CN102775955A - Environment-friendly solvent spraying glue and preparation method thereof - Google Patents
Environment-friendly solvent spraying glue and preparation method thereof Download PDFInfo
- Publication number
- CN102775955A CN102775955A CN2011101209542A CN201110120954A CN102775955A CN 102775955 A CN102775955 A CN 102775955A CN 2011101209542 A CN2011101209542 A CN 2011101209542A CN 201110120954 A CN201110120954 A CN 201110120954A CN 102775955 A CN102775955 A CN 102775955A
- Authority
- CN
- China
- Prior art keywords
- environment
- spray glue
- butadiene rubber
- agent
- friendly solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly solvent spraying glue and a preparation method thereof. The best weight ratio of the spraying glue is 7% of starburst SBS thermoplastic styrene-butadiene rubber, 1% of linear SBS thermoplastic styrene-butadiene rubber, 8% of rosin, 9.5% of hydrogenated rosin, 4% of C9 petroleum resin, 6% of a tackifying resin, 12% of No. 6 extraction solvent oil, 35% of methylal, 15% of methyl acetate, 0.2% of a wetting agent, 0.8% of an anti-aging agent, 0.5% of an antioxidant and 1.0% of a softening agent. The environment-friendly solvent spraying glue has the comprehensive superiorities of low VOC, high solid content, no heavy metals, low smell, excellent initial adhesion, excellent cohesive strength, excellent permanent adhesion, excellent heat-resistant and ageing-resistant performance, short drying time, long opening time, large spraying area per weight (glue economization), and the like, has the advantages of reducing environment pollution, improving operation and construction environment, being low cost and low smell, and the like, is widely used in software furniture industries of cases, sofas, swivel chairs, mattresses, pillows, screens, and the like, and is particularly suitable for applications in green high-grade export products of Europe and America.
Description
Technical field
The present invention relates to a kind of tackiness agent and preparation method thereof, more particularly relate to solvent-borne type spray glue of a kind of environmental protection and preparation method thereof.
Background technology
Spray glue is a kind of suitable viscosity that has, and is suitable for spray gun as the service tool spraying application, and two kinds of different material interfaces are closely coupled together, and plays the tackiness agent of delivery applications effect; Spraying application often more can reach than traditional brushing form of construction work save time, laborsaving, economize effects such as glue, synergy; Play a multiplier effect, spray glue has been widely used in bonding between the materials such as pachydermia, corium, imitation leather, regenerated bark, sponge, cloth, timber, metal, stone material, footwear material at present.Spray glue comprises solvent-borne type spray glue (oiliness spray glue) and water-soluble spraying glue; Chinese market still is applied as the master with low and middle-end solvent-borne type spray glue at present; A large amount of organic solvents comprise that deleterious halohydrocarbon and triphen (benzene,toluene,xylene) solvent get in the air when construction; Both consume the petroleum oil resource that is becoming tight a large amount of days, had a strong impact on people's lives environment and healthy again.
Although country rises on September 1st, 2009 and comes into effect standard GB 18583-2008 (the mandatory limit standard of objectionable impurities in the indoor decorating adhesive); But it is still too loose for limiting the quantity of of triphen and halohydrocarbon; For example: toluene+YLENE≤15%; Low toxicity halohydrocarbon methylene dichloride≤5%, for the high standard requirement of environmental protection, GB 18583-2008 GB is far from being enough according to American-European-Japanese western developed country that waits.At present, national environmental protection department and GB Committee have put into effect more strict environmental protection standard, and tackiness agent environmental labelling product authentication techniques require standard HJ/T 220-2005; Emphasis is to have done more strict limiting the quantity of for triphen, halohydrocarbon, acetone etc., for example: purified petroleum benzin≤0.2%, toluene+YLENE≤0.2%; Halohydrocarbon≤0.2%; Acetone≤0.75 ‰, heavy metal (lead, cadmium, mercury, chromium)≤0.5 ‰ etc., therefore; The solvent-borne type spray glue that satisfies the environmental labelling product standard does not still satisfy the adhesive products of high environmental protection standard of China at present, and can satisfy the high standard requirement of western developed country such as American-European-Japanese for environmental protection.
