CN102775898A - 无溶剂型聚氨酯自流平地坪漆及其制备方法 - Google Patents
无溶剂型聚氨酯自流平地坪漆及其制备方法 Download PDFInfo
- Publication number
- CN102775898A CN102775898A CN2012102911823A CN201210291182A CN102775898A CN 102775898 A CN102775898 A CN 102775898A CN 2012102911823 A CN2012102911823 A CN 2012102911823A CN 201210291182 A CN201210291182 A CN 201210291182A CN 102775898 A CN102775898 A CN 102775898A
- Authority
- CN
- China
- Prior art keywords
- lacquer
- leveling floor
- agent
- gravity flow
- solvent type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种无溶剂型聚氨酯自流平地坪漆，由主漆和固化剂组成，所述主漆中含有油脂多元醇树脂，所述固化剂为HDI、IPDI脂肪族异氰酸酯固化剂。本发明所述无溶剂型聚氨酯自流平地坪漆，采用油脂多元醇树脂，放弃了现有技术的聚醚和聚酯等，提高了产品的疏水性和抗潮气影响的能力，采用耐候性好的油脂多元醇树脂和HDI、IPDI脂肪族异氰酸酯固化剂来做无溶剂型聚氨酯自流平地坪漆，所得产品具有更好的耐磨性、韧性、耐候性等物化性能，同时所得漆膜较丰满，不含有害溶剂，更加环保。同时，本发明还公开了所述无溶剂型聚氨酯自流平地坪漆的制备方法。
Description
技术领域
本发明涉及一种聚氨酯自流平地坪漆及其制备方法，尤其是一种无溶剂型聚氨酯自流平地坪漆及其制备方法。
背景技术
目前，地坪漆产品主要是以环氧地坪漆为主，环氧树脂地坪漆的漆膜硬度高，但韧性不足，并且耐候性不好，制约了地坪漆的使用范围。目前，自流平地坪漆使用的是环氧材料，硬而脆，耐候性差，另外，环氧树脂的化学链上含有苯环，类双酚A结构，由于紫外线照射，苯环容易转化为醌式结构，使得漆膜变黄，有粉化倾向。聚氨酯地坪材料主要是使用溶剂型，溶剂型聚氨酯地坪靠大量溶剂，做薄涂膜，来规避气泡，地坪固含量低，含有害溶剂量大，污染大，漆膜薄，不耐用。
发明内容
本发明的目的在于克服现有技术的不足之处而提供一种具有更好的耐磨性、韧性和耐候性，同时漆膜较丰满，物化性能更全面的无溶剂型聚氨酯自流平地坪漆；同时，本发明还公开一种无溶剂型聚氨酯自流平地坪漆的制备方法。
为实现上述目的，本发明采取的技术方案为：一种无溶剂型聚氨酯自流平地坪漆，由主漆和固化剂组成，所述主漆中含有油脂多元醇树脂，所述固化剂为HDI、IPDI脂肪族异氰酸酯固化剂。
本发明所述无溶剂型聚氨酯自流平地坪漆，采用的油脂多元醇树脂具有非常好的紫外光稳定性，粘度也较低，适合做室内外自流平地坪漆。固化剂采用高耐候的HDI、IPDI脂肪族异氰酸酯固化剂，使得固化后的漆膜具有非常优秀的抗紫外、耐候性。使用时，当主漆和固化剂混合时，发生以下反应：
Primary reaction为无溶剂型聚氨酯自流平地坪的主要化学反应。
Secondary reaction为无溶剂聚氨酯自流平地坪的副反应，也就是和水的反应，这个副反应会产生二氧化碳，会使漆膜容易产生气泡。
所述无溶剂聚氨酯自流平地坪漆重点解决了环氧地坪的硬而脆、易受紫外光影响的问题，使地坪漆适用于更广泛的范围，减缓漆膜在室外的粉化、变色等现象。
作为本发明所述无溶剂型聚氨酯自流平地坪漆的优选实施方式，所述主漆中还含有分散剂、消泡剂、防沉剂、颜料、填料、沸石粉和恶唑烷。所述主漆还含有恶唑烷、沸石粉、消泡剂、分散剂、防沉剂、颜料、填料时，这些助剂的选择的结合，解决了现有技术中容易起气泡、有孔隙等弊病。
作为本发明所述无溶剂型聚氨酯自流平地坪漆的优选实施方式，所述主漆含有以下重量份的组分：
