CN102776788A - Production technology for single-hydrophilic single-resistant double-layer cloth coloring yarn dyed fabric - Google Patents
Production technology for single-hydrophilic single-resistant double-layer cloth coloring yarn dyed fabric Download PDFInfo
- Publication number
- CN102776788A CN102776788A CN2012102903812A CN201210290381A CN102776788A CN 102776788 A CN102776788 A CN 102776788A CN 2012102903812 A CN2012102903812 A CN 2012102903812A CN 201210290381 A CN201210290381 A CN 201210290381A CN 102776788 A CN102776788 A CN 102776788A
- Authority
- CN
- China
- Prior art keywords
- production technology
- speed
- controlled
- heated
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production technology for single-hydrophilic single-resistant double-layer cloth coloring yarn dyed fabric. The production technology comprises the technical steps as follows: pre-processing-> dyeing->finishing yarns at an external layer through a water proofing and oil proofing way-> singeing at the first time-> warping-> sizing-> weaving-> overhauling greige cloth-> singeing at the second time-> desizing-> absorbing wet, quickly drying and arranging-> parching, wherein the process of finishing yarns at an external layer through a water proofing and oil proofing way comprises: (1) feeding materials, wherein 50 to 80 g/L of nanometer waterproof oil-proof finishing agent, 10 to 40 g/L of smoothing agent, and 5 to 30 g/L of film are fed; (2) adjusting acidity, wherein pH is adjusted to 4.0 to 4.5 through 10% of glacial acetic acid; (3) dewatering, wherein the liquid containing rate is controlled to about 65%; (4) parching in a rotating cage, wherein the temperature is controlled to 80 to 90 DEG C, and the wet content is controlled to 10% after parching; and (5) parching for 1 to 5 minutes at temperature controlled to 160 DEG C. With the production technology, the fabric has the characteristics of water proofing and oil proofing performances; the process of sizing the yarns at the external layer is reduced; and the comfortable level of the fabric being worn is improved as well.
Description
Technical field
The present invention relates to the color-woven fabric production technology, be meant the singly anti-layer cloth color-woven fabric production technology of a kind of single parent especially.
Background technology
Along with the progress of expanding economy with society, the textiles with single performance can not satisfy people's life requirement and to the polyfunctional requirement of product.Traditional pure cotton fabric, because the existence of hydroxyl, wettability power is stronger, but the wet ability of loosing causes a kind of cold wet sense to the people, has destroyed the comfortableness of pure cotton fabric to a great extent.At present, a lot of research institutions and producer be at single parent's list prevention fabric, in the present production process of this kind lining; The general mode of coating that adopts gives fabric waterproof grease proofing effect; Though the lining that this mode is produced to a certain extent can waterproof and oilproof, greatly influenced the feel of fabric, and also variation of gas permeability; Wear more uncomfortable, the washing several times the back waterproof oil-proof result reduce significantly.
Summary of the invention
Technical problem to be solved by this invention is: a kind of single parent is provided singly anti-layer cloth color-woven fabric production technology; This production technology is both being given lining waterproof and oilproof characteristic; Improved the lining wearing comfortableness again, satisfied the consumer garment material comfortableness and functional requirement.
For solving the problems of the technologies described above; Technical scheme of the present invention is: the singly anti-layer cloth color-woven fabric production technology of single parent; Comprising following processing step: the waterproof oil-proof finishing of pre-treatment → dyeing → outer layer fiber → once singe → warping → sizing → weave → grey cloth maintenance → secondary singes → and destarch → hydroscopic fast-drying puts in order → bakes; Wherein, the waterproof oil-proof finishing operation comprises
(1) reinforced, add nano waterproof oil-proof finishing agent 50～80g/L, smooth agent 10～40g/L, film 5～30g/L;
(2) acidity adjustment is regulated the pH value 4.0～4.5 with 10% glacial acetic acid;
(3) dehydration is controlled at about 65% liquid carrying rate;
(4) rotating cage oven dry, temperature is controlled at 80～90 ℃, and oven dry back water capacity is controlled at about 10%;
(5) bake, 160 ℃ of control temperature bake 1～5min.
As a kind of preferred scheme, said hydroscopic fast-drying arranging process comprises
(1) lining is padded the moisture absorbing and sweat releasing agent at 40～60g/L with the speed of 40m/min;
(2) with 100 ℃ of hot-air seasonings;
(3) the control temperature is 160 ℃, bakes 2min.
As a kind of preferred scheme, secondary is singed and is light-burned hair, with coal gas as thermal source, the speed of a motor vehicle 150～200m/min, 900 ℃～1000 ℃ of temperature.