And traditional solvent-borne type spray glue is owing to used more poisonous organic solvent; On the environmental protection index, only can satisfy common standard such as GB GB 18583-2001; Still be difficult to satisfy high environmental protection standard such as Chinese environmental sign Valuation Standard HJ/T 220-2005, IKEA standard etc.; And at application performance such as initial bonding strength, hold aspects such as viscous force, heat-resisting ageing-resisting performance, open hour and also need optimize lifting, could satisfy the high-end market needs, in addition; Tradition spray glue industry too much depends on petroleum resources, and raw materials cost receives the influence of oil rising trend deeply.
Summary of the invention
The technical problem that the present invention will solve is exactly: overcome the above-mentioned defective that traditional solvent-borne type spray glue (oiliness spray glue) exists; Provide a kind of and make medium with the environmental protection mixed organic solvents that does not rely on oil basically; Composite having modification viton, tackifying resin, the environmental protection auxiliary agent of excellent dissolution performance with the environmental protection mixed organic solvents, so develop low VOC, high solids content, do not contain heavy metal, low flavor, have good initial bonding strength, cohesive strength excellent, hold that viscous force is excellent, heat-resisting ageing-resisting is excellent, time of drying is short, the open hour are long, the spray area of unit weight greatly the environment-friendly solvent type of (province's glue) spray glue.
Another technical problem that the present invention will solve provides a kind of preparation method of environment-friendly solvent type spray glue.
The technical scheme that solves the problems of the technologies described above employing is such.
Environment-friendly solvent type spray glue of the present invention comprises following component in percentage by weight:
SBS thermoplastic styrene butadiene rubber 5 ~ 15%
Rosin 5 ~ 10%
Staybelite 5 ~ 10%
C 9 petroleum resin 2 ~ 6%
Tackifying resin 2 ~ 6%
6# solvent oil 10 ~ 20%
Methylal 25 ~ 40%
Ritalin 10 ~ 20%.
Preferred scheme is that said spray glue also comprises following component in percentage by weight:
Anti-aging agent 0.5 ~ 1.0%
Oxidation inhibitor 0.3 ~ 0.6%
Wetting agent 0.1 ~ 0.2%
Softening agent 0.5 ~ 1.5%.
Comprise two types of hub-and-spoke configuration and linear structures in the said SBS thermoplastic styrene butadiene rubber, the weight percent that the star-shaped sbs thermoplastic styrene butadiene rubber accounts for said spray glue is 4 ~ 12%, and the weight percent that said type SBS thermoplastic styrene butadiene rubber accounts for spray glue is 1 ~ 3%.
The weight proportion of said environment-friendly solvent type spray glue can be star-shaped sbs thermoplastic styrene butadiene rubber 7%, type SBS thermoplastic styrene butadiene rubber 1%, rosin 8%, staybelite 9.5%, C 9 petroleum resin 4%, tackifying resin 6%, 6# solvent for extraction 12%, methylal 35%, ritalin 15%, wetting agent 0.2%, anti-aging agent 0.8%, oxidation inhibitor 0.5%, softening agent 1.0%.
Described rosin, staybelite all are select qualities, and softening temperature is higher than 76 ℃; Described C 9 petroleum resin belongs to industrial first grade, and softening temperature is 120 ℃; Described tackifying resin is Abietyl modified pentaerythritol ester, is industrial first grade, and softening temperature is 145 ℃.
Said anti-aging agent is selected the OPPD anti-aging agent for use; Oxidation inhibitor is selected 1010 oxidation inhibitor for use; Wetting agent is selected AEO for use; Softening agent is selected DOP for use.
Described 6# solvent for extraction is C
6～C
8Aliphatic hydrocarbon.
