为炼钢工业上一种不可缺少的精炼手段，它对钢液的微调、合金化、脱氧、去除夹杂物等有着独特的作用，并具有投资少、工艺简单等优势。积极开发各种炉外精炼新工艺，已经是世界炼钢技术发展的总趋势和技术主攻目标。
钢的合金化、元素的微调、夹杂物的去除和变态，钢中气体的去除等提高钢纯洁度和钢质量的任务，大都依靠炉外精炼(钢包冶金)来完成。
目前金属冶炼过程中所使用的挝边式纯钙包芯线所用的包覆层厚度为0.45mm～0.60mm，此类纯钙包芯线在使用过程中，由于外包覆层厚度较薄，在喂入钢水过程中，透渣能力较弱，易造成纯钙包芯线打弯，同时外包覆层厚度较薄易熔化，不能更好的插入到钢水包底部，造成内包覆的金属钙条只能在钢水中上部反应，很容易形成钙气泡上浮到钢渣表面，金属钙的收得率仅有7～15%左右，造成金属钙的浪费。同时还存在对环境污染大，喷溅严重，易烫伤操作人员等缺点。目前，还未有好的解决方案。
发明内容
本发明的技术任务是针对上述现有技术中的不足提供一种炼钢用纯钙包芯线，该一种炼钢用纯钙包芯线具有穿透钢渣的穿透能力大大增加，可以减小纯钙包芯线穿渣后的变形量，使其能更好的到达钢包底部，增加了金属钙条被钢水吸收时间，减少钙气泡的形成，可明显减少钙在钢水表面的喷溅，从而提高钙的收得率的特点。
本发明解决其技术问题所采用的技术方案是：它包括外包覆层和包覆在外包覆层内的包覆芯体，所述的外包覆层表面设置有立棱，所述的立棱垂直于外包覆层圆截面切线，所述的外包覆层厚度为0.75～2.0mm。
所述的外包覆层为SPCC级别以上冷轧钢带，厚度为1.2mm。
所述的立棱的厚度为3.6mm。
所述的包覆芯体为实芯金属钙条。
所述的包覆芯体的直径为6.6mm。
本发明的一种炼钢用纯钙包芯线和现有技术相比，具有以下突出的有益效果：设置有垂直立棱和外包覆较厚的钢带，大大提高了包覆芯体的强度，其穿透钢渣的穿透能力大大增加，可以减小纯钙包芯线穿渣后的变形量，使其能更好的到达钢包底部，增加了金属钙条被钢水吸收时间，减少钙气泡的形成，可明显减少钙在钢水表面的喷溅，从而提高钙的收得率，不会污染环境，不会烫伤操作人员，该包覆芯体的平均收得率是现有包芯线平均收得率的3倍以上，收得率可达到40%～60%等特点。
附图说明
附图1是一种炼钢用纯钙包芯线的截面结构示意图；
附图标记说明：1、外包覆层，2、包覆芯体，3、立棱。
具体实施方式
参照说明书附图1对本发明的一种炼钢用纯钙包芯线作以下详细地说明。
本发明的一种炼钢用纯钙包芯线，其结构包括外包覆层1和包覆在外包覆层1内的包覆芯体2，所述的外包覆层1表面设置有立棱3，所述的立棱3垂直于外包覆层1圆截面切线，所述的外包覆层1厚度为0.75～2.0mm。
所述的外包覆层1为SPCC级别以上冷轧钢带，厚度为1.2mm。
所述的立棱3的厚度为3.6mm。
所述的包覆芯体2为实芯金属钙条，纯度≥97%。
所述的包覆芯体2的直径为6.6mm。
通过包芯线机各组压辊的挝边、卷曲、压制定型后，将厚度为1.2mm的外包覆层1紧密的包覆在直径为6.6mm的包覆芯体2外，同时在外包覆层1外形成一厚度为3.6mm的加强筋立棱3，该立棱3垂直于外包覆层1圆截面切线。将该纯钙包芯线喂到钢水包底部，由于存在立棱3，增加其穿透钢渣的穿透能力，可以减小纯钙包芯线穿渣后的变形量，使纯钙包芯线能更好的到达钢包底部，使内包覆的金属钙条在钢包底部能充分反应，在钢水表面几乎没有喷溅，钙收得率达52%。
除说明书所述的技术特征外，均为本专业技术人员的已知技术。
Claims (5)
1.一种炼钢用纯钙包芯线，包括外包覆层和包覆在外包覆层内的包覆芯体，其特征是：所述的外包覆层表面设置有立棱，所述的立棱垂直于外包覆层圆截面切线，所述的外包覆层厚度为0.75～2.0mm。
2.根据权利要求1所述的一种炼钢用纯钙包芯线，其特征是：所述的外包覆层为SPCC级别以上冷轧钢带，厚度为1.2mm。
3.根据权利要求1所述的一种炼钢用纯钙包芯线，其特征是：所述的立棱的厚度为3.6mm。
4.根据权利要求1所述的一种炼钢用纯钙包芯线，其特征是：所述的包覆芯体为实芯金属钙条。
5.根据权利要求1所述的一种炼钢用纯钙包芯线，其特征是：所述的包覆芯体的直径为6.6mm。