CN102766782A - 一种环保锌合金 - Google Patents
一种环保锌合金 Download PDFInfo
- Publication number
- CN102766782A CN102766782A CN2012102659495A CN201210265949A CN102766782A CN 102766782 A CN102766782 A CN 102766782A CN 2012102659495 A CN2012102659495 A CN 2012102659495A CN 201210265949 A CN201210265949 A CN 201210265949A CN 102766782 A CN102766782 A CN 102766782A
- Authority
- CN
- China
- Prior art keywords
- content
- zinc alloy
- environmental protection
- environment
- protection zinc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提出了一种环保锌合金,包含有含量为3.9%~4.3%的铝,0.03%~0.06%的镁,余量为锌及其他杂质,其中铜的含量不大于0.03%,铁的含量不大于0.03%,铅的含量不大于0.003%,镉的含量不大于0.003%,锡的含量不大于0.001%,以上含量指质量百分比,所述环保锌合金通过达到上述标准,符合欧盟的RoHS指标,减少了对环境与人体的危害,节约了资源。
Description
技术领域
本发明涉及合金压铸领域,特别是指一种环保锌合金。
背景技术
合金是由两种或者两种以上的金属(或金属与非金属)熔合而成的具有金属特性的物质,合金的生成常会改善元素单质的性质,从而得到性能更好的物质,环保锌合金是以锌为基加入其它元素组成的合金,常加的合金元素有铝、铜、镁、镉、铅、钛等,锌合金具有熔点低,流动性好,易熔焊和塑性加工等,被广泛应用,当今锌合金压铸市场上,出现各种各样牌号环保锌合金,由于厂家非标生产,市场名称混乱,以次充好,由于用户不懂材料性能,往往在使用过程中,经常出现不合格品,同时由于市场没有一个统一的标准,生产出来的各种锌合金中有害杂质的含量过高,造成锌合金的晶间腐蚀变的非常敏感,降低机械性能,电镀气泡等诸多影响,同时,由这些有害杂质制成的设备也会对人体健康产生影响。
RoHS(关于限制在电子电器设备中使用某些有害成分的指令)是由欧盟立法制定的一项强制性标准,主要用于规范电子电气产品的材料及其工艺标准,使之更加有利于人体健康和环境保护,不合格的锌合金产品,基本都不符合RoHS标准,这些造成了严重经济损失,能燃资源重复浪费,同时也对人体健康带来危害等。
发明内容
本发明提出一种环保锌合金,解决了现有技术中由于有害杂质含量过高引起的锌合金材质整体下降,以及危害人体健康,造成环境污染等问题。
本发明的技术方案是这样实现的:一种环保锌合金,包含有含量为3.9%~4.3%的铝,0.03%~0.06%的镁,余量为锌及其他杂质,其中铜的含量不大于0.03%,铁的含量不大于0.03%,铅的含量不大于0.003%,镉的含量不大于0.003%,锡的含量不大于0.001%,以上含量指质量百分比。
进一步,所述环保锌合金在制备时溶液温度控制在390℃~410℃。
进一步,所述环保锌合金中还含有使所述环保锌合金增加密度和加强流动性的锌合金变质剂。
本发明的有益效果为:通过控制所述环保锌合金中杂质的含量在一个很低的水平,符合欧盟RoHS标准,一方面可以减少所述环保锌合金的晶间腐蚀,增加其机械性能,另一方面还减少了对人体与环境的危害,同时,控制所述环保锌合金在制备时溶液温度控制在390℃~410℃可以防止所述铝和所述镁的过度氧化,而所述锌合金变质剂的加入可以增加所述环保锌合金的密度以及加强流动性,在成品上则是表面更加光亮。
具体实施方式
为更好地理解本发明,下面通过一个实施例对本发明作进一步具体的阐述,但不可理解为对本发明的限定,对于本领域的技术人员根据上述发明内容所作的一些非本质的改进与调整,也视为落在本发明的保护范围内。
根据本发明规定的各金属的含量范围,我们得到以下实施例:
实施例1
环保锌合金中各元素的含量为:
锌:95.9%,铝:3.97%,镁:0.041%,铜:0.012%,铁:0.018%,铅:0.0024%,镉:0.0004%,锡:小于0.0004%,铟:小于0.0002%,锑:0.001%,铬:0.0006%,锰:小于0.0003%,镍:0.0053%,银:0.0001%。
实施例2
环保锌合金中各元素的含量为:
锌:95.65%,铝:4.21%,镁:0.052%,铜:0.015%,铁:0.022%,铅:0.0021%,镉:0.0008%,锡:小于0.0003%,铟:小于0.0002%,锑:0.001%,铬:0.0003%,锰:小于0.0003%,镍:0.0046%,银:0.0002%。
以下是RoHS中对六种有害物规定的上限浓度:
镉:小于100ppm,
铅:小于1000ppm,
钢合金中小于3500ppm,
铝合金中小于4000ppm,
铜合金中小于40000ppm,
汞:小于1000ppm,
六价铬:小于1000ppm。
实施例1实施例2的环保锌合金中有害元素的含量范围均小于上述的RoHS中规定的上限值,即以上含量范围符合RoHS标准,所以本发明的产品属于绿色环保产品,其在材质上具有较高的品质,同时也对人体的危害降至最低。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (3)
1.一种环保锌合金,其特征在于:包含有含量为3.9%~4.3%的铝,0.03%~0.06%的镁,余量为锌及其他杂质,其中铜的含量不大于0.03%,铁的含量不大于0.03%,铅的含量不大于0.003%,镉的含量不大于0.003%,锡的含量不大于0.001%,以上含量指质量百分比。
2.如权利要求1中所述的环保锌合金,其特征在于:所述环保锌合金在制备时溶液温度控制在390℃~410℃。
3.如权利要求2中所述的环保锌合金,其特征在于:所述环保锌合金中还含有使所述环保锌合金增加密度和加强流动性的锌合金变质剂。