The technical scheme that the present invention adopted also comprises a kind of preparation method of environment-friendly solvent type spray glue, comprises the steps:
A. the 6# solvent for extraction that measures, methylal, ritalin input are had in the container of whipping appts, start whipping appts, disperseing to stir after 10 minutes becomes homogeneous mixture solotion;
B. keeping metering input SBS thermoplastic styrene butadiene rubber under the prerequisite that stirs, disperse to stir material 30 minutes;
C. quantitative rosin, staybelite, C 9 petroleum resin, tackifying resin, anti-aging agent, oxidation inhibitor, wetting agent, softening agent interpolation are stirred after finishing;
D. above all materials all drop in the whisking appliance continued stirring and dissolving 5 hours at normal temperatures, after sampling detects all materials and all is dissolved as faint yellow even thick liquid fully, adopt 60 purpose filtering nets that material filtering is finished product.
Wherein, the rotating speed of whipping appts is 600 rev/mins.
Compared with prior art, solvent-borne type spray glue of the present invention has following advantage:
1. do not contain triphen, halocarbon class high toxicity organic solvent in this prescription fully;
2. this prescription has adopted methylal (Methylal(dimethoxymethane)), the ritalin of more ratio to substitute petrochemicals such as 6# solvent oil, 120# solvent oil, 200# solvent oil, triphen, halohydrocarbon; Seldom receive the influence of international petroleum fluctuation; Basically broken away from the serious restriction of international oil price to adhesive industry, with low cost;
3. low VOC high solids content, solid content has improved 5 ~ 8% than tradition spray glue, so the environmental protection index further promotes;
4. the 6# environmentally friendly solvent oil that adopts, to human non-toxic, methylal, ritalin all are the micro-virus kind solvents; Content is lower; Only account for 15 ~ 30% of glue, harmless basically to human body, the environmental protection index is apparently higher than standard GB 18583-2008; Meet the highest at present environmental protection standard HJ/T 220-2005 of country, protection workman and human consumer's physical and mental health;
5. the spraying of this prescription spray glue is very even, and construction economizes glue, and is with low cost;
6. filled a prescription because solvent all is the environmentally friendly solvent that adopts the lower boiling quick-dry type, like 6# solvent oil, methylal, ritalin, boiling point all is lower than 70 ℃; Especially methylal (Methylal(dimethoxymethane)); Just 42.3 ℃ of boiling points, and quick-dry type obviously shortens with respect to the traditional spray glue spray after drying time, general tradition spray glue time of drying is 5 ~ 10 minutes; And spray glue of the present invention is merely 1 ~ 2 minute time of drying, has greatly improved operating efficiency;
7. this prescription is owing to added the high functional agent of import; Like grade environmental protection anti-aging agent, oxidation inhibitor, wetting agent, softening agent; And then make this prescription spray glue than tradition spray glue have more good initial bonding strength, hold viscous force, heat-resisting ageing-resisting performance, pliability etc.; Open hour while are longer, can reach 20 ~ 25 minutes, and bigger construction convenience is provided.
Embodiment
Below in conjunction with embodiment, the present invention is explained further details.
Embodiment A
1. preparation is filled a prescription:
The material name proportioning
Star-shaped sbs thermoplastic styrene butadiene rubber 8
Type SBS thermoplastic styrene butadiene rubber 1
Rosin 6.8
Staybelite 9
C 9 petroleum resin 4
Tackifying resin 6
6# solvent for extraction 17
Methylal 30
Ritalin 15
Wetting agent 0.2
Anti-aging agent 1.0
Oxidation inhibitor 0.5
Softening agent 1.5
Add up to 100.