As a kind of preferred scheme, said pretreatment procedure may further comprise the steps:
(1). boiling-off: outer layer fiber yarn and inner fiber yarn are in the treatment fluid of 5g/L in complex enzyme concentration all, handle 40min down for 100 ℃.
(2). the oxidant bleach step: under the normal temperature, outer layer fiber yarn and inner fiber yarn are all adding 3～5g/L Na
2CO3 solution, 0.2～0.5ml/L bleeding agent, 0.1～0.2ml/L stabilizing agent, bath raio 1:20 heating is heated to 90 ℃ with the speed of 4 ℃/min, adds 30%H
2O
28～10ml/L is heated to 95 ℃ with the speed of 2 ℃/min, boil float 15～30min after, be cooled to 65 ℃, discharge opeing with the speed of 2 ℃/min; 2% acetum cold wash twice is heated to 80 ℃, and pickling stops 5～10min, is cooled to 40 ℃, twice of cold wash with the speed of 2 ℃/min;
(3). reductant blanching step: under 40 ℃, add 5～6g/L soap powder, be heated to 95 ℃, add 4～6g/L sodium hydrosulfite, be heated to 98 ℃, stop 20min, discharge opeing; Be cooled to 80 ℃, washing stops 10min, discharge opeing; Be cooled to 50 ℃, the neutralization of 2% acetum stops 10min, cold wash, discharge opeing.
After having adopted technique scheme, effect of the present invention is: in the waterproof oil-proof finishing operation, add smooth agent and film simultaneously; Give the grease proofing characteristic of waterproof outer of lining, improved the smooth degree of yarn, increased the fabric wearing comfortableness; Fabric is difficult for staining; Be easy to arrange, promote tenacity of yarn simultaneously, the problem that has existed when effectively having avoided simple employing coating way to increase lining waterproof and oilproof characteristic.The lining internal layer improves the speed of internal layer fabric moisture absorption through the hydroscopic fast-drying arranging process, the sweat of skin surface is washed fabric face with speed scatter and disappear, and keeps the dry and comfortable sense of touch of fabric.
Secondary is singed and is light-burned hair, with coal gas as thermal source, the speed of a motor vehicle 150～200m/min, 900 ℃～1000 ℃ of temperature, the speed of a motor vehicle that secondary is singed is very fast, reduces the influence of gasser's ordered pair fiber strength and apparent property.
The specific embodiment
Through specific embodiment the singly anti-layer cloth color-woven fabric production technology of single parent of the present invention is done further to describe in detail below.
Embodiment 1
The singly anti-layer cloth color-woven fabric production technology of single parent; Comprising following processing step: the waterproof oil-proof finishing of pre-treatment → dyeing → outer yarn → once singe → warping → sizing → weave → grey cloth maintenance → secondary singes → and destarch → hydroscopic fast-drying puts in order → bakes; Wherein, Said pre-treatment may further comprise the steps (1). and boiling-off: outer layer fiber yarn and inner fiber yarn are in the treatment fluid of 5g/L in complex enzyme concentration all; Handle 40min down, can remove impurity and grease in the fiber yarn for 100 ℃;
(2). the oxidant bleach step: under the normal temperature, outer layer fiber yarn and inner fiber yarn are all adding 3g/L Na
2CO
3Solution, 0.2ml/L bleeding agent, 0.1ml/L stabilizing agent, bath raio 1:20 heating is heated to 90 ℃ with the speed of 4 ℃/min, adds 30%H
2O
28ml/L is heated to 95 ℃ with the speed of 2 ℃/min, boil float 30min after, be cooled to 65 ℃, discharge opeing with the speed of 2 ℃/min; 2% acetum cold wash twice is heated to 80 ℃, and pickling stops 10min, is cooled to 40 ℃, twice of cold wash with the speed of 2 ℃/min;
(3). reductant blanching step: under 40 ℃, add the 5g/L soap powder, be heated to 95 ℃, add the 4g/L sodium hydrosulfite, be heated to 98 ℃, stop 20min, discharge opeing; Be cooled to 80 ℃, washing stops 10min, discharge opeing; Be cooled to 50 ℃, the neutralization of 2% acetum stops 10min, cold wash, discharge opeing.
Above-mentioned pre-treatment is bleached fabric lining, and yarn is guaranteeing that whiteness significantly improves under the powerful prerequisite, improves the power that is coloured in road, back simultaneously.
Wherein the waterproof oil-proof finishing operation comprises
(1) reinforced, add nano waterproof oil-proof finishing agent 50g/L, smooth agent 20g/L, film 20g/L;
(2) acidity adjustment is regulated the pH value 4.0～4.5 with 10% glacial acetic acid;
(3) dehydration is controlled at about 65% liquid carrying rate;
(4) rotating cage oven dry, temperature is controlled at 80～90 ℃, and oven dry back water capacity is controlled at about 10%;
(5) bake, 160 ℃ of control temperature bake 2min.
