CN102766315A - 一种聚甲醛改性料 - Google Patents
一种聚甲醛改性料 Download PDFInfo
- Publication number
- CN102766315A CN102766315A CN2012102260095A CN201210226009A CN102766315A CN 102766315 A CN102766315 A CN 102766315A CN 2012102260095 A CN2012102260095 A CN 2012102260095A CN 201210226009 A CN201210226009 A CN 201210226009A CN 102766315 A CN102766315 A CN 102766315A
- Authority
- CN
- China
- Prior art keywords
- polyoxymethylene
- polyformaldehyde
- modified material
- percent
- azotic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚甲醛改性料,它是由聚甲醛和占聚甲醛质量百分比如下组成构成:含氮类化合物稳定剂0.1~0.2%,抗氧化剂112,0.2~0.8%,滑石粉0.1~0.4%,三聚氰胺1~2%。本发明采用的配方科学,添加的含氮类化合物稳定剂、三聚氰胺,对聚甲醛的力学性能进行了改善,使聚甲醛尽量减少分解,提高产量;而且由于抗氧化剂、滑石粉的加入,使得聚甲醛力学性能、化学稳定性能提高,降低了生产成本。
Description
技术领域
本发明涉及一种改性料的技术领域,具体涉及一种聚甲醛改性料。
背景技术
聚甲醛(Polyformaldehyde,简写POM)是一种没有侧链,高密度,高结晶的热塑性工程塑料,具有优异的机械性能,突出的自润性、耐磨性和耐化学药品性,刚性大,耐蠕变性和疲劳性好,并能在较宽的温度范围内保持其所具有的力学、化学和电性能,是工程塑料中最接近金属的品种之一,可用来代替铝、锌等有色金属及合金制品。聚甲醛可采用注射、吹塑、挤压成型和螺旋铸造成型等方法进行加工,被广泛用于汽车工业、电子电气、家用电器、精密仪器和建材等行业。随现代塑料工业的高速发展,全世界的POM产品消费需求量迅速增长,已成为当今世界的一种极为重要的工程塑料之一。
但是聚甲醛的冲击韧性低、缺口敏感性差、加工过程中易分解等缺点极大的限制了其在各领域特别是高档产品领域中的应用,因此改善聚甲醛在加工过程中的分解就显得十分重要。
发明内容
发明目的: 本发明的目的是为了弥补现有技术的不足,提供一种聚甲醛改性料,使聚甲醛在加工过程中尽量减少分解。
技术方案:一种聚甲醛改性料,其特征在于:它是由聚甲醛和占聚甲醛质量百分比的如下组分构成:
含氮类化合物稳定剂 0.1~0.2%,
抗氧化剂112 0.2~0.8%,
滑石粉 0.1~0.4%,
三聚氰胺 1~2%。
有益效果:本发明采用的配方科学,添加的含氮类化合物稳定剂、三聚氰胺,对聚甲醛的力学性能进行了改善,使聚甲醛尽量减少分解,提高产量;而且由于抗氧化剂、滑石粉的加入,使得聚甲醛力学性能、化学稳定性能提高,降低了生产成本。
具体实施方式
下面结合具体实施例对本发明作进一步说明:
实施例1:
一种聚甲醛改性料,由聚甲醛和占聚甲醛质量百分比的如下组分构成:含氮类化合物稳定剂 0.1%,抗氧化剂112,0.2%,滑石粉0.1%,三聚氰胺1%。
将上述材料加入高速混合机中混合,采用双螺杆挤出机熔融混合,挤出造粒,其中螺杆转速由12转/分逐渐升至90转/分,螺杆料筒温度由160℃升至250℃,控制在235℃并保持,然后测试聚甲醛改性料的性能。
实施例2:
一种聚甲醛改性料,由聚甲醛和占聚甲醛质量百分比的如下组分构成:含氮类化合物稳定剂 0.2%,抗氧化剂112,0.8%,滑石粉0.4%,三聚氰胺2%。
将上述材料加入高速混合机中混合,采用双螺杆挤出机熔融混合,挤出造粒,其中螺杆转速由12转/分逐渐升至90转/分,螺杆料筒温度由160℃升至250℃,控制在235℃并保持,然后测试聚甲醛改性料的性能。
实施例3:
一种聚甲醛改性料,由聚甲醛和占聚甲醛质量百分比的如下组分构成:含氮类化合物稳定剂 0.15%,抗氧化剂112,0.5%,滑石粉0.25%,三聚氰胺1.5%。
将上述材料加入高速混合机中混合,采用双螺杆挤出机熔融混合,挤出造粒,其中螺杆转速由12转/分逐渐升至90转/分,螺杆料筒温度由160℃升至250℃,控制在235℃并保持,然后测试聚甲醛改性料的性能。
Claims (2)
1.一种聚甲醛改性料,其特征在于:它是由聚甲醛和占聚甲醛质量百分比的如下组分构成:
含氮类化合物稳定剂 0.1~0.2%,
抗氧化剂112 0.2~0.8%,
滑石粉 0.1~0.4%,
三聚氰胺 1~2%。
2.根据权利要求1所述的一种聚甲醛改性料,其特征在于:所述稳定剂包括尿素、酰胺、聚胺。