当采用如上所述的组分及质量配比时，所得产品的物化性能更好，同时，采用所述质量配比的恶唑烷、沸石粉、分散剂、消泡剂、防沉剂、颜料、填料等多种助剂搭配，解决了现有技术必须依靠真空反应釜等设备才能解决的脱泡、漆膜容易起泡等问题。
作为本发明所述无溶剂型聚氨酯自流平地坪漆的优选实施方式，使用时，所述主漆与固化剂的重量比为5:1。当所述主漆与固化剂的重量比为5:1时，所得地坪漆的物化性能更加优良，一般地，所述固化剂的含量可以在固化剂总量的10%范围内变化。
作为本发明所述无溶剂型聚氨酯自流平地坪漆的优选实施方式，所述分散剂为聚羧酸类分散剂、聚丙烯酸类分散剂中的至少一种；所述消泡剂为聚丙烯酸类、聚硅氧烷类中的至少一种；所述防沉剂为膨润土、聚酰胺蜡中的至少一种；所述颜料为钛白、铁黄、酞青蓝中的至少一种；所述填料为石英粉、玻璃粉、方解石粉中的至少一种。
同时，本发明还公开一种无溶剂型聚氨酯自流平地坪漆的制备方法，所述方法包括以下步骤：
（1）将油脂多元醇树脂投入釜中，依次将分散剂、消泡剂投入，搅拌均匀；
（2）在搅拌状态下，依次投入沸石粉、恶唑烷、防沉剂、颜料、填料，分散均匀，即得主漆；
（3）使用时，将HDI、IPDI脂肪族异氰酸酯固化剂与主漆混合均匀即可。
作为本发明所述无溶剂型聚氨酯自流平地坪漆的制备方法的优选实施方式，所述主漆中含有以下重量份的组分：
作为本发明所述无溶剂型聚氨酯自流平地坪漆的制备方法的优选实施方式，使用时，所述主漆与固化剂的重量比为5:1。
作为本发明所述无溶剂型聚氨酯自流平地坪漆的制备方法的优选实施方式，所述分散剂为聚羧酸类分散剂、聚丙烯酸类分散剂中的至少一种；所述消泡剂为聚丙烯酸类、聚硅氧烷类中的至少一种；所述防沉剂为膨润土、聚酰胺蜡中的至少一种；所述颜料为钛白、铁黄、酞青蓝中的至少一种；所述填料为石英粉、玻璃粉、方解石粉中的至少一种。
本发明所述无溶剂型聚氨酯自流平地坪漆，采用油脂多元醇树脂，放弃了现有技术的聚醚和聚酯等，提高了产品的疏水性和抗潮气影响的能力，采用耐候性好的油脂多元醇树脂和HDI、IPDI脂肪族异氰酸酯固化剂来做无溶剂型聚氨酯自流平地坪漆，所得产品具有更好的耐磨性、韧性、耐候性等物化性能，同时所得漆膜较丰满，不含有害溶剂，更加环保。
具体实施方式
为更好的说明本发明的目的、技术方案和优点，下面将结合具体实施例对本发明作进一步说明。
实施例1
本发明无溶剂型聚氨酯自流平地坪漆的一种实施例，包含以下重量份的组分：
主漆：
油脂多元醇树脂40份
分散剂：聚羧酸类分散剂0.8份
消泡剂：聚丙烯酸类0.2份
防沉剂：膨润土0.5份
颜料：钛白8份
填料：石英粉20份
沸石粉：3份
恶唑烷：5份。
所述主漆的制备方法包括以下步骤：
（1）将油脂多元醇树脂投入釜中，依次将分散剂、消泡剂投入，搅拌均匀；
（2）在搅拌状态下，依次投入沸石粉、恶唑烷、防沉剂、颜料、填料，分散均匀，即得主漆。
固化剂：HDI三聚体聚合物15.5份。
使用时，将主漆与固化剂混合均匀即可。
本实施例中，所述主漆与固化剂的重量比为5:1。所述油脂多元醇树脂购自科宁化工（中国）有限公司。
实施例2
本发明无溶剂型聚氨酯自流平地坪漆的一种实施例，包含以下重量份的组分：
主漆：
油脂多元醇树脂55份
分散剂：聚丙烯酸类分散剂0.2份
消泡剂：聚硅氧烷类0.4份
防沉剂：聚酰胺蜡0.4份
颜料：铁黄3份
填料：玻璃粉30份
沸石粉：8份
恶唑烷：3份。
所述主漆的制备方法包括以下步骤：
（1）将油脂多元醇树脂投入釜中，依次将分散剂、消泡剂投入，搅拌均匀；
（2）在搅拌状态下，依次投入沸石粉、恶唑烷、防沉剂、颜料、填料，分散均匀，即得主漆。
固化剂：IPDI三聚体聚合物20份。
使用时，将主漆与固化剂混合均匀即可。
本实施例中，所述主漆与固化剂的重量比为5:1。所述油脂多元醇树脂购自科宁化工（中国）有限公司。
实施例3
本发明无溶剂型聚氨酯自流平地坪漆的一种实施例，包含以下重量份的组分：
主漆：
油脂多元醇树脂50份
分散剂：聚羧酸类分散剂0.5份
消泡剂：聚硅氧烷类0.7份
防沉剂：膨润土0.3份、聚酰胺蜡0.5份