The hydroscopic fast-drying arranging process comprises
(1) lining is padded the moisture absorbing and sweat releasing agent at 50g/L with the speed of 40m/min;
(2) with 100 ℃ of hot-air seasonings;
(3) the control temperature is 160 ℃, bakes 2min.
Secondary is singed and is light-burned hair, with coal gas as thermal source, speed of a motor vehicle 150m/min, 900 ℃ of temperature.
In the above-mentioned technology; After after the dyeing outer layer fiber being carried out waterproof oil-proof finishing, outer layer fiber has had the function of waterproof and oilproof, outer layer fiber not starching basically during sizing; And normally starching of bottom fiber; When then after destarch, carrying out the hydroscopic fast-drying arrangement,, so whole fabric is carried out the hydroscopic fast-drying arrangement and in fact also just bottom fiber is carried out the hydroscopic fast-drying arrangement because outer layer fiber has possessed the waterproof and oilproof function; The function and the effect of the moisture absorption of bottom fiber like this, have just further been improved.
Embodiment 2
The singly anti-layer cloth color-woven fabric production technology of single parent, the waterproof oil-proof finishing of pre-treatment → dyeing → outer layer fiber → once singe → warping → sizing → weave → grey cloth maintenance → secondary singe → and destarch → hydroscopic fast-drying puts in order → bakes, wherein,
Said pre-treatment may further comprise the steps (1). and boiling-off: outer layer fiber yarn and inner fiber yarn are in the treatment fluid of 5g/L in complex enzyme concentration all, handle 40min down, can remove impurity and grease in the fiber yarn for 100 ℃;
(2). the oxidant bleach step: under the normal temperature, outer layer fiber yarn and inner fiber yarn are all adding 5g/L Na
2CO
3Solution, 0.5ml/L bleeding agent, 0.2ml/L stabilizing agent, bath raio 1:20 heating is heated to 90 ℃ with the speed of 4 ℃/min, adds 30%H
2O
210ml/L is heated to 95 ℃ with the speed of 2 ℃/min, boil float 15min after, be cooled to 65 ℃, discharge opeing with the speed of 2 ℃/min; 2% acetum cold wash twice is heated to 80 ℃, and pickling stops 5min, is cooled to 40 ℃, twice of cold wash with the speed of 2 ℃/min;
(3). reductant blanching step: under 40 ℃, add the 6g/L soap powder, be heated to 95 ℃, add the 6g/L sodium hydrosulfite, be heated to 98 ℃, stop 20min, discharge opeing; Be cooled to 80 ℃, washing stops 10min, discharge opeing; Be cooled to 50 ℃, the neutralization of 2% acetum stops 10min, cold wash, discharge opeing.
The waterproof oil-proof finishing operation comprises
(1) reinforced, add nano waterproof oil-proof finishing agent 80g/L, smooth agent 10g/L, film 30g/L;
(2) acidity adjustment is regulated the pH value 4～4.5 with 10% glacial acetic acid;
(3) dehydration makes liquid carrying rate be controlled at 65%;
(4) rotating cage oven dry, temperature is controlled at 80～90 ℃, and oven dry back water capacity is controlled at about 10%;
(5) bake, 160 ℃ of control temperature bake 2min.
The hydroscopic fast-drying arranging process comprises
(1) lining is padded the moisture absorbing and sweat releasing agent at 60g/L with the speed of 40m/min;
(2) with 100 ℃ of hot-air seasonings;
(3) the control temperature is 160 ℃, bakes 2min.
Secondary is singed and is light-burned hair, with coal gas as thermal source, speed of a motor vehicle 200m/min, 1000 ℃ of temperature.
Embodiment 3
The singly anti-layer cloth color-woven fabric production technology of single parent, the waterproof oil-proof finishing of pre-treatment → dyeing → outer layer fiber → once singe → warping → sizing → weave → grey cloth maintenance → secondary singe → and destarch → hydroscopic fast-drying puts in order → bakes, wherein,
Said pre-treatment may further comprise the steps (1). and boiling-off: outer layer fiber yarn and inner fiber yarn are in the treatment fluid of 5g/L in complex enzyme concentration all, handle 40min down, can remove impurity and grease in the fiber yarn for 100 ℃;
(2). the oxidant bleach step: under the normal temperature, outer layer fiber yarn and inner fiber yarn are all adding 4g/L Na
2CO
3Solution, 0.3ml/L bleeding agent, 0.15ml/L stabilizing agent, bath raio 1:20 heating is heated to 90 ℃ with the speed of 4 ℃/min, adds 30%H
2O
29ml/L is heated to 95 ℃ with the speed of 2 ℃/min, boil float 20min after, be cooled to 65 ℃, discharge opeing with the speed of 2 ℃/min; 2% acetum cold wash twice is heated to 80 ℃, and pickling stops 7min, is cooled to 40 ℃, twice of cold wash with the speed of 2 ℃/min;
(3). reductant blanching step: under 40 ℃, add the 5.5g/L soap powder, be heated to 95 ℃, add the 5g/L sodium hydrosulfite, be heated to 98 ℃, stop 20min, discharge opeing; Be cooled to 80 ℃, washing stops 10min, discharge opeing; Be cooled to 50 ℃, the neutralization of 2% acetum stops 10min, cold wash, discharge opeing.