2
.Preparation technology:
A. the 6# solvent oil that measures, methylal, ritalin input are had in the container of whipping appts, start whipping appts, disperseing to stir after 10 minutes becomes homogeneous mixture solotion;
B. keeping metering input SBS thermoplastic styrene butadiene rubber (comprising star-like and line style) under the prerequisite that stirs, disperse to stir material 30 minutes;
C. then quantitative rosin, staybelite, C 9 petroleum resin, tackifying resin, anti-aging agent, oxidation inhibitor, wetting agent, softening agent interpolation are stirred after finishing;
D. above all materials all drop in the whisking appliance continued stirring and dissolving 5 hours at normal temperatures, after sampling detects all materials and all is dissolved as faint yellow even thick liquid fully, adopt 60 purpose filtering nets that material filtering is finished product.
Wherein, the rotating speed of whipping appts is 600 rev/mins.
3. made resistance test index (test environment: temperature: 25 ℃, humidity: 70%) as shown in table 1:
Table 1
4. the purposes of made finished product:
This environment-friendly solvent type spray glue is applicable to bonding between the materials such as sponge, cloth, EVA, PU pachydermia, corium, PU imitation leather, regenerated bark, timber, metal, stone material, footwear material, and Application Areas is: software furniture industries such as sofa, mattress, case and bag, swivel chair, pillow, screen.
Spraying application behaviour does step:
A. clean material: glued the material surface clean, grease, dust or other impurity must not be arranged;
B. evenly spraying: about 0.5 meter of nozzle distance material surface, evenly walk rifle, evenly spraying;
C. appropriateness hangs: evenly after the spraying, hanging after 1-5 minute can be bonding (with the glue-line toughness but tack-free being as the criterion);
D. bonding pressurization: suitably pressurize when bonding, can make bonding effect better.
Bonding effect: material is destroyed but glue-line is excellent at qualified when firmly tearing with bonded material sample.
Embodiment B
1. preparation is filled a prescription:
The material name proportioning
Star-shaped sbs thermoplastic styrene butadiene rubber 7
Type SBS thermoplastic styrene butadiene rubber 1
Rosin 8
Staybelite 9.5
C 9 petroleum resin 4
Tackifying resin 6
6# solvent for extraction 12
Methylal 35
Ritalin 15
Wetting agent 0.2
Anti-aging agent 0.8
Oxidation inhibitor 0.5
Softening agent 1.0
Add up to 100.
2
.Preparation technology:
A. the 6# solvent oil that measures, methylal, ritalin input are had in the container of whipping appts, start whipping appts, disperseing to stir after 10 minutes becomes homogeneous mixture solotion;
B. keeping metering input SBS thermoplastic styrene butadiene rubber (comprising star-like and line style) under the prerequisite that stirs, disperse to stir material 30 minutes;
C. then quantitative rosin, staybelite, C 9 petroleum resin, tackifying resin, anti-aging agent, oxidation inhibitor, wetting agent, softening agent interpolation are stirred after finishing;
D. above all materials all drop in the whisking appliance continued stirring and dissolving 5 hours at normal temperatures, after sampling detects all materials and all is dissolved as faint yellow even thick liquid fully, adopt 60 purpose filtering nets that material filtering is finished product.
Wherein, the rotating speed of whipping appts is 600 rev/mins.
3. made resistance test index (test environment: temperature: 25 ℃, humidity: 70%) as shown in table 2:
Table 2
4. the purposes of made finished product:
This environment-friendly solvent type spray glue is applicable to bonding between the materials such as sponge, cloth, EVA, PU pachydermia, corium, PU imitation leather, regenerated bark, timber, metal, stone material, footwear material, and Application Areas is: software furniture industries such as sofa, mattress, case and bag, swivel chair, pillow, screen.
Spraying application behaviour does step:
A. clean material: glued the material surface clean, grease, dust or other impurity must not be arranged;
B. evenly spraying: about 0.5 meter of nozzle distance material surface, evenly walk rifle, evenly spraying;
C. appropriateness hangs: evenly after the spraying, hanging after 1-5 minute can be bonding (with the glue-line toughness but tack-free being as the criterion);
D. bonding pressurization: suitably pressurize when bonding, can make bonding effect better.
Bonding effect: material is destroyed but glue-line is excellent at qualified when firmly tearing with bonded material sample.