颜料：酞青蓝5份
填料：方解石粉25份
沸石粉：6份
恶唑烷：4份。
所述主漆的制备方法包括以下步骤：
（1）将油脂多元醇树脂投入釜中，依次将分散剂、消泡剂投入，搅拌均匀；
（2）在搅拌状态下，依次投入沸石粉、恶唑烷、防沉剂、颜料、填料，分散均匀，即得主漆。
固化剂：IPDI三聚体聚合物18.4份。
使用时，将主漆与固化剂混合均匀即可。
本实施例中，所述主漆与固化剂的重量比为5:1。所述油脂多元醇树脂购自科宁化工（中国）有限公司。
实施例4
本发明无溶剂型聚氨酯自流平地坪漆的一种实施例，包含以下重量份的组分：
主漆：
油脂多元醇树脂45份
分散剂：聚羧酸类分散剂0.1份、聚丙烯酸类分散剂0.1份
消泡剂：聚丙烯酸类0.5份、聚硅氧烷类0.3份
防沉剂：膨润土0.4份、聚酰胺蜡0.6份
颜料：钛白3份、铁黄3份
填料：石英粉8份、玻璃粉20份
沸石粉：5份
恶唑烷：5份。
所述主漆的制备方法包括以下步骤：
（1）将油脂多元醇树脂投入釜中，依次将分散剂、消泡剂投入，搅拌均匀；
（2）在搅拌状态下，依次投入沸石粉、恶唑烷、防沉剂、颜料、填料，分散均匀，即得主漆。
固化剂：IPDI三聚体聚合物18.2份。
使用时，将主漆与固化剂混合均匀即可。
本实施例中，所述主漆与固化剂的重量比为5:1。所述油脂多元醇树脂购自科宁化工（中国）有限公司。
实施例5
采用实施例1-4所述无溶剂型聚氨酯自流平地坪漆作为发明组，采用如下所述的现有产品作为对照组。
现有产品中的一种聚氨酯自流平地坪漆，包含以下重量份的组分：
主漆：
固化剂：MDI聚合物
使用时，主漆：固化剂=5:1（重量比）混合均匀即可。
分别采用发明组和对照组的地坪漆制板，并用同样的方法检测其性能，结果如表1。
表1
由表1可看出，发明组的无溶剂型聚氨酯自流平地坪漆与对照组的聚氨酯地坪漆相比，具有更好的硬度、耐磨性、耐酸碱性和耐候性等物化性能。
最后所应当说明的是，以上实施例仅用以说明本发明的技术方案而非对本发明保护范围的限制，尽管参照较佳实施例对本发明作了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的实质和范围。
Claims (9)
1.一种无溶剂型聚氨酯自流平地坪漆，其特征在于，由主漆和固化剂组成，所述主漆中含有油脂多元醇树脂，所述固化剂为HDI、IPDI脂肪族异氰酸酯固化剂。
2.如权利要求1所述的无溶剂型聚氨酯自流平地坪漆，其特征在于，所述主漆中还含有分散剂、消泡剂、防沉剂、颜料、填料、沸石粉和恶唑烷。
3.如权利要求2所述的无溶剂型聚氨酯自流平地坪漆，其特征在于，所述主漆含有以下重量份的组分：
4.如权利要求1所述的无溶剂型聚氨酯自流平地坪漆，其特征在于，使用时，所述主漆与固化剂的重量比为5:1。
5.如权利要求2或3所述的无溶剂型聚氨酯自流平地坪漆，其特征在于，所述分散剂为聚羧酸类分散剂、聚丙烯酸类分散剂中的至少一种；所述消泡剂为聚丙烯酸类、聚硅氧烷类中的至少一种；所述防沉剂为膨润土、聚酰胺蜡中的至少一种；所述颜料为钛白、铁黄、酞青蓝中的至少一种；所述填料为石英粉、玻璃粉、方解石粉中的至少一种。
6.一种无溶剂型聚氨酯自流平地坪漆的制备方法，其特征在于，包括以下步骤：
（1）将油脂多元醇树脂投入釜中，依次将分散剂、消泡剂投入，搅拌均匀；
（2）在搅拌状态下，依次投入沸石粉、恶唑烷、防沉剂、颜料、填料，分散均匀，即得主漆；
（3）使用时，将HDI、IPDI脂肪族异氰酸酯固化剂与主漆混合均匀即可。
7.如权利要求6所述的无溶剂型聚氨酯自流平地坪漆的制备方法，其特征在于，所述主漆中含有以下重量份的组分：
8.如权利要求6所述的无溶剂型聚氨酯自流平地坪漆的制备方法，其特征在于，使用时，所述主漆与固化剂的重量比为5:1。
9.如权利要求6所述的无溶剂型聚氨酯自流平地坪漆的制备方法，其特征在于，所述分散剂为聚羧酸类分散剂、聚丙烯酸类分散剂中的至少一种；所述消泡剂为聚丙烯酸类、聚硅氧烷类中的至少一种；所述防沉剂为膨润土、聚酰胺蜡中的至少一种；所述颜料为钛白、铁黄、酞青蓝中的至少一种；所述填料为石英粉、玻璃粉、方解石粉中的至少一种。