CN102775653A - 一种柔软避孕套的制备方法 - Google Patents
一种柔软避孕套的制备方法 Download PDFInfo
- Publication number
- CN102775653A CN102775653A CN2012102530200A CN201210253020A CN102775653A CN 102775653 A CN102775653 A CN 102775653A CN 2012102530200 A CN2012102530200 A CN 2012102530200A CN 201210253020 A CN201210253020 A CN 201210253020A CN 102775653 A CN102775653 A CN 102775653A
- Authority
- CN
- China
- Prior art keywords
- latex
- condoms
- raw material
- vultex
- polyisoprene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种柔软避孕套的生产方法,原料中的主要成分采用天然胶乳和聚异戊二烯混合而成,适当调整传统生产工艺,使二者具有很好的相容性,且制品性能上能够取长补短,能使避孕套变得柔软、舒适,比单纯使用聚异戊二烯胶乳的避孕套耐老化性能提高,并能保证较高的爆破性能,胶乳在加工过程中机械稳定性较高。蛋白质含量比单纯使用天然胶乳的避孕套进一步下降。
Description
技术领域
本发明涉及一种避孕套的生产方法,即柔软避孕套的制备方法。
背景技术
现在市售的胶乳橡胶避孕套一般都是天然橡胶薄膜制品,主要用于防止性疾病的传播和避孕,随着国内外市场需求,消费者对避孕套产品的要求不断提高,除了避孕套的安全性能外,消费者对于产品内在的质量如使用的舒适性即产品的柔软性和蛋白质含量等均有较高要求,对消费者来说舒适和良好的感觉并且无刺激和过敏是最重要的,纯天然胶乳的性质受生胶乳收割时间和胶乳产地影响较大,工艺控制波动较大,纯天然胶乳含有蛋白质成分,个别人群对于天然橡胶所含的蛋白质过敏,造成纯天然胶乳避孕套的使用受到限制。近年来天然胶乳的替代材料一直是各厂家研究的热点,人工合成的聚异戊二烯胶乳以其与天然胶乳极其相似的分子组成和材料性质,成为了首选的代替材料。但是,纯聚异戊二烯胶乳避孕套的爆破压力和耐老化性较纯天然胶乳避孕套低,胶乳预硫化进程较慢。
发明内容
本发明的目的是提供一种产品质量稳定、爆破压力大、耐老化的柔软避孕套的制备方法,使生产过程和产品质量集合纯天然胶乳和人工合成聚异戊二烯胶乳两者的优点,克服其各自单独使用的不足。
为达到上述目的,本发明采用如下的技术方案:
本发明所述柔软避孕套的制备方法,包括如下步骤:
A) 原材料配比,选取干态原料的重量份数比如下:
硫磺1.00-1.50份、氧化锌0.60-0.90份、二乙基二硫代氨基甲酸锌0.70-0.90份、2,6-二叔丁基-4-甲基苯酚0.80-1.10份、氢氧化钾0.03-0.07份、脂肪醇聚氧乙烯(20)醚0.20-0.30份、六偏磷酸钠0.04-0.08份、亚甲基二萘磺酸钠0.09-0.15份、天然胶乳45—90份、合成异戊二烯胶乳10—50份;分别将前述各干态原料加入去离子水配制成质量浓度如下的原料水溶液或分散液:天然胶乳 60%、聚异戊二烯胶乳 50%、硫磺 50%、氧化锌 50%、二乙基二硫代氨基甲酸锌 50%、2,6-二叔丁基-4-甲基苯酚 40%、氢氧化钾 25%、脂肪醇聚氧乙烯(20)醚 20%、六偏磷酸钠 20%、亚甲基二萘磺酸钠 10%;
B)硫化:将上述原料水溶液或分散液全部注入硫化罐中,边搅拌边加入去离子水,使硫化罐中的硫化胶乳的总固体浓度为53%—60%;启动硫化罐加温,升温至60℃-65℃开始保温;在保温的过程中,取样测溶胀系数,当溶胀系数达到2.5-2.4时,停止保温,打开硫化罐的冷却系统,对硫化胶乳降温,当硫化胶乳的温度降至45-40℃时关闭冷却系统;
C)将停放12小时以上的胶乳进行离心处理;离心处理后停放96-144小时输送至下序机台停放罐,
D) 浸渍使用,调总固体和PH值后浸渍使用。
采用上述技术方案后,因为相似的分子组成使得天然胶乳和聚异戊二烯胶乳二者相容性较好,且制品性能上能够取长补短,能使避孕套变得柔软、舒适,比单纯使用合成胶乳的耐老化性能提高,并能保证较高的爆破性能,胶乳在加工过程中机械稳定性较高。蛋白质含量比单纯使用天然胶乳的避孕套进一步下降。
具体实施方式
实施例1:
本发明所述的柔软避孕套的制备方法,包括依次进行的如下步骤:
A) 原材料配比,选取干态原料的重量份数比如下:
硫磺1.00份、氧化锌0.60份、二乙基二硫代氨基甲酸锌0.70份、2,6-二叔丁基-4-甲基苯酚0.80份、氢氧化钾0.03份、脂肪醇聚氧乙烯(20)醚0.20份、六偏磷酸钠0.04份、亚甲基二萘磺酸钠0.09份、天然胶乳60份、聚异戊二烯胶乳40份;分别将前述各干态原料加入去离子水配制成质量浓度如下的原料水溶液或分散液:天然胶乳 60%、异戊二烯胶乳-50%、硫磺 50%、氧化锌 50%、二乙基二硫代氨基甲酸锌 50%、2,6-二叔丁基-4-甲基苯酚 40%、氢氧化钾 25%、脂肪醇聚氧乙烯(20)醚 20%、六偏磷酸钠 20%、亚甲基二萘磺酸钠 10%;
B)硫化:将上述原料水溶液或分散液全部注入硫化罐中,边搅拌边加入去离子水,使硫化罐中的硫化胶乳的总固体浓度等于或略高于53%;启动硫化罐加温,升温至60℃开始保温;在保温的过程中,取样测溶胀系数,当溶胀系数达到2.5-2.4时,停止保温,打开硫化罐的冷却系统,对硫化胶乳降温,当硫化胶乳的温度降至45℃时关闭冷却系统;此时化验指标,应达到总固体≥53%、PH值≥10.5。
C)将停放12小时以上的胶乳进行离心处理;离心处理后停放96小时输送至下序机台停放罐,
D) 浸渍使用,将停放罐中的原料放出,通过加入去离子水调整总固体浓度和加入氨水调整PH值后浸渍使用。总固体浓度和PH值的指标与普通避孕套生产中的浸渍过程中对原料的指标要求一样。
采用本实施例生产的混合胶乳避孕套与纯天然胶乳避孕套和纯异戊二烯胶乳避孕套性能比较如下表:
不同胶乳品种避孕套 | 老化前平均爆破压力(kPa) | 老化前平均爆破体积(L) | 老化后平均爆破压力(kPa) | 老化后平均爆破体积(L) |
天然胶乳 | 1.95 | 40.0 | 1.75 | 35 |
聚异戊二烯胶乳 | 1.20 | 68.0 | 0.95 | 50.0 |
混合胶乳 | 1.90 | 55.0 | 1.70 | 50.0 |
老化条件:70℃×7天。
由上表中可以看出,本发明主要利用纯异戊二烯胶乳和天然胶乳混合来提高避孕套产品的品质,混合胶乳避孕套老化前的爆破体积比纯天然胶乳避孕套的要大大提高,从而制品的柔软性能提高,而爆破压力又比单纯使用聚异戊二烯胶乳避孕套大幅提高,老化后产品性能又能保持较高的水平,从而使产品满足国际标准的要求及消费者的使用舒适性的需求。
实施例2:
同实施例1,在步骤A,所述干态原料的重量份数比如下
硫磺1.50份、氧化锌0.90份、二乙基二硫代氨基甲酸锌0.90份、2,6-二叔丁基-4-甲基苯酚1.10份、氢氧化钾0.07份、脂肪醇聚氧乙烯(20)醚0.30份、六偏磷酸钠0.08份、亚甲基二萘磺酸钠0.15份、天然胶乳90份、聚异戊二烯胶乳10份。
实施例3:
同实施例1,在步骤A,所述干态原料的重量份数比如下
硫磺1.20份、氧化锌0.80份、二乙基二硫代氨基甲酸锌0.80份、2,6-二叔丁基-4-甲基苯酚1.00份、氢氧化钾0.05份、脂肪醇聚氧乙烯(20)醚0.25份、六偏磷酸钠0.06份、亚甲基二萘磺酸钠0.10份、天然胶乳70份、聚异戊二烯胶乳30份。
Claims (1)
1.一种柔软避孕套的制备方法,其特征在于包括如下步骤:
A) 原材料配比,选取干态原料的重量份数比如下:
硫磺1.00-1.50份、氧化锌0.60-0.90份、二乙基二硫代氨基甲酸锌0.70-0.90份、2,6-二叔丁基-4-甲基苯酚0.80-1.10份、氢氧化钾0.03-0.07份、脂肪醇聚氧乙烯(20)醚0.20-0.30份、六偏磷酸钠0.04-0.08份、亚甲基二萘磺酸钠0.09-0.15份、天然胶乳60—90份、合成异戊二烯胶乳10—40份;分别将前述各干态原料加入去离子水配制成质量浓度如下的原料水溶液或分散液:天然胶乳 60%、聚异戊二烯胶乳 50%、硫磺 50%、氧化锌 50%、二乙基二硫代氨基甲酸锌 50%、2,6-二叔丁基-4-甲基苯酚 40%、氢氧化钾 25%、脂肪醇聚氧乙烯(20)醚 20%、六偏磷酸钠 20%、亚甲基二萘磺酸钠 10%;
B)硫化:将上述原料水溶液或分散液全部注入硫化罐中,边搅拌边加入去离子水,使硫化罐中的硫化胶乳的总固体浓度为53%—60%;启动硫化罐加温,升温至60℃-65℃开始保温;在保温的过程中,取样测溶胀系数,当溶胀系数达到2.5-2.4时,停止保温,打开硫化罐的冷却系统,对硫化胶乳降温,当硫化胶乳的温度降至45-40℃时关闭冷却系统;
C)将停放12小时以上的胶乳进行离心处理;离心处理后停放96-144小时输送至下序机台停放罐;
D) 浸渍使用,将停放罐中的原料放出,调总固体和PH值后浸渍使用。