Embodiment C
1. preparation is filled a prescription:
The material name proportioning
Star-shaped sbs thermoplastic styrene butadiene rubber 7.5
Type SBS thermoplastic styrene butadiene rubber 1.5
Rosin 7.5
Staybelite 10
C 9 petroleum resin 4
Tackifying resin 6
6# solvent for extraction 17
Methylal 30
Ritalin 15
Wetting agent 0.1
Anti-aging agent 0.5
Oxidation inhibitor 0.4
Softening agent 0.5
Add up to 100.
2
.Preparation technology:
A. the 6# solvent oil that measures, methylal, ritalin input are had in the container of whipping appts, start whipping appts, disperseing to stir after 10 minutes becomes homogeneous mixture solotion;
B. keeping metering input SBS thermoplastic styrene butadiene rubber (comprising star-like and line style) under the prerequisite that stirs, disperse to stir material 30 minutes;
C. then quantitative rosin, staybelite, C 9 petroleum resin, tackifying resin, anti-aging agent, oxidation inhibitor, wetting agent, softening agent interpolation are stirred after finishing;
D. above all materials all drop in the whisking appliance continued stirring and dissolving 5 hours at normal temperatures, after sampling detects all materials and all is dissolved as faint yellow even thick liquid fully, adopt 60 purpose filtering nets that material filtering is finished product.
Wherein, the rotating speed of whipping appts is 600 rev/mins.
3. made resistance test index (test environment: temperature: 25 ℃, humidity: 70%) as shown in table 3:
Table 3
4. the purposes of made finished product:
This environment-friendly solvent type spray glue is applicable to bonding between the materials such as sponge, cloth, EVA, PU pachydermia, corium, PU imitation leather, regenerated bark, timber, metal, stone material, footwear material, and Application Areas is: software furniture industries such as sofa, mattress, case and bag, swivel chair, pillow, screen.
Spraying application behaviour does step:
A. clean material: glued the material surface clean, grease, dust or other impurity must not be arranged;
B. evenly spraying: about 0.5 meter of nozzle distance material surface, evenly walk rifle, evenly spraying;
C. appropriateness hangs: evenly after the spraying, hanging after 1-5 minute can be bonding (with the glue-line toughness but tack-free being as the criterion);
D. bonding pressurization: suitably pressurize when bonding, can make bonding effect better.
Bonding effect: material is destroyed but glue-line is excellent at qualified when firmly tearing with bonded material sample.
Among above-mentioned each embodiment:
(SBS is called for short described SBS thermoplastic styrene butadiene rubber: thermoplastic styrene butadiene rubber; Concrete name is called: styrene-butadiene-styrene three block macromolecular copolymer thermoplastic elastomericss) rubber of superfine hub-and-spoke configuration of import and homemade superfine linear structure is selected in collocation for use; Wherein, Hub-and-spoke configuration SBS has outstanding cohesive strength, ageing-resistant performance preferably, and linear structure SBS had both had cohesive strength preferably; Make glue-line have good pliability again, mix and match uses comprehensively both sides' advantage.
Said rosin, staybelite all are select qualities, and softening temperature is higher than 76 ℃.
Said C 9 petroleum resin belongs to industrial first grade, and softening temperature is 120 ℃.
Said tackifying resin is Abietyl modified pentaerythritol ester, and softening temperature is 145 ℃.
Said 6# solvent for extraction is C
6～C
8Aliphatic hydrocarbon, nontoxic fast dried solvent, boiling point is lower than 65 ℃.
Said methylal is a very easily quick dried environment protection solvent of little poison, 42.3 ℃ of boiling points; Described ritalin is little malicious quick dried environment protection solvent, 57.8 ℃ of boiling points.