The waterproof oil-proof finishing operation comprises
(1) reinforced, add nano waterproof oil-proof finishing agent 60g/L, smooth agent 40g/L, film 5g/L;
(2) acidity adjustment is regulated the pH value 4.5 with 10% glacial acetic acid;
(3) dehydration makes liquid carrying rate be controlled at 65%;
(4) rotating cage oven dry, temperature is controlled at 80～90 ℃, and oven dry back water capacity is controlled at about 10%;
(5) bake, 160 ℃ of control temperature bake 2min.
The hydroscopic fast-drying arranging process comprises
(1) lining is padded the moisture absorbing and sweat releasing agent at 40g/L with the speed of 40m/min;
(2) with 100 ℃ of hot-air seasonings;
(3) the control temperature is 160 ℃, bakes 2min.
Secondary is singed and is light-burned hair, with coal gas as thermal source, speed of a motor vehicle 180m/min, 950 ℃ of temperature.
Singly anti-each technical indicator of color-woven fabric of the single parent that following table is produced for embodiment 1,2 and 3.
Claims (4)
1. the single parent singly prevents layer cloth color-woven fabric production technology; It is characterized in that: comprise following processing step: the waterproof oil-proof finishing of pre-treatment → dyeing → outer yarn → once singe → warping → sizing → weave → grey cloth maintenance → secondary singes → and destarch → hydroscopic fast-drying puts in order → bakes, and wherein the waterproof oil-proof finishing operation of outer yarn comprises
(1) reinforced, add nano waterproof oil-proof finishing agent 50～80g/L, smooth agent 10～40g/L, film 5～30g/L;
(2) acidity adjustment is regulated the pH value 4.0～4.5 with 10% glacial acetic acid;
(3) dehydration makes liquid carrying rate be controlled at 60～70%;
(4) rotating cage oven dry, temperature is controlled at 80～90 ℃, and oven dry back water capacity is controlled at 10%;
(5) bake, 160 ℃ of control temperature bake 1～5min.
2. the single parent singly prevents layer cloth color-woven fabric production technology according to claim 1, and it is characterized in that: said hydroscopic fast-drying arranging process comprises
(1) lining is padded in the treatment fluid of the moisture absorbing and sweat releasing agent that contains 40～60g/L with the speed of 40m/min;
(2) with 100 ℃ of hot-air seasonings;
(3) the control temperature is 160 ℃, bakes 2min.
3. like the singly anti-layer cloth color-woven fabric production technology of the said single parent of claim 2, it is characterized in that: it is light-burned hair that secondary is singed, with coal gas as thermal source, the speed of a motor vehicle 150～200m/min, 900 ℃～1000 ℃ of temperature.
4. like the singly anti-layer cloth color-woven fabric production technology of the said single parent of claim 3, it is characterized in that: said pretreatment procedure may further comprise the steps:
(1). boiling-off: outer layer fiber yarn and inner fiber yarn are in the treatment fluid of 5g/L in complex enzyme concentration all, handle 40min down for 100 ℃.
(2). the oxidant bleach step: under the normal temperature, outer layer fiber yarn and inner fiber yarn are all adding 3～5g/L Na
2CO
3Solution, 0.2～0.5ml/L bleeding agent, 0.1～0.2ml/L stabilizing agent, bath raio 1:20 heating is heated to 90 ℃ with the speed of 4 ℃/min, adds 30%H
2O
28～10ml/L is heated to 95 ℃ with the speed of 2 ℃/min, boil float 15～30min after, be cooled to 65 ℃, discharge opeing with the speed of 2 ℃/min; 2% acetum cold wash twice is heated to 80 ℃, and pickling stops 5～10min, is cooled to 40 ℃, twice of cold wash with the speed of 2 ℃/min;
(3). reductant blanching step: under 40 ℃, add 5～6g/L soap powder, be heated to 95 ℃, add 4～6g/L sodium hydrosulfite, be heated to 98 ℃, stop 20min, discharge opeing; Be cooled to 80 ℃, washing stops 10min, discharge opeing; Be cooled to 50 ℃, the neutralization of 2% acetum stops 10min, cold wash, discharge opeing.