Described oxidation inhibitor is selected 1010 oxidation inhibitor { chemical name: four ［ β (3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid ］ pentaerythritol ester } environmental protection article for use; Anti-aging agent is selected OPPD anti-aging agent (chemical name: environmental protection article N-secondary octyl-N '-diphenyl-para-phenylene diamine) for use; Wetting agent is selected AEO environmental protection article for use; Softening agent is selected DOP environmental protection article for use.
Claims (9)
1. an environment-friendly solvent type sprays glue, it is characterized in that said spray glue comprises following component in percentage by weight:
SBS thermoplastic styrene butadiene rubber 5 ~ 15%
Rosin 5 ~ 10%
Staybelite 5 ~ 10%
C 9 petroleum resin 2 ~ 6%
Tackifying resin 2 ~ 6%
6# solvent oil 10 ~ 20%
Methylal 25 ~ 40%
Ritalin 10 ~ 20%.
2. environment-friendly solvent type spray glue according to claim 1 is characterized in that, also comprises following component in percentage by weight:
Anti-aging agent 0.5 ~ 1.0%
Oxidation inhibitor 0.3 ~ 0.6%
Wetting agent 0.1 ~ 0.2%
Softening agent 0.5 ~ 1.5%.
3. environment-friendly solvent type spray glue according to claim 2; It is characterized in that: comprise two types of hub-and-spoke configuration and linear structures in the said SBS thermoplastic styrene butadiene rubber; The weight percent that said star-shaped sbs thermoplastic styrene butadiene rubber accounts for said spray glue is 4 ~ 12%, and the weight percent that said type SBS thermoplastic styrene butadiene rubber accounts for spray glue is 1 ~ 3%.
4. environment-friendly solvent type spray glue according to claim 3; It is characterized in that the weight proportion of said spray glue is: star-shaped sbs thermoplastic styrene butadiene rubber 7%, type SBS thermoplastic styrene butadiene rubber 1%, rosin 8%, staybelite 9.5%, C 9 petroleum resin 4%, tackifying resin 6%, 6# solvent for extraction 12%, methylal 35%, ritalin 15%, wetting agent 0.2%, anti-aging agent 0.8%, oxidation inhibitor 0.5%, softening agent 1.0%.
5. according to each described environment-friendly solvent type spray glue of claim 1 to 4, it is characterized in that: described rosin, staybelite all are select qualities, and softening temperature is higher than 76 ℃; Described C 9 petroleum resin belongs to industrial first grade, and softening temperature is 120 ℃; Described tackifying resin is Abietyl modified pentaerythritol ester, is industrial first grade, and softening temperature is 145 ℃.
6. according to claim 2,3 or 4 described environment-friendly solvent type spray glue, it is characterized in that: said anti-aging agent is selected the OPPD anti-aging agent for use; Oxidation inhibitor is selected 1010 oxidation inhibitor for use; Wetting agent is selected AEO for use; Softening agent is selected DOP for use.
7. environment-friendly solvent type spray glue according to claim 1 and 2, it is characterized in that: described 6# solvent for extraction is C
6～C
8Aliphatic hydrocarbon.
8. the preparation method of an environment-friendly solvent type spray glue as claimed in claim 2 is characterized in that this method comprises the steps:
A. the 6# solvent for extraction that measures, methylal, ritalin input are had in the container of whipping appts, start whipping appts, disperseing to stir after 10 minutes becomes homogeneous mixture solotion;
B. keeping metering input SBS thermoplastic styrene butadiene rubber under the prerequisite that stirs, disperse to stir material 30 minutes;
C. quantitative rosin, staybelite, C 9 petroleum resin, tackifying resin, anti-aging agent, oxidation inhibitor, wetting agent, softening agent interpolation are stirred after finishing;
D. above all materials all drop in the whisking appliance continued stirring and dissolving 5 hours at normal temperatures, after sampling detects all materials and all is dissolved as faint yellow even thick liquid fully, adopt 60 purpose filtering nets that material filtering is finished product.
9. the preparation method of environment-friendly solvent type spray glue according to claim 8, it is characterized in that: the rotating speed of whipping appts is 600 rev/mins in the preparation.